• Journal of the Korea Concrete Institute
• /
• v.19 no.4
• /
• pp.433-439
• /
• 2007

The main objective of the paper is to investigate the static behavior of a prestressed concrete (PSC) girder that has been spliced with precast box segments. A 20 m long full-scale spliced PSC girder is fabricated and tested to compare its static performance against a monolithic girder. The monolithic girder has the same geometric and material properties with respect to the spliced girder. This includes infernal strain, deflections, neutral axis position, and crack patterns for both girders. The test also consists of monitoring relative displacements occurring across the joints. Both the horizontal displacement (gap) and vertical displacement (sliding) are measured throughout the loading procedure. All results have been compared to those obtained from the monolithic girder. It has been demonstrated that the spliced girder offers close behavior with respect to the monolithic girder up to the crack load. Both girders exhibits ductile flexural failure rather than abrupt shear failure at joints.

• Journal of the Korea Concrete Institute
• /
• v.20 no.3
• /
• pp.325-333
• /
• 2008

This study evaluated the mechanical performance, shrinkage crack and fire resistance of hybrid fiber (blended steel and polypropylene fiber with different diameter and length) reinforced concrete at elevated temperature. The compressive, splitting tensile, flexural, plastic shrinkage test were conducted to the evaluate the mechanical properties and the resistance of shrinkage crack. Also, the surface investigation, reduction rate of mass and residual compressive test were performed to evaluate the physical and mechanical properties after 400$^{\circ}C$, 600$^{\circ}C$, 800$^{\circ}C$ and 1,200$^{\circ}C$ exposure. Test results showed that the hybrid fiber reinforced concrete improved the mechanical performance, shrinkage crack and fire resistance. The reduction of performance with a temperature change were high at the temperature of $600\sim800^{\circ}C$.

• Journal of the Korea Concrete Institute
• /
• v.25 no.1
• /
• pp.81-90
• /
• 2013

The purpose of this study is to evaluate the horizontal shear strength on the interface between PC and cast-in-place concrete for PC composite beams. Six specimens were tested to examine the structural performance of the horizontal interface with different surface condition and stirrup detailing. Except for SF-291B specimen failed in flexural compression, strengths and deformation capacities of five specimens were determined by horizontal shear failure. Horizontal shear strengths by composite horizontal shear or shear friction in current codes could be used to predict the horizontal shear capacity of the interface for specimens. Also detailing for stirrup by PCI design provision could be used to accomplish the composite action in the interface.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.5 no.4
• /
• pp.366-374
• /
• 2017

This study investigates enzyme stabilization in clay-rock bricks through mechanical tests and image processing. Appropriate soil mixtures were designed using clay/crushed rock with ratios of 70/30, 60/40, 50/50, 40/60, and 30/70 by weight to verify the strength of the enzyme brick and soil compaction. The maximum compressive and flexural strengths in the 60/40 ratio mixture were found to be 5MPa and 1.25MPa, respectively; however, the maximum dry unit weight of $2.073g/cm^3$ was found in the 50/50 clay/gravel ratio mixture. Generally, the strength of the enzyme brick was improved by 27%. The paper concludes that in order to achieve optimal strength, soils should be mixed with the 60/40 clay/gravel ratio, which provides an adequate strength, while 50/50 ratio should be used for achieving more compaction. The SEM-EDX observation and Matlab image processing verified how the bond structure appeared after enzyme stabilization. It was found that enzymes created bond with the clay soil and the crushed rock for rendering strength and stability.

• Composites Research
• /
• v.29 no.4
• /
• pp.223-229
• /
• 2016

SiC nanoparticles were used to increase flexural properties of polymer matrix. This study was to manufacture huge concentration SiC nanoparticle/epoxy composites and to evaluate the dispersion. During mixing SiC nanoparticle and epoxy, 20 wt% SiC nanoparticle in total composites was used with both stirrer and sonication equipment together. Mixing speed and dispersion were improved with the method by using both stirrer and sonication equipment at the same time via mechanical test and FE-SEM. Based on the results, modeling of SiC nanoparticle dispersion could be established. Ultimately, unidirectional carbon fiber reinforced composites was manufactured using 20 wt% SiC nanoparticle/epoxy. Mechanical property of CFRP using dual stirrer and sonication mixing method was better than composites by single sonication mixing method.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.31 no.1A
• /
• pp.35-41
• /
• 2011

In concrete structural design provisons, two methods are normally provided to control deflection; direct method and indirect method. It is more efficient to use the indirect deflection control by which the span/depth ratio is limited not to exceed an allowable deflection limit. Because actual deflections are affected by many causes, it is complicated to evaluate actual deflections. In this study, limit span/depth ratios are derived from the deflection calculated directly at the serviceability limit state in RC members. The deflection is obtained from using average curvature, which depends on materials model used. The main variables examined are tension stiffening effect, concrete strength, cross section size and compressive steel ratio. It could be appeared that more analytical consistency is secured to use the 2nd order form of tension stiffening effect. And the limit span/depth ratio is dependent on material strength, tensile and compressive steel ratio but it is independent on cross-section size.

• Composites Research
• /
• v.29 no.5
• /
• pp.293-298
• /
• 2016

In this paper, Glass Fiber Reinforced Thermoplastic (GFRTP) for automotive headlight source module was fabricated by compounding and injection molding using PPS (Poly Phenylene Sulfide) resin with glass fiber which has three cross section (round type, cocoon type, flat type). Tensile, flexural, impact properties were investigated on effect of cross section, glass fiber contents. And it was observed flatness, dimensional stability, fluidity depending on glass fiber cross section. As a result, flat glass fiber reinforced thermoplastic's mechanical properties were most excellent. Also, dimensional stability and flatness showed better results when using flat glass fiber.

• Journal of Power System Engineering
• /
• v.15 no.6
• /
• pp.67-72
• /
• 2011

In the present study, crack healing effect and residual stress of $Al_2O_3$ ceramics were investigated by changing the sintering temperature and heat treatment conditions. And also it was investigated that the influence of different filler loadings of nano-sized SiC particles on the crack healing behavior of $Al_2O_3$ ceramics. The test samples were characterized by three point bend flexural tests to evaluate their mechanical properties. The morphological changes were studied by FE-SEM and EDS. The test results indicated that the $Al_2O_3$ with nano-sized SiC ceramics sintered at $1800^{\circ}C$ were showed highest density. Sintering temperature at $1800^{\circ}C$, the bending strength of heat treatment in air atmosphere specimens showed about 42 % increment in comparison to the un-heat treated specimens. The cracked specimens can be healed by heat treatment in vacuum atmosphere but the crack healing effect of $Al_2O_3$ ceramics, which is heat treated in air atmosphere was higher than that of heat treated in vacuum atmosphere. $Al_2O_3$ with 30 wt% of SiC ceramics indicated higher crack healing ability than that with 15 wt% of SiC ceramics. The FE-SEM images showed that the median cracks and pores were disappeared after heat treatment in air.

• Computers and Concrete
• /
• v.14 no.3
• /
• pp.211-231
• /
• 2014

Prestressed hollow-core slabs (HCS) are widely used for modern lightweight precast floor structures because they are cost-efficient by reducing materials, and have excellent flexural strength and stiffness by using prestressing tendons, compared to reinforced concrete (RC) floor system. According to the recently revised ACI318-08, the web-shear capacity of HCS members exceeding 315 mm in depth without the minimum shear reinforcement should be reduced by half. It is, however, difficult to provide shear reinforcement in HCS members produced by the extrusion method due to their unique concrete casting methods, and thus, their shear design is significantly affected by the minimum shear reinforcement provision in ACI318-08. In this study, a large number of shear test data on HCS members has been collected and analyzed to examine their web-shear capacity with consideration on the minimum shear reinforcement requirement in ACI318-08. The analysis results indicates that the minimum shear reinforcement requirement for deep HCS members are too severe, and that the web-shear strength equation in ACI318-08 does not provide good estimation of shear strengths for HCS members. Thus, in this paper, a rational web-shear strength equation for HCS members was derived in a simple manner, which provides a consistent margin of safety on shear strength for the HCS members up to 500 mm deep. More shear test data would be required to apply the proposed shear strength equation for the HCS members over 500 mm in depth though.

• Computers and Concrete
• /
• v.14 no.3
• /
• pp.299-313
• /
• 2014

Effects of polypropylene (PP) fibers, steel fibers (SF) and hybrid on the properties of highstrength fiber reinforced self-consolidating concrete (HSFR-SCC) under different volume contents are investigated in this study. Comprehensive laboratory tests were conducted in order to evaluate both fresh and hardened properties of HSFR-SCC. Test results indicated that the fiber types and fiber contents greatly influenced concrete workability but it is possible to achieve self consolidating properties while adding the fiber types in concrete mixtures. Compressive strength, dynamic modulus of elasticity, and rigidity of concrete were affected by the addition as well as volume fraction of PP fibers. However, the properties of concrete were improved by the incorporation of SF. Splitting tensile and flexural strengths of concrete became increasingly less influenced by the inclusion of PP fibers and increasingly more influenced by the addition of SF. Besides, the inclusion of PP fibers resulted in the better efficiency in the improvement of toughness than SF. Furthermore, the inclusion of fibers did not have significant effect on the durability of the concrete. Results of electrical resistivity, chloride ion penetration and ultrasonic pulse velocity tests confirmed that HSFR-SCC had enough endurance against deterioration, lower chloride ion penetrability and minimum reinforcement corrosion rate.