• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2002년도 춘계 학술발표강연 및 논문개요집
• /
• pp.148-148
• /
• 2002

• 한국입자에어로졸학회지
• /
• 제12권2호
• /
• pp.37-42
• /
• 2016

$CeO_2$ nanoparticles were prepared by a flame spray pyrolysis from aqueous solution of cerium nitrate. The morphology, structure crystallinity and specific surface area of as-prepared nanoparticles were characterized by transmission electron microscopy (TEM), X-ray diffraction (XRD), and Brunauer-Emmett-Telle (BET). The $CeO_2$ nanoparticles about 5 nm in diameter showed a cubic fluorite structure and polyhedral morphology. The average particle size increased as the cerium nitrate concentration increased. UV absorption performance of the as-prepared nanoparticles was measured by UV-visible spectroscopy. UV absorption of $CeO_2$ nanoparticles was more effective than that of commercial $TiO_2$ nanoparticles. Effect of dopants such as Ti and Zn to $CeO_2$ nanoparticles on UV absorption properties was also investigated. In case of $Ti/CeO_2$, and $Zn/CeO_2$ nanoparticles, they showed a little higher UV absorption values compared with $CeO_2$ nanoparticles. The as-prepared nanoparticles can be promising materials with high UV absorption value.

• 한국세라믹학회:학술대회논문집
• /
• 한국세라믹학회 2000년도 추계총회,초청강연,특별강연,연구발표회
• /
• pp.58.1-58
• /
• 2000

• 한국입자에어로졸학회지
• /
• 제6권1호
• /
• pp.29-35
• /
• 2010

Transition metals such as V, Fe, and Ni were used to synthesize doped zinc oxide nanoparticles from mixed liquid precursors by using the flame spray pyrolysis (FSP). The effects of dopants on the powder properties such as morphology, specific surface area, crystal structure, and light adsorption were analyzed by TEM, BET, XRD, and UV-Vis diffuse reflection spectrum (DRS), respectively. The results showed that hexagonal wurtzite structured ZnO:M (M = V, Fe, Ni) nanoparticles were successfully synthesized by the FSP. The transition metal-doping resulted in the decrease in its particle size and crystallite size. The UV-vis absorption spectra of ZnO:M nanoparticles were also red-shifted. ZnO:V showed the highest MB degradation of 99.4% under the UV irradiation after 3 hrs.

• 한국입자에어로졸학회지
• /
• 제8권2호
• /
• pp.69-74
• /
• 2012

This study describes how successfully a conventional flame aerosol synthesis was used to continuously synthesize Pt-Ru catalysts supported by carbon agglomerates. Nearly spherical catalysts produced in the flame were mainly composed of metallic Pt and Ru with the molar ratio of 1:1 and those sizes were controllable from ~1.5 nm to ~2.0 nm. Nevertheless, only Pt peaks were found from X-ray diffraction experiments, suggesting that amorphous-like Ru was well mixed in the crystalline Pt lattices. It was found from Cyclo-voltamograms and CO stripping experiments that the electrochemical properties of the catalysts are at least comparable to that of a conventional commercial sample.

• 자원리싸이클링
• /
• 제16권5호
• /
• pp.41-45
• /
• 2007

폐실리콘 슬러지로부터 테트라메틸오쏘실리케이트(TMOS)와 실리카 나노분말을 제조하였다. 먼저, 실리카 나노분말의 전구체인 TMOS를 폐실리콘 슬러지로부터 촉매 화학반응에 의해 합성하였다. TMOS의 합성실험에서 반응온도가 $130^{\circ}C$ 이상에서는 반응시간이 5시간 경과 시 반응온도에 무관하게 100%의 반응율을 나타내었다. 그러나 $150^{\circ}C$ 이상에서는 초기 반응속도가 빨라졌다. 메탄올 주입속도를 0.8 ml/min에서 1.4 ml/min로 증가시에는 3시간 경과 후에는 반응율이 변화하지 않았다. 이와 같이 합성된 TMOS로부터 화염분무열분해법에 의해 실리카 나노분말을 제조하였다. 제조된 실리카 나노분말은 구형이며, 무응집 형태이었다. 평균입자 크기는 전구체의 주입속도 및 농도변화에 따라 9 nm에서 30 nm로 변화하였다.