• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1992.05a
• /
• pp.137-139
• /
• 1992

By addition of 1～5mol% CeO$_2$to powders with composition in the BaO-Nd$_2$O$_3$-TiO$_2$, temperature coefficient of permittivity of sintered ceramics may be decreased from approximately-140ppm/$^{\circ}C$～-65ppm/$^{\circ}C$. Dense, fine grained ceramics were prepared with permitivity within the range of 78～92 and Q above 1000.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.540-541
• /
• 2006

SUS316L stainless steel, commercial pure Titanium and Ti-6Al-4V alloy powders applied by Mechanical Milling (MM) process are sintered by Hot Roll Sintering (HRS) process. Microstructure and mechanical properties of those HRS materials is investigated. The microstructures of materials produced by HRS process consist of fine grains and work-hardened structure, that is, the hybrid microstructure. Tensile test of the HRS material demonstrated the good mechanical properties. These results show that the HRS process is very effective to the improvement of mechanical properties in the SUS316L stainless steel, commercial pure Titanium and Ti-6Al-4V alloy.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.36-37
• /
• 2006

This study aims to investigate the usage of nano-scale particles in a micro metal injection molding ($\mu$-MIM) process. Nanoscale particle is effective to improve transcription and surface roughness in small structure. Moreover, the effects of hybrid micro/nano particles, Cu/Cu and SUS/Cu were investigated. Small dumbbell specimens were produced using various feedstocks prepared by changing binder content and fraction of nano-scale Cu particle (0.3 and $0.13{\mu}m$ in particle size). The effects of adding the fraction of nano-scale Cu powder on the melt viscosity of the feedstock, microstructure, density and tensile strength of sintered parts were discussed.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.12-13
• /
• 2006

The spherical and high quality Titanium fine powder "Tilop" has been produced with gas atomization furnace, Sumitomo Titanium Corporation originally designed. Recently, a new process which can produce Ti-alloy(Ti-6Al-4V) powders by utilizing our gas atomization process, of which raw material is sponge titanium pre-mixed with alloy chips or granules has been also developed. The particle size of gas atomized Ti-alloy powder and the mechanical properties of sintered Ti-alloy compacts prepared by metal injection molding were discussed in this study.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 1997.04a
• /
• pp.5-5
• /
• 1997

Rapidly-solidified P/M aluminium alloys for automobile and home appliance industries were developed. Rapidly-solidification made it possible to refine microstructures and to expand the range of alloy composition. For example, Al-Si alloys containing transition metal have lower thermal expansion coefficient, more excellent wear resistance, higher strength, and better machinability than those of conventional aluminium alloys. Therefore, in Japan, the technologies on powder-extrusion and powder-forging of aluminium alloy powders are developed for fifteen years, and applied to several parts, such as cylinder liners of motor cycle engines, rotors and vanes of compressors for car air conditioner, oil pump rotor for racing car, and so on. In this presentation, applications for automobile are mentioned. In particular, cylinder liners made of particle-dispersed composites with fine alumina and graphite are in detail described.

• Journal of Powder Materials
• /
• v.19 no.1
• /
• pp.19-24
• /
• 2012

The consolidation results of fine tungsten powders, W-Cu composite and W/Cu FGM by using a novel method combining resistance sintering with ultra high pressure have been reviewed. The densification effects of the consolidation parameters, including pressure, input power and sintering time, have been investigated. The sintering mechanism of this method was quite different from other sintering methods. Particle rearrangement, sliding, distortion and crushing due to the ultra high pressure are the dominant mehanisms at the initial stage, then the dominant sintering mechanisms are transient arc-fused processes controlled by the input power.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.305-305
• /
• 2007

고경도 및 내침식재료가 새로운 기계구조 및 기계 절삭공구재료로서 각광을 받고 있으며 질화붕소(BN)는 고융점, 고경도의 물리적 특성으로 다이아몬드 대체 물질로 주목되고 있다. 원하는 질화붕소의 합성을 위해서는 출발 원료와 합성법에 의존하는 것으로 보고되고 있다. 본 연구에서는 붕소 산화물과 환원제로써 활성 탄소를 출발 원료로 하였으며 치환제로써 질소를 사용하여 기상 반응로에서 질화붕소를 합성하였다. 합성된 시료는 XRD, SEM, PSA 등으로 물성을 측정하였고 합성 변수에 따라 순도의 차이를 보였으며, 본 연구를 통하여 최적의 합성 조건을 제시할 수 있었다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.264-267
• /
• 2005

Soft magnetic iron powders have been coated with polyester or phenol resin. And the coated powder (soft magnetic composite) have been pressed into ring type core over the pressure of 870 MPa. Green density, magnetic flux density, permeability, core loss of the samples were measured to look at the effect of the coating materials and the amount of them. Green density is increased with the amount of coating materials and shows the maximum value, 6.5 $g/cm^3$ at 5 w/o, but decreased over it. And lowest value of the core loss is showed for the 5 w/o coated samples.

• Journal of Magnetics
• /
• v.18 no.1
• /
• pp.1-4
• /
• 2013

Structural and magnetic properties of $Fe_{50}Mn_{50}$ nanocrystalline alloys prepared by the mechanical alloying technique (using commercial Fe and Mn powders as the precursors) are studied as a function of milling time, 1 hr to 48 hrs. The nano-crystallite size and shape are examined by using scanning electron microscopy (SEM). The effect of milling time on structural characterization was investigated using X-ray diffractometer (XRD) and extended X-ray absorption fine structure spectroscopy (EXAFS). Both XRD and EXAFS studies showed that the alloying process should be completed after 36 hrs milling. Concerning the magnetic behavior, the data obtained from superconducting quantum interference devices (SQUID) exhibited both magnetic saturation ($M_s$) and coercivity ($H_c$) depend strongly on the milling time, which are related to the changes in the crystallite size and magnetic dilution.

• Korean Journal of Materials Research
• /
• v.22 no.6
• /
• pp.280-284
• /
• 2012

Bismuth antimony telluride (BiSbTe) thermoelectric materials were successfully prepared by a spark plasma sintering process. Crystalline BiSbTe ingots were crushed into small pieces and then attrition milled into fine powders of about 300 nm ~ 2${\mu}m$ size under argon gas. Spark plasma sintering was applied on the BiSbTe powders at 240, 320, and $380^{\circ}C$, respectively, under a pressure of 40 MPa in vacuum. The heating rate was $50^{\circ}C$/min and the holding time at the sintering temperature was 10 min. At all sintering temperatures, high density bulk BiSbTe was successfully obtained. The XRD patterns verify that all samples were well matched with the $Bi_{0.5}Sb_{1.5}Te_{3}$. Seebeck coefficient (S), electric conductivity (${\sigma}$) and thermal conductivity (k) were evaluated in a temperature range of $25{\sim}300^{\circ}C$. The thermoelectric properties of BiSbTe were evaluated by the thermoelectric figure of merit, ZT (ZT = $S^2{\sigma}T$/k). The grain size and electric conductivity of sintered BiSbTe increased as the sintering temperature increased but the thermal conductivity was similar at all sintering temperatures. Grain growth reduced the carrier concentration, because grain growth reduced the grain boundaries, which serve as acceptors. Meanwhile, the carrier mobility was greatly increased and the electric conductivity was also improved. Consequentially, the grains grew with increasing sintering temperature and the figure of merit was improved.