• Restorative Dentistry and Endodontics
• /
• v.22 no.1
• /
• pp.35-60
• /
• 1997

Physical properties of composite resins such as strength, resistance to wear, discoloration, etc, depend on the degree of conversion of the resin components. The clinical behavior of restorative resins varies brand to brand. Part of this variation is associated with the filler and differences in the polymer matrix. The polymer matrix of resins may differ because the involved monomers are dissimilar and because of variation in the catalyst system. The purpose of this study was to evaluate the degree of conversion of the composite resins according to the depth of cure and light curing time. 7mm diameter cylindrical aluminum molds were filled with each of five different hybrid light curing composite resins(Z-100, Charisma, Herculite XRV, Prisma TPH, Veridonfil) on the thin resin films. The molds were 1mm, 2mm, 3mm, 4mm, and 5mm in depth to produce resin films of various heights. Each sample was given 20sec, 40sec, and 60sec illumination with a light source. The degree of conversion of carbon double bonds to single bonds in the resin films was examined by means of Fourier Transform Infrared Spectrometer. The results were obtained as follows; 1. There was difference in the degree of conversion among five light curing composite resins according to the depth of cure for 20sec, 40sec, and 60sec illumination with light source with statistical significance(P<0.05). 2. Five light curing composite resins show lower degree of conversion at surface of the resin than depth of 1mm. 3. The degree of conversion of five light curing composite resins was siginificantly reduced from the maximum for the resin film when the light passed through as little as 1mm of each composite. 4. The degree of conversion of five light curing composite resins decrease significantly at the depth of 4mm, and polymerization was not occured at the depth of 5mm except for Prisma TPH. 5. The degree of conversion of five light curing composite resins was increased with increased light curing time, and there was no significant differences in the degree of conversion above 4mm in Z-100, 3mm in Charisma, and at depth of 5mm in Herculite XRV and Veridonfil(P>0.05).

• Journal of Bio-Environment Control
• /
• v.10 no.3
• /
• pp.148-154
• /
• 2001

The uplift capacity of a pile for improving the wind resistance of the 1-2 W type plastic film pipe on greenhouses was tested using the plane and corrugated piles with various shapes and diameters. First, the resistant uplift capacity was measured by using the uplift loading on plane piles. As the uplift loading on plane piles increased, the resistant uplift capacity also increased until the loading was reached to ultimate uplift capacity. After ultimate uplift capacity was appeared the uplift displacement, the uplift capacity was decreased gradually. Secondly, the resistant uplift capacity was measured by using the uplift loading on corrugated piles. After the uplift capacity was reached the uplift displacement, the uplift capacity was continually increased or decreased. In general, the ultimate uplift capacity was independent of pile shapes, pile diameter length, and embedded pipe depth. However, the ultimate uplift capacity of a corrugated pile was twice more than that of a plane pile without regard to its diameter and embedded depth. The ultimate uplift capacity per unit pile area was increasing in deeper embedded depth. However, the longer a pile diameter was, the less ultimate uplift capacity. The uplift capacity of a plane pile, used in conjunction with the design wind velocity (26.9m.s$^{-1}$ ) of the project area, was unsatisfiable without regard to diameters and embedded depths of piles, while most of corrugated piles were well appeared uplift capacity under various experimental conditions.

• The Journal of Korean Institute of Communications and Information Sciences
• /
• v.42 no.4
• /
• pp.716-722
• /
• 2017

In this paper, a fully printed NFC tag operating at 13.56 MHz was designed and fabricated using silver nano-paste and carbon ink. The proposed NFC tag has a printed coil with an inductance of $2.74{\mu}H$ on a PI film for application to an NFC tag IC with an internal capacitance of 50 pF. Screen printing technology used in this paper has advantages such as large area printing for mass production, low cost and eco-friendly process compared to conventional PCB manufacturing process. The proposed structure consists of a circular coil implemented as a single layer using silver nano-paste and carbon ink, a jumper pattern for chip mounting between the outer edge and the center of the coil, and an insulation pattern between the coil and the jumper pattern. In order to verify the performance of the proposed NFC tag, we performed the measurements of the printing line width, thickness, line resistance, adhesion and environmental reliability, and confirmed the suitability of the NFC tag based on the full-printed manufacturing method.

• Membrane Journal
• /
• v.6 no.3
• /
• pp.173-181
• /
• 1996

Common volatile organic compounds(VOCs) such as toluene and methanol were removed successfully from N$_{2}$ using a novel silicone-coated hollow fiber membrane module. This novel membrane is a thin film composite(TFC) and was highly efficient in removing VOCs selectively from a N$_{2}$ stream. This membrane had some innate advantages over other silicone-based membrane in that the selective barrier was ultrathin(~1 $\mu$m) and the porosity of the polypropylene substrate was high which leads to a low permeation resistance. The substram was very strongly bonded to the coating layer by plasma polymerization and can withstand a very high pressure. A small hollow fiber module having a length of 25cm and 50 fibers could remove 96~99% of toluene as well as methanol vapors when the feed flow rate was up to 60cc/min. The percent removal of VOCs were even higher when the feed inlet concentration was higher. This process is especially suitable for treating streams having a low flow rate and high VOCs concentration. The permeances of VOCs through this membrane was in the range of $4~30 \times 10^{-9}gmol/sec \cdot cm^{2}\cdot cmHg$ for both toluene and methanol, and nitrogen permeance was between $3~9 \times 10^{-10}gmol/sec \cdot cm^{2} \cdot cmHg$. High separation factor between 10~55 for toluene/N$_{2}$ and 15~125 for methanol/N$_{2}$ were obtained depending on the feed flow rate ranges and feed VOCs concentration levels.

• Korean Journal of Materials Research
• /
• v.8 no.12
• /
• pp.1182-1189
• /
• 1998

High quality $TiN/TiSi_2$-bilayers were formed on the Si(100) substrate at room temperature and at $600^{\circ}C$ first by coevaporation of stoichiometric Si and Ti(Si:Ti = 2:1) fellowed by Ti reactive deposition in N, gas ambient, and in situ annealing in ultrahigh vacuum. Stoichiometric $Ti_{0.}N_{0.5}$, films with (111) texture and $C54-TiSi_2$ films were grown by annealing at temperatures above $700^{\circ}C$. $TiN/C54-TiSi_2$/Si(100) interface was clear and flat without agglomoration, and $CS4-TiSi_2$ film was epitxailly grown. The sheet resistance of the $TiN/TiSi_2$- bilayer decreased as the annealing temperature increased and about $2.5\omega/\textrm{cm}^2$ was obtained from the sample annealed over $700^{\circ}C$.

• Journal of the Korean Applied Science and Technology
• /
• v.31 no.1
• /
• pp.74-82
• /
• 2014

For this research, prepared ammonium dihydrogen phosphate aqueous solution and polyurethane dispersion. Use these resin, this article has been analyzed about change of mechanical properties by increasing amount of ammonium dihydrogen phosphate aqueous solution in polyurethan resin on coated leather and dried film. According to measure data for solvent resistance, DPU(polyurethane dispersion) resin and DPU-AD1, D2, D3(samples of polyurethaneresin with ammonium dihydrogen phosphate aqueous solution) had good property. As known in the results, increase of ammonium dihydrogen phosphate constant did not influence to big change of polyurethane resin properties. As test of tensile strength, DPU had highest tensile characteristic($3.114kg_f/mm^2$) and DPU-AD3 had lowest tensile characteristic($2.510kg_f/mm^2$). As same as tensile characteristic, abrasion test determined DPU(50.5 mg.loss) had highest properties. In elongation case, DPU had best properties(602 %) in this experiment.

• Solar Energy
• /
• v.17 no.4
• /
• pp.3-11
• /
• 1997

Because grain boundaries in polycrystalline silicon act as potential barriers and recombination centers for the photo-generated charge carriers, these defects degrade conversion effiency of solar cell. To reduce these effects of grain boundaries, we investigated various influencing factors such as thermal treatment, various grid pattern, selective wet etching for grain boundaries, buried contact metallization along grain boundaries, grid on metallic thin film. Pretreatment above $900^{\circ}C$ in $N_2$ atmosphere, gettering by $POCl_3$ and Al treatment for back surface field contributed to obtain a high quality poly-Si. To prevent carrier losses at the grain boundaries, we carried out surface treatment using Schimmel etchant. This etchant delineated grain boundaries of $10{\mu}m$ depth as well as surface texturing effect. A metal AI diffusion into grain boundaries on rear side reduced back surface recombination effects at grain boundaries. A combination of fine grid with finger spacing of 0.4mm and buried electrode along grain boundaries improved short circuit current density of solar cell. A ultra-thin Chromium layer of 20nm with transmittance of 80% reduced series resistance. This paper focused on the grain boundary effect for terrestrial applications of solar cells with low cost, large area, and high efficiency.

• Clean Technology
• /
• v.24 no.1
• /
• pp.50-54
• /
• 2018

In this work, N-methyl-2-pyrrolidone (NMP) was added into diethylenetriamine (DETA) aqueous solution for high $CO_2$ loading via phase splitting of absorbents during $CO_2$ absorption. Immiscible two phases were formed in the range of more than 30 wt% of NMP in 2 M DETA + NMP + water absorbents because of low solubility of DETA-carbamate in NMP solution. As the composition of NMP in the absorbents increased, the difference of $CO_2$ loading between each phase increased and the volume of bottom phase decreased. In $CO_2$ absorption in packed column by 2 M DETA + NMP + water absorbents, the absorption rate decreased in the range of more than 40 wt% of NMP. It is due to the increasing of mass transfer resistance in liquid film of absorbents at the high concentration of NMP. DETA + NMP + water absorbent is expected as the promising one for reducing the regeneration energy of absorbents according to volume reduction of $CO_2-rich$ phase.

• The Journal of Korean Academy of Prosthodontics
• /
• v.41 no.6
• /
• pp.699-713
• /
• 2003

Statement of problem. Titanium is the most important material for biomedical and dental implants because of their high corrosion resistance and good biocompatibility. These beneficial properties are due to a protective passive oxide film that spontaneously forms on the surface. Purpose. The purpose of this study was to evaluate the responses of osteoblast-like cells on different surface treatments on Ti discs. Material and Methods. Group 1 represented the machined surface with no treatment. Group 2 surfaces were sandblasted with $50{\mu}m\;Al_2O_3$ under $5kgf/cm^2$ of pressure. Groups 3 and 4 were sandblasted under the same conditions. The samples were treated on a titanium oxide surface with reactive sputter depositioning and thermal oxidation at $600^{\circ}C$ (Group 3) and $800^{\circ}C$ (Group 4) for one hour in an oxygen environment. The chemical composition and microtopography were analyzed by XRD, XPS, SEM and optical interferometer. The stability of $TiO_2$ layer was studied by petentiodynamic curve. To evaluate cell response, osteoblast extracted from femoral bone marrow of young adult rat were cultured for cell attachment, proliferation and morphology on each titanium discs. Results and Conclusion. The results were as follows : 1. Surface roughness values were, from the lowest to the highest, machined group, $800^{\circ}C$ thermal oxidation group, $600^{\circ}C$ thermal oxidation group and blasted group. The Ra value of blasted group was significantly higher than that of $800^{\circ}C$ thermal oxidation group (P=0.003), which was not different from that of $600^{\circ}C$ thermal oxidation group (P<0.05). 2. The degree of cell attachment was highest in the $600^{\circ}C$ thermal oxidation group after four and eight hours (P<0.05), but after 24 hours, there was no difference among the groups (P>0.05). 3. The level of cell proliferation showed no difference among the groups after one day, three days, and seven days (P>0.05). 4. The morphology and arrangement of the cells varied with surface roughness of the discs.

• Polymer(Korea)
• /
• v.36 no.4
• /
• pp.486-493
• /
• 2012

Photocurable sulfonated polyimide (SPI) polyelectrolyte containing chalcone group was prepared and fabricated on an alumina electrode pretreated with chalcone-containing silane-coupling agent. SPI films with bis(tetramethyl)ammonium 2,2'-benzidinedisulfonate ($Me_4N$-BDS)/4,4'-diaminochalcone (DAC)/pyromellitic dianhydride (PA)= 90/10/100 possessed very linear response(Y = -0.04528X+7.69446, $R^2=0.99675$) and showed resistance changing from 4.48 to $2.1k{\Omega}$ between 20 and 95 %RH. The response time for absorption and desorption measurements between 33 and 94 %RH% was about 79 s, which affirmed the high efficiency of crosslinked SPI film for rapid detection of humidity. A negative temperature coefficient showing $-0.49%RH/^{\circ}C$ was found and proper temperature compensation should be considered in future applications. Moreover, pretreatment of the substrates with chalcone-containing silane-coupling agent was performed to improve the water durability and the stability of the humidity sensors at a high humidity and a high temperature and long-term stability for 480 h. The crosslinked SPI films anchored to electrode substrate could be a promising material for the fabrication of efficient humidity sensors with superior characteristics compared to the commercially available sensors.