• Proceedings of the KIEE Conference
• /
• 1994.11a
• /
• pp.246-248
• /
• 1994

The Electrical properties of thin $SiO_2$ film by rapid thermal processing have been investigated and this film has been compared with thermal $SiO_2$ film by furnace. The RTO(rapid thermal oxide) film annealed in Ar ambient represent more superior properties than thermal $SiO_2$ film by furnace at breakdown field and leakage current. The RTO(rapid thermal oxide) film annealed in $NH_3$ ambient represent more inferior properties than thermal $SiO_2$ film by furnace at electrical properties, but the capacitance was improved 15-25% than the conventional oxide film.

• Journal of the Korean Ceramic Society
• /
• v.33 no.7
• /
• pp.735-742
• /
• 1996

Antimony-doped Tin oxide (ATO) thin films were deposited on soda-lime glass substrates by DC magnetron sputtering technique. Effects of DC power film thickness and post heat-treatment on electrical conductivity of ATO film were investigated. Other properties of ATO film such as optical anti-chemical and wear properties were also reported in this work. The obtained ATO films showed electrical resistivities ranging from 5$\times$10-3 $\Omega$cm to 3$\times$10-3 $\Omega$cm with the average optical transparency above 80% in visible wavelength range and excel-lent anti-chemical properties where the electrical resistivity was not changed even after soaking the films in 1M HCl or 1M NaOH solution for 10 days. These properties were found to be related to the crystallinity of ATO film and the films having higher crystallinity showed better properties.

• Korean Journal of Food Science and Technology
• /
• v.34 no.6
• /
• pp.1023-1029
• /
• 2002

Relationship between RVA properties and physical properties of film made from native corn starch and hydroxypropylated corn starch at various levels of plasticizers was examinel. Tensile strength of the film decreased, but its elongation and water vapor permeability increased with increasing plasticizer concentration. The film with glycerol showed greater changes in physical properties than that with sorbitol. Hydroxypropylated starch film showed lower tensile strength, higher elongation, and higher water vapor permeability than the native starch film. Sorbitol resulted in films with relatively high tensile strength, whereas glycerol produced films with increased elongation. The most reliable parameters for the relationship between RVA properties and film properties were RVA peak viscosity, tensile strength, and water vapor permeability. Water vapor permeability and tensile strength had linear relationship with RVA properties. The tensile strength and water vapor permeability of film could be predicted using the RVA peak viscosity.

• Journal of information and communication convergence engineering
• /
• v.9 no.4
• /
• pp.461-465
• /
• 2011

An aluminum doped zinc oxide (AZO) film for front contacts of thin film solar cells, in this work, were deposited by r.f. magnetron sputtering, and then etched in diluted hydrochloric acid solution for different times. Effects of surface texturing on the electro-optical properties of AZO films were investigated. Also, to clarify the light trapping of textured AZO film, amorphous silicon thin film solar cells were fabricated on the textured AZO/glass substrate and the performance of solar cells were studied. After texturing, the spectral haze at the visible range of 400 ~750 nm increased substantially with the etching time, without a change in the resistivity. The conversion efficiency of amorphous Si solar cells with textured AZO film as a front electrode was improved by the increase of short-circuit current density ($J_{sc}$), compared to cell with flat AZO films.

• Journal of the Korean Ceramic Society
• /
• v.37 no.1
• /
• pp.96-101
• /
• 2000

Comparative studies on microstructure, and mechanical and anti-oxidation properties between TiN and Ti-Si-N films were performed. The Ti-Si-N films were deposited on high-speed steel and silicon wafer substrates by plasma-assisted chemcial vapor deposition(PACVD) technique. The Si addition to TiN film caused to change the microstructure such as grain size refinement, randomly multi-oriented microstructure, and nano-sized codeposition of silicon nitride in the TiN matrix. The Ti-Si-N film, contains Si content of ∼7 at.%, showed the micro-hardness value of ∼3400 HK, which was higher than the pure TiN film whose hardness was ∼1500HK. The Ti-Si(7 at.%)-N film also showed much improved anti-oxidation properties compared with those of the pure TiN film. These properties were also related to the microstructure of Ti-Si(7 at.%)-N film was formed and retarded further oxidation of the nitridelayer. These properties were also related to the microstructure of Ti-Si(7 at.%)-N film which was characterized by nano-sized precipitates of silicon nitride phase in the TiN matrix and randomly oriented grains.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.3
• /
• pp.281-286
• /
• 2002

In odder to investigate the magnetic properties of CoCr-based bilayered thin films on kind of underlayer, we introduced amorphous Si layer to Co-Cr(-Ta) magnetic layer as underlayer. First, we prepared CoCr and CoCrTa single layer using the Facing Targets Sputtering system to investigate theirs properties. It was revealed that with increasing the film thickness of CoCr, CoCrTa single layer, crystalline orientation and perpendicular coercivity was improved. The CoCrTa thin film showed bettor crystalline and magnetic characteristics than CoCr thin film. As a result of investigating magnetic properties of CoCr and CoCrTa magnetic layer on introducing the Si underlayer, perpendicular coercivity and saturation magnetization of CoCr/Si and CoCrTa/Si bilayered thin film were decreased due to the increased grain size and diffusion of Si atoms to magnetic layer. And they showed constant with increasing the film thickness of Si thin film. However, in case of CoCrTa/Si bilayered thin film, in-plane coercivity was controlled low at about 250Oe. The c-axis orientations of CoCr/si and CoCrTa/Si bilayered thin film showed a good crystalline characteristics as about $2^{\circ}$.

• Elastomers and Composites
• /
• v.57 no.3
• /
• pp.114-120
• /
• 2022

The tensile properties of the extruded PC film were measured in the extrusion direction and perpendicular to the extrusion direction. The measured properties were the elastic modulus and Poisson's ratio at the glass transition temperature of PC. The measured orthotropic properties of the film were used for the computer simulation of vacuum forming. In this simulation, three mold shapes were tested: dome, trapezoid, and cubic, and the vacuum was applied between the mold surface and the heated film. The stress, strain, thickness, and stretch ratio distributions of the film in different mold shapes were observed and compared. The thermoforming simulation method used in this study and the obtained results, considering the determined orthotropic properties, can be applied to the thermoforming of various three-dimensional shapes.

• Macromolecular Research
• /
• v.14 no.6
• /
• pp.617-623
• /
• 2006

In order to achieve an oriental lacquer (OL) film with a thick consistency, UV-curable silicone acrylate (SA) was added to OL by a dual curing process. The addition of 5 wt% UV-curable SA to the OL fomulation enabled the preparation via a single drying step of a $77{\mu}m-thick$ film exhibiting excellent surface properties. FTIR-ATR was used to investigate the effect of UV-curable SA on the behavior of film formation during curing, and the relaxation behavior of the produced films was investigated by dielectric spectroscopy. Dielectric properties were measured in the frequency range $10^{-2}-10^5\;Hz$ at various temperatures between -100 and $200^{\circ}C$. The results demonstrated that OL modified by UV-curable SA has a higher glass transition temperature and stronger secondary relaxation at a lower temperature than the conventional OL system. The OL film modified with UV-curable SA was presumed to be harder at the surface and tougher than conventional OL film.

• Journal of the Korean institute of surface engineering
• /
• v.44 no.4
• /
• pp.137-143
• /
• 2011

The internal stress and magnetic properties (coercivity and squareness) of Ni-Fe nano thin film synthesized by electrodeposition method were studied as a function of acidic chloride bath conditions (composition and temperature) and current density. Fe deposition patterns were different depending on the temperature of the solution, the stress of film decreased with increasing the solution temperature, and the depending on the amount of Fe deposition showed a parabolic shape. The grain size of film was inversely proportional to stress of thin film. The internal stress of thin film and magnetic properties were deeply relevant, and the stress of thin film had a relationship with bath conditions and grain size of the thin film surface.

• Food Science and Biotechnology
• /
• v.15 no.1
• /
• pp.133-137
• /
• 2006

Wheat gluten-chitosan composite film (WGCCF) can prevent moisture migration and enhance the antimicrobial properties of gluten in intermediate-moisture foods like sandwiches. To mimic the structure of actual sandwich-type products we developed multi-layer food models, where moisture content and water activity differ. Water activity gradients direct moisture migration and therefore determine product characteristics and product stability. A 10% wheat gluten film-forming solution was mixed with chitosan film-forming solution (0-3%, w/w) and evaporated to generate WGCCF. Addition of 3% chitosan enhanced the mechanical properties of the film composite, lowered its water vapor permeability, and improved its ability to protect against both, Streptococcus faecalis and Escherichia coli, in a 24 hr sandwich test (reduction of 1.3 and 2.7 log cycles, respectively, compared to controls). Best barrier and antimicrobial performance was found for 3% chitosan WGCCF at pH 5.1. Film of this type may find application as barrier film for intermediate-moisture foods.