• Journal of the Korean Ceramic Society
• /
• v.39 no.9
• /
• pp.884-889
• /
• 2002

In order to investigate the calcium phosphate forming ability of nanocrystalline $ZrO_2$ film, we prepared $ZrO_2/Si$ structure by using a chemical solution deposition with a zirconium naphthenate as a starting material. Precursor sol was spin-coated onto the (100)Si substrate and prefired at 500$^{\circ}C$ for 10 min in air, followed by final annealing at 800$^{\circ}C$ for 30 min in air. Crystallinity of the annealed film was examined by X-ray diffraction analysis. Surface morphology and surface roughness of the film were characterized by field emission-scanning electron microscope and atomic force microscope. After annealing, nanocrystalline $ZrO_2$ grains were obtained on the surface of the film with a homogeneous interface between the film and substrate. After immersion for 1 or 5 days in a simulated body fluid, formation of calcium phosphate was observed on $ZrO_2$ film annealed at 800$^{\circ}C$ by energy dispersive X-ray spectrometer. The fourier transform infrared spectroscopy revealed that carbonate was substituted into the calcium phosphate.

• Korean Journal of Materials Research
• /
• v.5 no.6
• /
• pp.754-762
• /
• 1995

Strontium titanate(SrTiO$_3$) thin film was prepared on Si substrates by RF magnetron sputtering for a high capacitance density required for the next generation of LSTs. The optimum deposition conditions for SrTiO$_3$thin film were investigated by controlling the deposition parameters. The crystallinity of films and the interface reactions between SrTO$_3$film and Si substrate were characterized by XRD and AES respectively. High quality films were obtained by using the mixed gas of Ar and $O_2$for sputtering. The films were deposited at various bias voltages to obtain the optimum conditions for a high quality file. The best crystallinity was obtained at film thickness of 300nm with the sputtering gas of Ar+20% $O_2$and the bias voltage of 100V. The barrier layer of Pt(100nm)/Ti(50nm) was very effective in avoiding the formation of SiO$_2$layer at the interface between SrTiO$_3$film and Si substrate. The capacitor with Au/SrTiO$_3$/Pt/Ti/SiO$_2$/Si structure was prepared to measure the electric and the dielectric properties. The highest capacitance and the lowest leakage current density were obtained by annealing at $600^{\circ}C$ for 2hrs. The typical specific capacitance was 6.4fF/$\textrm{cm}^2$, the relative dielectric constant was 217, and the leakage current density was about 2.0$\times$10$^{-8}$ A/$\textrm{cm}^2$ at the SrTiO$_3$film with the thickness of 300nm.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.11a
• /
• pp.63-63
• /
• 2009

Many researchers have been studied as active and transparent electrode using ZnO (Zinc oxide) inorganic semiconductor material due to their good properties such as wide band-gap and high electrical properties compared with amorphous-Si. In this study, we fabricated ZnO films by the RF magnetron sputtering method at a low temperature for a channel layer in thin-film transistor (TFT) and investigated the characteristics of sputtered ZnO films. Also, the electrical properties of TFT using ZnO channel layer such as field effect mobility(${\mu}$), threshold voltage ($V_{th}$), and $I_{on/off}$ ratio are investigated for the application of the display and electronic devices.

• Proceedings of the IEEK Conference
• /
• 2000.06b
• /
• pp.318-321
• /
• 2000

We showed that the change of Ar to $N_2$flow during the TiN deposition by the reactive sputtering decides the crystallinity of LPCVD W, as well as the electrical properties of the W-TiN/SiO$_2$Si capacitor. In particular, the threshold voltage can be controlled by the Ar to $N_2$ratio. As compared to the results obtained from the LPCVD W/SiO$_2$/Si MOS capacitor, the insertion of approximately 50 nm TiN film effectively prohibits the fluorine diffusion during the deposition and annealing of W films, resulting in negligible leakage currents at the low electric fields.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.218-219
• /
• 2009

$TiO_2$ thin films were deposited on si wafer and glass substrates by rf magnetron sputtering. The films were coated under argon atmosphere at different working pressures: 3mTorr, 5mTorr, 7mTorr, 10mTorr. The films were annealed at $550^{\circ}C$ for 5h after deposition. Film structures were analyzed with XRD, As the increase of working pressure, $TiO_2$ films have been good crystallinity. At 3mTorr and 5mTorr, the films were observed in rutile phase and anatase phase.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1995.05a
• /
• pp.187-191
• /
• 1995

Thin film of the (Pb$\_$1-x/La.sub x/)(Zr$\_$0.25/Ti/Sub 0.48/) O$_3$(x=0~13[at%]) were prepared by Sol - Gel method. Multi-layer PLZT thin films were fabricated by spin-coating on Pt/Ti/SiO$_2$/Si substrate. The crystallinity and microstructure of the films were investigated with the sintering condition. At the sintering temperature of of 600[$^{\circ}C$], the perovskite phase was dominat. PLZT(11/52/48)thin films sintered at 600[$^{\circ}C$], 1[hr] had good dielectric constant (1236), dielectric loss (2.2[%]), remanent polarization (1.38[${\mu}$C/$\textrm{cm}^2$] and coercive field(16.86[ kV/cm]) respectively.

• Journal of the Korean Ceramic Society
• /
• v.35 no.9
• /
• pp.1002-1005
• /
• 1998

Bismuth titanate thin films were prepared on {{{{ { SrTiO}_{3 } }}(100) and Si(100) substrates by dipping-pyrolysis pro-cess using metal naphthenates as starting materials. crystallinity and in-phase alignment of the films were analyzed by X-ray diffraction $\theta$-2$\theta$ scans and $\beta$ scans (pole-figures) respectively. Highly c-axis-oriented {{{{ { { {Bi }_{4 }Ti }_{3 }O }_{12 } }} thin films with smooth surfaces were obtained after heat treatment at 75$0^{\circ}C$ on {{{{ { SrTiO}_{3 } }}(100) sub-strate while the films grown of Si(100) exhibited polycrstalline characteristics. C-axis oriented film show-ed an epitaxial relationship with the {{{{ { SrTiO}_{3 } }} substrate.

• Carbon letters
• /
• v.14 no.2
• /
• pp.117-120
• /
• 2013

In this study, an electro-catalyst of Pt nanoparticles supported by polypyrrole-functionalized graphene (Pt/PPy-reduced graphene oxide [RGO]) is reported. The Pt nanoparticles are deposited on the PPy-RGO composite by chemical reduction of H2PtCl6 using NaBH4. The presence of graphene (RGO) caused higher activity. This might have been due to increased electro-chemically accessible surface areas, increased electronic conductivity, and easier charge-transfer at polymer-electrolyte interfaces, allowing higher dispersion and utilization of the deposited Pt nano-particles. Microstructure, morphology and crystallinity of the synthesized materials were investigated using X-ray diffraction and transmission electron microscopy. The results showed successful deposition of Pt nano-particles, with crystallite size of about 2.7 nm, on the PPy-RGO support film. Catalytic activity for methanol electro-oxidation in fuel cells was investigated using cyclic voltammetry. The fundamental electrochemical test results indicated that the electro-catalytic activity, for methanol oxidation, of the Pt/PPy-RGO combination was much better than for commercial catalyst.

• Journal of the Korean Ceramic Society
• /
• v.34 no.12
• /
• pp.1227-1234
• /
• 1997

ZnO thin films were prepared by rf-magnetron sputter at various conditions. Crystallinity, microstructure, chemical composition, and optical composition, and optical properties of the films were investigated as functions of substrate temperature (R. T.-50$0^{\circ}C$) an sputter gas (O2/Ar=0-50%). ZnO thin films grown at 50$0^{\circ}C$ with sputter gas of pure argon as well as at R. T. with sputter gas of a mixture of argon & oxygen(O2/Ar=2%) exhibit a strong tendency of (002) preferred orientation, compared with a considerable random orientation at the other conditions. The thin films with (002) preferred orientation has a chemical stoichiometry of Zn/O-1.01, a band gap of 3.3eV, and a packing density of 98% respectively.

• Journal of the Korean Ceramic Society
• /
• v.35 no.9
• /
• pp.969-973
• /
• 1998

Pb(Zr, Ti)O3 (PZT) (Zr:Ti= 52: 48) thin films were prepared on MgO(100) substrates by dipping-py-rolysis process using metal naphthenates as starting materials. Thin films were fabricated by spin coating technique and the precursor films were prefired at 20$0^{\circ}C$ in air for 0.5, 1, 2, 3, and 24 h followed by final heat treatment at 75$0^{\circ}C$ for 30min. Film prefired for 24 h lost orientational properties and pole figure analysis showed the lost of the epitaxial relationship between the films and substrate while highly a/c-axis oriented thin films were obtained for the samples prefired for 1, 2, and 3h.