• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.1
• /
• pp.7-15
• /
• 2004

The ferroelectric SBT thin films as a material of capacitors for non-volatile FRAMs have some problems that its remanent polarization value is relatively low and the crystallization temperature is quite high abovc 80$0^{\circ}C$. Therefore, in this paper, SBTN solution with S $r_{0.9}$B $i_{2.1}$T $a_{1.8}$N $b_{0.2}$$O_{9}$ composition was synthesized by sol-gel method. Sr(O $C_2$ $H_{5}$)$_2$, Bi(TMHD)$_3$, Ta(O $C_2$ $H_{5}$)$_{5}$and Nb(O $C_2$ $H_{5}$)$_{5}$ were used as precursors, which were dissolved in 2-methoxyethanol. SBTN thin films with 200 nm thickness were deposited on Pt/Ti $O_2$/ $SiO_2$/Si substrates by spin-coating. UV-irradiation in a power of 200 W for 10 min and rapid thermal annealing in a 5-Torr-oxygen ambient at 76$0^{\circ}C$ for 60 sec were used to promote crystallization. The films were well crystallized and fine-grained after annealing at $650^{\circ}C$ in oxygen ambient. The electrical characteristics of 2Pr=11.94 $\mu$C/$\textrm{cm}^2$, Ps＋/Pr＋=0.54 at the applied voltage of 5 V were obtained for a 200-nm-thick SBTN films. This results show that 2Pr values of the UV irradiated and rapid thermal annealed SBTN thin films at the applied voltage of 5 V were about 57% higher than those of no additional processed SBTN thin films. thin films.lms.s.s.

• Electrical & Electronic Materials
• /
• v.9 no.3
• /
• pp.251-258
• /
• 1996

Sol-Gel derived ferroelectric Pb(Z $r_{0.52}$ $Ti_{0.48}$) $O_{3}$ thin films have been fabricated on Pt/Ti/ $SiO_{2}$/Si substrate. Two kinds of fast annealing methods, F-I (six times of intermediate and final annealing) and F-II(one final annealing after six times of intermediate annealing) were used for preparation of multi-coated PZT thin films. As the annealing temperature was increased, high capacitance could be obtained, for instance, 2700.angs.-thick PZT thin film annealed at 680.deg. C had a capacitance value of approximately 20nF at 1kHz. In addition, it is found that the dielectric constant is a function of the perovskite phase fraction. In case of F-I method, PZT thin film had a remanent polarization(Pr) of 8-15.mu.C/c $m^{2}$ and a coercive field( $E_{c}$) of 35-44kV/cm according to annealing temperature, whereas PZT film fabricated by F-II method had as high as 24-25.mu.C/c $m^{2}$ and 48-59kV/cm, respectively. As a result of measuring Curie temperature, PZT thin film had a range of 460-480.deg. C by F-I method and more or less higher range of 525-530.deg. C by F-II method, which implied that different microstructures could cause the different Curie temperature. Through I-V measurement, leakage current of PZT thin film fabricated by F-I and F-II methods was 64nA/c $m^{2}$ and 2.2.mu.A/c $m^{2}$ in the electric field of 100kV/cm, respectively.y.y.y.

• Proceedings of the KIEE Conference
• /
• 1998.11c
• /
• pp.801-803
• /
• 1998

We investigated Pt and $RuO_2$ as a bottom electrode and PZT thin film for ferroelectric applications. XRD examination shows that a mixed phase of (111) and (200) Pt peak for the temperature ranged from RT to $200^{\circ}C$, and a preferred (111) orientation for the substrate temperature of $300^{\circ}C$. From the XRD and AFM results, we recommend the substrate temperature of $300^{\circ}C$, 80 W for the Pt bottom electrode growth. From the study of an oxygen partial pressure from 0 to 50%, we learned that only Ru metal was grown with $0{\sim}5%$, a mixed phase of Ru and $RuO_2$ for $10{\sim}40%$, pure $RuO_2$ at 50%. Having optimized the bottom electrode growth conditions, we employed two step process in PZT film capacitor: PZT film growth at the low substrate temperature of $300^{\circ}C$ and then post RTA anneal treatments. PZT films were randomly oriented on $RuO_2$ and (110) preferentially oriented on Pt electrode. Leakage current density of PZT film demonstrated two to three orders higher for $RuO_2$ bottom electrode. From C-V results we observed a dielectric constant of PZT film higher than 1200. This paper presents the optimized process conditions of the bottom electrodes and properties of PZT thin films on these electrodes.

• Journal of the Korean Ceramic Society
• /
• v.40 no.2
• /
• pp.153-158
• /
• 2003

Self-patterning of thin films using photosensitive sol solution has advantages such as simple manufacturing process compared to photoresist/dry etching process. In this study,$La_{0.5}SR_{0.5}CoO_3$(LSCO) thin films as an electrode material for ferroelectric memories have been prepared by spin coating method using photosensitive sol solution. La-2methoxyethoxide, Sr-ethoxide, Co-2methoxyethoxide were used as starting materials. As UV exposure time to the LSCO gel thin film increased, the UV absorption peak intensity of metal${beta}$-diketonate decreased due to reduced solubility by M(metal)-O-M bond formation. Solubility difference by UV irradiation on LSCO gel thin film allows to obtain a fine patterning of thin film. The LSCO thin films annealed over$680{\circ}C$ in air showed perovskite phase and the lowest resistivity$(4{ imes}10^{-3}{Omega}cm)$ of the thin films were obtained by annealing at$740{\circ}C$.

• The Korean Journal of Ceramics
• /
• v.6 no.1
• /
• pp.64-67
• /
• 2000

Reactively sputtered $Pb(Zr,Ti)O_3$(PZT) films on $IrO_2$and Ir were evaluated with particular consideration on interface properties. The $IrO_2$and Ir were previously annealed at $650^{\circ}C$ in $O_2$or $N_2$atmosphere, respectively. There was no appreciable roughening in the interface of the $PZT/IrO_2$respective to that of the PZT/Ir; the rms roughness of $IrO_2$and Ir was about 3nm and 10nm, respectively. The ferroelectric properties of the $PZT/IrO_2$were found to be better than that of the PZT/Ir; however, the leakage current of the $PZT/IrO_2$was slightly larger than that of the PZT/Ir. The $PZT/IrO_2$thin films did not exhibit any fatigue up to $10^{11}$ cycles; the $P^*\;_r-P^r$ value decreased only from 16.6 to 14$\mu$C/$\textrm{cm}^2$ until $10^{12}$ polarization reversals. On the other hand, although thin $IrO_2$layer was formed between PZT and Ir, the PZT/Ir thin films began to undergo fatigue after $10^9$ polarization reversals.

• Korean Journal of Materials Research
• /
• v.30 no.2
• /
• pp.61-67
• /
• 2020

BiFeO₃ with perovskite structure is a well-known material that has both ferroelectric and antiferromagnetic properties called multiferroics. However, leaky electrical properties and difficulty of controlling stoichiometry due to Bi volatility and difficulty of obtaining high relative density due to high dependency on the ceramic process are issues for BiFeO₃ applications. In this work we investigated the sintering behavior of samples with different stoichiometries and sintering conditions. To understand the optimum sintering conditions, nonstoichiometric Bi_1±xFeO_3±δ ceramics and Ti-doped Bi_1.03Fe_1-4x/3Ti_xO₃ ceramics were synthesized by a conventional solid-state route. Dense single phase BiFeO₃ ceramics were successfully fabricated using a two-step sintering and quenching process. The effects of Bi volatility on microstructure were determined by Bi-excess and Ti doping. Bi-excess increased grain size, and Ti doping increased sintering temperature and decreased grain size. It should be noted that Ti-doping suppressed Bi volatility and stabilized the BiFeO₃ phase.

• Transactions on Electrical and Electronic Materials
• /
• v.6 no.2
• /
• pp.51-56
• /
• 2005

Ferroelectric Bi$_{3.35}$Sm$_{0.65}$Ti$_{3}$O$_{12}$(BSmT) thin films were synthesized using a sol-gel process. Bi(TMHD)$_{3}$, Sm$_{5}$(O$^{i}$Pr)13, Ti(O$^{i}$Pr)4 were used as the precursors, which were dissolved in 2­methoxyethanol. The BSmT thin films were deposited on Pt/TiO$_{x}$/SiO$_{2}$/Si substrates by spin­coating. The electrical properties of the thin films were enhanced using rapid thermal annealing process (RTA) at 600 $^{circ}$C for 1 min in O$_{2}$. Thereafter, the thin films were annealed from 600 to 720 $^{circ}$C in oxygen ambient for 1 hr, which was followed by post-annealed for 1 hr after depositing a Pt electrode to enhance the electrical properties. X-ray diffraction (XRD) and scanning electron microscopy (SEM) were used to analyze the crystallinity and surface morphology of layered perovskite phase, respectively. The remanent polarization value of the BSmT thin films annealed at 720 $^{circ}$C after the RTA treatment was 35.31 $\mu$C/cmz at an applied voltage of 5 V.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.05b
• /
• pp.74-77
• /
• 2002

Ferroelectric Random Access Memory(FRAM) and MEMS applications require noble metal or refractory metal oxide electrodes. In this study, Ru thin films were etched using $O_2$+10% $CF_4$ plasma in an inductively coupled plasma(ICP) etching system. The etch rate of Ru thin films was examined as function of rf power, DC bias applied to the substrate. The enhanced etch rate can be obtained not only with increasing rf power and DC bias voltage, but also with small addition $CF_4$ gas. The selectivity of $SiO_2$ over Ru are 1.3. Radical densities of oxygen and fluorine in $CF_4/O_2$ plasma have been investigated by optical emission spectroscopy(OES). The etching profiles of Ru films with an photoresist pattern were measured by a field emission scanning electron microscope (FE-SEM). The additive gas increases the concentration of oxygen radicals, therefore increases the etch rate of the Ru thin films and enhances the etch slope. In $O_2$+10% $CF_4$ plasma, the etch rate of Ru thin films increases up to 10% $CF_4$ but decreases with increasing $CF_4$ mixing ratio.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1995.05a
• /
• pp.14-16
• /
• 1995

Pb($Zr_{0.52}Ti_{0.48}$)$O_3$ ceramic thin films were fabricated from an alkoxide-based solution by Sol-Gel method. Pb($Zr_{0.52}Ti_{0.48}$)$O_3$ co-ramic thin films were formed by spin coating method on Pt/$SiO_2$/Si substrate at 4000[rpm] for 30 [sec]. Coated specimens were dried on the hot-plate at 400[$^{\circ}C$] for 10[min]. The coating process was repeated 6 times and then sintered at temperature between 500 ~ 800[$^{\circ}C$] for 1 hour. The ferroelectric perovskite phases precipitated under the sintering of 700[$^{\circ}C$] for 1 hour. Pb($Zr_{0.52}Ti_{0.48}$)$O_3$ thin film sintered at 700[$^{\circ}C$] for 1hour showed good dielectric constant (2133) and dielectric loss (2.2[%]) Properties. The switching voltage, switching time and leakage currents density were 3.0[V], 1.7[${\mu}$sec] , 160[pA/$\textrm{cm}^2$] repectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.27 no.5
• /
• pp.297-302
• /
• 2014

$La_{0.5}Sr_{0.5}CoO_3$ (LSCO) electrode thin films with a resistivity of ~ 1,600 ${\mu}{\Omega}cm$ were grown on c-$Al_2O_3$ (0001) substrate. $ZnSnO_3$ (ZTO) thin films with different thicknesses were directly grown on LSCO/c-$Al_2O_3$ (0001) substrates at a substrate temperature that ranged from 550 to $750^{\circ}C$ using Pulsed Laser Deposition (PLD). The secondary phase $Zn_2SnO_4$ occurred during the growth of ZTO films and it became more significant with further increasing substrate temperature. Polarization-electric-field (P-E) hysteresis characteristics, with a remnant polarization and coercive field of 0.05 ${\mu}C/cm^2$ and 48 kV/cm, respectively, were obtained in the ZTO film grown at $700^{\circ}C$ in 200 mTorr.