• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2001.05a
• /
• pp.1-4
• /
• 2001

A new non-destructive fatigue prediction model of the composite laminates is developed. The natural frequencies of fatigue-damaged laminates under extensional loading are related to the fatigue lift of the laminates by establishing the equivalent flexural stiffness reduction as a function of the elastic properties of sublaminates. The flexural stiffness is derived by relating the $90^{\circ}$-ply elastic modulus reduction, and using the laminate plate theory to the degraded elastic modulus and the intact elastic modulus of other laminate. The natural frequency reduction model, in which the dominant fatigue mode can be identified from the sensitivity scale factors of sublaminate elastic properties, provides natural frequency vs. fatigue cycle curves for the composite laminates. Vibration tests were also conducted on $[\textrm{90}_{2}\textrm{0}_{2}]_s$ carbon/epoxy laminates to verify the natural frequency reduction model. Correlations between the predictions of the model and experimental results are good.

• Composites Research
• /
• v.14 no.3
• /
• pp.1-9
• /
• 2001

A new non-destructive fatigue prediction model of the composite laminates is developed. The natural frequencies of fatigue-damaged laminates under extensional loading are related to the fatigue life of the laminates by establishing the equivalent flexural stiffness reduction as a function of the elastic properties of sublaminates. The flexural stiffness is derived by relating the 90-ply elastic modulus reduction, and using the laminate plate theory to the degraded elastic modulus and the intact elastic modulus of other laminates. The natural frequency reduction model, in which the dominant fatigue mode can be identified from the sensitivity scale factors of sublaminate elastic properties, provides natural frequency vs. fatigue cycle curves for the composite laminates. Vibration tests were also conducted on $[{90}_2/0_2]_s$ carbon/epoxy laminates to verify the natural frequency reduction model. Correlations between the predictions of the model and experimental results are good.

• Composites Research
• /
• v.36 no.1
• /
• pp.16-24
• /
• 2023

This paper presents a multi-scale progressive fatigue damage model incorporating the model for interfacial debonding between fibers and matrix. The micromechanics model for the progressive interface debonding was adopted, which defined the four different interface phases: (1) perfectly bonded fibers; (2) mild imperfect interface; (3) severe imperfect interface; and (4) completely debonded fibers. As the number of cycles increases, the progressive transition from the perfectly bonded state to the completely debonded fiber state occurs. Eshelby's tensor for each imperfect state is calculated by the linear spring model for a damaged interface, and effective elastic properties are obtained using the multi-phase homogenization method. The fatigue damage evolution formulas for fiber, matrix and interface were proposed to demonstrate the fatigue behavior of CFRP laminates under cyclic loading. The material parameters for the fiber/matrix fatigue damage were characterized using the chaotic firefly algorithm. The model was implemented into the UMAT subroutine of ABAQUS, and successfully validated with flat-bar UD laminate specimens ([0]₈,[90]₈, [30]₁₆) of AS4/3501-6 graphite/epoxy composite.

• Composites Research
• /
• v.12 no.6
• /
• pp.74-82
• /
• 1999

The static and fatigue characteristics of polyurethane foam cored sandwich structures are investigated. Three types of the specimens with the glass fabric faces and the polyurethane foam core are used; non-stitched. stitched, and stiffened sandwich specimen. Especially additional structural reinforcements with the twisted polyester and glass fiber for thickness direction are made to stitched sandwich structure panel to minimize the delamination of structure which is stitched the upper and lower faces through the core and the resin is impregnated Into stitched fiber with the characteristics of low viscosity of resin at resin flow temperature and cured together with during the curing process. Bending strength of stitched specimen which is 50 mm $50{\times}50{\;}mm$ pitched is improved by 50 % as com-pared with non-stitched specimen and stiffened specimen is improved 10 times more than non-stitched structure. After fatigue testing of $10^6$cycles by 20% of ultimate load under monotonic load, the bending fatigue strength of non-stitched specimen is decreased by 27% of monotonic bending strength, 39% for stitched structure and 20% for stiffened specimen. To verify the aging effect of polyurethane form core, Ultrasonic C-scanning equipment is used to detect the damage of skin laminate alone after fatigue test. From results of UT C-scan images, there is no defect that can be damaged occurred during fatigue test. It is concluded that the decrease of bending strength for foam cored sandwich specimen is caused by the decrease of stiffness due to the aging of polyurethane foam core during fatigue cycles.