• Elastomers and Composites
• /
• v.43 no.1
• /
• pp.1-7
• /
• 2008

Far-infrared vulcanization of ethylene-propylene-diene terpolymer(EPDM) compounds has been studied in comparison with hot air vulcanization. Vulcanization characteristics of EPDM compounds were measured by degree of curing and temperature of specimens in vulcanization process. As a result, degree of curing by far-infrared of EPDM compounds was shown to be higher value than that by hot air at the same vulcanization temperature. Especially, degree of curing by far-infrared on 3 mm thickness of EPDM compounds was increased by two times compared to that by hot air. While the increase of thermal conductivity of EPDM compounds highly improved degree of curing by far-infrared, that hardly improved degree of curing by hot air.

• Elastomers and Composites
• /
• v.44 no.1
• /
• pp.47-54
• /
• 2009

EPDM(Ethylene-propylene-diene-terpolymer) compound reinforced with carbon black having four different particle size, acetylene black(thermal conductivity carbon black), and silica were manufactured by internal mix and open mill. To investigate the effect of particle size of filler and filler type on far-infrared vulcanization, intermal temperature of compound, degree of curing, infrared spectroscopy, and thermal analysis were measured. The thermal conductivity of far-infrared vulcanized EPDM compound increased with increasing particle size of carbon filler, but hot air vulcanized EPDM compound is not affected by particle size. The thermal conductivity was increased in the order of carbon black < silica < acetylene black(thermal conductivity carbon black).