• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2022.04a
• /
• pp.49-50
• /
• 2022

This study examined the potential of halophilic bacteria in reducing the chloride ion concentration within the cement mortars exposed to chloride attack. As a result of the experiment, the compressive strength of mortar with Halomonas venusta showed an equivalent performance to that of counterpart mortars without bacteria. Also, the chloride ion concentration measured in mortars including Halomonas Venusta was 71% lower than that of the counterpart mortars without bacteria.

• International Journal of Concrete Structures and Materials
• /
• v.8 no.4
• /
• pp.289-299
• /
• 2014

Alkali-activated slag concretes are being extensively researched because of its potential sustainability-related benefits. For such concretes to be implemented in large scale concrete applications such as infrastructural and building elements, it is essential to understand its early and long-term performance characteristics vis-a'-vis conventional ordinary portland cement (OPC) based concretes. This paper presents a comprehensive study of the property and performance features including early-age isothermal calorimetric response, compressive strength development with time, microstructural features such as the pore volume and representative pore size, and accelerated chloride transport resistance of OPC and alkali-activated binder systems. Slag mixtures activated using sodium silicate solution ($SiO_2$-to-$Na_2O$ ratio or $M_s$ of 1-2) to provide a total alkalinity of 0.05 ($Na_2O$-to-binder ratio) are compared with OPC mixtures with and without partial cement replacement with Class F fly ash (20 % by mass) or silica fume (6 % by mass). Major similarities are noted between these binder systems for: (1) calorimetric response with respect to the presence of features even though the locations and peaks vary based on $M_s$, (2) compressive strength and its development, (3) total porosity and pore size, and (4) rapid chloride permeability and non-steady state migration coefficients. Moreover, electrical impedance based circuit models are used to bring out the microstructural features (resistance of the connected pores, and capacitances of the solid phase and pore-solid interface) that are similar in conventional OPC and alkali-activated slag concretes. This study thus demonstrates that performance-equivalent alkali-activated slag systems that are more sustainable from energy and environmental standpoints can be proportioned.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.34 no.6
• /
• pp.1743-1751
• /
• 2014

It is well known that latex modification can lead to enhancement compressive and flexural performance, tensile bond strength, chloride penetration resistance and freezing-thawing resistance for concrete. For these, many studies for LMC pavement have been widely conducted more than those for conventional pavement concrete. However, due to several problems such as noise and construction cost, new approaches for LMC have been executed to improve the performance of LMC. Recently, Remicon LMC was developed in order to solve the problems of LMC. In this study, the durability of Remcion LMC was compared with latex and mineral additive mixing ratio. From the results, when latex and mineral additive were mixed in Remicon LMC, compressive, flexural and bond strength were satisfied with Korea Highway Construction Guide Specification. And, it showed that the qualitative effect of latex and mineral additive mixing ratio on the durability of Remicon LMC was investigated experimentally. Also, the latex mixed in Remicon LMC must be at least 8%, in order to ensure the durability equivalent or higher than conventional LMC.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.9 no.3
• /
• pp.287-294
• /
• 2021

In this study, tests were performed to analyze the feasibility of using the ground stabilizer from recycled resources such as blast furnace slag powder as filling material of prebored piles. For this, specimens were prepared by applying 70% and 83% of the general water/binder ratio of the filling material of prebored piles. And compression test, model test, and shaking table test were performed to determine the compressive strength, skin friction on the surface between prebored pile and filling material, and seismic performance of ground stabilizer. As a result of the tests, the compressive strength exceeded the relevant domestic standards, and the skin friction was equivalent to that of ordinary portland cement. In addition, the amount of vertical and horizontal displacement caused by earthquakes was found to be much smaller than the domestic standard. Therefore, when considering the test results comprehensively, it is judged that the feasibility of using a ground stabilizer from recycled resources as filling material for prebored pile is sufficient.

• Geomechanics and Engineering
• /
• v.28 no.3
• /
• pp.255-263
• /
• 2022

Lime stabilization has conventionally been listed amid the key techniques of chemical stabilization. Replacing lime with sustainable agro-based by-products have gained prominence in recent decades. Bagasse ash (BA) is one such potential alternatives, an industrial waste with abundance in production, and industries exploring sustainable solutions for its safe disposal. Supplementing BA with lime could be an ideal approach to reduce lime consumption. However, suitability of BA and lime for the stabilization of expansive clays, such as black cotton (BC) soil is yet to be explored. This paper therefore aims to investigate the suitability of BA-lime mixtures to stabilize BC soil with emphasis to compaction behaviors and unconfined compressive strength (UCS) using standard laboratory procedures. Suitability of BA-lime mixture is then assessed against addition of calcium sulphate which, from previous experience, is detrimental with lime stabilization. Experimental outcomes nominate 15% BA as the optimum value observed from both compaction and UCS data, while addition of 4% lime to 15% BA showed the best results. Mineralogical and microstructural analysis show the presence of cementitious compounds with addition of lime and calcium sulphate with curing periods. While, formation of Ettringite needles were noted with the addition of calcium sulphate in BA-lime mixtures (at optimum values) after 90-day curing, and UCS results showed a decrease at this point. To this end, addition of BA in lime stabilization showed encouraging results as assessed from the compaction and UCS results. Nonetheless usage of calcium salts, with utmost emphasis on calcium sulphate and equivalent should be avoided.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.11 no.1
• /
• pp.25-31
• /
• 2023

In this study, the basic properties of CO₂ immobilized desulfurized gypsum (CFBG) and the possibility of being used as a stimulus for slag cement were reviewed, and performance evaluation was conducted through a concrete mixing test. The main components of CFBG were CaO and SO₃, and CaO and SO₃ increased as the drying temperature increased. The moisture content of undried CFBG was 15.7 %, the drying temperature was 1.7 % and the drying temperature was 0.03 % at 105 ℃. Mortar using CFBG tended to have a lower flow value as the drying temperature increased, and the compressive strength was equivalent to that of the FGB use mixture. As a result of the concrete experiment using CFBG SC, both slump and air volume satisfied the target range after 60 minutes, and the compressive strength tended to increase overall compared to the ternary binder mixture.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.12 no.1
• /
• pp.25-32
• /
• 2024

In this study, the mechanical properties of PHC pile concrete using alpha-type hemihydrate gypsum were evaluated. As the replacement ratio of alpha-type hemihydrate gypsum increased, the setting time rapidly accelerated. In particular, when replacement ratio exceeded 20 %, the setting time was shortened due to rapid hydration reaction, making it impossible to secure working time. As the replacement ratio of alpha-type hemihydrate gypsum increased, the ettringite and gypsum peaks tended to increase, and it is believed that the shrinkage of concrete decreased due to the increase in the ettringite peak. At a As the replacement ratio of 5 to 15 % for alpha-type hemihydrate gypsum, the compressive strength increased or was found to be equivalent to that of OPC. But at 20 % substitution, workability deteriorated due to rapid setting, so use of the 5 to 15 % range is considered appropriate.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.11 no.4
• /
• pp.407-415
• /
• 2023

In this study, a carbonation test was conducted on cementitious composites reinforced with recycled waste rope fibers (W series) according to EN 12390-12 standards. The test results were compared to those of commercially available polypropylene fibers (P series). In the carbonation test, both the carbonation depth and area were significantly influenced by the water-to-cement ratio. Notably, the carbonation resistance performance of cementitious composites containing waste rope fibers surpassed that of commercially available PP fibers under equivalent conditions. Throughout the 250-day test period, the W series exhibited higher compressive strength values than the P series, while both series displayed a similar trend of strength increase during the same duration. During the initial stage, the W series exhibited flexural strength levels similar to those of the P series. However, in the later stages, the P series showed a higher mean flexural strength by 1.0 MPa.

• Journal of the Korea Institute of Building Construction
• /
• v.14 no.1
• /
• pp.68-75
• /
• 2014

In order to increase the integrity of the wellbore which is used to prevent the leakage of supercritical $CO_2$, it is necessary to develop a concrete that is strongly resistant to carbonation. In an environment where the concentration of $CO_2$ is exceptionally high, $Ca^{2+}$ ion concentration in pore solution of Portland cement concrete will drop significantly due to the rapid consumption of calcium hydroxide, which decreases the stability of the calcium silicate hydrate. In this research, calcium phosphates were used to modify Portland cement system in order to produce hydroxyapatite, a hydration product that is strongly resistant to carbonation under such an environment. According to the experimental results, calcium phosphates reacted with Portland cement to form hydroxyapatite. The formation of hydroxyapatite was verified using X-ray diffraction analyses with selective extraction techniques. When using dicalcium phosphate dihydrate and tricalcium phosphate, the 28-day compressive strength was lower than that of plain cement paste. However, the specimen with monocalcium phosphate monohydrate showed equivalent strength to that of plain cement paste.

• Computers and Concrete
• /
• v.6 no.6
• /
• pp.451-472
• /
• 2009

Based on a numerical method to analyse the full-range behaviour of prestressed concrete beams with unbonded tendons, parametric studies are carried out to investigate the influence of 11 parameters on the curvature ductility of unbonded prestressed concrete (UPC) beams. It is found that, among various parameters studied, the depth to prestressing tendons, depth to non-prestressed tension steel, partial prestressing ratio, yield strength of non-prestressed tension steel and concrete compressive strength have substantial effects on the curvature ductility. Although the curvature ductility of UPC beams is affected by a large number of factors, rather simple equations can be formulated for reasonably accurate estimation of curvature ductility. Conversion factors are introduced to cope with the difference in partial safety factors, shapes of equivalent stress blocks and the equations to predict the ultimate tendon stress in BS8110, EC2 and ACI318. The same equations can also be used to provide conservative estimates of ductility of UPC beams with compression steel.