• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2020.06a
• /
• pp.128-129
• /
• 2020

In this study, flexural strength and tile adhesion strength were evaluated by using a mortar, dry mortar and an epoxy resin reinforced mortar to examine the adhesion performance by reinforcing the epoxy resin adhesive. As a result, it was clearly confirmed that the effect of improving the adhesion strength by reinforcing the epoxy resin adhesive regardless of the type of tile, and in particular, when applying the epoxy resin adhesive to the porcelain and polishing tiles, it is judged that sufficient adhesion performance can be secured.

• Journal of the Korea Institute of Building Construction
• /
• v.7 no.3
• /
• pp.107-113
• /
• 2007

This study is to investigate adhesive properties depending on the temperature, humidity, and freeze-thraw of the Steel plate adhesive strengthening method by the epoxy resin. The results are summarized as following. For the temperature variation, the debonding failure appear only after 1 cycle of temperature varoation because the coefficient of thermal expansion of the epoxy resin is comparatively large, and the bonding strength is decreased. The deformation properties and ultrasonic pulse velocity on each materials are similar until 4 cycles on the dry and moisture test. As the freeze-thraw test, the epoxy resin is degraded easily subjected to freeze-thaw cycle, comparatively easy, so the debonding failure may occur in short term because of the freeze-thaw repeatition.p

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2018.11a
• /
• pp.79-80
• /
• 2018

Recently, the interest in remodeling of new and old buildings is increasing worldwide. As a result, the frequency of use of architectural adhesives has increased. Currently, adhesives used in buildings are made of organic materials in most cases, and epoxy resin adhesives are most widely used. However, epoxy resin adhesives contain formaldehyde and VOCs in the room during construction, which can cause sick house syndrome. In case of building fire, it may cause damage due to carbon monoxide generated from organic materials. It is urgent to study the problem of epoxy fill adhesive made of such organic materials. Therefore, the purpose of this study is to investigate the effect of the adhesion of epoxy resin adhesive, which is a problem of epoxy resin adhesive, which is an existing organic adhesive by using inorganic materials such as magnesia and phosphate, And the inorganic adhesive which does not emit the release amount as an inorganic material.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1998.04b
• /
• pp.627-632
• /
• 1998

This study deals with the effect on adhesive strength properties of waterproofing and reinforcing layer and mortar or concrete substrate applicated by epoxy resin anticorrosive and bonding materials. Properties of adhesive strength change condition of concrete substrate, temperature, moisture, curing and cleaning and so on. The purpose of this study is that it makes the estimation value of bond strength of concrete wall and epoxy resin layer when coated epoxy resin as anticorrosive materials for durability performance estimation depend on concrete watertightness, and when penetrated epoxy resin for the reinforcement of concrete used the carbon fiber sheet.

• Textile Coloration and Finishing
• /
• v.34 no.3
• /
• pp.157-164
• /
• 2022

This study tried to analyze the heat resistance properties by blending epoxy and phenolic resin in a certain ratio, and to analyze the adhesive properties at the time of metal-polymer hetero-adhesion by applying Epoxy-phenolic resin between a silicon steel sheet and m-aramid sheet, the viscosity, adhesive peel strength, and adhesive cross section were measured using a rotational rheometer, a tensile tester(UTM), and a field emission scanning electron microscopy(FE-SEM). The thermal stability and heat resistance were confirmed by measuring the mass loss according to the temperature increase using Thermogravimetric analysis(TGA). After blending with epoxy and Phenolic resin(1:0.25 ratio) curing at 110℃ for 10 min, high adhesive strength was improved more than 40% compared to the adhesive strength using epoxy alone. When the space between the silicon steel sheet and m-aramid sheet, which is created during curing of the E-P blend, is cured with a slight weight, it is possible to control the empty space and improve adhesion.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2020.11a
• /
• pp.163-164
• /
• 2020

The purpose of this study was to evaluate the shrinkage properties of a tile reinforced with epoxy resin, which has the advantages of high adhesion and low shrinkage, and causes a hardening reaction by chemical bonding with cement mortar. As a result, since the epoxy resin adhesive suppresses the moisture evaporation of the mortar, the drying shrinkage of the mortar itself is reduced, accordingly, the shrinkage of the tile itself is greatly reduced, and it is thought that it is possible to prevent a decrease in adhesion due to shear stress.

• Elastomers and Composites
• /
• v.43 no.1
• /
• pp.39-48
• /
• 2008

Peel strength of epoxy adhesives can be increased by adding some amounts of XNBR. In this case, thermal resistance of the adhesive will be decreased by decrease of glass transition temperature of the adhesive. Epoxy resin modified with siloxane-imide was synthesized to improve thermal resistance and peel strength of the adhesive, after that the properties of modified epoxy resin were compared with the commercial epoxy resin. When 5% XNBR was added to 30% modified epoxy resin, this adhesive showed 0.42 N/mm of peel strength and $155^{\circ}C$ of glass transition temperature. These properties are enough compared to the required properties by the industry, i.e., 0.3 N/mm and $150^{\circ}C$, respectively. Weight loss of the modified epoxy resin by the treatment of nitric acid and 0.1N NaOH was reduced, but weight gain by the humid condition was increased by the presence of benzene ring and imide ring. 30% modified epoxy resin blended with 5% XNBR showed 220% improvement in tensile strength and elongation compared to the case of common epoxy resin. This is due to the flexibility of the siloxane in the modified epoxy resin.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1998.04b
• /
• pp.613-617
• /
• 1998

This study deals with the effect on adhesive strength properties of fiber sheet layer and maintenance position of coccrete structure reinforced using epoxy resin carbon and aramit fiber sheet. Properties of epoxy resin adhesive strength of the concrete bridge slab, tunnel and wall etc. reinforced using fiber sheet under many different environment change according to condition of concrete substrate, temperature, moisture, curing, cleaning, and chemical effects and so on. The purpose of this study is that it makes the estimation value of adhesive strength of concrete substrate and fiber sheet reinforcing layer penetrated epoxy resin under high temperature(9$0^{\circ}C$), chemical attack and condition of curing.

• Journal of the Korean institute of surface engineering
• /
• v.49 no.6
• /
• pp.549-554
• /
• 2016

Low melting metals are difficult to weld because it is vaporized. But epoxy resin make bonding possible using low melting material and dismissal materials. This study is to improve the bonding strength of epoxy and substrate by mechanical and electrochemical methods. In case of mechanical work, bonding strength is 17.6MPa and in case of pre-work, bonding strength is 15.3MPa. When anodizing and mechanical work is applied, bonding strength is 25.3Mpa is increased 165%. When anodizing is applied, bonding strength is 27.6Mpa.

• Restorative Dentistry and Endodontics
• /
• v.26 no.4
• /
• pp.316-325
• /
• 2001

The purpose of this study was to evaluate the effect of adhesive curing timing on the direction of polymerization shrinkage of light-curing composite resin. In this study, the curing times of adhesive and composite resin were measured by differential scanning calorimeter(DSC). 28 extracted human molars were embedded in clear resin and box-type cavities were prepared. Based on DSC data, the experimental teeth were divided into 4 groups. Group 1: no bond; Group 2: late curing; Group 3: Intermediate curing; Group 4: Early curing. After treating with adhesive, the buccal cavities were filled with Z-100 hybrid composite resin and the lingual ones were filled with AEliteflo flowable composite resin. The depressions at the surface were measured by surface profilometer, then the specimens were embedded in clear resin and sectioned. Impressions were obtained and used to get epoxy resin replicas. The epoxy replicas were gold-coated and observed under SEM. Average Maximum Gap(AMG), Gap Proportion(GP), Average Marginal Index(AMI) were used to compare the shrinkage gap of each group. The results were statistically analyzed using the Kruskal-Wallis One Way ANOVA, Student-Newman-Keuls method. The results of this study were as follows. 1. Average Maximum Gap, Gap Proportion, Average Marginal Index and depression at the surface or Z-100 hybride composite resin were smaller than those of AEliteflo flowable composite resin(P<0.05). 2. When the bonding between composite resin and tooth structure was strong, the shrinkage gap was small, and depression at the surface was deep(P<0.05). 3. In the well-bonded group, light-curing composite resin shrank toward bonded cavity wall, not toward light source. The result suggested that the direction of polymerization shrinkage was affected by the quality of bonding in the dentin-resin interface. The strong was the bonding between composite resin and tooth structure, the smaller was the gap and the deeper was the depression at the surface. Then the flow to compensate the polymerization shrinkage proceeded from surface to bonded cavity wall.