The purposes of this research were to evaluate the relationships of between characteristics of noise and annoyance of dental hygienist by noise in dental clinic. To investigate the dental clinic workers' reactions to noise when occurred in dental clinic, the noise level test in dental clinic and questionnaire were taken. As a result of noise evaluation, It shows that the range of noise level was 67.7~78.3dB(A) and frequency was very high (more than 4KHz). It's seem to be begins occurrence of stamina-loss, contraction of peripheral blood vessel, decrease of adrenocortical hormones. Most of respondents were affected by noise: 67% of respondents were nervous about noise and the rest of respondents were bearable. Analysis by NR-curve showed that it was exceed the noise permit level in working space. As a result of correlation - test, the more exposed dental hygienist to noise, the more felt the unpleasantness and fatigue. It's hard to sufficient explanation to patients about the dental treatment. So it's thoughts that insufficient explanation will negative impact on the patients' satisfaction and increase competitiveness in dental clinics. To remedy a unpleasantness and fatigue of noise in dental hygienist, it's considered that making an offer the ear protection and choosing the low noise-vib. equipment and using the masking effect. Therefore, It can be provide a pleasant working environment with dental hygienist and It will have a great advantage to dental clinics to improve their competitiveness.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.37 no.6
• /
• pp.1043-1051
• /
• 2017

Asphalt overlay on deteriorated concrete pavement has a problem of early damage due to reflective cracking. There is a need for a new method capable of reducing reflection cracking and ensuring the durability of pavement. The purpose of this study was to obtain durability of asphalt overlay with stress absorbing membrane interlayer (SAMI) using epoxy asphalt binder. The tensile performance, durability, water resistance and bonding performance of Epoxy-SAMI were evaluated by various tests. As a result of tests, Epoxy-SAMI meets the quality standard of the bridge waterproofing material. The repeated direct tensile test was carried out to investigate the effect of reflective cracking reduction. When the Epoxy-SAMI was applied, it had 1.2~1.56 times higher reflective cracking resistance than PSMA asphalt concrete with the thickness of 10cm even if the section thickness decreased. 4-point bending beam test results showed the number of fatigue failures increased 7.5 times when Epoxy-SAMI was applied. The Epoxy-SAMI was found to be effective in improving the durability of the asphalt pavement overlay because it serves to prevent reflective cracking, increase lifespan, and function as a waterproof layer.