• Journal of the Semiconductor & Display Technology
• /
• v.2 no.4
• /
• pp.27-30
• /
• 2003

The effect of fabrication method of catalytic layer on electrode performance has been investigated. Brush, spray gun and screen printer were used as fabrication tool and catalytic layers were formed by several methods in screen printing. Direct screen printing on polymer membrane, screen printing on carbon paper, and their combined method were applied. In the electrode fabricated by the screen printing method, Pt loading of Pt/C catalysts could be cut down to 50%, compared with results by the brushing and spraying methods. The best result of electrode was obtained as 0.6 V, at 1 A/$\textrm{cm}^2$ when catalytic layer was formed by the combined way.

• Journal of the Korean Electrochemical Society
• /
• v.12 no.1
• /
• pp.81-87
• /
• 2009

An indium-tin oxide (ITO) coated spinel manganese oxide (${LiMn_2}{O_4}$, LMO) is prepared and its high-temperature ($55^{\circ}C$) cycle performance and rate capability are examined. A severe electrolyte decomposition and film deposition is observed on the un-coated ${LiMn_2}{O_4}$ cathode, which leads to a significant electrode polarization and capacity fading. Such an electrode polarization is, however, greatly reduced for the ITO-coated (> 2 mol%) LMO cathode, which leads to an improved cycle performance. This can be rationalized by a suppression of electrolyte decomposition, which is in turn indebted to a decrease in the direct contact area between LMO and electrolyte. The suppression of film deposition on the ITO-coated LMO cathode is confirmed by infra-red spectroscopy. The rate capability is also improved by the surface coating, which may be resulted from a suppression of resistive film deposition and high electric conductivity of ITO itself.

• Journal of the Microelectronics and Packaging Society
• /
• v.19 no.4
• /
• pp.65-69
• /
• 2012

Composite coating can be manufactured during the electroplating with the bath containing a suspension of particles: ceramic, polymer, nanopowders. Improvement of hardness, wear resistance, corrosion resistance and lubrication properties are well-known advantage of composite coating. In this study, nano $TiO_2$ powder dispersed Ni composite plating was investigated. The improvement of surface hardness and photo decomposition effects can be expected in this coating. Zeta potential was measured with pH. The effect of ultrasonication time and types of ultrasonicator were studied to minimize the agglomeration of $TiO_2$ nanopowders in the electrolyte. Optimum conditions for nano $TiO_2$ dispersed Ni composite coating were $40mA/cm^2$ of current density, pH 3.5, and $50^{\circ}C$. At these conditions, $TiO_2$ nanoparticles contents in the Ni deposit was 15-20 at.%.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.22 no.10
• /
• pp.890-896
• /
• 2009

Li(Ni, Co, Mn)$O_2$ has been known as one of the most promising cathode materials for lithium secondary batteries. However, it has some problems to overcome for commercialization such as inferior rate capability and unstable thermal stability. In order to address these problems, surface modification of cathode materials by coating has been investigated. In the coating techniques, selection of coating material is a key factor of obtaining enhanced properties of cathode materials. In this work, we introduced solid electrolyte (Li-La-Ti-O) as a coating material on the surface of $Li[Ni_{0.3}Co_{0.4}Mn_{0.3}]O_2$ cathode. Specially, we focused on a rate performance of Li-La-Ti-O coated $Li[Ni_{0.3}Co_{0.4}Mn_{0.3}]O_2$ cathode. Both bare and Li-La-Ti-O 2 wt.% coated sample showed similar discharge capacity at 0.5C rate. However, as the increase of charge-discharge rate to 3C, the coated samples displayed better discharge capacity and cyclic performance than those of bare sample.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.06a
• /
• pp.235-235
• /
• 2010

The Anti-reflection coating(ARC) properties can be formed on silicon substrate using a simple electrochemical etching technique. This etching step can be improve solar cell efficiency for a solar cell manufacturing process. This paper is based on the removal of silicon atoms from the surface a layer of porous silicon(PSi). Porous silicon is form by anodization and can be obtained in an electrolyte with hydrofluoric. It have demonstrated the feasibility of a very efficient porous Si layer, prepared by a simple, cost effective, electrochemical etching method. We expect our research can results approaching to lower than 10% of reflectance by optimization of process parametaer.

• Journal of the Korean institute of surface engineering
• /
• v.31 no.1
• /
• pp.3-11
• /
• 1998

Molten Carbonate Fuel cell is a promising new type electric power generation system which can achieve high efficiency, lower matrrial cost and high operating temperature Making internal reforming possible. Although the development of the MCEC is progressing rapidly toward commercialization, two important tchological problems such as dissolution of NiO cathode and not corrosion of metallic separator plate must be resolved. Because MCFC is operated at $650^{\circ}C$ and the electrolyte is very corrosive, corrosion-resistance of separator plated against oxidation abd molten carbonate is required. Al-coating on separator material for corrosion-resistance was carried out by painting, thermal spraying. hot dipping and vacuum vapour deposition. The corrosion of Al-coated STS 316S and 316L in molten carbonate at $700^{\circ}C$was studied. Vacuum vapour deposition and thermal spraing for Al-coating on STS 310S and 316L were the most effective methods for protecting thestainless steel corrosion in molten carbonate.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.05b
• /
• pp.5-9
• /
• 2005

$LiFePO_4$ is a potential candidate for the cathode material of the lithium polymer batteries. $LiFePO_4$ cathode active materials were synthesized by coating on the $LiFePO_4$ was tried using $TiO_2$ and corbon in oreder to increase cyclic performance and electronic conductivity. Highly dispersed on the particles enhances the electronic conductivity and increases the capacity. For lithium polymer battery applications, $LiFePO_4$/SPE/Li and $LiFePO_4$-$TiO_2$/SPE/Li 'cells were characterized electrochemically by cyclic volatammetry and charge/discharge cycling. The $LiFePO_4$-carbon-$TiO_2$ cathode in PVDF-PC-EC-$LiCIO_4$ electrolyte showed high capacity at high current density.

• Journal of the Semiconductor & Display Technology
• /
• v.12 no.3
• /
• pp.7-12
• /
• 2013

Ni-CNT(Carbon Nanotube) composite coatings is were formed by electrodeposition and their physical properties were investigated with variations of CNT content(1, 3, 6. 9 g/L) in the electrolyte solution, while the current density and electroplating time were fixed respectively at $6A/dm^2$ and 90 min.. With increasing CNT content from 1 to 9 g/L, incorporated CNTs into the composite coating were limited from 4.65 wt.% to 7.38 wt.%. Microhardness and contact angle values were increased with increasing CNT content of upto 3 g/L. With increasing the CNT content further, physical properties were degraded due to agglomeration, poor adhesion of CNTs to Ni matrix and thus rough surfaces. Optimum electroplating conditions were found to be the CNT content of 3 g/L, current density of 6 A/dm2 and electroplating time of 90 min.

• Transactions on Electrical and Electronic Materials
• /
• v.12 no.1
• /
• pp.1-6
• /
• 2011

This paper summarized concept, manufacture and results of the micro-tubular solid oxide fuel cells (SOFCs). The cells were fabricated by co-sintering of extruded micro-tubular anode support and electrolyte coating layer, and then additional cathode coating. The cells showed quick voltage rising within 1 minute, and the electrochemical performances were closely related to the balance of fuel utilization and performance loss. And a thermal-fluid simulation model was also reported in combination with the electrochemical evaluation results on the GDC-based micro-tubular SOFCs.

• Journal of Ceramic Processing Research
• /
• v.13 no.spc2
• /
• pp.198-201
• /
• 2012

The electrolytes in thermal batteries are nonconductive solids at ambient temperature, which prevent the self-discharge and corrosion. To meet severe environmental requirements and guarantee acceptable handling yields, all the pellets in cells should have adequate strength, especially for the cathodes due to their poor binding properties among FeS2 particles. By modifying the surface microstructure of FeS2 through molten-salt heat treatment, the inter-particle binding strength is greatly increased, resulting in the enhanced pellet strength and yield. The addition of Li2O also promoted the soft salt coating coverage of hard FeS2 particles, which can be explained by the enhanced wettability of the molten salt.