• Polymer(Korea)
• /
• v.31 no.3
• /
• pp.184-188
• /
• 2007

Monodisperse PMMA/HDDA polymer particles were coated via electroless Ni plating using sodium hypophosphite as a reducing agent in an acidic environment. In this study, the effects of 1) the pretreatment conditions, 2) the plating temperature, 3) the plating pH, and 4) the initial pH, control of plating bath on the variation of plating rate, surface state of plated particles and plating reproducibility were investigated. It was observed that every pretreatment steps, especially conditioning and acceleration step, were very important for obtaining uniform Ni plating and the plating rate was increased with the increase of plating temperature and pH. Moreover, the initial pH control of plating bath was critical for the plating reproducibility.

• Korean Journal of Materials Research
• /
• v.10 no.12
• /
• pp.853-863
• /
• 2000

In this study, a new UBM materials system for solder flip chip interconnection of Cu pads were investigated using electroless copper (E-Cu) and electroless nickel (E-Ni) plating method. The interfacial reaction between several UBM structures and Sn-36Pb-2Ag solder and its effect on solder bump joint mechanical reliability were investigated to optimife the UBM materials design for solder bump on Cu pads. Fer the E-Cu UBM, continuous coarse scallop-like $Cu_{6}$ $Sn_{5}$ , intermetallic compound (IMC) was formed at the solder/E-Cu interface, and bump fracture occurred this interface under relative small load. In contrast, Fer the E-Ni/E-Cu UBM, it was observed that E-Ni effectively limited the growth of IMC at the interface, and the Polygonal $Ni_3$$Sn_4$ IMC was formed because of crystallographic mismatch between monoclinic $Ni_3$$Sn_4$ and amorphous E-Ni phase. Consequently, relatively higher bump adhesion strength was observed at E-Ni/E-Cu UBM than E-Cu UBM. As a result, it was fecund that E-Ni/E-Cu UBM material system was a better choice for solder flip chip interconnection on CU PadS.

• Journal of the Microelectronics and Packaging Society
• /
• v.11 no.2 s.31
• /
• pp.11-16
• /
• 2004

Electronic devices are getting smaller due to integration of electronic chip, and heat generated in electronic devices can cause loss of performance and/or reliability of the devices. In this research, metals such as gold, nickel and copper are plated onto a porous membrane by electroless plating method to make an efficient micro-heatsinks. Electroless plating includes sensitization and activation steps in pre-treatment steps. A polycarbonate(PC) membrane was sensitizied, activated and deposited in each metal solution for plating. Among manufactured microfibrils, heat transfer and radiation properties of Ni-microfibril with high surface area were more effective than those of $Au^-$ and Cu-microfibril.

• Transactions of the Korean hydrogen and new energy society
• /
• v.20 no.5
• /
• pp.361-370
• /
• 2009

Ni-PTFE composite plated on graphite (C/Ni-PTFE) and PTFE (PTFE/Ni-PTFE) particles were prepared uniformly by electroless composite plating. The conductivity of C/Ni-PTFE particles was 280 S/m higher than 95 S/m of PTFE/Ni-PTFE particles at same composite plating condition (Ni:35~36 wt%, PTFE:8 wt%). The C/Ni-PTFE particles were formed into the C/Ni-PTFE plate using heat treatment at $350^{\circ}C$ under 10~$1000\;kg/cm^2$. The C/Ni-PTFE plate showed 1) high conductivity of $5.7\;{\times}\;10^4\;S/m$ due to the existence of graphite as conducting aid and the formation of 3-dimensional Ni network 2) good gas diffusion caused by various pore volumes (0.01~$100\;{\mu}m$) in the plate. The plate could be useful for an electrode in an alkaline fuel cell (AFC). The current density of C/Ni-PTFE electrode indicated $84\;mA/cm^2$ at 0.3V and it was 3.0 times higher than that of PTFE/Ni-PTFE electrode.

• Journal of the Microelectronics and Packaging Society
• /
• v.12 no.2 s.35
• /
• pp.95-103
• /
• 2005

The interfacial reaction between 42Sn-58Bi solder (in wt.$\%$ unless specified otherwise) and electroless Ni-P/immersion Au has been investigated before and after thermal aging, with a focus on formation and growth of an intermetallic compound (IMC) layer, consumption of under bump metallurgy (UBM), and bump shear strength. The immersion Au layer with thicknesses of 0 (bare Ni), 0.1, and $1{\mu}m$ was plated on the $5{\mu}m$ thick electroless Ni-P ($14{\~}15 at.\%$P) layer. Then, the 42Sn-58Bi solder balls were fabricated on three different UBM structures by screen-printing and pre-reflow. The $Ni_3Sn_4$ layer (IMC1) was formed at the joint interface after pre-reflow for all the three UBM structures. On aging at $125^{\circ}C$, a quaternary phase (IMC2) was observed above the $Ni_3Sn_4$ layer in the Au-containing UBM structures, which was identified as $Sn_{77}Ni{15}Bi_6Au_2$ (in at.$\%$). The thick $Sn_{77}Ni{15}Bi_6Au_2$ layer deteriorated the integrity of the solder joint and the shear strength of the solder bump was decreased by about $40\%$ compared with non-aged joints.

• Journal of the Korean Magnetics Society
• /
• v.15 no.3
• /
• pp.202-206
• /
• 2005

The present investigation provides an electromagnetic radiation absorptive composition which comprises silver-coated ferrite microspheres dispersed in silicon rubber matrix for the aim of thin microwave absorber in GHz frequencies. Ni-Zn ferrite spheres with $50{\mu}m$ size in average were prepared by spray-drying and sintering at $1130^{\circ}C$. Conductive silver layer was plated on ferrite spheres by electroless plating. Conductive Ni-Zn ferrite sphere with uniform silver layer were obtained in the concentration of 10 g/L $AgNO_3$ per 20 g ferrite spheres. For this powder, electrical resistance is reduced as low as $10^{-2}\~10^{-3}\;\Omega$. The most sensitive material parameters with silver plating is real and imaginary parts of complex permittivity. The conductive Ni-Zn ferrite spheres have large values of dielectric constant. Due to this high dielectric constant of microspheres, matching thickness is reduced to as low as 2 mm at the frequency of 7 GHz, which is much thinner than conventional ferrite absorbers.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.192-193
• /
• 2007

An evaporated Ti/Pd/Ag contact system is most widely used to make high-efficiency silicon solar cells, however, the system is not cost effective due to expensive materials and vacuum techniques. Commercial solar cells with screen-printed contacts formed by using Ag paste suffer from a low fill factor and a high shading loss because of high contact resistance and low aspect ratio. Low-cost Ni and Cu metal contacts have been formed by using electro less plating and electroplating techniques to replace the Ti/Pd/Ag and screen-printed Ag contacts. Ni/Cu alloy is plated on a silicon substrate by electro-deposition of the alloy from an acetate electrolyte solution, and nickel-silicide formation at the interface between the silicon and the nickel enhances stability and reduces the contact resistance. It was, therefore, found that nickel-silicide was suitable for high-efficiency solar cell applications. Cu was electroplated on the Ni layer by using a light induced plating method. The Cu electroplating solution was made up of a commercially available acid sulfate bath and additives to reduce the stress of the copper layer. In this paper, we investigated low-cost Ni/Cu contact formation by electro less and electroplating for crystalline silicon solar cells.

• Polymer(Korea)
• /
• v.30 no.4
• /
• pp.332-337
• /
• 2006

Monodisperse polymer particles were prepared via one-step seeded polymerization using PMMA seed particles and HDDA (or EGDMA) as crosslinking monomer. For the study, the effects of 1) the ratio of the absorbed monomer or monomer mixture to the seed polymer particles (swelling ratio), 2) the ratio of EGDMA in absorbed monomer mixture, 3) the dosage of initiator, and 4) electro less Ni plating on the variation of mechanical properties of monodisperse polymer particles, such as recovery rate, K-values, breaking strength and breaking displacement, were investigated by using MCT (micro compression test). It was observed that monomer swelling ratio influenced only breaking strength, but EGDMA ratio in monomer mixture, dosage of initiator and electroless Ni plating affected both K-values and breaking strength.

• Korean Journal of Materials Research
• /
• v.5 no.7
• /
• pp.794-801
• /
• 1995

To connect the driver IC and Al coated glass, a method has been developed to plate electrolessly Ni on Al/PR system. It Is necessary to pretreat Al to remove oxide film before plating. In order to find pretreatment process which does not damage photoresist or glass, alkaline and fluoride zincate process have been investigated. Because photoresist and aluminum thin film can easily dissolve in alkaline solution, it is considered that the fluoride zincate process was a suitable one. After immersion in the zincate solution containing 1.5 g/$\ell$ ammonium bifluoride and 100 g/$\ell$ zinc sulfate, electroless nickel plating could be performed. The additive in the zincate solution and thiourea in the plating solution increased smoothness of the plated surface. Acld dip could improve the uniformit of the surface.

• Journal of environmental and Sanitary engineering
• /
• v.18 no.3 s.49
• /
• pp.35-42
• /
• 2003

The electric resistance and constant current were investigated on the nickel-thallium-phosphorus alloy deposits by electroless-plating. The Ni-Tl-P alloy deposits were achieved with a bath using sodium hypophosphit as the reducing agent and sodium citrate as the comlexing agent. The basic plating solution is composed of 0.1M NiSO$_4$, 0.005${\sim}$0.0IM Tl$_2$S0$_4$, 0.1${\sim}$O.2M sodium hypophosphite and 0.02${\sim}$O.IM sodium citrate and the plating condition were pH 5${\sim}$6, temperrature 80$_4$90${\circ}$C. The results obtained are summarized as follows: 1) The crystal structure of deposit was amorphous structure as deposited state, became microcrystallized centering on Ni(111) plane by heat treatment at 200${\circ}$C, and grew as polycrystalline Ni, Ni$_3$P, Ni$_5$p$_2$,Tl, etc. by heat treatment higher than 350${\circ}$C. The grain size of plated deposits was grown up to 28.3~42.0nm by heat treatment for 1hour at 500${\circ}$C. 2) The electrical resistivity showed a comparatively high value of 192.5$_4$208.3 ${\mu}$${\Omega}$Cm and its thermal stability was great with resistivity value less than 0.22% in the thermal surroundings of 200${\circ}$C. 3) Ni-Tl-P alloy deposit showed such good constant current-making-effect in the variation of electric voltage, heat treatment temperature, and the composition of the deposit that it can be put to practical use as the matter of constant current device.