• 한국재료학회지
• /
• 제19권2호
• /
• pp.61-67
• /
• 2009

Electrolessly deposited Co (Re,P) was investigated as a possible capping layer for Cu wires. 50 nm Co (Re,P) films were deposited on Cu/Ti-coated silicon wafers which acted as a catalytic seed and an adhesion layer, respectively. To obtain the optimized bath composition, electroless deposition was studied through an electrochemical approach via a linear sweep voltammetry analysis. The results of using this method showed that the best deposition conditions were a $CoSO_4$ concentration of 0.082 mol/l, a solution pH of 9, a $KReO_4$ concentration of 0.0003 mol/l and sodium hypophosphite concentration of 0.1 mol/L at $80^{\circ}C$. The thermal stability of the Co (Re,P) layer as a barrier preventing Cu was evaluated using Auger electron spectroscopy and a Scanning calorimeter. The measurement results showed that Re impurities stabilized the h.c.p. phase up to $550^{\circ}C$ and that the Co (Re,P) film efficiently blocked Cu diffusion under an annealing temperature of $400^{\circ}C$ for 1hr. The good barrier properties that were observed can be explained by the nano-sized grains along with the blocking effect of the impurities at the fast diffusion path of the grain boundaries. The transformation temperature from the amorphous to crystal structure is increased by doping the Re.

• 지질공학
• /
• 제26권1호
• /
• pp.79-85
• /
• 2016

방사성폐기물 처분시설 공학적방벽을 구성하는 콘크리트는 주변 환경의 영향으로 내구 수명에 영향을 받게 된다. 현재까지 개발된 수치해석 모델 및 실험을 통하여 방사성폐기물 처분시설 공학적방벽 소재로 가장 널리 사용되는 콘크리트에 대해 주변환경을 고려하여 그 영향을 살펴보았다. 본 연구에 해당하는 철근 콘크리트 구조물은 지리적으로 해안과 인접한 지하수 포화대에 위치하고 있다. 일반적인 철근콘크리트 구조물의 가장 민감한 열화인자인 염해에 의한 철근부식에 대한 영향을 염화물 확산모델을 이용하여 평가한 결과 철근 부식 개시기간이 1,284년이며, 최종적으로 구조물이 내구수명을 상실하는데 도달하는 시간은 1,924년인 것으로 예측되었다. 또한, Mock-up 실험을 통해 공극분포, 공극률, 부식정도 등 물리화학적 특성을 평가한 결과 콘크리트 내 철근 부식정도는 미비한 것으로 나타나 500년 이상의 상당히 오랜 기간 건전성을 유지할 수 있는 것으로 판단된다.

• 공업화학
• /
• 제9권1호
• /
• pp.44-51
• /
• 1998

본 실험에서 QCA를 사용하여 $NaClO_4$, $LiClO_4$, $KClO_4$전해질 용액에서 전기중합한 폴리피롤 박막의 점탄성 특성을 in situ 분석하였다. 수정진동자를 특수 제작한 전기화학 분석셀에 넣어 수정진동자의 한쪽 전극을 작용전극으로 사용하였다. 공진주파수와 공진저항 상관도 (F-R)도를 이용하여 폴리피롤 박막의 점탄성을 해석하였고 AFM 사진과 비교 검토하였다. 피롤을 정전류에서 중합하여 피막한 수정진동자를 이용하여 순환전위주사하면서 공진주파수, 공진저항, 전류를 측정하여 폴리피롤 박막의 산화-환원 반응 거동을 분석하였다. 본 실험 결과, 전기중합 초기에는 피롤 박막이 탄성적으로 거동하다가 중합되어 감에 따라 점차 점탄성막으로 변하여 감을 알 수 있었다. 동시에 박막 사이로 전해질 용액이 침투됨에 따라 박막의 두께가 증가하면서 표면 형상도 변화하였다. 이와 같은 현상은 중합할 때의 전해질과 전위주사할 때의 전해질 용액을 변화시키면서 순환전위주사하여도 발생하였다.

• 한국세라믹학회지
• /
• 제42권4호
• /
• pp.251-259
• /
• 2005

혼합전도체 산화물, LSCF의 전극반응점 분포에 따른 분극현상을 관찰하기 위해 다공성 양극의 기공률을 변화시켜가며 분극특성을 관찰하였다. 전극의 기공률을 달리하기 위해 크기가 다른 두 종류의 LSCF 분말들을 혼합비를 달리하여 사용하였으며 GDC 전해질 기판에 스크린 인쇄법을 통해 전극을 구성한 후 반쪽전지 실험을 수행하였다. 제조된 후막전극의 기공률은 화상 분석법을 통해 측정하였으며 전극의 전체 비표면적을 유추하기 위해 2차원 이미지에서의 기공의 둘레 길이를 측정하였다. 교류 임피던스법을 이용해 분극 특성을 관찰한 결과 혼합전도체인 LSCF 양극에서의 전극반응은 i) 양극표면에서 이온화된 산소이온이 전해질과의 삼상계면까지 이동해 오는 단계, ii) 이동해온 산소이온이 양극으로부터 전해질로 전달되는 반응단계에 의해 제어됨을 알 수 있었다. 이러한 양극에서의 분극은 기공률의 증가에 따라 전극 반응에 필요한 활성 표면이 증가됨으로써 줄어드는 것을 알 수 있었다.

• 한국세라믹학회지
• /
• 제42권4호
• /
• pp.269-275
• /
• 2005

단전지의 성능을 혼합전도체인 LSCF 양극의 미세구조, 특히 전극반응에 필요한 표면적의 양과 연관되는 앙극의 기공률의 변화에 따라 평가하였다. 기공률이 서로 다른 양극을 제조하기 위해 미세한 양극분말과 조대한 양극분말의 혼합비를 달리하여 양극을 제조한 결과 양극의 기공률을 각각 14, 23, 27, $39\%$로 얻을 수 있었다. 양극 기공률이 서로 다른 4종류의 단전지에 대한 직류 전류차단법과 교류임피던스법을 이용한 전기화학적 평가 결과 전극에서의 분극은 양극의 기공률이 증가할수록 감소하는 결과를 얻었다. 이러한 분극특성은 양극의 기공률이 증가하며 전극반응에 필요한 활성면적이 증가했기 때문으로 추론되며 이러한 이유로 단전지의 성능 또한 양극의 기공률이 증가하면서 향상되는 것으로 나타났다.

• The Korean Journal of Ceramics
• /
• 제4권2호
• /
• pp.95-98
• /
• 1998

We have developed new type of superconducting-superionic conducting nanohybrids, $Ag_xI_wBi_2Sr_2Ca_{n-1}Cu_nO_y$ (n=1 and 2) by applying the chimie douce reaction to the superconducting Bi-based cuprates. These nanohybrids can be achieved by the stepwise intercalation whereby the $Ag^+$ ion is thermally diffused into the pre-intercalated iodine sublattice of $IBi_2Sr_2Ca_{n-1}Cu_nO_y$. According to the X-ray diffraction analysis, the Ag-I intercalates are found to have an unique heterostructure in which the superionic conducting Ag-I layer and the superconducting $IBi_2Sr_2Ca_{n-1}Cu_nO_y$ layer are regularly interstratified with a remarkable basal increment of ~7.3$\AA$. The systematic XAS studies demonstrate that the intercalation of Ag-I accompanies the charge transfer between host and guest, giving rise to a change in hole concentration of $CuO_2$ layer and to a slight $T_c$ change. The Ag K-edge EXAFS result reveals that the intercalated Ag-I has a $\beta$-AgI-like local structure with distorted tetrahedral symmetry, suggesting a mobile environment for the intercalated $Ag^+$ ion. In fact, from ac impedance analyses, we have found that the Ag-I intercalates possess a fast ionic conductivity ($\sigma_i=10^{-1.4}\sim 10^{-2.6}\Omega^{-1}\textrm{cm}^{-1}\;at\;270^{\circ}C$ with an uniform activation energy ($\DeltaE_a=0.22\pm 0.02$ eV). More interesting finding is that these intercalates exhibit high electronic conducting as well as ionic ones ($t_i$=0.02~0.60) due to their interstratified structure consisting of superionic conducting and superconducting layers. In this respect, these new intercalates are expected to be useful as an electrode material in various electrochemical devices.

• 방사성폐기물학회지
• /
• 제15권2호
• /
• pp.125-133
• /
• 2017

KAERI에서는 파이로프로세싱에서 발생하는 금속폐기물의 부피 및 무게 감량을 위해 고방사성 장반감기 핵종을 포함하는 anode sludge내 NM의 고화매질로써 폐피복관과 첨가금속을 재활용하는 연구를 진행하고 있다. 본 연구에서는 Cr 함량을 조절한 Zr-17Cr-8NM, Zr-22Cr-8NM, Zr-27Cr-8NM 합금을 유도용융을 통해 제조하였고, 전기화학적 부식시험을 실시하여 부식특성을 평가하였다. 모든 조성에서 기존 연구 중인 Zr계 합금고화체 조성보다 우수한 부식특성을 나타냈다. 또한 Zr-22Cr-8NM 시편의 부식시험 후 침출용액 조성 분석 결과, 500 mV 전압 조건 이하에서는 NM 침출이 없었고 이를 통해 우수한 화학적 안정성을 갖는 합금고화체 조성을 확보하였다.

• Corrosion Science and Technology
• /
• 제6권6호
• /
• pp.316-321
• /
• 2007

The effect of annealing on the pitting corrosion resistance of anodized Al-Mg alloy (AA5052) processed by equal-channel angular pressing (ECAP) was investigated by electrochemical techniques in a solution containing 0.2 mol/L of $AlCl_3$ and also by surface analysis. The Al-Mg alloy was annealed at a fixed temperature between 473 and 573 K for 120 min in air after ECAP. Anodizing was conducted for 40 min at $100-400A/m^2$ at 293 K in a solution containing 1.53 mol/L of $H_2SO_4$ and 0.0185 mol/L of $Al_2(SO_4)_3$. The internal stress generated in anodic oxide films during anodization was measured with a strain gauge to clarify the effect of ECAP on the pitting corrosion resistance of anodized Al-Mg alloy. The time required to initiate the pitting corrosion of anodized Al-Mg alloy was shorter in samples subjected to ECAP, indicating that ECAP decreased the pitting corrosion resistance. However, the pitting corrosion resistance was greatly improved by annealing after ECAP. The time required to initiate pitting corrosion increased with increasing annealing temperature. The strain gauge attached to Al-Mg alloy revealed that the internal stress present in the anodic oxide films was compressive stress, and that the stress was larger with ECAP than without. The compressive internal stress gradually decreased with increasing annealing temperature. Scanning electron microscopy showed that cracks occurred in the anodic oxide film on Al-Mg alloy during initial corrosion and that the cracks were larger with ECAP than without. The ECAP process of severe plastic deformation produces large internal stresses in the Al-Mg alloy; the stresses remain in the anodic oxide films, increasingthe likelihood of cracks. It is assumed that the pitting corrosion is promoted by these cracks as a result of the higher internal stress resulting from ECAP. The improvement in the pitting corrosion resistance of anodized AlMg alloy as a result of annealing appears to be attributable to a decrease in the internal stresses in anodic oxide films

• Corrosion Science and Technology
• /
• 제6권6호
• /
• pp.275-281
• /
• 2007

The effect of annealing on the pitting corrosion resistance of anodized Al-Mg alloy (AA5052) processed by equal-channel angular pressing (ECAP) was investigated by electrochemical techniques in a solution containing 0.2 mol/L of $AlCl_3$ and also by surface analysis. The Al-Mg alloy was annealed at a fixed temperature between 473 and 573 K for 120 min in air after ECAP. Anodizing was conducted for 40 min at $100-400A/m^2$ at 293 K in a solution containing 1.53 mol/L of $H_2SO_4$ and 0.0185 mol/L of $Al_2(SO_4)_3$. The internal stress generated in anodic oxide films during anodization was measured with a strain gauge to clarify the effect of ECAP on the pitting corrosion resistance of anodized Al-Mg alloy. The time required to initiate the pitting corrosion of anodized Al-Mg alloy was shorter in samples subjected to ECAP, indicating that ECAP decreased the pitting corrosion resistance. However, the pitting corrosion resistance was greatly improved by annealing after ECAP. The time required to initiate pitting corrosion increased with increasing annealing temperature. The strain gauge attached to Al-Mg alloy revealed that the internal stress present in the anodic oxide films was compressive stress, and that the stress was larger with ECAP than without. The compressive internal stress gradually decreased with increasing annealing temperature. Scanning electron microscopy showed that cracks occurred in the anodic oxide film on Al-Mg alloy during initial corrosion and that the cracks were larger with ECAP than without. The ECAP process of severe plastic deformation produces large internal stresses in the Al-Mg alloy; the stresses remain in the anodic oxide films, increasingthe likelihood of cracks. It is assumed that the pitting corrosion is promoted by these cracks as a result of the higher internal stress resulting from ECAP. The improvement in the pitting corrosion resistance of anodized AlMg alloy as a result of annealing appears to be attributable to a decrease in the internal stresses in anodic oxide films

• Korean Chemical Engineering Research
• /
• 제48권4호
• /
• pp.519-533
• /
• 2010

본 연구에서는 L-형 아미노산인 L-Alanine과 무기염인 NaCl, KCl, $NaNO_3$ 및 $KNO_3$의 각 전해질로 이루어진 L-Alanine/전해질 수용액 계에서 L-Alanine의 활동도계수와 용해도를 298.15 K에서 측정하였다. L-Alanine의 활동도계수는 양이온 및 음이온의 선택성 전극으로 이루어진 화학전지에서 두 전극간의 기전력을 측정하는 전기화학 법으로 측정하였으며, 용해도는 L-Alanine의 고체상과 상평형을 이루고 있는 포화용액을 중량 분석하여 측정하였다. 한편 본 연구에서는 아미노산(L-Alanine)/전해질 수용액 계의 잔류(residual) Helmholtz 자유에너지를 섭동사슬-통계역학적 회합성유체이론(perturbed chain-statistical associating fluid theory)과 단순-평균구근사(primitive-mean spherical approximation)이론을 결합한 관계로 모델링 하였으며, 이로부터 아미노산의 활동도계수 및 용해도에 대한 열역학적 관계식을 얻었다. Helmholtz 자유에너지를 모델링 하는 과정에서는 아미노산은 양쪽성 이온(zwitterion) 형태로 존재하며 아미노산의 양쪽성 이온은 같은 이온끼리 자기-회합(self-association)하며 동시에 물분자와 교차-회합(cross-association)하는 회합체로 가정하였으며, 또한 아미노산의 양쪽성 이온이 전해질(무기염)로부터 해리된 양이온 및 음이온과 상호작용하여 이온복합체(ion complex)를 형성하는 과정을 회합현상으로 가정하였다. 본 연구에서 제안된 이론적 모델로부터 L-Alanine/전해질 수용액 계에서 계산되는 L-Alanine의 활동도계수 및 용해도 값은 본 연구의 실험값과 일치하는 경향을 보였다.