• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.11a
• /
• pp.78-78
• /
• 2009

In this study, multilayer piezoelectric ceramics was manufactured using the PMW-PNN-PZT ceramics. Then, their physical characteristics for applicaton of electric power generation were investigated according to the numbers of multilayer. With increasing the numbers of multilayer, effective electromechanical coupling factor($k_{eff}$) and capacitance were decreased and increased, respectively.

• Proceedings of the KIEE Conference
• /
• 2006.10a
• /
• pp.63-64
• /
• 2006

In this paper, multilayer piezoelectric actuator was fabricated in order to develop ultrasonic linear motor. Multilayer actuator showed a high density of 7.78[$g/cm^3$], a large effective electromechanical coupling factor($K_{eff}$) of 0.259, a high mechanical quality factor( Qm ') of 1301, and high capacitance(c) of 19.32[nF]. Curie temperature was $343[^{\circ}C]$.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.21 no.6
• /
• pp.524-529
• /
• 2008

In this paper, in order to develop low loss multilayer actuator, piezoelectric properties of PZW-PMN-PZT multilayer actuator sintered at $900^{\circ}C$ low temperature were investigated according to the number of multilayer. The multilayer actuator was fabricated using tape casting method and used pure Ag internal electrode. The density above $8.0\;g/cm^3$ was obtained at all specimens. With increasing number of multilayer, effective electromechanical coupling factor($k_{eff}$) was increased. $k_{eff}$ of multilayer actuator shows the maximum value of 0.283 at 11 layers actuator. However, effective mechanical quality factor(Qm') was decreased according to the increase of number of multilayer. The Qm' of multilayer actuator showed the maximum value of 920 at 5 layers actuator.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.270-271
• /
• 2007

In this study, piezoelectric properties of PZW-PMN-PZT multilayer actuator sintered at $900^{\circ}C$ low temperature have been investigated. The multilayer actuator was fabricated by tape casting methods. The density above $8[g/cm^3]$ was obtained at all the specimens. Also, according to increasing the number of multilayer, effective electromechanical coupling factor$(k_{eff})$ showed increasing trend. The $k_{eff}$ of multilayer actuator showed the maximum value of 0.283 at 11 layer. However, according to increasing the number of multilayer, mechanical quality factor(Qm') showed decreasing tend. The Qm' of multilayer actuator showed the maximum value of 920 at 5 layer.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.9
• /
• pp.838-842
• /
• 2006

0.03Pb$(Sb_{0.5}Nb_{0.5})O_{3}-0.03Pb(Mn{1/3}Nb{2/3)O_{3}-(0.94-x)PbTiO_{3}-xPbZrO_{3}$ ceramics doped with $CeO_{2}$ were synthesized by conventional bulk ceramic processing technique. Phases analysis, microstructures and piezoelectric properties were investigated as a function of $CeO_{2}$ content (0.03, 0.05, 0.1 0.3, 0.5 and 0.7 wt%). Microstructures and phases information were characterized using a scanning electron microscope (SEM) and an X-ray diffractometer (XRD). Mechanical quality factor ($Q_{m}$) and coupling factor(kp) were obtained from the resonance measurement method. Both $Q_{m}$ and $k_{p}$ were shown to reach to the maximum at 0.1 wt% $CeO_{2}$. In order to evaluate the stability of resonance frequency and effective electromechanical coupling factor ($K_{eff}$) as a function of $CeO_{2}$, the variation of resonance and anti-resonance frequency were also measured using a high voltage frequency response analyzer under various alternating electric fields from 10 V/mm to 80 V/mm. It was shown that the stability of resonance frequency and effective electromechanical coupling factor were increased with increasing the $CeO_{2}$ contents.

• Journal of the Korean Institute of Illuminating and Electrical Installation Engineers
• /
• v.20 no.4
• /
• pp.7-11
• /
• 2006

In this paper, it is reported that film-bulk-acoustic resonator with high c-axis oriented AIN film on $Mo/SiO_2/Si(100)$ using metal-organic-chemical-vapor deposition was fabricated. The resonant frequency and anti-resonant frequency of the fabricated resonator were observed with 3.189[GHz] and 3.224[GHz], respectively. The quality factor and the effective electromechanical coupling coefficient(${k_{eff}}^2$) were measured with 24.7 and 2.65[%], respectively. The conditions of AIN deposition were substrate temperature of $950[^{\circ}C]$, pressure of 20Torr, and V-III ratio of 25000. A high c-axis oriented AIN film with $4{\times}10^{-5}[\Omega{cm}]$ resistivity of Mo bottom electrode and $4[^{\circ}]$ of AIN(0002) full-width at half-maximum(FWHM) on $Mo/SiO_2/Si(100)$ was grown successfully. The FWHM value of deposited AIN film is useful for the RF band pass filter specification for GHz-band wireless local area network.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.11a
• /
• pp.225-227
• /
• 2006

Multilayer step down piezoelectric transformers were manufactured using PZN-PMN-PZT and PMN-PNN-PZT ceramics respectively. Sintering temperature of the ceramics was $940^{\circ}C$. And then. their electrical properties were investigated according to the variations of frequency and load resistance. The voltage step-up ratio of multilayer piezoelectric transformer showed the maximum values in the vicinity of 69 and 71kHz, respectively. At the load resistance of $100{\Omega}$, the piezoelectric transformers showed the temperature rises of about 21 and $18^{\circ}C$ at the output power of 15W and 18W, respectively. At the transformer with high effective electromechanical coupling factor($k_{eff}$), lower temperature increase was appeared.