• Progress in Superconductivity and Cryogenics
• /
• v.4 no.1
• /
• pp.45-59
• /
• 2002

Evaluation of the mechanical properties of Bi-2223/Ag HTS tapes was carried out by the tension and bending tests. Most of the Bi-2223/Ag tapes retained critical current up to 10 kgf/mm$_2$ axial tension stress, and 0.2% tension strain at room temperature. Applied tension strain exceeding 0.3% in superconducting tapes at 77 K leaded to rapid degradation of the critical current. It was observed that the more filaments, the better axial tension property at 77 K, self-field The influence of bending strain on critical current degradation was revealed to be less sensitive for Bi-2223/Ag HTS tapes with a more number of filaments and higher silver ratio.

• Proceedings of the KSR Conference
• /
• 2008.06a
• /
• pp.2073-2079
• /
• 2008

This study aims to investigate the residual strength of sandwich composites with Al honeycomb core and carbon fiber face sheets after the quasi-static indentation damage by the experimental investigation. The 3-point bending test and the edge-wise compressive strength test were used to find the mechanical properties. The quasi-static point load and damaged hole was applied to introduce the simulated damage on the Each damaged specimens were finally assessed by the 3-point bending test and the compressive strength test. The investigation results revealed the residual strength of the damaged specimens due to the quasi-static indentation.

• Composites Research
• /
• v.22 no.2
• /
• pp.24-29
• /
• 2009

This study aims to investigate the residual strength of sandwich composites with Al honeycomb core and carbon fiber face sheets after the quasi-static indentation damage by the experimental investigation. The 3-point bending test and the edge-wise compressive strength test were used to find the mechanical properties, and the quasi-static point load was applied to introduce the simulated damage on the specimen. The damaged specimens were finally assessed by the 3-point bending test and the compressive strength test. The investigation results revealed the residual strength of the damaged specimens due to the quasi-static indentation. The both test results showed that the residual strength of the damaged specimen was decreased according to increases of the damaged depth.