Titanium aluminides have attracted special interest as light-weight/high-temperature materials for structural applications. The major problem limiting practical use of these compounds is their poor ductility and formability. The powder metallurgy processing route has been an attractive alternative for such materials. A mixture of Ti and Al elemental powders was fabricated to a mechanical alloying process. The processed powder was hot pressed in a vacuum, and a fully densified compact with ultra-fine grain structure consisting of Ti₃Al intermetallic compound was obtained. During the compressive deformation of the compact at 1173 K, typical dynamic recrystallization (DR), which introduces a certain extent of grain refinement, was observed. The compact had high density and consisted of an ultra-fine equiaxial grain structure. Average grain diameter was 1.5 ㎛. Typical TEM micrographs depicting the internal structure of the specimen deformed to 0.09 true strain are provided, in which it can be seen that many small recrystallized grains having no apparent dislocation structure are generated at grain boundaries where well-developed dislocations with high density are observed in the neighboring grains. The compact showed a large m-value such as 0.44 at 1173 K. Moreover, the grain structure remained equiaxed during deformation at this temperature. Therefore, the compressive deformation of the compact was presumed to progress by superplastic flow, primarily controlled by DR.

• Metals and materials international
• /
• v.24 no.6
• /
• pp.1249-1255
• /
• 2018

High temperature compression tests for newly developed Al-Zn-Mg alloy were carried out to investigate its hot deformation behavior and obtain deformation processing maps. In the compression tests, cylindrical specimens were deformed at high temperatures ($300-500^{\circ}C$) and strain rates of 0.001-1/s. Using the true stress-true strain curves obtained from the compression tests, processing maps were constructed by evaluating the power dissipation efficiency map and flow instability map. The processing map can be divided into three areas according to the microstructures of the deformed specimens: instability area with flow localization, instability area with mixed grains, and stable area with homogeneous grains resulting from continuous dynamic recrystallization (CDRX). The results suggest that the optimal processing conditions for the Al-Zn-Mg alloy are $450^{\circ}C$ and a strain rate of 0.001/s, having a stable area with homogeneous grains resulting from CDRX.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2001.10a
• /
• pp.301-304
• /
• 2001

Hot-compression tests were carried out to investigate the hot workability of Ti64 and Ti6246 alloys at different temperatures and strain rates. Processing maps were developed on the basis of the dynamic material model unifying the relationship among constitutive behavior, hot workability and microstructure development. Stable regions, defined on the basis of four stability criteria 0${\delta}log(m)/\frac{\bot}{\varepsilon})<0$, s<1 and ${\delta}log(s)/\frac{\bot}{\varepsilon})<0$, were found to be associated with dynamic recovery and recrystallization.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2003.05a
• /
• pp.53-56
• /
• 2003

The disappearance of continuous yielding and the formation of an extended region in engineering stress-strain curves at tempering temperatures of 673-873K is closely related to the reduction of mobile dislocations during tempering and dynamic recovery during tensile deformation. In addition, the occurrence of discontinuous yielding at tempering temperature above 923K would be attributed to the formation of new strain-free polygonal ferrite grain.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 1998.03a
• /
• pp.76-79
• /
• 1998

High temperature plastic deformation behavior of Al 6061 alloy was characterized by hot torsion test. The Al 6061 alloy deformed continuously in the temperature range of 400∼550$^{\circ}C$, and strain rate range of 0.05∼5/sec. The softening mechanism of Al 6061 alloy was dynamic recrystallization and identified by hyperbolic sine law and zener-Hollmon parameter. The evolution of grain size and deformation resistance were calculated by the relationships of deformation variables.

• Transactions of Materials Processing
• /
• v.10 no.4
• /
• pp.347-354
• /
• 2001

Compression tests were carried out to investigate the hot-deformation behavior of Ti-6Al-4V alloy in the temperature range of $915^{\circ}C$ to $1015^{\circ}C$ and the strain rate range of $10^{-3}s^{-i}$ to $10s^{-1}$. Under the given test conditions, the hot-deformation of Ti-6Al-4V alloy was mainly led by dynamic recovery rather than by dynamic recrystallization. The activation energy for the plastic deformation in $\alpha+\beta$ field was about 894 kJ/mol and $\beta$ field was 332kJ/mo1. Processing map for hot working are developed on the basis of the variations of efficiency of power dissipation($\eta$=2m/m＋1) and flow instability criterion using the dynamic material model. The optimum process condition in the ($\alpha＋\beta$) field was obtained at the temperature ranges of $930^{\circ}C$ to $955^{\circ}C$$^{\circ}C$ and a strain rate of $10^{-3}s{-1}$.

• Journal of the Korean Society for Heat Treatment
• /
• v.31 no.4
• /
• pp.180-186
• /
• 2018

High temperature flow behaviors of Fe-Cr-Mo-V-W-C tool steel were investigated using isothermal compression tests on a Gleeble simulator. The compressive test temperature was varied from 850 to $1,150^{\circ}C$ with the strain rate ranges of 0.05 and $10s^{-1}$. The maximum height reduction was 45%. The dynamic softening related to the dynamic recrystallization was observed during hot deformation. The constitutive model based on Arrhenius-typed equation with the Zener-Hollomon parameter was proposed to simulate the hot deformation behavior of Fe-Cr-Mo-V-W-C steel. An artificial neural network (ANN) model was also developed to compare with the constitutive model. It was concluded that the ANN model showed more accurate prediction compared with the constitutive model for describing the hot compressive behavior of Fe-Cr-Mo-V-W-C steel.

• Transactions of Materials Processing
• /
• v.32 no.5
• /
• pp.239-246
• /
• 2023

To reduce the forming load due to the temperature drop, during the hot forging process, a reheating hot forging process design is required that to repeat heating and forging. However, if the critical strain required for recrystallization is not induced during forging and grain growth becomes dominant due to the reduction in dislocation density due to repeated heating, the mechanical properties may deteriorate. Therefore, in this study, Inconel 706 alloy was applied, and the grain refinement behavior was comparatively analyzed according to the number of reheating times and effective strain during reheating hot forging process. Reheating was carried out with a total compression rate of 40% up to 4 times. The Inconel 706 compression test specimens heated once showed finer grains as the effective strain increased due to the dynamic recrystallization phenomenon. However, as the number of heating increases, grain refinement was observed even in a low effective strain distribution of 0.43 due to static recrystallization during reheating. Moreover, grain growth occurs at a relatively low effective strain of 0.43 when the number of reheating is four or more. Therefore, it was effective to apply an effective strain of 0.43 or more during hot forging to Inconel 706 in order to induce crystallization through grain refinement and improve the properties of forged products. In addition, we could notice that up to three reheating times condition was appropriate to prevent grain growth and maintain fine grain size.

• Transactions of Materials Processing
• /
• v.7 no.2
• /
• pp.158-167
• /
• 1998

Hot restoration mechanism flow stress and stain of the Al2024 composites reinforced with 1,8,15,36, and $44{\mu}m\;SiC_p$(10 vol. %) were studied by hot torsion tests. The hot restoration mechanism of all the composites was found to be dynamic recrystallization(DRX) at $320^{\circ}C$ while that of the composites reinforced with 1 and $8{\mu}m\;SiC_p$ was found to be dynamic recovery(DRX) at $480^{\circ}C$. It was found that the Al2024 composite with $15{\mu}m\;SiC_p$ showed the highest flow stress(${\sim}$223 MPa) at $320^{\circ}C$ under a strain rate of 1.0/sec. Also the highest flow strain of the composites was obtained at $430^{\circ}C$. The com-posites reinforced with 1 and $8{\mu}m\;SiC_p$ showed lower flow stress and higher flow strain at $480^{\circ}C$ than those of the composites reinforced with 15, 36, and $44\;{\mu}m\;SiC_p$ These result were discussed in relation to the transition of the hot restoration mechanism. $DRX{\leftrightarrow}DRV$. The dependence of flow stress on strain rate and temperature was attempted to fit with the hyperbolic sine equation ($\dot{\varepsilon}=A[sinh({\alpha}{\cdot}{\sigma}_p]^n$ exp(-Q/RT)and Zener-Hollomon parameter($Z=\;\dot{\varepsilon}\;exp(Q/RT))$.

• Journal of the Korean Society for Heat Treatment
• /
• v.30 no.5
• /
• pp.187-196
• /
• 2017

High temperature flow behaviors of AISI 4340 steel were investigated using isothermal compression tests under the temperature range from 850 to $1100^{\circ}C$ and a strain rate from 0.01 to $10s^{-1}$. The flow stress decreased with increasing compression temperature and decreasing strain rate. The dynamic softening related to the dynamic recrystallization was observed during hot deformation. The constitutive model based on Arrheniustyped equation with the Zener-Hollomon parameter was used to simulate the hot deformation behavior of AISI 4340 steel. The modification of the Zener-Hollomon parameter and lnA parameter resulted in the improvement of the calculation accuracy of the proposed constitutive model compared with the experimental flow curves. In addition, the process map of AISI 4340 steel was proposed. The instable process condition for hot deformation was predicted and its reliability was verified with the experimental observation.