• Elastomers and Composites
• /
• v.49 no.4
• /
• pp.267-274
• /
• 2014

Self vulcanizable blend system for magnetorheological elastomer (MRE) has been studied by dispersing magneto responsible particle (MRP) on elastomeric matrix. Chloroprene rubber was modified with maleic anhydride (MAH) using heat and pressure which is called dynamic maleation process. The optimum graft ratio of MAH was found at 10 phr contents and reaction temperature of $100^{\circ}C$. This could be confirmed by FT-IR analysis. Epoxided natural rubber (ENR) was blended with modified CR-g-MAH for self vulcanization. The optimum amounts of ENR was 30 wt% in terms of scorch time and curing rate. MRE was manufactured by electromagnetic equipment and orientation of MRE was confirmed by SEM. Finally, it was found that the tensile strength of anisotropic-MRE was higher than that of isotropic-MRE and the hardness was reverse.

• Elastomers and Composites
• /
• v.56 no.1
• /
• pp.6-11
• /
• 2021

In order to develop an ultra-high-density elastomeric material for substitution of steel dynamic dampers, a new curing system and technique for high-loading of the filler were examined in this study. Mechanochemical modification of chloroprene rubber (MAH-g-CR) using an internal mixer was carried out with maleic anhydride (MAH) as a reactive monomer. The optimum amount of MAH was 10 phr and the efficient grafting of MAH on CR could be achieved at a mixing temperature of 100℃. After preparing MAH-g-CR, 50 mol% epoxidized natural rubber (ENR 50) was blended with MAH-g-CR to develop a "self-curable rubber blend system" via reaction between the functional groups of the elastomeric matrices without the curing agent and additives. The content of ENR 50 was fixed at 30 wt.% throughout evaluation of the curing behavior of the MAH-g-CR/ENR blend. Tungsten powder was added to the MAH-g-CR/ENR matrix up to 60 vol.% to obtain ultra-high-density, and the maximum density obtained was 7.57 g/㎤. Stable ts2 (scorch time) and t90 (90% cure time) could be obtained even when tungsten powder was incorporated up to 60 vol.%. In addition, the tensile strength and damping properties of MAH-g-CR/ENR containing 60 vol.% of tungsten were better than those of CR containing 60 vol.% of tungsten.