• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2015년도 춘계학술대회 논문집
• /
• pp.123-123
• /
• 2015

0.087 wt.% Gd-lean duplex stainless steels were inert arc-melted and cast in a mold. The micro-hardnesses of the rolling, transverse, short transverse directions were 258.5, 292.3, 314.7 HV, respectively. The 33% cold rolled specimen had the crystallographic texture that mainly (100) pole was concentrated to normal direction and (110) pole was concentrated in the center of normal and rolling directions. The corrosion potential and corrosion rate in artificial sea water were in the range of $105.6-221.6mV_{SHE}$, $0.59-1.06mA/cm^2$, respectively. The friction coefficient and wear loss of the 0.087 wt.% Gd-lean duplex stainless steels in artificial sea water were about 67% and 65% lower than in air, whereas, the wear efficiency was 22% higher. The corrosion and wear behaviors of the 0.087 wt.% Gd-lean duplex stainless steels significantly depended on the gadolinium phases.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.507-508
• /
• 2006

In this communication the development of a new metal injection moulding (MIM) system for duplex stainless steels is presented. The metal powders were prepared by premixing 316L and 430L stainless steels gas atomised powders in a ratio of 50:50. The binder used to prepare the feedstock was composed by HDPE and paraffin wax. Torque measurements of the mixture indicated that the maximum amount of metal was 68 vol%. The polymeric part was driven off by thermal debinding and the sintering was performed in low vacuum. The final densities were close to the theoretical ones.

• Journal of Welding and Joining
• /
• 제5권3호
• /
• pp.38-45
• /
• 1987

An investigation was conducted to find out the factors influencing on the impact toughness of austenitic-and duplex stainless steel weld metal. Various welding process with commerically available consumables was adopted to get weld doposited metal. The oxygen content of each weld metal was very sensitiive to welding process, involving flux composition, shielding gas and structural features. The results of this study show tat the content of oxygen as an oxide inclusion significantly affects impact toughness, and .delta.-ferrite distribution is also correlated with resultant toughness value.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2005년도 창립60주년 기념 추계 학술대회
• /
• pp.136.2-136.2
• /
• 2005

• 한국해양공학회지
• /
• 제9권1호
• /
• pp.152-152
• /
• 1995

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2008년도 춘계학술대회 논문집
• /
• pp.187-188
• /
• 2008

• 한국재료학회지
• /
• 제24권11호
• /
• pp.610-616
• /
• 2014

In this study, we investigated the precipitation behavior of the R-phase precipitated at the initial stage of aging and its effect on the pitting corrosion of 25%Cr-7%Ni-4%Mo super duplex stainless steel. The R-phase in super duplex stainless steel was mainly precipitated at the interface of ferrite/austenite phases and inside of the ferrite phase during the initial stage of aging, and it was transformed into the ${\sigma}$-phase with an increase in aging time. The ferrite phase was decomposed into a new austenite phase and ${\sigma}$-phase. The R phase was an intermetallic compound, which represented a lower Ni and higher Mo than the matrix, and also had a higher Mo and Cr concentration than the ${\sigma}$ phase. With an increasing aging time, the pitting potential $E_p$ was increased slowly by the precipitation of the R-phase, and it was then steeply decreased by the precipitation of the ${\sigma}$-phase. The R-phase was decreased the pitting potential, but its effect was smaller than effect of ${\sigma}$-phase.

• 한국해양공학회지
• /
• 제24권5호
• /
• pp.55-59
• /
• 2010

The effect of aging on the precipitation of the $\sigma$ phase and corrosion resistance in W-substituted, super-duplex stainless steel was investigated. The volume fraction of the $\sigma$ phase and the current density increased as the aging temperature increased up to $750^{\circ}C$, and, then, they decreased. As aging time increased, the volume fraction of the $\sigma$ phase and the current density also increased. The $\sigma$ phase considerably influenced to corrosion resistance. When Mo was substituted for W in super-duplex stainless steel, the volume fraction of the $\sigma$ phase and the current density both decreased markedly.

• 한국해양공학회지
• /
• 제23권6호
• /
• pp.87-92
• /
• 2009

The effect of aging on the precipitation of the $\sigma$ phase and the corrosion resistance in tungsten substituted super duplex stainless steels was investigated. The volume fraction of the $\sigma$ phase and the current density increased with aging at temperatures up to $750^{\circ}C$ and then decreased. With an increase in aging time, the volume fraction of the $\sigma$ phase and the current density also increased. The $\sigma$ phase hardly influenced the corrosion resistance. With the substitution of tungsten for molybdenum in super duplex stainless steel, the volume fraction of the $\sigma$ phase and the current density decreased remarkably.

• 한국해양공학회지
• /
• 제22권4호
• /
• pp.46-50
• /
• 2008

Super duplex stainless steel has along life in severe environments because of its strength and corrosion resistance. If 0.2$\sim$0.3% Nitrogen in aninterstitial solid solution is added, the austenite structure is reinforced. This improves the solid solution hardening and the anticorrosionability. In this study, the mechanical properties and structures of the super duplex stainless steel with the 0.2% N additive were investigated to determine the effect of various volume fractions on the austenite phase. The various volume fractions and distributions of the austenite structure in the applied test specimens were obtained by changing the heat treatment temperature and cycle. The characteristics by amounts of the $\sigma$ phase obtained from the precipitation heat treatment were alsoinvestigated. From the results, when the austenite volume fraction increases, the tensile strength decreases and elongation increases. And the $\sigma$ phase was rapidly increased by increasing the heat treatment time. When the volume fraction of the $\sigma$ phase increased, tensile strength increased.