• Journal of the Korean institute of surface engineering
• /
• v.30 no.4
• /
• pp.248-254
• /
• 1997

The sulfidation behavior of a sputter-deposited amorphous coating of 69.0%Nb-16.9Ni-11.9%Al-2.2%Si (at.%) has been investigated as a funtion of temperature.(973-1173K) in pure sulfur pressure of 0.01atm. The sulfidation kinetics of the casting obyed the parabolic rate low over the whole temperature ranges studied. The stlfidation rate increased with the temperature, as expected. The sulfide scale, the composition of which was $Al_2S_3,\;NbS_2,\;Ni_{3-x}S_2\;and\;FeCrS_4$, formed on the amorphous coating was primarily bilayered. Both the outer fastgrowing non-protective 4Al_2S_3$scale and the inner slowly-growing protective $NbS_2$,/TEX> scale and the inner slowly-growing protective $NbS_2$ scale had some Fe and Cr dissolution, which evidently came from the base substrate alloy of stainless steel type 304. Belows the coating, Kirkendall void formation was noticed. Nevertheless, a dramatic improvement of sulfidation resistance was achieved by sputter-depositing Nb-2 Ni-Al-Si layer on the stainless steel 304.

• Corrosion Science and Technology
• /
• v.11 no.4
• /
• pp.108-111
• /
• 2012

The effects of volume fraction (15-30%) of SiC particulate reinforcements on the corrosion behavior of SiCp/7091 Al composites in the 3.5% NaCl solution were studied by electrochemical techniques and scanning electron microscopy. The results showed that the amount of SiC particulate reinforcements did not cause much difference in the corrosion behavior of SiCp/7091 Al composites but the corrosion rate was proportional to the amount of SiCp reinforcement. And numerous pits and severe dissolution of the matrix was observed probably due to the discontinuities and galvanic effects between Al matrix and SiC reinforcements.

• Journal of the Korean institute of surface engineering
• /
• v.30 no.5
• /
• pp.320-332
• /
• 1997

The development of colored surface on zinc coating by the oxidation of a melten alloy of zinc with a minor amount of oxygen-avid additive such as tianium has been studied. Using a galvanizing Zinc alloy containing 0.1 to 0.3wt%Ti, gold, purple or blue color was developed clearly and stably, depending upon the extent of oxidation, by air cooling after hot dipping in a bath at temperature of $550^{\circ}C$ to $600^{\circ}C$. The source of the color is light interference with surface oxide layer. THe final color depends on the thickness of the color depends on the thickness of $TiO_2$, played So compositing, temperature and time at elevated temperature after are all controlling variables. Since oxidation film such as $TiO_2$ played role of passivation film, the corrosion resistance in a colored galvanized steel sheet. It is also thought that surface oxide layer of $TiO_2$ inhibited dissolution of the coating layer.

• Corrosion Science and Technology
• /
• v.9 no.2
• /
• pp.67-73
• /
• 2010

Niobium microalloying is effective in hot-rolled and cold-rolled steels by providing a fine-grained microstructure resulting in increased strength. To optimize the strengthening effect, alloy design and hot-rolling conditions have to be adapted. As a key issue the dissolution and precipitation characteristics of Nb are discussed in particular with regard to the run-out table conditions. It is then considered how the hot-rolled microstructure and the solute state of Nb interact with the hot-dip galvanizing cycle. The adjusted conditions allow controlling the morphology and distribution of phases in the cold-rolled annealed material. Additional precipitation hardening can be achieved as well. The derived options can be readily applied to produce conventional HSLA and IF high strength steels as well as to modern multiphase steels. It will be explained how important application properties such as strength, elongation, bendability, weldability and delayed cracking resistance can be influenced in a controlled and favorable way. Examples of practical relevance and experience are given.

• Corrosion Science and Technology
• /
• v.2 no.6
• /
• pp.277-282
• /
• 2003

Holographic interferometry, an electromagnetic method, was used to study corrosion of carbon steel, aluminum and copper nickel alloys in NaOH, KCI and $H_2SO_4$ solutions respectively. The technique, called electrochemical emission spectroscopy, consisted of in-situ monitoring of changes in the number of fringe evolutions during the corrosion process. It allowed a detailed picture of anodic dissolution rate changes of alloys. The results were compared to common corrosion measurement methods such as linear polarization resistance measurements and electrochemical impedance spectroscopy. A good agreement between both data was found, thus indicating that holographic interferometry can be a very powerful technique for in-situ corrosion monitoring.

• Proceedings of the Korean Environmental Sciences Society Conference
• /
• 2001.05a
• /
• pp.236-237
• /
• 2001

In this study, experiments were carried out to measure the variations in the corrosion potential and current density of polarization curves with amorphous $Fe_{70}Cr_5Si_{10}B_{15}$ and $Co_{70}Cr_5Si_{10}B_{15}$ alloy ribbon. The results were particularly examined to identify the influences of corrosion potential including various conditions such as hydrochloric acid, temperature, salt, pH, and oxygen. The optimum conditions were established with variations including temperature, salt, pH, oxygen, corrosion rate, and resistance of corrosion potential. The mass tranfer coefficient(${\alpha}$) value was determined with the Tafel's slope for the anodic dissolution based on the polarization effect with optimum conditions. The second anodic current density peak and maximum passive current density were designated as the critical corrosion sensitivity($I_{r}/I_{f}$).

• Journal of the Korean Society for Heat Treatment
• /
• v.34 no.6
• /
• pp.281-286
• /
• 2021

Arc ion plating (AIP), laser cladding, and nitriding are methods that can prevent mold damage or repair and create cracks and breakages on the die surface. The dissolution and soldering behavior of coated SKD61 by using arc ion plating, laser cladding, and nitriding was investigated. The structure of the coating was investigated as a function of deposition conditions by X-ray diffraction and the crystallographic orientation was determined using the texture factor. The TiAlN film deposited with AIP showed excellent corrosion resistance in the molten aluminum alloy at 680℃. In this paper, we have detailed the corrosion and mass loss phenomena associated with these steel-cast metal interactions.

• Applied Chemistry for Engineering
• /
• v.10 no.6
• /
• pp.832-837
• /
• 1999

Stability of a cathode material was determined by Tafel plot in 1 M LiOH solution. The stabilized $LiM_xMn_{2-x}O_4$ (x=0.05~0.1) electrode resulted in overpotential of 0.13~0.15 mV at 100 mA. This overpotential was 0.05 mV lower than that of the spinel structured $LiMn_2O_4$ electrode. Conductivity test at various potentials showed that the conductivity of $LiM_xMn_{2-x}O_4$ was higher than that of the spinel structured $LiMn_2O_4$ and the bulk resistance of $LiM_xMn_{2-x}O_4$ due to the dissolution of $Mn^{2+}$ was lowered.

• Journal of Electrochemical Science and Technology
• /
• v.7 no.3
• /
• pp.234-240
• /
• 2016

The effect of initial electrolyte loading (IEL) on cell performance in a coin-type molten carbonate fuel cell (MCFC) was investigated in this work. Since the material of MCFC depends on the manufacturer, optimisation requires experimental investigation. In total, four IEL values, 1.5, 2.0, 3.0, and 4.0 g, were used, corresponding to a pore filling ratio (PFR) of 38, 51, 77, and 102%, respectively. The cell performance with respect to the PFR was analysed via steady-state polarisation, step-chronopotentiomtery, and impedance methods. The electrochemical analyses revealed that internal resistance and overpotential of the cell decreased with increasing PFR, and a large overpotential was observed when the PFR was 102%, probably due to the flooding phenomenon. After operation, cross-section of the cell was analysed via surface analysis of SEM and EDS methods, and the remaining electrolyte was estimated by dissolution of the cell in 10 wt% acetic acid. A linear relationship between IEL and the weight reduction ratio by dissolution was obtained. Thus, the remaining amount of electrolyte could be measured after operation. The results of SEM and EDS showed that a PFR of 38 and 102% showed a lack and flooding of electrolytes at the cell, respectively, which led to a large overpotential. This work reports that MCFC performance is allowed only in the narrow range of PFR.

• Korean Journal of Materials Research
• /
• v.33 no.8
• /
• pp.337-343
• /
• 2023

3Y-TZP (3 mol% yttria-stabilized tetragonal zirconia polycrystals) ceramics have excellent mechanical properties including high fracture toughness, good abrasion resistance as well as chemical and biological stability. As a result, they are widely used in mechanical and medical components such as bearings, grinding balls, and hip implants. In addition, they provide excellent light transmittance, biocompatibility, and can match tooth color when used as a dental implant. Recently, given the materials' resemblance to human teeth, these ceramics have emerged as an alternative to titanium implants. Since the introduction of CAD/CAM in the manufacture of ceramic implants, they've been increasingly used for prosthetic restoration where aesthetics and strength are required. In this study, to improve the surface roughness of zirconia implants, we modified the 3Y-TZP surface with a biocomposite of hydroxyapatite and forsterite using room temperature spray coating methods, and investigated the mixed effect of the two powders on the evolution of surface microstructure, i.e., coating thickness and roughness, and biological interaction during the in vitro test in SBF solution. We compared improvement in bioactivity by observing dissolution and re-precipitation on the specimen surface. From the results of in vitro testing in SBF solution, we confirmed improvement in the bioactivity of the 3Y-TZP substrate after surface modification with a biocomposite of hydroxyapatite and forsterite. Surface dissolution of the coating layer and the precipitation of new hydroxyapatite particles was observed on the modified surface, indicating the improvement in bioactivity of the zirconia substrate.