• Journal of the Korean Ceramic Society
• /
• v.32 no.5
• /
• pp.617-625
• /
• 1995

In order to reduce reflectance of soda-lime glass having average reflectance of 7.35% and refractive index of 1.53, single (SiO2), double (SiO2/20SiO2-80ZrO2), and triple (SiO2/ZrO2/75SiO2-25ZrO2) layers were designed and fabricated on the glass substrate by Sol-Gel method. Stble sols of SiO2-ZrO2 binary system for antireflective (AR) coatings were synthesized with tetraethyl orthosilicate (TEOS) and zirconium n-butoxide as precursors and ethylacetoacetate (EAcAc) as a chelating agent in an atmosphere environment. Films were deposited on soda-lime glass at the withdrawal rates of 3~11 cm/min using the prepared polymeric sols by dip-coating and they were heat-treated at 45$0^{\circ}C$ for 10 min to obtain homogeneous, amorphous and crack-free films. In case of SiO2-ZrO2 binary system, refractive index of film increased with an increase of ZrO2 mol%. Designed optical constant of films could be obtained through varying the withdrawal rate. In the visible region (380~780nm), reflectance was measured with UV/VIS/NIR Spectrophotometer. Average reflectances of the prepared single-layer [SiO2 (n=1.46, t=103nm)], double-layer [SiO2 (n=1.46, t=1-4nm)/20SiO2-80ZrO2 (n=1.81, t=82nm)], and triple-layer [SiO2 (n=1.46, t=104nm)/ZrO2 (n=1.90, t=80nm)/75SiO2-25ZrO2 (n=1.61, t=94 nm)] were 4.74%, 0.75% and 0.38%, respectively.

• Korean Journal of Materials Research
• /
• v.24 no.5
• /
• pp.259-265
• /
• 2014

$ZrO_2$ films were coated on aluminum etching foil by the sol-gel method to apply $ZrO_2$ as a dielectric material in an aluminum(Al) electrolytic capacitor. $ZrO_2$ films annealed above $450^{\circ}C$ appeared to have a tetragonal structure. The withdrawal speed during dip-coating, and the annealing temperature, influenced crack-growth in the films. The $ZrO_2$ films annealed at $500^{\circ}C$ exhibited a dielectric constant of 33 at 1 kHz. Also, uniform $ZrO_2$ tunnels formed in Al etch-pits $1{\mu}m$ in diameter. However, $ZrO_2$ film of 100-200 nm thickness showed the withstanding voltage of 15 V, which was unsuitable for a high-voltage capacitor. In order to improve the withstanding voltage, $ZrO_2$-coated Al etching foils were anodized at 300 V. After being anodized, the $Al_2O_3$ film grew in the directions of both the Al-metal matrix and the $ZrO_2$ film, and the $ZrO_2$-coated Al foil showed a withstanding voltage of 300 V. However, the capacitance of the $ZrO_2$-coated Al foil exhibited only a small increase because the thickness of the $Al_2O_3$ film was 4-5 times thicker than that of $ZrO_2$ film.

• Journal of the Korean Ceramic Society
• /
• v.51 no.4
• /
• pp.337-343
• /
• 2014

A single layer ultrafiltration(UF) ceramic membrane was prepared using boehmite sol. Boehmite was synthesized using a typical sol-gel process with optimization of the viscosity, pH, molar ratio of aluminum isopropoxide(AIP) and $HNO_3$. Boehmite sol was coated on a microfiltration(MF) support using the dip-coating method. MF support was dipped into the boehmite sol with a withdrawal speed of 5 mm/s and was maintained for 10 s in the boehmite sol, resulting in a uniform UF membrane layer of $10{\mu}m$ thickness. The porosity of the obtained membrane was measured and found to be 41.2%; the pore size was found to range from 80~100 nm, corresponding to the pore size of the UF membrane. The flux of the obtained membrane was initially 540 $L/m^2h$ and approximately 85% of the initial flux was recovered using a periodic back-flushing process.

• Journal of the Korean Ceramic Society
• /
• v.27 no.5
• /
• pp.583-588
• /
• 1990

Glass films in the binary system B2O3-SiO2 and Al2O3-SiO2 were prepared on soda-lime-silica slide glass by the dip-coating technique from TEOS and boric acid or aluminum nitrate. Thickness of the films varying with viscosity and withdrawal speed were measured and effect of composition and firing temperature on the properties such as transmittance and refractive index were investigated. nM2O3.(100-n)SiO2(M=B or Al) films containing up to 20mol% B2O3 and 40mol% Al2O3 were transparent. Maximum transmittance at visible range were obtained for the sample containing 15mol% Ba2O3 and 32.5mol% Al2O3 and heat-treated at 50$0^{\circ}C$, respectively. Refractive index of the film containing 15mol% B2O3 was mininum in the B2O3-SiO2 binary system and minimal refractive index was appeared at the film containing 32.5mol% Al2O3. In IP spectra, addition of B2O3 were increased absorption peak intensity of B-O and Si-O-B bond and addition of Al2O3 were decreased absorption peak intensity of Si-O bond, respectively.