• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.11
• /
• pp.1000-1004
• /
• 2006

In this paper, thermal stability of Ni-silicide formed on the SOI substrate with $B_{11}$ has been characterized. The sheet resistance of Ni-silicide on un-doped SOI and $B_{11}$ implanted bulk substrate was increased after the post-silicidation annealing at $700^{\circ}C$ for 30 min. However, in case of $B_{11}$ implanted SOI substrate, the sheet resistance showed stable characteristics after the post-silicidation annealing up to $700^{\circ}C$ for 30 min. The main reason of the excellent property of $B_{11}$ sample is believed to be the retardation of Ni diffusion by the boron and bottom oxide layer of SOI. Therefore, retardation of Ni diffusion is highly desirable lot high performance Ni silicide technology.

• Korean Journal of Materials Research
• /
• v.12 no.9
• /
• pp.696-700
• /
• 2002

The Ti-aluminide intermetallic compound was formed from high purity elemental Ti and Al foils by self-propagating, high-temperature synthesis(SHS) in hot press. formation of $TiAl_3$ at the interface between Ti and Al foils was controlled by temperature, pressure, heating rate, and so on. According to the thermal analysis, it is known in this study that the heating rate is the most important factor to form the intermetallic compound by this SHS reaction. The V layer addition between Al and Ti foils increased SHS reaction temperatures. The fully dense, well-boned inter-metallic composite($TiA1/Ti_3$Al) sheets of 700 m thickness were formed by heat treatment at $1000^{\circ}C$ for 10 hours after the SHS reaction of alternatively layered 10 Ti and 9 Al foils with the V coating layer. The phases and microstructures of intermetallic composite sheets were confirmed by EPMA and XRD.

• Journal of the Korean Vacuum Society
• /
• v.9 no.3
• /
• pp.267-272
• /
• 2000

Electroplating Cu was deposited on Si(100) wafer after seed Cu was deposited by sputtering first. TaN was deposited as a diffusion barrier before depositing the seed Cu. Electroplating Cu thin films show highly (111)-oriented microstructure for both before and after annealing at $450^{\circ}C$ for 30min and no copper silicide was detected in the same samples, which indicates that TaN barrier layer blocks well the Cu diffusion into silicon substrate. After annealing the electroplating Cu film up to $450^{\circ}C$, the Cu film became columnar from non-columnar, its grain size became larger about two times, and also defects density of stacking faults, twins and dislocations decreased greatly. Thus the heat treatment will improve significantly electromigration property caused by the grain boundary in the Cu thin films.

• Journal of the Korean Solar Energy Society
• /
• v.33 no.4
• /
• pp.31-38
• /
• 2013

The chemical composition of the black Cr solar selective coatings electrodeposited were investigated for property analysis by using a XPS(X-ray photoelectron spectroscopy) before and after annealing in air at $300^{\circ}C{\sim}500^{\circ}C$ for 120 hours. Black Cr selective coating exposed by solar radiation for 5 months was compared with annealed sample. In addition, The Cu solar selective coatings were prepared by thermal oxidation method for low temperature application. The samples obtained were characterized by using the optical reflectance measurements by using a spectrometer. Optical properties of oxidized Cu solar coatings were solar absorptance $({\alpha}){\simeq}0.62$ and thermal emittance $({\epsilon}){\simeq}0.41(100^{\circ}C)$. In the as-prepared Cr black selective coating, the surface of the coating was found to have Cr hydroxide and Cr. The Cr hydroxide of the major component was converted to $Cr_2O_3$ or $CrO_3$ form after annealing at $500^{\circ}C$ with the desorption of water molecules. The black Cr selective coating was degraded significantly at temperature of $500^{\circ}C$. The main optical degradation modes of this coating were diffusion of Cu substrate materials.

• Korean Journal of Materials Research
• /
• v.31 no.12
• /
• pp.727-731
• /
• 2021

In this study, we have investigated a selective emitter using a UV laser on BBr₃ diffusion doping layer. The selective emitter has two regions of high and low doping concentration alternatively and this structure can remove the disadvantages of homogeneous emitter doping. The selective emitters were fabricated by using UV laser of 355 nm on the homogeneous emitters which were formed on n-type Si by BBr₃ diffusion in the furnace and the heavy boron doping regions were formed on the laser regions. In the optimized laser doping process, we are able to achieve a highly concentrated emitter with a surface resistance of up to 43 Ω/□ from 105 ± 6 Ω/□ borosilicate glass (BSG) layer on Si. In order to compare the characteristics and confirm the passivation effect, the annealing is performed after Al₂O₃ deposition using an ALD. After the annealing, the selective emitter shows a better effect than the high concentration doped emitter and a level equivalent to that of the low concentration doped emitter.

• Journal of the Korean Ceramic Society
• /
• v.41 no.6
• /
• pp.450-455
• /
• 2004

NiCr thin films were fabricated by thermal evaporation method using NiCr alloy as evaporating source. NiCr thin films were annealed at various temperatures in air atmosphere in order to investigate effects of annealing conditions on phase change, composition, and microstructures of NiCr films. Typical multilayer was formed after annealing in air atmosphere. This results from the diffusion and oxidation of Cr toward surface during annealing. In the case of annealing at 700$^{\circ}C$, large columnar grains of NiO were formed on Cr-oxide layer through the diffusion and oxidation of Ni over Cr-oxide layer. Especially, NiO layer was formed additionally on surface, sustaining the underlayer structure with the formation of porous Ni layer.

• Journal of the Korean Magnetics Society
• /
• v.15 no.4
• /
• pp.226-230
• /
• 2005

In this research, magnetic properties and annealing effects of the spin valve structures were investigated, which have Ta underlayer deposited with Ar and $N_2$ gas mixture. Also, TaN underlayer as a diffusion barrier and the substrate were investigated. The structure of the spin valve was Si($SiO_2$)/Ta(TaN)/NiFe/CoFe/Cu/CoFe/FeMn/Ta. Deposition rate was decreased and resistivity and roughness of the TaN films were increased as the $N_2$ gas flow was increased. The XRD results after high temperature annealing showed that Silicides were created in Si/Ta layer, but not in Si/TaN layer. Magnetoresistance ratio (MR) and exchange coupling field ($H_{ex}$) were decreased when the $N_2$ gas flow was increased over 4.0 sccm. The MR of the spin valves with Ta and TaN films deposited with up to 4.0 sccm of $N_2$ gas flow was increased about $0.5\%$ until the annealing temperature of up to $200^{\circ}C$ and then, decreased. TaN film deposited with 8.0 sccm of $N_2$ gas flow showed twice the adhesion of the Ta film. The above results indicate that with 3.0 sccm of $N_2$ gas flow during the Ta underlayer deposition, the magnetic properties of the spin valves are maintained, while the underlayer may be used as a diffusion barrier and the adhesion between the Si substrate and the underlayer is increased.

• Korean Journal of Materials Research
• /
• v.18 no.9
• /
• pp.486-491
• /
• 2008

The effect of annealing treatment conditions on the interfacial adhesion energy between electrolessplated Ni film and polyimide substrate was evaluated using a $180^{\circ}$ peel test. Measured peel strength values are $26.9{\pm}0.8,\;22.4{\pm}0.8,\;21.9{\pm}1.5,\;23.1{\pm}1.3,\;16.1{\pm}2.0\;and\;14.3{\pm}1.3g/mm$ for annealing treatment times during 0, 1, 3, 5, 10, and 20 hours, respectively, at $200^{\circ}C$ in ambient environment. XPS and AES analysis results on peeled surfaces clearly reveal that the peeling occurs cohesively inside polyimide. This implies a degradation of polyimide structure due to oxygen diffusion through interface between Ni and polyimide, which is also closely related to the decrease in the interfacial adhesion energy due to thermal treatment in ambient conditions.

• Applied Science and Convergence Technology
• /
• v.26 no.6
• /
• pp.208-213
• /
• 2017

Flexible opto-electronic devices are developed on the insulating layer deposited stainless steel (STS) substrates. The silicon dioxide ($SiO_2$) material as the diffusion barrier of Fe and Cr atoms in addition to the electrical insulation between the electronic device and STS is processed using the plasma enhanced chemical vapor deposition method. Noble silver (Ag) films of approximately 100 nm thickness have been formed on $SiO_2$ deposited STS substrates by E-beam evaporation technique. The films then were annealed at $650^{\circ}C$ for 20 min using the rapid thermal annealing (RTA) technique. It was investigated the variation of the surface morphology due to the interaction between Ag films and $SiO_2$ layers after the RTA treatment. The results showed the movement of Si atoms in silver film from $SiO_2$. In addition, the structural investigation of Ag annealed at $650^{\circ}C$ indicated that the Ag film has the material property of p-type semiconductor and the bandgap of approximately 1 eV. Also, the films annealed at $650^{\circ}C$ showed reflection with sinusoidal oscillations due to optical interference of multiple reflections originated from films and substrate surfaces. Such changes can be attributed to both formation of $SiO_2$ on Ag film surface and agglomeration of silver film between particles due to annealing.

• Elastomers and Composites
• /
• v.57 no.1
• /
• pp.1-8
• /
• 2022

In this study, the photo-deposition method was used to introduce Ag onto the surface of TiO₂ to synthesize an Ag-TiO₂ composite. The effects of the varying amounts of AgNO₃ precursor and annealing time periods on the Ag content in the composites, as well as their antibacterial characteristics under visible light conditions were studied. SEM analysis revealed the spherical morphology of the Ag-TiO₂ composite. Compared with TiO₂, the Ag particles were too small to be observed. An XPS analysis of the Ag-TiO₂ surface confirmed the Ag content and showed the peak intensities for elements such as Ag, Ti, O, C, and Si. The highest Ag content was observed when 33.3 wt.% of AgNO₃ and an annealing time of 6 h were employed; this was the optimum annealing time for Ti-Ag-O bonding, in that the lowest number of O bonds and the highest number of Ag bonds were confirmed by XPS analysis. Superior antibacterial properties against Bacillus and Escherichia coli, in addition to the widest inhibition zones were exhibited by the Ag-TiO₂ composite with an increased Ag content in a disk diffusion test, the bacterial reduction rate against Staphylococcus aureus and Escherichia coli being 99.9%.