• Archives of Metallurgy and Materials
• /
• v.64 no.3
• /
• pp.883-888
• /
• 2019

439L stainless steel composites blended with fifteen micron SiC particles were prepared by uniaxial pressing of raw powders at 100 MPa and conventional sintering at 1350℃ for 2 h. Based on the results of X-ray diffraction analysis, dissolution of SiC particles were apparent. The 5 vol% SiC specimen demonstrated maximal densification (91.5%) among prepared specimens (0-10 vol% SiC); the relative density was higher than the specimens in the literature (80-84%) prepared by a similar process but at a higher forming pressure (700 MPa). The stress-strain curve and yield strength were also maximal at the 5 vol% of SiC, indicating that densification is the most important parameter determining the mechanical property. The added SiC particles in this study did not serve as the reinforcement phase for the 439L steel matrix but as a liquid-phase-sintering agent for facilitating densification, which eventually improved the mechanical property of the sintered product.

• Korean Journal of Materials Research
• /
• v.10 no.9
• /
• pp.642-647
• /
• 2000

Nanocrystalline NiAl alloy containing 36at.%Al was synthesized by mechanical alloying (MA). Synthesized powder was sintered by a pulse electric current sintering (PECS) facility. Effecting parameters on the phase transformation were discussed in terms of cooling rate and time spent on heat treatment. The behavior of phase transformation for sintered parts was examined by differential scanning calorimetry (DSC) and X-ray diffraction (XRD) method. Microstructure was observed by scanning electron microscopy (SEM). Martensitic lattice parameter and volume fraction was calculated by direct comparison method in X-ray diffraction analysis.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2000.02a
• /
• pp.167-167
• /
• 2000

전지 재료의 충방전 과정 연구에는 X-선 분말회절(x-ray powder diffraction techniques)과 중성자회절을 많이 사용하였다. 하지만 이러한 분석기술은 long-range order의 구조에 관한 정보를 제공하는데 유용하지만 atomic scale의 구조에 관한 정보를 얻기에는 한계가 있다. Li 전지에서의 전기화학적 반응에서는 cathode 물질에 포함된 전이금속의 산화, 환원 반응에 의한 Li 이온의 intercalation (charge process)과 deintercalation (discharge process) 현상이 일어난다. 이러한 충방전 과정은 알려지지 않은 다양한 형태의 위상 변화를 동반하게 되는데 x-선 이나 중성자를 이용한 powder diffraction techniques 로는 단지 정성적인 결정학적 정보를 얻을 수 있다. 따라서 최근에 원자 단위의 local structure에 관한 정보와 electrochemical state에 관한 정보를 동시에 얻을 수 있는 X-ray Absorption Fine Structure (XAFS) 분석기술을 Li 전지분석에 활용하기 시작하였다. XAFS는 하나의 x-ray 흡수원자에 대해서 주변원자들의 원자구조에 관한 정보와 구성 원소의 electrochemical state에 관한 정보를 얻을 수 있는 분석방법이다. X-ray Induced Electron Emission Spectroscopy (XIEES)는 x-ray에 의해서 방출된 전자를 검출하여 스펙트럼을 얻는 기능을 함축적으로 나타낸 것으로, x-ray를 물질 표면에 조사하여 발생하는 광전자, Auger 전자, 이차전자 등을 전자검출기(Channel Electron Multiplier: CEM)로 검출하는 기능과, 시료를 투과한 x-ray와 시료에서 발생하는 형광 x-ray를 비례계수기로 검출하는 기능을 가지고 있다. 이러한 검출 능력을 바탕으로 EXAFS, XANES, Standing Wave Technique, Elemental Composition Analysis, DXRD, Total Reflection Technique 등을 이용하여 물질을 구성하고 있는 원소의 성분, 미세원자구조, 전자구조에 관한 정보를 얻을 수 있는 새로운 spectrometer이다. 본 연구에서는 자체 개발한 XIEES의 XAFS 기능을 이용하여 여러 가지 방법으로 제조한 LiMn2-xO4와 LiMnO2, MnO2에서 Mn K-absorption edge에 대한 chemical state 변화를 측정하였다. Absorption edge에서 chemical shift를 측정하기 위해서는 방사광 가속기 수준의 에너지 분해능(~0.3eV)이 필요하다. 이번 연구에서는 SiO2(3140) monochromator를 사용하고 여기에 맞는 적절한 parameter를 적용하여 x-ray 에너지 분해능을 포항방사광가속기 수준으로 개선하였다. XIEES에서 얻은 스펙트럼과 포항방사광가속기에서 얻은 스펙트럼을 비교하였다. Chemical shift가 일어나는 경향은 두 실험 결과가 잘 일치하였다.

• Journal of the Korean GEO-environmental Society
• /
• v.14 no.5
• /
• pp.49-56
• /
• 2013

The necessity of exploration in deep sea increases to develop the natural resources. The deep marine sediments, which were recovered from the hydrate occurrence regions during the Ulleung Basin Gas Hydrate Expedition 2 (UBGH2), East Sea, Korea in 2010, are explored to obtain the geotechnical characteristics and strength parameters. The index properties of the specimens including the atterberg limits, specific surface, and particle size distribution are measured and compared with the previous studies. X-ray diffraction, scanning electron microscope, and X-ray energy dispersive spectroscopy are conducted to analyze the clay mineralogy, chemical composition, and microstructure of the sediments. Strength parameters and shear wave velocities are measured with the axial strain by using an instrumented triaxial device. The strength parameters estimated by empirical equations are compared with the experimental results.

• Korean Journal of Materials Research
• /
• v.8 no.10
• /
• pp.898-904
• /
• 1998

Ni-W alloys containing 10 to 50wt% W were prepared by electrodeposition. Tungsten content in the alloy increased with current density. X-ray diffraction analysis revealed that the alloy was crystalline phase when deposited at current densities lower than 50mA/${cm}^2$. Their crystal structure transformed to amorphous at higher current densities. In terms of tungsten content, the crystal -+ amorphous transition occurred at 40-46wt% which was identified by the 3 fold increase in the width of a diffraction peak. The lattice parameter of crystalline phase increased with W upto 40wt% which is higher than the solubility limit of W (about 30wt%) in Ni. Therefore, the alloys are considered to be Ni solid solution supersaturated with W. The amorphous Ni-W alloys were recrystallized by annealing them at temperatures over $400^{\circ}C$. This was evidenced by the appearance a strong [ 11 11 annealing texture. The supersaturated W was precipitated during the annealing at over $800^{\circ}C$. The current-density dependence of W content and crystallinity was utilized to produce alternating layers of crystalline (30wt% W) and amorphous (50wt%) phases which may exhibit unique mechanical and corrosion properties.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.27 no.8
• /
• pp.486-490
• /
• 2014

$Al_2O_3$ films on silicon carbide were fabricated by Aerosol deposition with annealing temperature at $800^{\circ}C$ and $1,000^{\circ}C$. The effect of thermal treatment on physical properties of $Al_2O_3$ thin films has been investigated by XRD (X-ray diffraction), AFM (atomic force microscope), SEM (scanning electron microscope), and AES (auger electron spectroscopy). Also electrical properties have been investigated by Keithley 4,200 semiconductor parameter analyzer to explain the interface trapped charge density ($D_{it}$), flatband voltage ($V_{FB}$) and leakage current ($I_o$). $Al_2O_3$ films become crystallized with increasing temperature by calculating full width at half maximum (FWHM) of diffraction peaks, also surface morphology is observed by topography measurement in non-contact mode AFM. $D_{it}$ was $2.26{\times}10^{-12}eV^{-1}.cm^{-2}$ at $800^{\circ}C$ annealed sample, which is the lowest value in all samples. Also the sample annealed at $800^{\circ}C$ has the lowest leakage current of $4.89{\times}10^{-13}A$.

• Korean Journal of Materials Research
• /
• v.34 no.1
• /
• pp.21-26
• /
• 2024

In this investigation, samples of the chemical (Hg_1-xPb_xBa₂Ca_1.8Mg_0.2Cu₃O_8+δ) were prepared utilizing a solid-state reaction technique with a range of lead concentrations (x = 0.0, 0.05, 0.10, and 0.20). Specimens were pressed at 8 tons per square centimeter and then prepared at 1,138 K in the furnace. The crystalline structure and surface topography of all samples were examined using X-ray diffraction (XRD) and atomic force microscopy (AFM). X-ray diffraction results showed that all of the prepared samples had a tetragonal crystal structure. Also, the results showed that when lead was partially replaced with mercury, an increase in the lead value impacted the phase ratio, and lattice parameter values. The AFM results likewise showed excellent crystalline consistency and remarkable homogeneity during processing. The electrical resistivity was calculated as a function of temperature, and the results showed that all samples had a contagious behavior, as the resistivity decreased with decreasing temperature. The critical temperature was calculated and found to change, from 102, 96, 107, and 119 K, when increasing the lead values in the samples from 0.0 to 0.05, 0.10, and 0.20, respectively.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.24 no.4
• /
• pp.140-144
• /
• 2014

Co-(0.7 wt%) and Pr-(2.0, 3.5 or 5.0 wt%) doped cubic zirconia ($ZrO_2:Y_2O_3=50:50wt%$) single crystals grown by a skull melting method were heat-treated in $N_2$ at $1150^{\circ}C$ for 5 hrs. The brown colored as-grown single crystals were changed into either dark brownish green, greenish blue and light green color after the heat treatment. Before and after the heat treatment, the YSZ (yttria-stabilized zirconia) single crystals were cut for wafer form (${\phi}7.5mm{\times}t3mm$). The optical and structural properties were examined by UV-VIS spectrophotometer and X-ray diffraction. Absorption by $Co^{2+}$(${\fallingdotseq}589nm$: ${\Gamma}_8[^4A_2(^4F)]{\rightarrow}{\Gamma}_8+{\Gamma}_7[^4T_1(^4F)]$, ${\fallingdotseq}610nm$: ${\Gamma}_8[^4A_2(^4F)]{\rightarrow}{\Gamma}_8[^4T_1(^4F)]$], ${\fallingdotseq}661nm$: ${\Gamma}_8[^4A_2(^4F)]{\rightarrow}{\Gamma}_6[^4T_1(^4F)]$]) and $Pr^{3+}$(${\fallingdotseq}450nm$: ${^3}H{_4}-{^3}P{_2}$, ${\fallingdotseq}473nm$: ${^3}H{_4}{\rightarrow}{^3}P{_1}$, ${\fallingdotseq}484nm$: ${^3}H{_4}{\rightarrow}{^3}P{_0}$), change of ionization energy and lattice parameter were confirmed.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.22 no.2
• /
• pp.73-77
• /
• 2012

Co-(0.8 wt%) and Ce-(0.4 wt%) doped cubic zirconia ($ZrO_2$ : $Y_2O_3$ = 80 : 20, 70 : 30, 60 : 40, 50 : 50 wt%) single crystals grown by a skull melting method were heat-treated in $N_2$ at $1000^{\circ}C$ for 5 hrs. The orange, yellowish brown and brown colored as-grown single crystals were changed into either brownish red, yellow and green color after the heat treatment. Before and after the heat treatment, the YSZ (yttria-stabilized zirconia) single crystals were cut for wafer form (${\phi}6.5mm{\times}t2mm$). The optical and structural properties were examined by UV-VIS spectrophotometer and X-ray diffraction. Absorption by $Ce^{3+}(^2F_{5/2,7/2}(4f){\rightarrow}^2T_g(5d^1))$, $Co^{2+}(^4A_2(^4F){\rightarrow}^4T_1(^4F)$ or $^4T_1(^4P))$ and $Co^{3+}$, change of ionization energy and lattice parameter were confirmed.

• Journal of the Korean Ceramic Society
• /
• v.34 no.2
• /
• pp.145-156
• /
• 1997

ZrO2 phase transformations depending on the type and amount of dopants and the sintering temperatures were studied for the 2 components (CaO-, Y2O3-, MgO-ZrO2) and the 3 components(MgO-ZrO2-Al2O3)ZrO2 powder by X-ray diffraction and Raman spectroscopy. In the CaO- and Y2O3-ZrO2 systems, as the CaO and Y2O3 contents increased to 6~15mol% and 3~15mol% respectively, we were not able to identify between tetragonal and cubic in the X-ray diffraction patterns. On the other hand, all Raman modes shifted to lower wavenumbers, decreasing in intensity and the number of bands, markedly. These phenomena were caused by tetragonallongrightarrowcubic phase transformation and interpreted by the breakdown of the wave vector selection rule(k=0) and the structural disorder associated with the formation of oxygen sublattice which was caused by the substitution between Zr4+ ion and Ca2+ or Y3+ ion in ZrO2 matrix. The monoclinic to cubic phase transformation occurred in 10mol% MgO-ZrO2 system. As the Al2O3 content increased from 0 to 20mol% in the MgO-ZrO2-Al2O3 systems, cubic phase transformed to monoclinic phase, this is because the MgO didn't play a role in a stabilizer because of the formation of the spinel(MgAl2O4) by the reaction between MgO and Al2O3, Also, the ZrO2 phase transformation was explained by the change of it's lattice parameters depending on the type and amount of dopants. Namely, as the amount of dopant increased to 10~13mol%, the axial ra-tio c/a came close to unity with increasing the lattice parameter a and decreasing the lattice parameter c. At that time, the tetragonallongrightarrowcubic phase transformation occurred.