• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2003년도 international symposium on advanced powder metallurgy
• /
• pp.62-63
• /
• 2003

The inter-particle distance between diamonds on the segment surface of sawing blade predicted theoretically and measured experimentally followed a Gamma or Weibull function, rather than a normal distribution function. These results suggest that random dispersion of diamond particles in the segment may not be an efficient way of improving cutting efficiency of the blade.

• 한국분말재료학회지
• /
• 제15권5호
• /
• pp.378-385
• /
• 2008

This article presents the successful consolidation of the mixed Co and Diamond powders for a drilling segment by the combined application of magnetic pulsed compaction (MPC) and subsequent sintering, and their properties were analyzed. Homogeneous hardness (Hv 220) and density (97%) of sintered bulks fabricated by MPC were obtained by the new technique, where higher pressure has been employed for short period of time than that of general process. A fine microstructure and homogeneous hardness in the consolidated bulk were observed without cracks. Relatively higher drilling speed of 9.61 cm/min and life time of 6.55 m were found to the MPCed specimens, whereas the value of the specimens fabricated by general process was 11.71 cm/min and 7.96 m, respectively. A substantial improvement of mechanical properties of segment was achieved through this study.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.1311-1312
• /
• 2006

Diamond tools were fabricated by cold pressing and sintering under pressure at the temperature up to $750^{\circ}C$. Investigation of the microhardness behaviour of the segments was showed that increasing the cobalt ratio causes the increase of the hardness of the matrix material. This caused to decrease of the wear rate of the matrix. Because the matrix wears more slowly than the diamonds, the space between the cutting edges and the matrix is constantly reduced. The swarf cannot be carried away properly, and the segment will continuously lose its ability to cut with higher cobalt contents.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.1140-1141
• /
• 2006

Diamond tools with several layers of diamond grits through thickness direction were tested by sawing. The saw blades with evenly distributed grits showed better cutting performance compared to the random distributed saw. At a given concentration of grits, as the spacing between layers was increased, the cutting performance was improved, and as decreased, it showed more tool life

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.1146-1147
• /
• 2006

Diamond segments were fabricated by cold pressing and sintering under pressure at the temperature up to $750^{\circ}C$. Based on the results of this investigation, it can be concluded that the segments containing 39wt.% cobalt in the matrix material have the highest bending strength at a fracture probability of 50 % due to the weibull distribution method. According to the weibull statistics, it was also determined that the transverse rupture strength was the best for 39 wt.% cobalt ratio in the matrix material for the fracture probability when the other variables are the same.

• 한국레이저가공학회:학술대회논문집
• /
• 한국레이저가공학회 2002년도 춘계학술발표대회 논문개요집
• /
• pp.65-70
• /
• 2002

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2002년도 춘계학술발표대회 개요집
• /
• pp.232-235
• /
• 2002

• Restorative Dentistry and Endodontics
• /
• 제47권1호
• /
• pp.4.1-4.13
• /
• 2022

Objectives: This study evaluated the effects of different smear layer preparations on the dentin permeability and microtensile bond strength (µTBS) of 2 self-etching adhesives (Clearfil SE Bond [CSE] and Clearfil Tri-S Bond Universal [CTS]) under dynamic pulpal pressure. Materials and Methods: Human third molars were cut into crown segments. The dentin surfaces were prepared using 4 armamentaria: 600-grit SiC paper, coarse diamond burs, superfine diamond burs, and carbide burs. The pulp chamber of each crown segment was connected to a dynamic intra-pulpal pressure simulation apparatus, and the permeability test was done under a pressure of 15 cmH₂O. The relative permeability (%P) was evaluated on the smear layer-covered and bonded dentin surfaces. The teeth were bonded to either of the adhesives under pulpal pressure simulation, and cut into sticks after 24 hours water storage for the µTBS test. The resin-dentin interface and nanoleakage observations were performed using a scanning electron microscope. Statistical comparisons were done using analysis of variance and post hoc tests. Results: Only the method of surface preparation had a significant effect on permeability (p < 0.05). The smear layers created by the carbide and superfine diamond burs yielded the lowest permeability. CSE demonstrated a higher µTBS, with these values in the superfine diamond and carbide bur groups being the highest. Microscopic evaluation of the resin-dentin interface revealed nanoleakage in the coarse diamond bur and SiC paper groups for both adhesives. Conclusions: Superfine diamond and carbide burs can be recommended for dentin preparation with the use of 2-step CSE.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2002년도 Proceedings of the International Welding/Joining Conference-Korea
• /
• pp.639-643
• /
• 2002

The main purpose of this study was to investigate the formation mechanisms of imperfections such as irregular humps, outer cavity and inner cavity in the laser fusion zone of diamond saw blade. Laser beam welding was conducted to join two parts of blade; mild steel shank and Fe-Co-Ni sintered tip. The variables were beam power and travel speed. The microstructure and elements distributions of specimens were analyzed with SEM, AES, EPMA and so on. It was found that these imperfections were responded to heat input. Irregular humps were reduced in 10.4∼17.6kJ/m heat input range. However there were no clear evidences, which could explain the relations between humps formation and heat input. The number of outer cavity and inner cavity decreased as heat input was increased. Considering both possible defects formations mechanisms, it could be thought that outer cavity was caused by insufficient refill of keyhole, which was from rapid solidification of molten metal and fast molten metal flow to the rear keyhole wall at low heat input. More inner cavities were found near the interface of the fusion zone and sintered segment and in the bottom of the fusion zone. Inner cavity was mainly formed in the upper fusion zone at high heat input whereas was in the bottom at low heat input. Inner cavity was from trapping of coarsened preexist pores in the sintered tip and metal vapor due to rapid solidification of molten metal before the bubbles escaped.

• International Journal of Korean Welding Society
• /
• 제2권1호
• /
• pp.21-24
• /
• 2002

The main purpose of this study was to investigate the formation mechanisms of imperfections such as irregular humps, outer cavity and inner cavity in the laser fusion zone of diamond saw blade. Laser beam welding was conducted to join two parts of blade; mild steel shank and Fe-Co-Ni sintered tip. The variables were beam power and travel speed. The microstructure and elements distributions of specimens were analyzed with SEM, AES, EPMA and so on. It was found that these imperfections were responded to heat input. Irregular humps were reduced in 10.4∼l7.6kJ/m heat input range. However there were no clear evidences, which could explain the relations between humps formation and heat input. The number of outer cavity and inner cavity decreased as heat input was increased. Considering both possible defects formations mechanisms, it could be thought that outer cavity was caused by insufficient refill of keyhole, which was from rapid solidification of molten metal and fast molten metal flow to the rear keyhole wall at low heat input. More inner cavities were found near the interface of the fusion zone and sintered segment and in the bottom of the fusion zone. Inner cavity was mainly formed in the upper fusion zone at high heat input whereas was in the bottom at low heat input. Inner cavity was from trapping of coarsened preexist pores in the sintered tip and metal vapor due to rapid solidification of molten metal before the bubbles escaped.