In order to investigate the properties of diamond-like carbon(DLC) thin films depending on the deposition parameters, DLC thin films were systematically fabricated by pulsed laser deposition (PLD), DLC thin films have been shown advantageous field emission properties due to a negative electron affinity (NEA) and a low work function. At the atomic level. DLC is referred to the group of carbon materials with strong chemical bonding composition of $sp^2$ and $sp^3$ arrangements of atoms incorporated with an amorphous structure. The experiment was performed at substrate temperature in the range of room temperature to $600^{\circ}C$. The laser energy densiy was used to be in the range of $6J/cm^2$ to $20J/cm^2$, SEM, Raman, PL, XPS and field emission characteristics were used to investigate the DLC thin films.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2002.10b
• /
• pp.69-69
• /
• 2002

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2004.05a
• /
• pp.141-141
• /
• 2004

다이아몬드상 탄소(diamond-like carbon, DLC) 박막은 명칭에 함축된 의미로 알 수 있듯이 다이아몬드와 유사한 특징을 지니고 있다. DLC 박막은 비정질(amorphous) 고상 탄소 박막으로 구조적으로 Sp$^1$, Sp$^2$, Sp$^3$의 결합들로 구성되어 있다. DLC 박막의 물성으로는 우수한 경도, 내마모성, 낮은 마찰계수, 화학적 안정성 그리고 적외선(IR) 영역에서의 높은 투과율 등이 있다. 현재 DLC 박막은 앞서 열거된 물성들의 장점을 활용하여 다양한 산업분야에서 활발히 응용되고 있다.(중략)

• Proceedings of the KIEE Conference
• /
• 1990.11a
• /
• pp.97-100
• /
• 1990

Diamond thin films were synthesized by the MPECVD (Microwave Enhanced Chemical Deposition) using the mixture of the hydrogen and organic compounds($CH_3COCH_3$, $CH_3OH$). In X-ray Diffraction, the d values of all the deposits on the Si substrates with the experimental conditions coincide with those of natural diamond in POD (Powder Diffraction Data). The changes of the morphology of all the deposits were examined by SEM. The amount of amorphous carbon or graphite in the diamond films were increased as the acetone concentration was increased. The morphology of the diamond particles can be changed from ball-like to euhedral by adding the small amount of the methanol in the reaction gases of the high acetone concentration.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.3
• /
• pp.278-282
• /
• 2004

The Hydrogenated amorphous carbon(a-C:H) thin films are deposited on silicon with a close field unbalanced magnetron(CFUBM) sputtering systems. The experimental data are obtained on the depositon rate and physical properties of a-C:H films using DC bias voltage and Ar/C$_2$H$_2$ pressure. The depostion rate and the surface roughness decrease with DC bias voltage, but the hardness of the thin films increases with DC bias voltage. And the position of G-peak moves to lower wavenumber indicating an increase in diamond-like carbon characteristics with the lower Ar/C$_2$H$_2$ pressure.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07b
• /
• pp.748-752
• /
• 2004

The Hydrogenated amorphous carbon (a-C:H) thin films are deposited to fabricate suppored layer on silicon substrate with a closed field unbalanced magnetron(CFUBM) sputtering system. This study focuses on the characteristic of Diamond like carbon (DLC) films and Pb(Zr,Ti)$O_3$ (PZT) films for membrane structure. The deposition rate and the surface roughness of DLC fims decrease with DC bias voltage. hardness is 26 GPa at -200 V. Interface of DLC/Si and Pt/DLC layers was excellent.

• Korean Journal of Materials Research
• /
• v.20 no.11
• /
• pp.570-574
• /
• 2010

A diamond-like carbon (DLC) film deposited on a WC disk was investigated to improve disk wear resistance for injection molding of zirconia optical ferrule. The deposition of DLC films was performed using the filtered vacuum arc ion plating (FV-AIP) system with a graphite target. The coating processing was controlled with different deposition times and the other conditions for coating, such as input power, working pressure, substrate temperature, gas flow, and bias voltage, were fixed. The coating layers of DLC were characterized using FE-SEM, AFM, and Raman spectrometry; the mechanical properties were investigated with a scratch tester and a nano-indenter. The friction coefficient of the DLC coated on the WC was obtained using a pin-on-disk, according to the ASTM G163-99. The thickness of DLC films coated for 20 min. and 60 min. was about 750 nm and 300 nm, respectively. The surface roughness of DLC films coated for 60 min. was 5.9 nm. The Raman spectrum revealed that the G peak of DLC film was composed of $sp^3$ amorphous carbon bonds. The critical load (Lc) of DLC film obtained with the scratch tester was 14.6 N. The hardness and elastic modulus of DLC measured with the nano-indenter were 36.9 GPa and 585.5 GPa, respectively. The friction coefficient of DLC coated on WC decreased from 0.2 to 0.01. The wear property of DLC coated on WC was enhanced by a factor of 20.

• Tribology and Lubricants
• /
• v.11 no.5
• /
• pp.59-65
• /
• 1995

Tribological behaviors of nitrogen incorporated amorphous diamond-like carbon films were experimentally measured under a vacuum ($3 \times 10^{-5}$ Torr) using a ball (AISI 52100 steel)-on-disk wear-rig. Nitrogen incorporated DLC films were deposited by r.f. plasma assisted chemical vapor deposition method. Mixtures of benzene and ammonia or nitrogen gases were used as the reaction gases for the r.f. PACVD, and Si (100) wafer was used as the substrate. In the tribo-test, effects of DLC film thickness and normal load in friction were measured and discussed. Results showed that friction of nitrogen incorporated DLC films from a mixture gas of benzene and ammonia was lower than that of 100% benzene, specially in the measurement of minimum coefficient of friction. Differences in frictional characteristics of nitrogen incorporated DLC films were explained with the changes in chemical structures of the films. Result also showed that friction of DLC films increased with the sliding contact cycle, which remarkably accompanied with roll-shaped wear debris. Mechanisms and roles of the polymer-like wear debris were presented and discussed.

• Korean Journal of Materials Research
• /
• v.33 no.4
• /
• pp.124-129
• /
• 2023

This study assessed the influences of fluorine introduced into DLC films on the structural and mechanical properties of the sample. In addition, the effects of the fluorine incorporation on the compressive stress in DLC films were investigated. For this purpose, fluorinated diamond-like carbon (F-DLC) films were deposited on cobalt-chromium-molybdenum substrates using radio-frequency plasma-enhanced chemical vapor. The coatings were examined by Raman scattering (RS), Attenuated total reflectance Fourier transform infrared spectroscopic analysis (ATR-FTIR), and a combination of elastic recoil detection analysis and Rutherford backscattering (ERDA-RBS). Nano-indentation tests were performed to measure hardness. Also, the residual stress of the films was calculated by the Stony equation. The ATR-FTIR analysis revealed that F was present in the amorphous matrix mainly as C-F and C-F₂ groups. Based on Raman spectroscopy results, it was determined that F made the DLC films more graphitic. Additionally, it was shown that adding F into the DLC coating resulted in weaker mechanical properties and the F-DLC coating exhibited lower stress than DLC films. These effects were attributed to the replacement of strong C = C by feebler C-F bonds in the F-DLC films. F-doping decreased the hardness of the DLC from 11.5 to 8.8 GPa. In addition, with F addition, the compressive stress of the DLC sample decreased from 1 to 0.7 GPa.

• Journal of the Korean institute of surface engineering
• /
• v.48 no.3
• /
• pp.87-92
• /
• 2015

Carbon thin films were deposited on STS 316L sheets by inductively coupled plasma enhanced magnetron sputtering with or without substrate bias voltage. Typical Raman spectrum for amorphous diamond-like carbon (DLC) was obtained, and the interfacial contact resistance (ICR) was measured to show its conductive nature. The electrochemical impedance spectroscopy (EIS) was used to investigate the corrosion mechanism of the carbon coating under the polymer electrolyte membrane fuel cell (PEMFC) condition. According to the pore-corrosion mechanism, the electrolyte penetrates the carbon coating through the pores and reacts with the substrate. As the substrate corrosion proceeds, the pore enlargement occurs and the surface area of the substrate exposed to the electrolyte. Applicability of the carbon coating for the PEMFC bipolar plate was evaluated by potentiodynamic polarization experiments. Finally, an adhesion problem was briefly considered.