• Restorative Dentistry and Endodontics
• /
• v.22 no.2
• /
• pp.609-621
• /
• 1997

The purpose of this study was to evaluate the shear bond strength of three light-cured glass ionomer cements to blood contaminated bovine dentin. The materials used in this study were Fuji II LC, Dyract and Variglass VLC. The dentin conditioners were 10% polyacrylic acid, 10% maleic acid and 10% phosphoric acid. 180 lower anterior bovine teeth were selected in this study. The teeth were embedded in acrylic resin and were grounded with 320 to 600 grit silicon carbide paper to create a flat dentin surface. The teeth were divided into SIX groups. The experimental procedures in six groups were as follows; Group l(GF) : Samples bonded to dentin surface with Fuji II LC after 10% polyacrylic acid treatment. Group 2(BGF) : Samples bonded to dentin surface with Fuji II LC after 10% polyacrylic acid treatment and blood contamination. Group 3(MD) : Samples bonded to dentin surface with Dyract after 10% maleic acid treatment. Group 4(BMD) : Samples bonded to dentin surface with Dyract after 10% maleic acid treatment and blood contamination. Group 5(PV) : Samples bonded to dentin surface with Variglass VLC after 10% phosphoric acid treatment. Group 6(BPV) : Samples bonded-to dentin surface with Variglass VLC after 10% phosphoric acid treatment and blood contamination. Group 1,3 and 5 were classified into the control groups, while group 2,4 and 6 were classified into the experimental groups. Each group contained 30 samples. After 24 hours water storage at $37^{\circ}C$, all smples were subjected to a shear load to fracture at a cross head speed of 1.0 mm/min with Instron universal testing machine(No. 4467). Debonded surfaces were observed under Scanning Electron Microscope(Hitachi S-2300) at 20kvp. The data were evaluated statistically at the 95% confidence level with Student's t-test. The following results obtained; 1. Shear bond strengths were higher in the control groups(1,3,5 group) than in the experimental groups(2,4,6 group). 2. The shear bond strength of group 5(PV) was the highest in the control groups, and the group 5 was significantly higher than the group l(GF) on the shear bond strength. 3. The group 4(BMD) was the highest on the shear bond strength, and the group 2(BGF) was the lowest in the experimental groups. The group 4(BMD) and 6(BPV) showed a significant difference with the group 2 on the shear bond strength. 4. All the groups showed an adhesive-cohesive failure. except the group 2(BGF) showing adhesive failure.

• Restorative Dentistry and Endodontics
• /
• v.29 no.5
• /
• pp.430-438
• /
• 2004

This study evaluated the influence of application time of self-etching primers on microtensile bond strength (${\mu}$TBS) to dentin using three self-etching primer adhesive systems. Dentin surfaces were exposed from forty-eight human molars. They were conditioned with three self-etching primers (Clearfil SE Bond [SE], Unifil Bond [UF], Tyrian SPE + One Step Plus [TY]) and different primining times (10s, 20s, 30s and 40s). Composite resins were bonded to dentin surfaces and specimens were made. ${\mu}TBS$ was tested and statistically compared using by one-way ANOVA and Tukey's Test. The results of this study presented that priming time for 10s in SE and UF groups and for 30s and 40s in TY group was highly decreased ${\mu}TBS$ to dentin.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.23 no.4
• /
• pp.867-886
• /
• 1996

The purpose of this study was to evaluate the shearbond strength and resin-dentin interface of three different dentinal bonding systems in primary and permanent teeth. Thirty extracted human primary molars and premolars, which were non-carious and free of obvious defect, were selected for this study. All specimens were divided into six groups with two groups allocated for each of the three dentinal bonding system(All-bond 2, Scotchbond Multi-Purpose, Gluma bonding system). After completion of bonding composite to dentin using each tested dentin bonding system, bond strength measurement and histological observation were performed. The results are as follows: 1. All-bond 2 and Scotchbond Multi-Purpose, A good quality hybrid layer was identified, the morphology of which could be equated with the zone of H-E and Brown-Brenn staining. In Gluma bonding system, hybrid layer was very thin, and separated from the solid polymer. 2. All-bond 2 had the highest mean shearbond strength, followed by Scotchbond Multi-Purpose and Gluma bonding system in both primary and permanent teeth. There was no statistically significant difference between All-bond 2 and Scotchbond Multi-Purpose. Statistically significant difference could be found between Gluma bonding system and the other two groups(p<0.05). 3. The fracture patterns observed were mainly the mixture of adhesive failure and dentin dettachment pattern in All-bond 2 and Scotchbond Multi-Purpose while adhesive failure prevailed in Gluma bonding system.

• Restorative Dentistry and Endodontics
• /
• v.28 no.6
• /
• pp.498-503
• /
• 2003

The purpose of this study was to evaluate the rewetting effect of water-based primer on the air-dried dentin. In this in vitro study, freshly extracted non-caries human molars and three-step adhesive system(SBMP) were used. Freshly extracted non-caries human molars and three-step adhesive system(SBMP) were used. Flat occlusal dentin surface were prepared using low-speed diamond saw, Prepared teeth were randomly divided into three groups. Group 1.(W): etched(35% phosphoric acid for 15s) and blot-dried, Group 2.(5D): 5s air-dried, Group 3.(30D): 30s ail-dried, To obtain color contrast in CLSM observation, primer was mixed with rhodamine B and bonding resin was mixed with fluorescein. Microscopic sample of each group were obtained after longitudinal section. Morphological investigation of resin-dentin interface and thickness of hybrid layer measurement using CLSM were done. Microtensile bond strength for each specimen was measured. Specimen were observed under microscope to examine the failure patterns of interface between resin and dentin. The results of this study were as follows: 1. The results(mean) of Thickness of hybrid layer were W:19.67, 5D:20.9, 30D:10$\mu\textrm{m}$. Only 30D had statistically significant differences to Wand 5D(P<0.05). 2. The results(mean) of Microtensile bond strength were W:16.02, 5D:14.69, 30D:11.14MPa. Only 30D had statistically significant differences to Wand 5D(P<0.05). 3. There were positive correlation between Thickness of hybrid layer and microtensile bond strength(P<0.05).

• Restorative Dentistry and Endodontics
• /
• v.12 no.2
• /
• pp.101-108
• /
• 1987

The purpose of this study was to investigate the pulpal responses of dental adhesive resins. A total of 40 cavities of the permanent healthy teeth from 4 dogs were prepared. In the experimental group, the cavities were etched for 1 minute with citric acid and filled with experimental resins (ie. Super-Bond C & B$^{(R)}$). In the control group, the cavities were filled with calcium hydroxide base materials (ie. Dycal$^{(R)}$) without etching. The dogs were sacrificed at one, two, three and four weeks after the time of filling and the specimens were routinely prepared and stained with Hematoxylin-Eosin. The microscopic findings were as follows: Infiltration of inflammatory cells was not observed in both experimental and control groups. Change in the odontoblastic layer was not observed in all control groups but severe swelling was observed in deep dental pulp tissue of the control two and three week cases. Pulp tissue was recovered with plenty of fibrous component in the control four week case and reparative dentin formation was not occurred in all cases. Slight changes of the odontoblastic layer beneath the cavity were observed in the experimental one week case. In experimental two and three week cases, swelling of deep pulp tissue was increased and localized reparative dentin formation was observed. In the experimental four week case, odontoblastic layer was recovered with regular appearance and fibrous component of the pulp was increased, but reparative dentin formation was not evident.

• The Journal of Advanced Prosthodontics
• /
• v.12 no.2
• /
• pp.89-99
• /
• 2020

PURPOSE. The effects of four different self-adhesive resin cement materials on cell viability and apoptosis after direct and indirect exposure were evaluated using different cell culture techniques. MATERIALS AND METHODS. Self-adhesive cements were applied to NIH/3T3 mouse fibroblasts by the extract test method, cell culture inserts, and dentin barrier test method. After exposure periods of 24 h and 72 h, the cytotoxicity of these self-adhesive materials was evaluated using the MTT assay (viability) and the Annexin-V-FITC/PI staining (apoptosis). RESULTS. The lowest cell viability was found in cells exposed to BeautiCem SA for 24 h in the extract test method. Cell viability was reduced to 70.6% compared to negative controls. After the 72 h exposure period, viability rate of cell cultures exposed to BeautiCem SA decreased more than 2- fold (29.5%) while cells exposed to RelyX U200 showed the highest viability rate of 71.4%. In the dentin barrier test method, BeautiCem SA induced the highest number of cells in apoptosis after a 24 h exposure (4.1%). Panavia SA Cement Plus was the material that caused the lowest number of cells in apoptosis (1.5%). CONCLUSION. The used self-adhesive cements have showed different cytotoxic effects based on the evaluation method. As exposure time increased, the materials showed more cytotoxic and apoptotic effects. BeautiCem SA caused significantly more severe cytotoxic and apoptotic effects than other cements tested. Moreover, cements other than BeautiCem SA have caused necrotic cell death rather than apoptotic cell death.

• Restorative Dentistry and Endodontics
• /
• v.49 no.2
• /
• pp.18.1-18.13
• /
• 2024

Objectives: This study was conducted to evaluate the mechanical properties of relined and non-relined fiberglass posts when cemented to root canal dentin using a conventional dual-cure resin cement or a self-adhesive resin cement. Materials and Methods: Two types of resin cements were utilized: conventional and self-adhesive. Additionally, 2 cementation protocols were employed, involving relined and non-relined fiberglass posts. In total, 72 bovine incisors were cemented and subjected to push-out bond strength testing (n = 10) followed by failure mode analysis. The cross-sectional microhardness (n = 5) was assessed along the root canal, and interface analyses (n = 3) were conducted using scanning electron microscopy (SEM). Data from the push-out bond strength and cross-sectional microhardness tests were analyzed via 3-way analysis of variance and the Bonferroni post-hoc test (α= 0.05). Results: For non-relined fiberglass posts, conventional resin cement exhibited higher pushout bond strength than self-adhesive cement. Relined fiberglass posts yielded comparable results between the resin cements. Type II failure was the most common failure mode for both resin cements, regardless of cementation protocol. The use of relined fiberglass posts improved the cross-sectional microhardness values for both cements. SEM images revealed voids and bubbles in the incisors with non-relined fiberglass posts. Conclusions: Mechanical properties were impacted by the cementation protocol. Relined fiberglass posts presented the highest push-out bond strength and cross-sectional microhardness values, regardless of the resin cement used (conventional dual-cure or self-adhesive). Conversely, for non-relined fiberglass posts, the conventional dual-cure resin cement yielded superior results to the self-adhesive resin cement.

• Proceedings of the KACD Conference
• /
• 2003.11a
• /
• pp.600-600
• /
• 2003

I. Objectives Effective endodontic obturation must provide a complete, three-dimensional filling of the root canal system, preventing the communication of fluids between root canal and surrounding periapical tissues. The objective of this study was to compare the apical leakage with or without the use of dentin adhesive system. II. Materials and Methods Forth extracted human teeth with single canals were decoronated. Root canals were instrumented using GT rotary files and Profile .04 file up to #40, 1mm short of the apex. After each instrumentation, copious irrigation with 5.25% sodium hypochlorite solution and confirmation of apical patency were performed.(omitted)

• Journal of the korean academy of Pediatric Dentistry
• /
• v.44 no.1
• /
• pp.72-81
• /
• 2017

The aim of this study was to evaluate the effectiveness of artificial saliva contamination and decontamination procedures at different stages of a bonding procedure on the microtensile bond strength (MTBS) of two one-step self-etch adhesives and a two-step total-etch adhesive to dentin of primary teeth. Forty-two extracted sound primary molars were randomly divided into three groups depending on three adhesives, Scotchbond Universal Adhesive (SBU), All-Bond Universal (ABU) and Prime & Bond NT (PNT). For each adhesive, the teeth were allocated into seven groups. Except for control group, group 1, the groups were contaminated with artificial saliva at three different stages: the groups 2 and 3 - before adhesive application; the groups 4 and 5 - before adhesive polymerization; the groups 6 and 7 - after adhesive polymerization. Decontaminating procedures were rinsing, air-drying (group 2, 4, 6) and air-drying (group 3, 5, 7). The specimens were restored with composite resin (Filtek, Z350) and microtensile bond strength was measured. The data was analyzed with one-way ANOVA and Tukey HSD test (p < 0.05). In the control group, using PNT resulted in significantly higher bond strength than when ABU and SBU were used (p < 0.001). For three adhesives, the groups 2, 4 and 6 had greater bond strength than the groups 3, 5 and 7. Also, when the artificial saliva was contaminated before adhesive polymerization (group 4, 5), it showed a significantly lower bond strength. Generally the two-step total-etch adhesive generated a higher bond strength than the one-step self-etch adhesive. Artificial saliva contamination before adhesive polymerization led to a drastic decrease in bond strength, and rinsing with water followed by air-drying could not recover the bond strength.

• Restorative Dentistry and Endodontics
• /
• v.23 no.1
• /
• pp.468-476
• /
• 1998

The purpose of this study was to observe the morphologic change of dentinal surface, adhesion in interface between dentin and bonding agents, and penetration pattern of resin tags into dentinal tubles according to bonding procedure of ONE-STEP universal adhesive system. Ten extracted human molars were mounted in dental stone and sectioned to expose mid-coronal occlusal dentin and again sectioned tooth crown apically. Specimens were randomly assigned to three groups for dentin conditioning with 32% phoshoric acid, two coats of bonding agents after dentin conditioning, and bond of composite resin. The surfaces of dentin were treated with etch ant and applied bonding agent, and bonded composite resin according to the directions of manufacturer. Specimens which were boned composite were sectioned longitudinally for observing interfaces between resin and dentin. Two of specimens which were sectioned longitudinally were immersed in 6 N HCL for 30 seconds and 1% NaOCL for 12 hours to partially demineralize and deproteinize the dentin substrate. Each specimen was mounted on a brass stub, sputter-coated with gold and observed under SEM. The result were as follows : 1. On the dentinal surface which was conditioned with 32% phosphoric acid. the smear layer was completely removed. orifices of dentinal tubules were opened 3-$5{\mu}m$ wide. and dentinal surface was irregular. 2. On the dentinal surface which was applied ONE-STEP. bonding agent. resin particles were observed on the orifices of dentinal tubules and intertubular dentin. 3. There were close adaptation between dentin and resin and were the pattern which composite invaded into dentin. 4. 1-$3{\mu}m$-wide hybrid layer was visible in the interface between dentin and resin. 5. Long and funnel shaped resin tags were observed in demineralized specimens. and the surfaces of tags were rough.