• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.47 no.5
• /
• pp.104-111
• /
• 2015

Factors influencing penetration of PVAm solution into paper during impregnation were investigated with ultrasonic Penetration Evenness Analyzer (PEA). Paper structure was varied by changing basis weight, freeness of pulp, calendering, and filler addition, and hydrophobicity of paper was varied by adding AKD. In addition, the viscosity of PVAm solution was varied by changing the concentration of PVAm solution. Important factors influencing penetration of PVAm solution into paper were found to be the pore structure and the hydrophobicity of paper, and the viscosity of PVAm solution. Pore structure of paper could be controlled by refining degree and filler addition and hydrophobicity of paper could be controlled by internal sizing. Denser structure of paper, higher hydrophobicity and higher liquid viscosity slowed down the penetration of PVAm solution into paper.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2002.10a
• /
• pp.245-248
• /
• 2002

Research on the high performance and strength thermoplastic/continuous fiber composites was performed. New concept of impregnating die for developing continuous strand and prepreg tape of engineering plastic/glass fiber was introduced and estimated. Fully impregnated prepreg strand and tape was successfully manufactured through the new pin structure of impregnating die and control of spreading variable. Also design variables for stability of increasing processing speed were shown. And tensile strength of prepreg tape manufactured in this study was much higher than composites made by other competition company.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2000.04a
• /
• pp.199-210
• /
• 2000

복합재료의 성형 공정 중 하나인 Filament Winding 공정에 열가소성 기지재료인 폴리프로필렌(Polypropylene)과 강화섬유인 유리섬유로 이루어진 Commingled Yarn 을 이용한 연구를 수행하였다. 함침 과정을 해석하기 위한 계산모델을 제시하였다. 그리고 위의 모델링을 해석하는 데 필요한 복합재료 내의 온도 분포를 수치해석을 통해 계산하였고 실험을 통해 이를 검증하였다. 온도계산 결과를 함침도 예측에 이용하였다. 모델링을 통해 Filament Winding 공정의 주요 공정 변수를 찾아내었고 제시한 모델을 검증하기 위해 직접 Filament Winding 실험 장치를 제작하여 제품을 생산하고 모델과 비교하였다. 제작된 시편으로부터 함침도를 계산하는 방법을 제시하였다. 그 결과 함침도에 관해서 실험 결과가 모델과 그 경향이 뚜렷이 일치함을 확인하였다.

• Bulletin of the Korean Chemical Society
• /
• v.35 no.7
• /
• pp.1979-1984
• /
• 2014

We have developed an efficient method to generate highly active Pd and PdO nanoparticles (NPs) dispersed on graphene and graphene oxide (GO) by an impregnation method combined with thermal treatments in $H_2$ and $O_2$ gas flows, respectively. The Pd NPs supported on graphene (Pd/G) and the PdO NPs supported on GO (PdO/GO) demonstrated excellent carbon-carbon cross-coupling reactions under a solvent-free, environmentally-friendly condition. The morphological and chemical structures of PdO/GO and Pd/G were fully characterized using X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and transmission electron microscopy (TEM). We found that the remarkable reactivity of the Pd/G and PdO/GO catalysts toward the cross-coupling reaction is attributed to the high degree of dispersion of the Pd and PdO NPs while the oxidative states of Pd and the oxygen functionalities of graphene oxide are not critical for their catalytic performance.

• Journal of the Korean Ceramic Society
• /
• v.35 no.7
• /
• pp.740-748
• /
• 1998

The inertia friction properties of C/C composites manufactured by the processes of pressure and at-mospheric carbonizaton with a commerciallized and two kinds of modified coal-tar pitch as a matrix pre-cursor were investigated. The modifications of a pitch such as the introduction of mesophase and the ad-dition of sulphur into a raw pitch were not effective for a impregnation efficiency conducted in a vacuum and at the same time in a pressure of 5kg/cm2 due to the increase of the pitch viscosity. There was not a difference in the densification increment between the pitch modifications however it was revealed that a pressure carbonization was more advantageous than an atmospheric in the densification and the formation of anisotropic carbon matrix. The friction and wear propertis of C/C having higher degree of matrix cry-stallization higher density and hardness of friction surface showed superiority. As the braking energy was increased the friction coefficients were decreased and reached almost same level at the high kinetic energy of 99.6kJ. The wear trends at 99.6kJ were different from the behaviors of friction ceofficient under the same energy in which an oxidation wear is being considered along with a mechnical wear although the wear rates were almost similar to the friction coefficient at the low energy.

• Carbon letters
• /
• v.9 no.4
• /
• pp.316-323
• /
• 2008

The factors that influence ablation resistance in fiber composites are properties of the reinforced fiber and matrix, plugging quantity of fiber, geometrical arrangement, crack, pore size, and their distributions. To examine ablation resistance according to distribution of crack and pore size that exist in carbon/carbon composites, this study produced various sizes of unit cells of preforms. They were densified using high pressure impregnation and carbonization process. Reinforced fiber is PAN based carbon fiber and composites were heat-treated up to $2800^{\circ}C$. The finally acquired density of carbon/carbon composites reached more than $1.932\;g/cm^3$. The ablation test was performed by a solid propellant rocket engine. The erosion rate of samples is below 0.0286 mm/s. In conclusion, in terms of ablation properties, the higher degree of graphitization is, the more fibers that are arranged vertically to the direction of combustion flame are, and the less interface between reinforced fiber bundle and matrix is, the better ablation resistance is shown.

• Carbon letters
• /
• v.11 no.3
• /
• pp.192-200
• /
• 2010

Common reed (Fragmites australis), a local invasive grass, was investigated as a possible feedstock for the production of activated carbon. Dried crushed stems were subjected to impregnation with phosphoric acid (30, 40 and 50%) followed by pyrolysis at $400{\sim}500^{\circ}C$ with final washing and drying. Obtained carbons were characterized by determining: carbon yield, ash content, slurry pH, textural properties and capacity to remove color bodies from factory-grade sugar liquor. Produced carbons possessed surface area up to 700 $m^2/g$, total pore volumes up to 0.37 $cm^3/g$, and proved to be microporous in nature. Decolorization of hot sugar liquor at $80^{\circ}C$ showed degrees of color removal of 60 up to 77% from initial color of 1100~1300 ICU, at a carbon dose of 1.0 g/100 ml liquor. No correlation seems to hold between synthesis conditions and % R but depends on the degree of microporosity. A commercial activated carbon N showed a comparative better color removal capacity of 91%. Common reed proved to be a viable carbon precursor for production of good adsorbing carbon suitable for decolorization in the sugar industry, as well as in other environmental remediation processes.

• Composites Research
• /
• v.28 no.4
• /
• pp.197-203
• /
• 2015

Tensile properties of polypropylene based self-reinforced composites were investigated as a function of process variables of the double-belt lamination equipment such as pressure, temperature and cooling conditions. Elastic modulus was enhanced approximately 6 times from 0.2 to 1.2 GPa. The improvement mechanism was studied by identification of crystalline structure changes using DSC and XRD analysis. In addition, morphology change of self-reinforced composites was also investigated by SEM analysis in order to reveal the degree of impregnation.

• Korean Chemical Engineering Research
• /
• v.53 no.3
• /
• pp.372-381
• /
• 2015

The effect of preparation method on the catalytic activities of the $Ni/Al_2O_3$ catalysts on steam reforming of ethylene glycol was investigated. The catalysts were prepared with various preparation methods such as an incipient wetness impregnation, wet impregnation, and coprecipitation method. In the case of coprecipitation method, various precipitants such as KOH, $K_2CO_3$, and $NH_4OH$ were compared. The prepared catalysts were characterized by using $N_2$ physisorption, inductively coupled plasma-atomic emission spectroscopy, X-ray diffraction, temperatureprogrammed reduction, pulsed $H_2$ chemisorption, temperature-programmed oxidation, scanning electron microscopy, and thermogravimetric analysis. Among the catalysts reduced at 773 K, the $Ni/Al_2O_3$ catalyst prepared by a coprecipitation with KOH or $K_2CO_3$ as precipitants showed the best catalytic performance. The preparation method affected the particle size of Ni, reducibility of nickel oxides, catalytic performance (activity and stability), and types of coke formed during the reaction. The $Ni/Al_2O_3$ catalyst prepared by a coprecipitation with KOH showed the increasing catalytic activity with an increase in the reduction temperature from 773 to 1173 K because of an increase in the reduction degree of Ni oxide species even though the particle size of Ni increased with increasing reduction temperature.

• Journal of the Korean Wood Science and Technology
• /
• v.3 no.1
• /
• pp.3-15
• /
• 1975

How to stabilize wood against shrinking and swelling in variable atmospheric moisture conditions is important to the wood-using industry and a challenge to research. Polyethylene glycol stabilize wood by bulking the fiber. PEG also serve as a chemical seasoning agent, suppress decay in high concentrations, and have slight effect on physical properties, gluing or finishing. The study designed to determine the effect of PEG-400 on the dimensional stabilization of local hardwoods for wood carvings that could supply a greatly expanding tourist trade and making curved furniture parts, lamp stands and other decorative objects, and possible gunstock. The species examined were 6 species, Seo-Namoo (Carpinus laxiflora), Cheungcheung-Namoo (Cornus controversa), Gorosae-Namoo (Acer mono), Karae-Namoo (Juglans mandshurica), Jolcham-Namoo (Quercusserrata) and Sanbud-Namoo (Prunus sargentii), used as block of 5cm thick radially to the grain, 7cm wide tangentially, and 70cm long parallel to the wood grain. All these test piecies were conditioned above the fiber saturation point before impregnation. The stabilization effects were determined for PEG-400 treated woods in a 50 percent solution for 20 days. The following conclusions were obtained. PEG retentions increased with treating time. It was more effective to treat at 60$^{\circ}C$ than at room temperature. In degree of PEG-400 impregnation on species, Cheungcheung-Namoo havinglow specific gravity had the highest retentions, 68.77% but the lowest, 56.33% was shown in Jolcham-Namoo with high specific gravity. Specific gravity of treated wood increased considerably with effectiveness of polymer loading. The increases in specific gravity were 5.36 to 13.16 percent. The highest was Jolcham-Namoo, the lowest Karae-Namoo. On the dimensional stability, a 40 percent of effectiveness of polymer loading was just as effective as 60 percent in reduction in water absorptivity (RWA), antishrinkage efficiency (ASE) and antiswelling efficiency (AE), and from over 60 percent they increased more rapidly. Also species response varied considerably. ASE was 30.12 to 69.97 percent tangentially and 27.86 to 56.37 percent radially, AE 34.06 to 73.76 percent tangentially and 30.11 to 70.12 percent radially, and RWA 42.31 to 65.32 percent. No differences in volume swelling among the 6 species were observed. Its values were ranged from 14.98 to 19.55 percent and also increased with PEG retentions. On the mechanical properties, the strengths very much decreased with PEG-400 loadings as shown in Figure 12; that were 11.41 to 22.90 percent in compression, 21.61 to 34.35 percent in bending and 22.83 to 36.83 percent in tensile strength. PEG retention in cell wall was less than 1 percent and the most of PEG were immersed in cell lumen. Except for Korae-Namoo, effectivenesses of polymer loading were as much high as 61.58 to 75.02 percent. This is believed to be due to the effect of PEG-400 on excellant dimensional stability of treated woods.