• Resources Recycling
• /
• v.23 no.1
• /
• pp.48-57
• /
• 2014

In this study, we have investigated the influence of the nature of solvent on the grafting reaction of maleic anhydride onto polyethylene wax obtained as a by-product in a high density polyethylene plant. The results show that the grafting ratio in xylene as a solvent was higher than toluene. This is because xylene has excellent monomer solubility, swelling property and miscibility. It has been also observed that grafting degree shows an initial jump in percentage of grafting with increasing amount of solvent, from 0% v/w to 200% v/w giving maximum grafting in 200% v/w and then slightly decreases on further increase in the amount of solvent and becomes almost constant. It can be also seen that gel content was not formed under the use of solvent. It means that solvent prevented cross-linking reaction due to chain transfer reactions to solvent molecules. Studies of melt viscosity at $140^{\circ}C$ showed that viscosity increased after grafting of maleic anhydride onto polyethylene wax.

• Journal of the Korean Applied Science and Technology
• /
• v.36 no.4
• /
• pp.1443-1459
• /
• 2019

Polyglycerol fatty acid ester nonionic surfactants have been used for a long time in foods and have been suggested as an alternative to the safety problems of PEG based nonionic surfactants. The polyglycerol fatty acid ester surfactants are synthesized by combining a hydrophilic polyglycerin and a lipophilic fatty acid. The hydrophilic polyglycerin is polymerized using glycerin, glycidol, epichlorohydrin, etc. The main issues of the polyglycerol polymerization reaction are to increase the content of the polyglycerol in the form of linear rather than branched or cyclic forms and to narrow the distribution of the degree of polymerization. The method of binding a lipophilic fatty acid group to a hydrophilic polyglycerin includes chemical synthesis such as esterification reaction and enzyme synthesis using lipase enzyme. The main issues of polyglycerin fatty acid ester synthesis are to increase the yield and to control the degree of esterification while reducing side reactions.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.458-458
• /
• 2010

The process window for the etch selectivity of silicon nitride ($Si_3N_4$) layers to extreme ultra-violet (EUV) resist and variation of line edge roughness (LER) of EUV resist were investigated durin getching of $Si_3N_4$/EUV resist structure in a dual-frequency superimposed capacitive coupled plasma (DFS-CCP) etcher by varying the process parameters, such as the $CH_2F_2$ and $N_2$ gas flow rate in $CH_2F_2/N_2$/Ar plasma. The $CH_2F_2$ and $N_2$ flow rate was found to play a critical role in determining the process window for infinite etch selectivity of $Si_3N_4$/EUV resist, due to disproportionate changes in the degree of polymerization on $Si_3N_4$ and EUV resist surfaces. The preferential chemical reaction between hydrogen and carbon in the hydrofluorocarbon ($CH_xF_y$) polymer layer and the nitrogen and oxygen on the $Si_3N_4$, presumably leading to the formation of HCN, CO, and $CO_2$ etch by-products, results in a smaller steady-state hydrofluorocarbon thickness on $Si_3N_4$ and, in turn, in continuous $Si_3N_4$ etching due to enhanced $SiF_4$ formation, while the $CH_xF_y$ layer is deposited on the EUV resist surface. Also critical dimension (and line edge roughness) tend to decrease with increasing $N_2$ flow rate due to decreased degree of polymerization.

• Polymer(Korea)
• /
• v.34 no.2
• /
• pp.159-165
• /
• 2010

Dipyridine-terminated polystyrenes and polybutadienes were synthesized by the chain endfunctionalization reaction of polystyryllithium (PSLi) and polybutadienyllithium (PBDLi) with di(2-pyridyl) ketone(DPK) using a living anionic polymerization method in the Ar-glove box. Living polymeric lithiums with low molecular weights (Mw=1000~2000 g/mol) were used to investigate the chain end-functionalization yield with DPK and the degree of coupling reaction by the attack of organolithium to the pyridine ring in the presence of TMEDA using GPC, $^1H$-NMR, $^{13}C$ analysis. DPK-terminated PBD exhibited much higher functionalization yield and less amount of coupling reaction compared with DPK-terminated PS. 86% functionalization yield with 9% degree of coupling was obtained when the PBDLi was added dropwise to DPK solution at room temperature. The functionalization yield was increased as the reaction temperature decreased, however, no LiCl effect was observed in this chain end-functionalization reaction with DPK.

• The Journal of Korean Academy of Prosthodontics
• /
• v.44 no.3
• /
• pp.333-342
• /
• 2006

Statement of problem. Although many studies have been carried out to investigate the correlation between the degree of conversion and the flexural strength of composite resins, there is minimal information in the literature attempting to compare degree of conversion, flexural strength and their correlation between restorative composite resins and flowable composite resins. Purpose. The purposes of this study were to measure the degree of conversion and flexural strength of composite resins with different rheological behavior and to correlate the two properties. Materials and methods. Four restorative (Vit-1-escence, Z-250, Tetric ceram, Esthet-X) and four flowable (Aeliteflo, Admiraflow, Permaflo, Revolution) light-curing composite resins were investigated. The degree of conversion(DC) was analyzed with Fourier transfer infra-red spectroscopy(FTIR) spectrum by a potassium bromide(KBr) pellet transmission method. The spectrum of the unpolymerized specimen had been measured before the specimen was irradiated for 60s with a visible light curing unit. The Poiymerized specimen was scanned for its in spectrum. The flexural strength(FS) was measured with 3-point bending test according to ISO 4049 after storage in water at $37^{\circ}C$ for 24 hours. The data were statistically analyzed by an independent sample t-test and one-way ANOVA at the significance level of 0.05. The dependence of flexural strength on the degree of conversion was also analyzed by regression analysis. Results. Mean DC and FS values ranged from 43% to 61% and from 84.7MPa to 156.7MPa respectively. DC values of the flowable composite resins were significantly higher than those of restorative composite resins (P < 0.05). The FS values of restorative composite resins were greater than those of flowable composite resins. No statistically significant correlation was observed between the DC and the FS tested in any of the composites. The dependence of FS on DC in restorative or flowable composite resins was not significant. Conclusion. It can be concluded that radical polymerization of the organic matrix is not a major factor in determining flexural strength of the commercially available composite resins.

• Elastomers and Composites
• /
• v.38 no.4
• /
• pp.303-315
• /
• 2003

Inorganic/organic composite particles were also synthesized by changing an initiator an it's concentration, concentration of an adsorbed surfactant, reaction temperature, and agitation speed in the presence of $CaCO_3$ adsorbed SDBS. The polymerization conditions were optimized according to the conversion of the core-shell composite particles. In the inorganic/organic core-shell composite particle polymerization, $CaCO_3$ absorbed surfactant SDBS of 0.5 wt % was prepared first and then core $CaCO_3$ was encapsulated by sequential emulsion polymerization using MMA, concentration of APS $3.16{\times}10^{-3}mol/L$ to minimize the formation of new PMMA particle during MMA shell polymerization. The structure characterization of the inorganic/organic core-shell particles was verified by measuring the decomposition degree of $CaCO_3$ using HCl solution. It was found that $CaCO_3$ was encapsulated by shell PMMA due to having excellent dispersion in the epoxy resin, smooth surface distinctly from spindle shape, and broad particle distribution after the capsulation.

• Carbon letters
• /
• v.11 no.3
• /
• pp.176-183
• /
• 2010

PAN precursor fibers were produced via wet-spinning process, and effects of polymerization and spinning processes, especially the stretching process, were investigated on mechanical properties and micro-morphologies of precursor fibers. An increase in molecular weight, dope solid and densification and a decrease in surface defects were possible by controlling polymerization temperature, the number of heating rollers for densification and the jet stretch ratio, which improved the mechanical properties of precursor fibers. The curves for strength, modulus, tensile power and diameter as a function of stretch ratio can be divided into three stages: steady change area, little change area and sudden change area. With the increase of stretch ratio, the fiber diameter became smaller, the degree of crystallization increased and the structure of precursor fibers became compact and homogeneous, which resulted in the increase of strength, modulus and tensile power of precursor fibers. Empirical relationship between fiber strength and stretch ratio was studied by using the sub-cluster statistical theory. It was successfully predicted when the strengths were 0.8 GPa and 1.0 GPa under a certain technical condition, the corresponding stretch ratio of the fiber were 11.16 and 12.83 respectively.

• Journal of Adhesion and Interface
• /
• v.11 no.3
• /
• pp.89-99
• /
• 2010

In this paper, for polymerization of poly(vinyl acetate-co-ethylene) (VAE) by redox system using poly(vinyl alcohol) (PVOH) as emulsifier on the properties of the final emulsion, and pH changes affect the physical properties of the final emulsion was investigated. The results of the molecular weight of PVOH had a dramatic impact on the emulsion properties. The used a low molecular weight of PVOH products was obtained low viscosity and using the high molecular weight of PVOH were obtained high viscosity product. However, changing the pH of the final polymerized product properties for the PVOH obtained different results. Generally, a poly(vinyl acetate) emulsion by a high degree of polymerization and high molecular weight of PVOH was obtained high viscosity of the final emulsion. But, in VAE was lower emulsion viscosity in high pH. This is the molecular weight of the emulsion during the synthesis of PVOH is considered to be affected by degradation. The final viscosity was decreased by grafting ratio and molecular weight were decreased with increasing of pH.

• Fibers and Polymers
• /
• v.2 no.2
• /
• pp.108-115
• /
• 2001

Vinyl acetate was polymerized in ultraviolet-ray initiated bulk system at low temperatures using 2,2-azobis(2,4-dimethylvaleronitrile) (ADMVN) or 2,2-azobis(isobutyronitrile) (AIBN) as the photoinitiator, respectively. High molecular weight (HMW) poly(vinyl alcohol) (PVA) having number-average degree of polymerization ($P_n$) of 3,900-7,800 and syndiotactic diad (S-diad) content of 52.5-54.0% could be prepared by complete saponification of synthesized linear poly(vinyl acetate) (PVAc) having $P_n$ 5,900-9,400 obtained at conversion of below 30%. $P_n$ of PVA using ADMVN was larger than that of PVA using AIBN. On the other hand, conversion of the former was smaller than that of the latter, and it was found that the initiation rate of the ADMVN was lower than that of AIBN. This could be explained by a fact that the rate of photolysis of AIBN is faster than that of ADMVN due to the higher quantum yield or dissociation rate constant of AIBN than that of ADMVN. The $P_n$, syndiotacticity, and whiteness of PVA from PVAc polymerized at lower temperatures were superior to those of PVA from PVAc polymerized at higher temperatures.

• Journal of Environmental Science International
• /
• v.17 no.11
• /
• pp.1255-1263
• /
• 2008

The efficiency of PP-g-AA and PP-g-St nonwoven fabric synthesized by photoinduced polymerization as an adsorbent for removal $NH_3-N$ from waste water was evaluated. The results evidently indicate that the adsorption capacities of $NH_3-N$ onto PP-g-AA nonwoven fabric were extremely superior to those onto sulfonated PP-g-St nonwoven fabric, PK and zeolite. PP-g-AA nonwoven fabric showed the maximum adsorption capacity of $NH_3-N$ at the degree of grafting of 80 wt.%. The adsorption behaviour of $NH_3-N$ onto PP-g-AA and sulfonated PP-g-St nonwoven fabric was controlled by an ion exchange reaction, and tended to be similar to both trends of Langmiur and Freundlish isotherm. Futhermore, PP-g-AA non-woven fabric could be regenerated more than 5 times by a simple washing with 0.1N HCl with no decrease of adsorption capacity and no degradation of physical properties. Also sulfonated PP-g-St nonwoven fabric could be regenerated by washing with 0.1N ${H_2}{O_4}$. However, their regeneration efficiency was significantly low because grafting layer acted as functional radical for adsorption was continuously desquamated in the adsorption or regeneration processes, which resulted in decrease of adsorption capacity and weight of adsorbent. All results obtained from this study indicate that the $NH_3-N$ removal capacity of PP-g-AA non-woven fabric was extremely superior to those of PP-g-St non-woven fabric, PK and zeolite.