• Journal of the Korean Wood Science and Technology
• /
• v.36 no.5
• /
• pp.1-10
• /
• 2008

Decay and mold resistance of zinc borate (ZB) and calcium borate (CB) modified oriented strandboard (OSB) from southern mixed hardwood and southern yellow pine was investigated in this study. Brown rot fungus Gloeophyllum trabeum and white-rot fungus Trametes versicolar were used to examine the decay resistance of the OSB. The OSB test specimens were colonized by brown and white rot fungal mycelium in both the brown and white-rot culture bottles after 8 and 12 weeks, respectively. The wood species and fungus type had the significant effects on the decay resistance. Brown rot decay was evident for all untreated southern pine and mixed hardwood controls. The white-rot decay, however, did not show significant weight loss at both species control samples. The incorporation of ZB and CB composites provides suitable protection against brown-and white-rot fungi. No significant weight loss was observed from the borate treated OSB.

• Journal of the Korean Wood Science and Technology
• /
• v.44 no.6
• /
• pp.880-889
• /
• 2016

To evaluate the resistance of wood to decay caused by fungi, sapwood and heartwood of red pine (Pinus densiflora) and sapwood and heartwood of larch (Larix kaempferi) were conducted. Wood samples were immersed for 96 h in pyroligneous liquor. Then, the brown-rot fungus, Fomitopsis palustris, was used to examine the decay resistance of red pine and larch. Weight and density of wood from the all conditions increased after immersion treatment. Weight loss after decay resistance test was also dropped with a immersion treatment. The lowest weight loss indicated at immersion-treated heartwood of larch. Immersion treatment using pyroligneous liquor effectively increased the resistance of wood to decay caused by fungi.

• Journal of the Korean Wood Science and Technology
• /
• v.45 no.2
• /
• pp.195-201
• /
• 2017

This study was conducted to evaluate the resistance of heat-treated wood using the catalyst to decay caused by fungi for sapwood and heartwood of two tree species, Korean red pine (Pinus densiflora) and Japanese larch (Larix kaempferi), respectively. Wood samples were immersed for 10 min in sulfuric acid (7.5%) and then heat-treated at $130^{\circ}C$ for 90 min. Fomitopsis palustris, a brown-rot fungus, was used to examine the decay resistance of Korean red pine and Japanese larch wood. Weight and density of wood from the all conditions increased after heat treatment using the catalyst. Weight loss after decay resistance test was also dropped with a heat treatment. The lowest weight loss indicated at heat-treated heartwood of Japanese larch. Heat treatment using the catalyst effectively increased the resistance of wood to decay caused by fungi.

• Progress in Superconductivity
• /
• v.14 no.1
• /
• pp.1-10
• /
• 2012

We fabricated a closed coils by using resistive-joint method and the joint resistance of the coils were estimated by field decay technique in liquid nitrogen. We used the Runge-kutta method for the numerical analysis to calculate the decay properties. The closed coil was wound by $(Bi,Pb)_2Sr_2Ca_2Cu_3O_x$/Ag tape. Both ends the tape were overlapped and soldered to each other. The current was induced in a closed coils by external magnetic flux density. Its decay characteristic was observed by means of measuring the magnetic flux density generated by induced current at the center of the closed coil with hall sensor. The joint resistance was calculated as the ratio of the inductance of the loop to the time constants. The joint resistances were evaluated as a function of critical current of loop, contact length, sweep time, and external magnetic flux density in a contact length of 7 cm. It was observed that joint resistance was dependent on contact length of a closed coil, but independent of critical current, sweep time, and external magnetic flux density. The joint resistance was measured to be higher for a standard four-probe method, compared with that for the field decay technique. This implies that noise of measurement in a standard four-probe method is larger than that of field decay technique. It was estimated that joint resistance was $8.0{\times}10^{-9}{\Omega}$ to $11.4{\times}10^{-9}{\Omega}$ for coils of contact length for 7 cm. It was found that 40Pb/60Sn solder are unsuitable for persistent mode.

• Journal of the Korean Wood Science and Technology
• /
• v.49 no.6
• /
• pp.602-615
• /
• 2021

Red jabon wood is a potential fast-growing species for veneer, furniture, and many other wood products, but its durability is very low. The purpose of this study was to investigate the effects of castor bean oil and heating on boron leaching, dimensional stability, and resistance to decay fungi in treated jabon wood. Red jabon wood was preserved with boron solutions containing 5% boron (boric acid, borax, or borax-boric acid). Following that, castor bean oil impregnation and heating were used as posttreatments. Furthermore, all the wood samples were tested in terms of leaching, dimensional stability, and resistance against Schizophyllum commune and Fomitopsis palustris fungi. This study discovered that boron compounds, castor bean oil, and heating treatments influenced the leaching, dimensional stability, and resistance of red jabon wood to decay fungi. The double impregnation of boric acid or borax and castor bean oil, followed by heating at 160℃, significantly reduced water absorption and leaching while increasing the dimensional stability and resistance of red jabon wood against the two tested decay fungi.

• Proceedings of the Korea Institute of Applied Superconductivity and Cryogenics Conference
• /
• 2002.02a
• /
• pp.294-296
• /
• 2002

Considering the application of high temperature superconductor to MRI, the loss at conductor joint would be very important. Therefore, we have carried out a measurement of joint resistance of Bi-2223/Ag tapes at 77 K. A pancake coil was wound by Bi-2223/Ag tape. Both ends the tape were overlapped and soldered to each other. The DC current is induced in the pancake coil by energizing the excitation coil wound by copper wire closely located to the pancake coil. The decay behaviour of the current in coils was clearly separated in two regimes, and initial fast decay of the order of minutes followed by a slow logarithmic-like decay, From this data, the resistance of the joint was evaluated as 2.74 n$\Omega$.

• Journal of the Korea Furniture Society
• /
• v.25 no.3
• /
• pp.233-237
• /
• 2014

The eco-friendly preservatives such as ACQ or CUAZ have been used in landscape architectural facilities these days. In this study, the decay efficacies of ACQ treatments were evaluated according to domestic veneer species, concentration of ACQ, weathering test, adhesive type, and fungus type. In case of veneer species, hinoki cypress and yellow poplar showed the highest and lowest decay resistance, respectively. And the decay resistance appeared to be greater in plywoods bonded by resorcinol resin-bonded plywood and non-weathering treated plywood than polyurethane resin-bonded plywood and weathering treated plywood.

• Journal of the Korean Wood Science and Technology
• /
• v.32 no.6
• /
• pp.7-13
• /
• 2004

In this study, the Korean pine wood (Pinus densiflora Sieb. et Zucc) and Italian poplar wood (Populus euramericana Guinier) was treated with a mixture of monoammonium phosphate (MAP) and boric acid. Their usability as fire retardant and as decay-resistant construction and interior materials were evaluated by testing of chemicals, corrosion rate and absorption rate, weight loss and chemical contents. An experiment was performed to compare treated pine wood and Italian poplar wood. According to the results, Italian poplar wood had higher specific gravity and retention of chemicals than pine wood, and treated wood showed higher decay-resistance than untreated one. Weight loss was less in treated wood than untreated one because the degree of decay was lower in the former than the latter. Corrosion rate and absorption rate met the KS standard for wood preservative performance. The chemical contents analysis was carried out to determine the degree of decay and it was found that the preservative effect of chemical treatment was lower in Italian poplar wood than in pine wood.

• Journal of the Korean Wood Science and Technology
• /
• v.25 no.4
• /
• pp.92-98
• /
• 1997

To make good use of chitosan forming complex with heavy metals in wood preservative treatment, woods impregnated with chitosan and copper sulfate were prepared. Amounts of leached copper, decay resistance, anti-mold efficacy, iron corrosion rates, moisture regain rates and degradation pattern in chitosan pre-treated and untreated wood were compared. After leaching test, amounts of leached copper from chitosan pre-treated wood had a much smaller than chitosan untreated wood, and good decay resistance was retained even after leaching test. From these results, it was proved that chitosan-copper complex formed in wood played and important role for decay durability. In chitosan pre-treated wood, damage values by test molds became remarkably smaller, but the growth of test molds was not perfectly inhibited. Distinct differences in iron corrosion rates between chitosan pre-treated and untreated woods was not recognized but chitosan pre-treated wood showed the lower moisture regain rates than chitosan untreated wood because of water insoluble chitosan membrane formed in wood. After leaching test, the tracheid walls in the wood treated with 2.0% copper sulfate only were eroded by the fungal attacks, but those in the wood pre-treated with chitosan remained almost intact.

• Journal of the Korean Wood Science and Technology
• /
• v.46 no.5
• /
• pp.497-510
• /
• 2018

In this study, the decay resistance of larch wood, which was heat treated by superheated steam, was evaluated by the field decay test. During the field decay test of 12 months, non-treated wood has been severely damaged by termite, however, no visible damage has occurred in the preservative-treated wood and superheated steam heat-treated wood. Results of field decay test showed approximately 5% mass loss of the non-treated wood and the preservative-treated wood, and approximately 1% mass loss of the superheated steam heat-treated wood. After the field decay test for 12 months, the residual amount of preservatives remaining in the preservative-treated wood was lower than that before the field decay test. It was considered that the preservative was partially eluted during the field decay test, and the mass loss of the preservative-treated wood was thought to be similar to that of the non-treated wood. Through this study and additional long-term monitoring test, superheated steam heat treatment can be considered to be an environmental-friendly method to enhance the decay resistance of wood against rot fungi and/or insect without chemical treatment such as preservative injection.