• Journal of the Korean Vacuum Society
• /
• v.22 no.5
• /
• pp.250-256
• /
• 2013

It is described that the proton beam induces micro-size defects and electronic deep levels in luminescence Thin Film. Coincidence Doppler Broadening Positron Annihilation Spectroscopy (CDBPAS) and Positron lifetime Spectroscopy were applied to study of characteristics of a poly crystal samples. In this investigation the numerical analysis of the Doppler spectra was employed to the determination of the shape parameter, S-parameter value. The samples were exposed by 3.0 MeV proton beams with the intensities ranging between 0 to ${\sim}10^{14}$ particles. The S-parameter values decreased as increased the proton beam, that indicates the protons trapped in vacancies. Lifetime ${\tau}_1$ shows that positrons are trapped in mono vacancies. Lifetime ${\tau}_2$ is not changed according to proton irradiation that indicate the cluster vacancies of the grain structure.

• Korean Journal of Materials Research
• /
• v.9 no.1
• /
• pp.46-50
• /
• 1999

$\textrm{Zn}_{2-x}\textrm{Mn}_{x}\textrm{SiO}_{4}$ green phosphors have been prepared by the solution reaction method and the photoluminescence and crystalline properties were studied as a function of both the firing temperature ($900^{\circ}C$~$1200^{\circ}C$) and the concentration of Mn activator (x=0.01~0.20). Under 147 nm and 254nm and excitation sources, the emission intensity of the phosphors was increased about 4 times increasing firing temperatures from $900^{\circ}C$ to $1200^{\circ}C$. From the XRD analysis, $\textrm{Zn}_{2}\textrm{SiO}_{4}$:Mn phosphors fired above $1100^{\circ}C$ showed willemite crystal structure. Under 147nm excitation, the maximum emission intensity was obtained at the Mn concentration of x=0.02 for $\textrm{Zn}_{2-x}\textrm{Mn}_{x}\textrm{SiO}_{4}$ phosphors fired at $1200^{\circ}C$ and the concentration quenching was occurred at the Mn concentration above x=0.10. The phosphor particles showed almost spherical shapes with the average size of around 2~3$\mu\textrm{m}$ by the SEM morphology.

• Korean Journal of Materials Research
• /
• v.10 no.5
• /
• pp.375-381
• /
• 2000

Aluminium foil for electrolytic capacitors was anodized at the voltage of 100V and 140V for 10 minutes in ammonium adipate solution to form aluminum oxide layer on aluminum substrate as an dielectric film. The thickness, the stoichiometry and the crystal structure of the layer were investigated by using RBS and TEM . In addition EIS technique was employed to study the effects of addition of sulfuric acid on the increment of the foil surface area. It was found that the thickness values of the layers anodized at 100V and 140V were about 130 nm and 190 nm respectively and the stoichiometry of the elements of aluminum and oxygen was 2:3. The anodic oxide layer was shown to be amorphous. but the structure irradiated with electron beam resulted in the transformation into crystalline structure of $${\gamma}$-Al_2$$O_3$ . From a comparison of the impedance results and the capacitance variation to investigate the ef- fects of sulfuric acid addition to the etching bath of hydrochloric acid, the EIS techinque could be useful to analyze the capacitance variation.

• Korean Journal of Materials Research
• /
• v.4 no.1
• /
• pp.81-89
• /
• 1994

Ti film of lOnm thickness and Co film of 18nm thickness were sequentially e-heam evaporated onto Si (100) substrates. Metal deposited samples were rapidly thermal-annt.aled(KTA) in thr N1 en vironment a t $900^{\circ}C$ for 20 sec. to induce the reversal of metal bilayer, so that $CoSi_{2}$ thin films could be formed. The sheet resistance measured by the 4-point probe was 3.9 $\Omega /\square$This valur was maintained with increase in annealing time upto 150 seconds, showing high thermal stab~lity. Thc XRII spectra idrn tified the silicide film formed on the Si substrate as a $CoSi_{2}$ epitaxial layer. The SKM microgr;iphs showed smooth surface, and the cross-sectional TKM pictures revealed that the layer formed on the Si substrate were composed of two Co-Ti-Si alloy layers and 70nm thick $CoSi_{2}$ epl-layer. The AES analysis indicated that the native oxide on Si subs~rate was removed by TI ar the beginning of the RTA, and Ihcn that Co diffused to clean surface of Si substrate so that epitaxial $CoSi_{2}$ film could bt, formed. In thc rasp of KTA at $700^{\circ}C$. 20sec. followed by $900^{\circ}C$, 20sec., the thin film showed lower sheet resistance, but rough surface and interface owing to $CoSi_{2}$ crystal growth. The application scheme of this $CoSi_{2}$ epilayer to VLSI devices and the thermodynarnic/kinetic mechan~sms of the $CoSi_{2}$ epi-layer formation through the reversal of Co/Ti bdayer were discussed.

• Polymer(Korea)
• /
• v.24 no.4
• /
• pp.488-498
• /
• 2000

Molecular bottle-brush was prepared by hydrogen-bonding between poly(4-vinylpyridine)(P4VP) as main chain and 3-pentadecylphenol (PDP) as amphiphilic side chain. Variation of long period ( $L_{p}$), order-disorder transition temperature ( $T_{ODT}$) and mesomorphic structure of bottle-brush were investigated by changing various mole ratio (x) of pyridine group in P4VP and PDP and molecular weight of P4VP. Upper critical solution temperature (UCST) behaviour was observed. For x 0.8-0.9, maximum critical temperature was found. As molecular weight of P4VP was increased, phase transition occurred at higher temperature. It was found that phase behaviour of the bottle-brush was affected by mobility of P4VP as well as size and regularity of lamellar structure. The $L_{p}$ determined from analysis of crystal structure was in the range of 35 $\AA$ and 40 $\AA$ and was more affected by the molecular weight of P4VP than by mole ratio (x). However, if the molecular weight of P4VP was high, LP value was little affected.ted.d.

• Journal of Korean Society of Environmental Engineers
• /
• v.30 no.5
• /
• pp.560-566
• /
• 2008

In this paper, the solidification behaviour and compressive strength of fly ash, cement, and waste stone powder were studied each separately and with addition of each in different proportions. And also, we assessed stabilizing ability of waste stone powder in cement which was added in fly ash. The particle size of waste stone powder was found smaller than the fly ash and cement particle sizes. Moreover, when mixing all(fly ash, cement, and waste stone powder) showed distinctive crystal structure, and improved stiffness. In case of mixing fly ash, cement and waste stone powder in different proportions, the compressive strength was exceeded to the predicted compressive strength of 10 kgf/cm$^2$. The XRD analysis showed high contents of CaO in fly ash and SiO$_2$ in case of waste stone powder sample. Heavy metal emission experiment showed the 3mg/L of Pb after 14 days of mixing 150 kg/m$^3$ of cement with the 80$\sim$100 kg/m$^3$ of waste stone powder, which is fulfilling the National Waste Management Policy.

• The Journal of the Korea Contents Association
• /
• v.7 no.5
• /
• pp.102-109
• /
• 2007

This is an analysis study about the pictorial frame of Georges Schwizgebel's animation "The Subject of Picture", focusing on Deleuze's frame theory. First of all, the shapes in the frame of the animation is the representation of the tactile sensation from the erased vestiges of the characters. It shows the metamorphosis of the erased vestiges of the shapes by Deleuze's sensibility theory. Besides, the layout of the animation's background has similar property with the aplat which was mentioned by Deleuze. It means that the background of the animation correspond to the aplat which is other boundary different from reality, and the character which has the minimum embodiment about the object makes the shape newly through the distortion of the shape. Secondly, as the problem of frames in terms of the continuity of time, the meaning in Schwizgebel's animation is created by the relation between each frame. It means that the depiction of the shape itself by the composition between each frame is composed of the frame. Eventually, Schwizgebel's work is the animation which has the characteristic of the modem cinema and is the crystal depiction that deviates from rules and logics of the object which was mentioned by Deleuze.

• Journal of Korean Ophthalmic Optics Society
• /
• v.13 no.1
• /
• pp.71-76
• /
• 2008

Purpose: A simple and efficient method to prepare nanocrystalline ZnO thin film with pure strong UV emission on soda-lime-silica glass substrates by low-temperature annealing was improved. Methods: Crystal structural, surface morphological, and optical characteristics of nanocrystalline ZnO thin films deposited on soda-lime-silica glass substrates by prefiring final annealing process at 300$^{\circ}C$ were investigated by using X-ray diffraction analysis, field emission-scanning electron microscope, scanning probe microscope, ultraviolet-visible-near infrared spectrophotometer, and photoluminescence. Results: Highly c-axis-oriented ZnO films were obtained by prefiring at 300$^{\circ}C$. A high transmittance in the visible spectra range and clear absorption edge in the ultra violet range of the film was observed. The PL spectrum of ZnO thin film with a deep near band edge emission was observed while the defect-related broad green emission was nearly quenched. Conclusions: Our work will be possibly adopted to cheaply and easily fabricate ZnO-based optoelectronic devices at low temperature, below 300$^{\circ}C$, in the future.

• Journal of Korean Society for Atmospheric Environment
• /
• v.29 no.1
• /
• pp.97-104
• /
• 2013

Methyl alcohol is one of the basic intermediates in the chemical industry and is also being used as a fuel additive and as a clean burning fuel. In this study, conversion of carbon dioxide to methyl alcohol was investigated using catalytic chemical methods. Ceramic monoliths (M) with $400cell/in^2$ were used as catalyst supports. Monolith-supported CuO-ZnO catalysts were prepared by wash-coat method. The prepared catalysts were characterized by using ICP analysis, TEM images and XRD patterns. The catalytic activity for carbon dioxide hydrogenation to methyl alcohol was investigated using a flow-type reactor under various reaction temperature, pressure and contact time. In the preparation of monolith-supported CuO-ZnO catalysts by wash-coat method, proper concentration of precursors solution was 25.7% (w/v). The mixed crystal of CuO and ZnO was well supported on monolith. And it was known that more CuO component may be supported than ZnO component. Conversion of carbon dioxide was increased with increasing reaction temperature, but methyl alcohol selectivity was decreased. Optimum reaction temperature was about $250^{\circ}C$ under 20 atm because of the reverse water gas shift reaction. Maximum yield of methyl alcohol over CuO-ZnO/M catalyst was 5.1 mol% at $250^{\circ}C$ and 20 atm.

• Korean Journal of Materials Research
• /
• v.22 no.1
• /
• pp.54-60
• /
• 2012

The particle size of MgO was examined as a function of the Na content in $Mg(OH)_2$ powders and the calcination temperature. $Mg(OH)_2$ suspension was obtained by dropwise precipitation of $Mg(NO_3)_2{\cdot}6H_2O$ and NaOH solutions. The suspension was diluted by varying the dilution volume ratio of distilled water to $Mg(OH)_2$ suspension to change the Na salt concentration in the suspension. $Mg(OH)_2$ slurry was filtered and dried at $60^{\circ}C$ under vacuum, and then its $Mg(OH)_2$ powder was calcined to produce MgO with different amount of Na content at $500\sim900^{\circ}C$ under air. Investigation of the physical and chemical properties of the various MgO powders with dilution ratio and calcination temperature variation was done by X-ray diffraction, transmission electron microscopy, BET specific surface area and thermal gravimetric analysis. It was observed that MgO particle size could depend on the condition of calcination temperature and dilution ratio of the $Mg(OH)_2$ suspension. The particle size of the MgO depends on the Na content remaining in the $Mg(OH)_2$ powder, which powder was prepared by changing the dilution ratio of the $Mg(OH)_2$ suspension. This change increased as the calcination temperature increased and decreased as the dilution ratio increased. The growth of MgO particle size according to the increase of temperature was more effective when there was a relatively high content of Na. The increase of Na content lowered the temperature at which decomposition of $Mg(OH)_2$ to MgO took place, thereby promoting the crystal growth of MgO.