• 한국음향학회지
• /
• 제16권3호
• /
• pp.51-56
• /
• 1997

본 논문에서는 SLAM(Scanning Laser Acoustic Microscope) 시스템을 이용하여 고체 내부에 발생한 크랙의 깊이를 측정하는 방법을 연구하였다. SLAM 시스템은 초음파의 투과계수에 따른 그림자 영상을 재생시키므로 크랙 깊이에 대한 정확한 측정방법이 요구된다. 이를 위하여 시료에 초음파를 사각으로 입사시켜 얻은 SLAM 영상의 그림자영역과 시료내의 초음파 모드 변환에 대한 기하학적 구조를 이용하여 크랙의 깊이를 측정할 수 있는 방법을 제안하고 실험을 통하여 확인하였다. 실험을 위하여 알루미늄에 서로 다른 깊이로 수직형 라인-크랙의 결함을 갖는 시료를 가공하였고 시료에 초음파를 사각 입사시키기 위하여 20$^{\circ}$ 각도로 웨지를 제작하였다. 실험 결과, 크랙의 깊이가 증가할수록 SLAM 영상의 그림자 영역이 비례적으로 증가함을 보였고, 결함의 깊이에 대한 측정치와 실제치를 비교한 결과 약 6% 이하의 측정오차를 보였다.

• Restorative Dentistry and Endodontics
• /
• 제42권4호
• /
• pp.332-341
• /
• 2017

Objectives: To determine the incidence of crack formation and propagation in apical root dentin after retreatment procedures performed using ProTaper Universal Retreatment (PTR), Mtwo-R, ProTaper Next (PTN), and Twisted File Adaptive (TFA) systems. Materials and Methods: The study consisted of 120 extracted mandibular premolars. One millimeter from the apex of each tooth was ground perpendicular to the long axis of the tooth, and the apical surface was polished. Twenty teeth served as the negative control group. One hundred teeth were prepared, obturated, and then divided into 5 retreatment groups. The retreatment procedures were performed using the following files: PTR, Mtwo-R, PTN, TFA, and hand files. After filling material removal, apical enlargement was done using apical size 0.50 mm ProTaper Universal (PTU), Mtwo, PTN, TFA, and hand files. Digital images of the apical root surfaces were recorded before preparation, after preparation, after obturation, after filling removal, and after apical enlargement using a stereomicroscope. The images were then inspected for the presence of new apical cracks and crack propagation. Data were analyzed with ${\chi}^2$ tests using SPSS 21.0 software. Results: New cracks and crack propagation occurred in all the experimental groups during the retreatment process. Nickel-titanium rotary file systems caused significantly more apical crack formation and propagation than the hand files. The PTU system caused significantly more apical cracks than the other groups after the apical enlargement stage. Conclusions: This study showed that retreatment procedures and apical enlargement after the use of retreatment files can cause crack formation and propagation in apical dentin.

• 비파괴검사학회지
• /
• 제32권4호
• /
• pp.376-387
• /
• 2012

비선형 스프링 모델과 섭동법을 기초로 비선형 균열면에 경사 입사된 초음파에 의해 발생되는 2차 고조파 초음파의 크기를 계산하였다. 비선형 균열계면에서 만들어지는 반사파와 굴절파의 기본주파수 성분과 2차 고조파 성분의 크기를 입사각과 균열계면의 계면강성을 변화키면서 조사하였다. 계면강성에 관계없이 균열계면이 초음파 진행 방향과 비슷한 경우 반사와 굴절파 모두에서 2차 고조파의 발생은 거의 없었지만, 그렇지 않은 경우에는 계면 입사각은 물론 계면 강성에 따라 2차 고조파의 크기는 크게 변화하였다. 투과파는 물론 반사파에서도 2차 고조파 성분이 유의성 있게 발생됨을 수치 해석을 통해 확인하였다.

• 한국응용과학기술학회지
• /
• 제22권3호
• /
• pp.234-240
• /
• 2005

In this study, we have prepared three kinds of enteric tablet coating formulations for prevention the crack incidence and enhanced process improvement of enteric tablet using aqueous system. we determined the mechanical strength of three formulatons on the enteric film-coating process. The compared experiment of one-layer and two-layer (A), (B) coating treated having placebo tablets without breakline and logo. In result, the breaking force time of two-layer (B) film strength was found to increase 0.8min than two-layer (A). We confirmed the half reduction of working hour and the simplification in the one-layer coating process, and the coating troubles was solved as setting up a dehumidifier in inlet of coater. In result, we recovered that optimum running capacity(g/kg) of dehumidifier is 10g/kg and below.

• 비파괴검사학회지
• /
• 제24권4호
• /
• pp.354-361
• /
• 2004

SH파의 균열 산란장 해석을 위하여 먼저 균열개구변위(COD)를 미지수로 하는 경계적분방정식(BIE)을 수립하였다. 폭 2a의 고립된 2차원 균열(slit)에 임의의 각도로 입사하는 시간조화 평면파에 대하여 COD를 주파수 ka의 함수로 구하였으며, 다른 연구 결과와 잘 일치함을 확인하였다. 초음파 비파괴평가에서 중요한 변수로 취급되는 원거리 산란음장을 두 가지 방법으로 구하였다. 펄스-에코 모드에서 Kirchhoff 근사법과 BIE-COD에 기초한 엄밀해의 결과를 입사각도와 주파수의 함수로 계산하고 서로 비교하였다. SH파가 균열면에 수직으로 입사/반사한 경우 산란음장은 최대가 되고, 두 방법은 정확히 일치하였다. 수직입사에서 멀어질수록 산란진폭은 모두 급격히 감소하며, Kirchhoff 근사법은 엄밀해와 차이를 보였다. 시간 영역의 원거리 산란진폭 거동을 구하기 위하여 대역폭을 갖는 중심주파수 10MHz를 곱하고, 퓨리에 역변환으로 시간영역 신호를 계산하였다. 경사 입사시에 시간영역의 진폭은 좌우 균열 선단에 의해 분리되며, 두 신호 사이의 시간 간격은 균열의 크기와 관련된다 엄밀해와 비교할 때 Kirchhoff 근사법은 정확한 시간 간격을 제공하나, 동일한 크기의 균열 선단 신호를 제공하는 부정확함이 있다.

• Restorative Dentistry and Endodontics
• /
• 제40권4호
• /
• pp.286-289
• /
• 2015

Objectives: The aim was to evaluate dentinal crack formation after root canal preparation with ProTaper Next system (PTN) with and without a glide path. Materials and Methods: Forty-five mesial roots of mandibular first molars were selected. Fifteen teeth were left unprepared and served as controls. The experimental groups consist of mesiobuccal and mesiolingual root canals of remaining 30 teeth, which were divided into 2 groups (n = 15): Group PG/PTN, glide path was created with ProGlider (PG) and then canals were shaped with PTN system; Group PTN, glide path was not prepared and canals were shaped with PTN system only. All roots were sectioned perpendicular to the long axis at 1, 2, 3, 4, 6, and 8 mm from the apex, and the sections were observed under a stereomicroscope. The presence/absence of cracks was recorded. Data were analyzed with chi-square tests with Yates correction. Results: There were no significant differences in crack formation between the PTN with and without glide path preparation. The incidence of cracks observed in PG/PTN and PTN groups was 17.8% and 28.9%, respectively. Conclusions: The creation of a glide path with ProGlider before ProTaper Next rotary system did not influence dentinal crack formation in root canals.

• 한국전자파학회논문지
• /
• 제25권9호
• /
• pp.938-943
• /
• 2014

대규모 PEC 물체의 표면에 존재하는 Gap/Crack 구조에 의한 산란파는 RCS가 매우 낮은 물체에 있어서 그 중요성이 매우 크지만, 고주파 근사법을 사용하여 해석할 수가 없다. 만약 이들의 전기적 폭이 충분히 작다면, 적절한 임피던스 스트립으로 모델링 한 후, 저주파 근사법을 통하여 해석적으로 산란파 공식을 얻을 수 있다. 저주파 공식은 TE(Transverse Electric)파와 TM(Transverse Magnetic)파에 대해 2차원 해의 형태로 주어지며, 이를 바탕으로 3차원 ILDC(Incremental Length Diffraction Coefficients)를 추출할 수 있고, 이를 통하여 물체 표면에 존재하는 임의의 형태의 크랙의 산란파도 계산할 수 있다. 기존의 방법은 TE파에 의한 결과만을 사용하여, TM파가 중요한 경우에 정확도가 떨어진다. 본 논문에서는 TE파와 TM파에 의한 결과를 동시에 사용하여 향상된 ILDC 수식을 제안하고, 그 정확성을 시뮬레이션을 통하여 검증한다.

• 소성∙가공
• /
• 제27권2호
• /
• pp.100-106
• /
• 2018

In the continuous casting process, the incidence of transverse surface cracks on the piece may occur by multiple and diverse variables. It is noted that mathematical models may predict only the occurance of the transverse surface cracks, but can require a lot of time (more than three days) to produce a result with this process. This study applied neural networks to predict whether the cracks on the piece surface occurs or does not occur. The computation time was shortened to three minutes, making it applicable to an on-line program, which predicts the non-cracks or cracks of the piece surface in the actual continuous casting process. In addition, the operating conditions to prevent the occurrence of the transverse surface cracks, using decision boundaries were also suggested.

• Restorative Dentistry and Endodontics
• /
• 제22권2호
• /
• pp.546-559
• /
• 1997

본 연구의 목적은 초음파를 이용하여 치근단 역충전와동을 형성하는 경우 와동형성의 효율과 치질의 균열 발생을 알아보기 위함이다. 발거된 상악 제 1 대구치 원심협측 치근 91개를 대상으로 치근단 3 mm를 치아의 장축에 직각되게 절단 제거한 다음 저속 round bur를 사용한 군을 대조군으로 하고 제 1에서 제 10까지의 출력 각 단계의 stainless steeel 초음파 기구를 이용한 군을 실험군으로 하여 치근단 역충전 와동을 형성하고 각 치근단 역충전 와동을 형성하는 데 소요되는 시간 및 stroke 수를 측정하였으며, 역충전와동 형성 전후의 치아 균열 발생을 fiberoptic을 이용한 입체현미경으로 측정 비교하여 다음과 같은 결과를 얻었다. 초음파의 출력 단계가높을수록 역충전와동을 형성하는데 소요된 시간 및 stroke 수가 감소 하였으며 (p<0.001) 감소되는 양상은 선적 관계를 보였다 (p<0.001). 제7에서 제 10 단계까지의 고출력의 초음파 기구로 와동 형성한 군에서는 저속 round bur로 와동 형성한 군이나 제 1 단계에서 제 3 단계까지의 저출력 초음파 군, 제 4 단계에서 제 6 단계까지의 중출력 초음파 군에 비해 치아 균열의 발생 빈도가 유의하게 높게 나타났고 (p<0.01), 저속 round bur, 저출력의 초음파 기구 그리고 중출력의 초음파 기구로 형성한 군 사이에는 치아 균열의 발생 빈도에 유의한 차이가 나타나지 않았다 (p>0.05). 고출력의 초음파를 이용한 경우에, 와동형성전에 균열이 이미 존재했던 치아에서는 균열이 존재하지 않았던 치아에서보다 와동형성 후 균열이 유의하게 많이 발생하였다(p<0.001). 저출력의 초음파를 이용한 경우에, 초기 근단공의 크기가 작았던 경우가 근단공의 크기가 컸던 경우에 비해 와동형성 후 균열이 유의하게 많이 발생하였다 (p<0.05).

• Restorative Dentistry and Endodontics
• /
• 제23권1호
• /
• pp.54-67
• /
• 1998

치근단 역충전 와동 형성을 위한 초음파 다이아몬드 기구의 임상적 적용의 타당성 및 특성을 평가하기 위해, 다이아몬드 기구의 상아질 삭제능력, 역충전 외동 형성효율 및 치질에 미치는 영향을 관찰하여 스테인레스 스틸 기구와 비교, 평가하였다. 치근단 역충전 와동 형성시 다이아몬드 기구와 스테인레스 스틸 기구를 발거된 소의 치아에서 노출시킨 상아질 표변에 일정한 출력과 시간 조건 하에서 작동시켜 상아질 표면으로부터의 삭제된 깊이를 측정하였다. 역충전 와동 형성효율을 평가하기 위하여 발거된 상악 제 1 대구치 치근에서 근관을 형성하고 gutta-percha로 충전한 다음 근단 3mm부위를 치아 장축에 직각되게 절제하고 초음파 기구의 와동형성 소요 시간 및 소요 stroke 수를 측정하였다. 초음파 기구를 이용한 와동 형성이 치질에 미치는 영향을 평가하기 위하여 초음파 와동 형성 전후의 치근단부 치질의 균열 발생빈도를 측정, 평가하여 다음과 같은 결과를 얻었다. $\cdot$ 저출력 또는 중출력에서 그리고 노출된 상아질에 수직 또는 수평으로 기구를 적용한 경우 모두에서, 다이아몬드 기구가 스테인레스 스틸 기구에 비해 높은 상아질 삭제효과를 나타내었다(p<0.01). $\cdot$ 초음파기구를 상아질 표면에 수직으로 적용한 경우에 출력이 높을수록 상아질 삭제효과가 우수하였으며, 수평으로 적용한 경우에는 출력에 따른 유의한 증가가 나타나지 않았다(p<0.01). $\cdot$ 중출력에서는 다이아몬드 기구가 스테인레스 스틸 기구에 비해 와동형시 소요되는 stroke 수와 시간으로 본 와동형성효율이 유의하게 우수하게 나타났다(p<0.05). $\cdot$ 저출력에서는 다이아몬드 기구가 스테인레스 스틸 기구에 비해 외동형성 후 치근단 균열 발생빈도가 유의하게 적게 나타났다(p<0.01).