• The Journal of Korean Academy of Prosthodontics
• /
• v.44 no.6
• /
• pp.683-689
• /
• 2006

Statement of problem. Interfacial toughness is important in the mechanical property of layered dental ceramics such as core-veneered all-ceramic dental materials. The interfaces between adjacent layers must be strongly bonded to prevent delamination, however the weak interface makes delamination by the growth of lateral cracks along the interface. Purpose. The purpose of this study was to determine the effect of the reaction layer on the interfacial fracture toughness of the core/veneer structure according to the five different divesting. Materials and methods. Thirty five heat-pressed Lithia-based ceramic core bars (IPS Empress 2), $20mm{\times}3mm{\times}2mm$ were made following the five different surface divesting conditions. G1 was no dissolution or sandblasting of the interaction layer. G2 and G3 were dissolved layer with 0.2% HF in an ultrasonic unit for 15min and 30 min. G4 and G5 were dissolved layer for 15min and 30min and then same sandblasting for 60s each. We veneered bilayered ceramic bars, $20mm{\times}2.8mm{\times}3.8mm$(2mm core and 1.8mm veneer), according to the manufacturer's instruction. After polishing the specimens through $1{\mu}m$ alumina, we induced five cracks for each of five groups within the veneer close to interface under an applied indenter load of 19.6N with a Vickers microhardness indenter. Results. The results from Vickers hardness were the percentage of delamination G1:55%, G2:50%, G3:35%, G4:0% and G5:0%. SEM examination showed that the mean thickness of the reaction layer were G1 $93.5{\pm}20.6{\mu}m$, G2 $69.9{\pm}14.3{\mu}m$, G3 $59.2{\pm}20.2{\mu}m$, G4 $0.61{\pm}1.44{\mu}m$ G5 $0{\pm}0{\mu}m$. The mean interfacial delamination crack lengths were G1 $131{\pm}54.5{\mu}m$, G2 $85.2{\pm}51.3{\mu}m$, and G3 $94.9{\pm}81.8{\mu}m$. One-way ANOVA showed that there was no statistically significant difference in interfacial crack length among G1, G2 and G3(p> 0.05). Conclusion. The investment reaction layer played important role at the interfacial toughness of body ceramic bonded to Lithia-based ceramic.

• Journal of the Korean Institute of Gas
• /
• v.16 no.2
• /
• pp.18-24
• /
• 2012

This research seeks to evaluate damage on type II gas cylinder by an acoustic emission test when executing 20000 cycles fatigue test and thereafter burst test. Used gas cylinders in the experimental are three types as follows; one is sound cylinder, others are cylinders which contain longitudinal and transverse artificial defect. The size of artificial defect is a depth of 3 mm, width of 3 mm and length of 50 mm. In the case of the cylinder which artificial defect, unlike the expectation that it will burst in low pressure, the burst pressure of the cylinder did not differ much according to whether or not there were defects. However, when there was longitudinal defect, the location of burst was near the location of defect. This leads to the effect in which the thickness of the composite material becomes thinner according to the length of the longitudinal defect and this is judged to have an effect on the location of initiation and growth of crack in the liner. Also, for the acoustic emission signal, when there is longitudinal defect, the ratio of an event occurring at defect position among overall hits is more than 50 %, and the source location also accords very precisely with defect position.