• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.31 no.4
• /
• pp.413-422
• /
• 1995

Cavitation erosion-corrosion implies damage to materials due to the shock pressure or shock wave that results when bubbles form and collapse at a metal surface within a liquid. If the liquid is corrosive to the material, a condition typically encountered in industry, the component materials may suffer serious damage by a combination of mechanical and electrochemical attack. In this study, the mild steel(SS41) was tested by using the piezoelectric vibrator with 20kHz, 24$\mu$m to cavity generation apparatus. The damage behaviour of vibration cavitation erosion-corrosion and the environment characteristics were investigated in various solutions which are seawater, tap water and distilled water. The main results obtained are as follows; 1) The cavitation erosion-corrosion damage behaviour in the seawater increases to occur at the equal degree on the middle portion and the outside portion of specimen. The distilled water specimen, on other hand, occurs beginning on the outside portion across to the middle portion of specimen. 2) The cavitation erosion-corrosion damage in the tap water of low specific resistance more increases than that in the distilled water of high specific resistance at the initial testing time and more decreases than that in it by the CaCO sub(3) film with testing time. 3) Cavitation erosion-corrosion damage characteristic divides into four regions; incubation region, acceleration region, deceleration region and steady state region.

• Journal of Welding and Joining
• /
• v.11 no.2
• /
• pp.42-52
• /
• 1993

The corrosion fatigue fracture behaviour of dual phase steel was investigated in 3% NaCl solution at 302MPa and 137MPa. Fatigue test was conducted by cantilever type of self-made rotary bending fatigue testing machine. The fatigue strength increased with increasing the hardness of 2nd phase. Corrosion pit originated at the boundary of the 2nd phase. The size and number of corrosion pits were influenced by the 2nd phase hardness, and pits remained constant in size just after they were transited into cracks. The life of crack initiation was effected by stress level. The shape of relation of .DELTA. K and da/dN has smaller scattering in it in 3% NaCl solution than that in air. The higher the 2nd phase hardness is, the greater the corrosion fatigue life becomes. Corrosion fatigue fracture behaviour was primarily effected by mechanical factor in case of high stress(302MPa), but by electro-chemical reaction in a lower stress(137MPa). As stress level got lower and hardness of the 2nd phase got higher, the roughness of fracture surface increased.

• Corrosion Science and Technology
• /
• v.14 no.4
• /
• pp.190-194
• /
• 2015

The splash zone is the most corrosive area of the marine environment, and the corrosion of steel structures exposed in this area is a serious concern. DH36 steel is one of most commonly used steels for offshore oil platforms in China, and its corrosion behaviour in splash zones was studied in this paper. Polarization curves were obtained from the corroded steel exposed in this area while the morphologies and rusts of the rust steel were characterized using scanning electron microscopy and X-ray diffraction. Double rust layers were formed in the splash zone. The inner layer contained magnetite and fine flaky lepidocrocite, and the outer layer was composed of accumulated flaky lepidocrocite and a small amount of goethite. In the wet period, the iron dissolved and reacted with lepidocrocite, and magnetite appeared, while the magnetite was oxidized to lepidocrocite again during the dry period. Electrochemical reduction and chemical oxidization cycled in intermittent wetting and drying periods, and magnetite and lepidocrocite were involved in the reduction reaction, leading to serious corrosion.

• Corrosion Science and Technology
• /
• v.4 no.1
• /
• pp.8-14
• /
• 2005

The corrosion behaviour of mild steel in phosphoric acid solution in the presence and absence of pollutants viz. Chloride, Fluoride and Sulfate ions at 302K-333K was studied using mass loss and potentiostatic polarization methods. The addition of chloride and sulfate ions inhibits the mild steel corrosion in phosphoric acid while fluoride ions stimulate it. The effect of temperature on the corrosion behaviour of mild steel indicated that inhibition of chloride and sulfate ions decreased with increasing temperature. The adsorption of these ions (Chloride and sulfate) on the mild steel surface in acid has been found to obey Langmuir adsorption isotherm. The values of activation energy (Ea) and free energy of adsorption ($\Delta$) indicated physical adsorption of these ions (chloride and sulfate) on the mild steel surface. The plot of $logW_{f}$ against time (days) at 302K gives a straight line, which suggested that it obeys first order kinetics and also calculate the rate constant k and half-life time $t_{1/2}$.

• Corrosion Science and Technology
• /
• v.18 no.4
• /
• pp.121-128
• /
• 2019

Electrochemical Impedance Spectroscopy (EIS) was used to predict corrosion behaviour of metallic Cultural Heritage assets in two monitoring campaigns: 1) an iron bar chain exposed indoor from over 500 years in the Notre Dame Cathedral in Amiens (France); and 2) a large weathering steel sculpture exposed outdoor from tens of years in Ferrara (Italy). The EIS portable instrument employed was battery operated. In situ EIS measurements on the iron chain could be used to investigate the phenomena involved in the electrochemical interfaces among various corrosion products and assess and predict their corrosion behaviour in different areas of the Cathedral. Meanwhile, the sculpture of weathering steel, like most outdoor artefacts, showed rust layers of different chemical composition and colour depending on the orientation of metal plates. The EIS monitoring campaign was carried out on different areas of the artefact surface, allowing assessment of their protective effectiveness. Results of EIS measurements evidenced how employing a simple test that could be performed in situ without damaging the artefacts surface is possible to quickly gain knowledge of the conservation state of an artefact and highlight potential danger conditions.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2009.05a
• /
• pp.289-290
• /
• 2009

In this study, the resistance of calcium aluminate cement (CAC) against chloride-induced corrosion was assessed by testing for the strength, chloride transport, and corrosion behaviour. The study found that the CAC concrete had better performance than ordinary Portalnd cement(OPC) in resisting the corrosion of steel.

• Proceedings of the KIEE Conference
• /
• 1995.07c
• /
• pp.1048-1050
• /
• 1995

Lead-acid battery is used widely as a power source at a automobile, industrial machines, folk lifts, U.P.S. etc. Lead-acid battery is cheaper than arty other secondary battery, but this battery has many disadvantages such as heavy, low energy density, environment problem etc. In this article, we introduce cyclic voltammetry methods to investigate corrosion behaviour of positive grids of Pb-Ca alleys.

• Steel and Composite Structures
• /
• v.48 no.1
• /
• pp.27-41
• /
• 2023

Under the long-term effect of corrosive environment, many cold-formed steel (CFS) structures have serious corrosion problems. Corrosion leads to the change of surface morphology and the loss of section thickness, which results in the change of instability mode and failure mechanism of CFS structure. This paper mainly investigates the elastic local buckling behavior of corroded CFS columns. The surface morphology scanning test was carried out for eight CFS columns accelerated corrosion by the outdoor periodic spray test. The thin shell finite element (FE) eigen-buckling analysis was also carried out to reveal the influence of corrosion surface characteristics, corrosion depth, corrosion location and corrosion area on the elastic local buckling behaviour of the plates with four simply supported edges. The accuracy of the proposed formulas for calculating the elastic local buckling stress of the corroded plates and columns was assessed through extensive parameter studies. The results indicated that for the plates considering corrosion surface characteristics, the maximum deformation area of local buckling was located at the plates with the minimum average section area. For the plates with localized corrosion, the main buckling shape of the plates changed from one half-wave to two half-wave with the increase in corrosion area length. The elastic local buckling stress decreased gradually with the increase in corrosion area width and length. In addition, the elastic local buckling stress decreased slowly when corrosion area thickness was relatively large, and then tends to accelerate with the reduction in corrosion area thickness. The distance from the corrosion area to the transverse and longitudinal centerline of the plate had little effect on the elastic local buckling stress. Finally, the calculation formula of the elastic local buckling stress of the corroded plates and CFS columns was proposed.

• Advances in concrete construction
• /
• v.5 no.2
• /
• pp.117-143
• /
• 2017

The attack of environmental aggressive agents progressively reduces the structural reliability of buildings and infrastructures and, in the worst exposition conditions, may even lead to their collapse in the long period. A change in the material and sectional characteristics of a structural element, due to the environmental damaging effects, changes its mechanical behaviour and varies both the internal stress redistribution and the kinematics through which it reaches its ultimate state. To identify such a behaviour, the evolution of both the damaging process and its mechanical consequences have to be taken into account. This paper presents a computational approach for the analysis of reinforced and prestressed concrete elements under sustained loading conditions and subjected to given damaging scenarios. The effects of the diffusion of aggressive agents, of the onset and development of the corrosion state in the reinforcement and the corresponding mechanical response are studied. As known, the corrosion on the reinforcing bars influences the damaging rate in the cracking pattern evolution; hence, the damage development and the mechanical behaviours are considered as coupled phenomena. The reliability of such an approach is validated in modelling the diffusion of the aggressive agents and the changes in the mechanical response of simple structural elements whose experimental behaviour is reported in Literature. A second set of analyses studies the effects of the corrosion of the tendons of a P.C. beam and explores potentially unexpected structural responses caused by corrosion under different aggressive exposition. The role of the different types and of the different positions of the damaging agents is discussed. In particular, it is shown how the collapse mode of the beam may switch from flexural to shear type, in case corrosion is caused by a localized chloride attack in the shear span.

• Journal of the Korean Society of Safety
• /
• v.16 no.2
• /
• pp.44-50
• /
• 2001

The rotated bending fatigue test was conducted in air md in 3.5% NaCl salt solution to investigate the fatigue fracture behaviour of raw material and F.E.M dual phase steel made from raw material(SS41) by a suitable heat treatment. This study has compared the initial microcrack creation of material by tensile test with that by fatigue test. And the rotated bending test of cantilever type under the condition of 3.5% NaCl salt solution and air has investigated the corrosion fatigue fracture behaviour with the variation of stress concentration factor determined by each of notch shapes. The initial microcrack have been developed in fragile grainboundary with general corrosion occurring in raw material : in the pits built up by corrosion in F.E.M. dual phase steel because pits bring out stress concentration. It is small that the degree of decrease in corrosion fatigue life for F.E.M. dual phase steel compared with raw material because the notch sensitivity of F.E.M. dual phase steel is lower than raw material in reason of characteristics with two-phase construction.