• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.14 no.2
• /
• pp.299-305
• /
• 1994

An experimental test section was placed in Pangyo-Guri Expressway to monitor the performance of CRCP(Continuously Reinforced Concrete Pavement). So far early-age behaviors of the test section have been monitored for about two years. The purposes of this paper are to analyze the early-age behavior and temperature pattern of the test section and to compare the results with those of similar test sections placed in Houston. As results of this study, following findings were obtained. The results of Pangyo-Guri test section were generally better than those of Houston test sections in terms of the early-age crack patterns. Type II cement was more effective than type I cement in controlling the early-age cracking. Afternoon placement was more effective than morning construction in controlling the early-age cracking in summer season.

• International Journal of Highway Engineering
• /
• v.12 no.4
• /
• pp.101-110
• /
• 2010

In this paper, it has been studied about the CRCO to maintain or rehabilitate the aged JCP. The CRCO and JCO was constructed at useless section of Seo-Hae-Ahn express highway in South Korea. The performance evaluation was conducted. Especially, it was focused on the roll of longitudinal reinforced steels inserted into the CRCO. On crack survey results from field construction section, the reflection cracks at joint of the existing pavement occurred in CRCO. However, due to the constraints of longitudinal reinforced steels, crack width was small. Total crack length and quantity in the CRCO more than that in the JCO. And crack spacing in the CRCO was narrower than it in the CRCP. Through the bonding strength test results, if the cold milling and cleaning as well as surface treatment is applied, there will be no debonding problem at interlayer in the early age. From analysis of the horizontal behavior at the joint, the longitudinal reinforced steels constrained crack width which became wider than initial state over time. Also, that steel in the CRCO reduced the horizontal movement due to temperature variation(4 times than that in the JCO). But, if interface is debonded, the roll decreased. Vertical VWG data showed that CRCO did not occur debonding problem at steel location, but there was some problem in JCO. It was confirmed by field coring. The tensile strain appeared in the CRCO, But the compressive strain occurred in the JCO in early age. Through the FWD test result, deflection in the CRCO was less than that in the JCO. And K value in the CRCO was greater than it in the JCO.

• International Journal of Highway Engineering
• /
• v.11 no.2
• /
• pp.121-132
• /
• 2009

Thin bonded continuously reinforced concrete overlay(CRCO) was constructed on He existing jointed plain concrete pavement(HCP) surface at Seo-Hae-Ahn express highway in South Korea in order to evaluate its applicability and performance. Two sections of road were considered for this evaluation. In the first section, the concrete overlayer was placed and cut down to the existing layer to form transverse joints while CRCO was constructed on top of the existing layer in the second section. Early strength concrete(Type III) was utilized for both overlay sections. The depth of milling and the thickness of overlaid layer were 5 cm and 10 cm, respectively. Several vibrating wire gauges(VWG) were installed to evaluate the performance of CRCO with respect to curling, delamination, and crack propagation. As a result of the strength test, it was found that strength of the material reaches the design criteria within 1-3 days. Analysis with vibrating wire gauge(VWG) showed CRCO effectively restricts joint movement. High adhesive strength also was observed from the material regardless of length of aging. Meanwhile, transverse cracks were observed on the middle of the section where JPCP overlay was applied whereas arbitrarily cracks in transverse direction were observed on the section where CRCP was applied.