• The Korean Journal of Ceramics
• /
• v.4 no.3
• /
• pp.213-221
• /
• 1998

$BaCe_{0.9}Gd_{0.1_O_{2.95}$ powder was synthesized by oxalate coprecipitation method. Precipitate with a stoichimetric ratio of the cations was prepared by adding a mixture of Ba, Ce and Gd nitrate solution to an oxalic acid solution at pH 4. Reaction between the constituent oxides to form a perovskite phase was initiated at $800^{\circ}C$ and a single phase $BaCe_{0.9}Gd_{0.1_O_{2.95}$ powder having good sinterability was obtained after calcination at $1000^{\circ}C$. Sintering green compacts of this powder for 6 h showed a considerable densification to start at $1100^{\circ}C$ and resulted in 93% and 97% relative densities at $1300^{\circ}$ and at $1450^{\circ}C$, respectively. Whereas the power compacts prepared by solid state reaction had lower relative densities, 78% at $1300^{\circ}$and 90% at $1450^{\circ}C$. Fine particles of $CeO_2$ second phase were observed in the surface of the sintered compacts. This was attributed to the evaporation of BaO from the surface that had been exposed during thermal etching.

• Korean Journal of Materials Research
• /
• v.11 no.10
• /
• pp.863-868
• /
• 2001

The present study was carried out to investigate the effect of MA processing variables on the microstructural properties of composite powders and the coefficient of thermal expansion of pulse electric current sintered AlN-Cu powder compacts. The AlN-Cu powders had a size of less than 15 $\mu\textrm{m}$ with 25 nm size of copper crystallite after MA 32 hours. The finely distributed AlN-Cu powder compacts were completely achieved after PECS. The residual oxygen was considerably removed after hydrogen reduction treatment. The residual carbon was completely removed to 97%. The CTE of AlN-Cu powder compacts showed a good consistency with Kingery-Tuner model when the volume fraction of copper was less than 60%. When it was more than 60%, the CTE had a good agreement with Series model.

• Journal of Powder Materials
• /
• v.1 no.2
• /
• pp.181-189
• /
• 1994

The compacts of pure and phosphorus-coated iron powder with 0~0.8%C were sintered at $1100^{\circ}C$ for 40 min. in cracked ammonia gas atmosphere. The tensile and impact strengths were measured and the relationship of the results with carbon content, phosphorus, quenching and tempering was investigated. The results obtained can be summarized as follows : (1) The tensile strength of sintered compacts increased slowly with carbon content. Increase in tensile strength by heat treatment was evident especially in the low carbon specimen. The specimen with phosphorus showed higher strength compared to pure iron compacts value. (2) No inflection point of elasticplastic deformation on stress-strain curve was observed in sintered steel. The elastic modulus of sintered steel had the same tendency as tensile strength. But the elongation showed the opposite tendency. (3) The impact absorption energy of sintered steel without addition of phosphorus decreased successively with carbon content and by quenching and tempering. On the contrary, addition of phosphorus resulted in an increase of the impact absorption energy. Quenching and tempering did not affect the impact energy especially in high carbon content. (4) The main fracture source was pore in specimen and the propagation of crack occured mostly along the grain boundaries. But the intragranular fracture was also observed in high carbon, quenched and tempered specimen, and especially in the specimen with phosphorus.

• Journal of the Korean Ceramic Society
• /
• v.55 no.4
• /
• pp.352-357
• /
• 2018

The slip casting process is widely used to make green bodies from ceramic slips into dense compacts with homogeneous microstructure. However, stress may be generated inside the green body during drying, and can lead to cracking and bending during sintering. When starting from the spherical powders with mono-size distribution to make the close packed body, interstitial voids on octahedral and tetrahedral sites are formed. In this research, experiments were carried out with powders of three size types (host powder (H), octahedral void filling powder (O) and tetrahedral void filling powder (T)) controlled for average particle size by milling from two commercial alumina powders. Slips were prepared using three different powder batches from H only, H+O or H+O+T mixed powders. After manufacturing green compacts by solid-casting, compacts were dried at constant temperature and humidity and sintered at $1650^{\circ}C$. Alumina samples fabricated from the multi-sized powder mixture had improved compacted and sintered densities.

• Journal of Powder Materials
• /
• v.8 no.4
• /
• pp.223-230
• /
• 2001

Ti-37.5at%Si elemental powder mixtures were mechanically alloyed by a high-energy ball mill, followed by CIP (cold isostatic pressing) and HIP (hot isostatic pressing) for different processing conditions. Only elemental phases (Ti and Si) were observed for the 5 min mechanically alloyed (MA 5 min) powder, but only $Ti_5Si_3$phase was observed for the 30 min mechanically alloyed (MA 30 min) powder. $Ti_5Si_3$phase was observed for the HIPed compact of MA 5 min and 30 min powders at 150 and 190 MPa for 3 hr at $1000^{\circ}C$. For the HIPed compacts, the highest sintered density was obtained to be 99.5% of theoretical density by a HIP step at $1350^{\circ}C$ at 190MPa for 3hr. The hardness values of the HIPed $Ti_5Si_3$compacts at $1350^{\circ}C$ at 150/190 MPa for 3hr were higher than HRC 76. The densification and mechanical property of HIPed $Ti_5Si_3$compacts was found to depend on more HIP temperature than HIP pressure.

• 한국기계연구소 소보
• /
• s.9
• /
• pp.67-74
• /
• 1982

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2001.11a
• /
• pp.32-32
• /
• 2001

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 1999.10a
• /
• pp.15-15
• /
• 1999

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2002.04b
• /
• pp.35-36
• /
• 2002

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2002.04b
• /
• pp.64-64
• /
• 2002