• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2004.10a
• /
• pp.725-728
• /
• 2004

In this study, the effect of mode II by variation of multilevel loading direction was experimentally investigated in the fatigue crack propagation behavior. To generate mixed-mode I+II loading state, the compact tension shear(CTS) specimen and loading device were used in this tests. The experimental method divided into three steps and three cases that were step I(0$^{\circ}$), step II(30$^{\circ}$, 60$^{\circ}$, 90$^{\circ}$),step III(0$^{\circ}$) and case I(0$^{\circ}$ ⇒ 30$^{\circ}$ ⇒ 0$^{\circ}$), case II(0$^{\circ}$ ⇒ 60$^{\circ}$ ⇒ 0$^{\circ}$), case III(0$^{\circ}$ ⇒ 90$^{\circ}$ ⇒ 0$^{\circ}$). The result of test, the step II affected to the step III in the all case. Specially, The fatigue crack propagation rate was faster and the fatigue life was smaller than of mixed mode I+II(30$^{\circ}$,60$^{\circ}$) due to the effect of mode II in the step III of the case III

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2002.05a
• /
• pp.104-109
• /
• 2002

In this paper, a statistical analysis of fatigue crack growth behavior under constant amplitude loads has been carried out. Fatigue crack growth tests were conducted on sixteen pre-cracked compact tension (CT) specimens of the pressure vessel (SPV50) steel in controlled identical load and environmental conditions. The assessment of the statistical distribution of fatigue crack growth experimental data obtained from SPV50 steel was studied and also the correlation of the parameter C and m in the Paris-Erdogan law was discussed. The probability distribution function of fatigue crack growth life seems to follow the 3-parameter Weibull. The fatigue crack growth rate seems to follow the 3-parameter Weibull and the log-normal distribution. The coefficient of variation (COV) of fatigue crack growth life was observed to decrease as the crack grows. A strong negative linear correlation exists between the coefficient C and the exponent m in Paris model. Fatigue crack growth rate data shows a normal distribution for both m and logC.

• International Journal of Ocean System Engineering
• /
• v.2 no.3
• /
• pp.160-169
• /
• 2012

Flux Cored Arc Welding (FCAW) is a common practice to join thick plates such as the structural members of large scale offshore structures and very large container ships. The objective of this study was to investigate the mechanical properties and variability of the fatigue crack initiation life in the flux cored arc welded API 2W Gr.50 steel joints typically applied to offshore structures with a focus on the effect of the materials in fatigue crack growth life from the notch root of a compact tension specimen. Offshore structural steel (API 2W Gr.50) plates (60-mm thick) were used to fabricate multi-path flux core arc welded butt welded joints to clearly consider fatigue fractures at the weld zone from the notch. Fatigue tests were performed under a constant amplitude cyclic loading of R = 0.4. The mean fatigue crack initiation life of the HAZ specimen was the highest among the base metal (BM), weld metal (WM), and heat affected zone (HAZ). In addition, the coefficient of variation was the highest in the WMl specimen. The variability of the short fatigue crack growth rates from the notch tips in the WM and HAZ specimens was higher than in BM.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.32 no.4
• /
• pp.402-410
• /
• 1996

Recently carbon fiber reinforced plastic(CFRP) has been used structural materials in corrosive environment such as for water, chemical tank and chemical pipes. However, mechanical properties of such materials may change when CFRP are exposed to corrosive environment for long periods of time. Therefore, it is important to understand the effect of moisture absorption on mechanical properties of the CFRP. In this study, degradation behavior of immersed carbon fiber/epoxy resin composite material was investigated using acoustic emission(AE) technique. Fracture toughness test are performed on the compact tension(CT) test specimens that are pilled by two types of laminates $[0^{\circ}_2$/$90^{\circ}_2]_3s$ and $[0^{\circ}_2$/$90^{\circ}_2]_6s$During the fracture toughness test, AE test was carried out to monitor the damage of CFRP by moisture absorption. In spite of the change of moisture absorption rate, the fracture toughness of CFRP was not change. As immersion time increased, AE event count numbers decreased in low amplitude range of AE for amplitude distribution histogram. The event in low amplitude range was known to be generated by debonding of matrix-fiber interface. Therefore, decrease of AE event count numbers in low amplitude range represents that debonding of matrix-fiber interface which was probably generated by moisture absorption.

• Journal of the Korean Society of Safety
• /
• v.13 no.4
• /
• pp.79-86
• /
• 1998

The effect of specimen thickness on fatigue crack growth behavior has been carried out by compact tension specimens of thickness of 3mm, 10mm and 25mm for maraging steel and Al 7075-T6. The closure points were determined during the test by means of a clip-gage situated at the notch mouth. Specimen thickness have no apparent influence on the fatigue crack growth rate of maraging steel, but the crack growth rate of 25mm thickness specimen for Al 7075-T6 is faster than that of 3 and 10mm specimens. The difference of crack growth rates can be successfully explained by considering the different stress state of plane strain and plain stress due to the variation of specimen thickness. Also the crack opening ratio of 25mm specimen is greater than those of 3 and 10mm specimens. When a side groove is introduced in a 10mm specimen, the crack growth rate is approximately similar to that of 25mm specimen. The effective thickness expression of $B_e=B_o-(B_o-B_N)^2B_o$ is the most appropriate to evaluate the crack growth rate of side-grooved specimen. Fatigue crack growth rates can be well described by $\Delta K_{eff}$ of the crack closure points in regardless of all thickness and side-grooved specimens.

• Structural Engineering and Mechanics
• /
• v.53 no.5
• /
• pp.867-880
• /
• 2015

Mechanical fastening is still one of the main methods used for joining components. Different techniques have been applied to reduce the effect of stress concentration of notches like fastener holes. In this work we evaluate the feasibility of combining laser shock peening (LSP) and cold expansion to improve fatigue crack initiation and propagation of open hole specimens made of 6061-T6 aluminum alloy. LSP is a new and competitive technique for strengthening metals, and like cold expansion, induces a compressive residual stress field that improves fatigue, wear and corrosion resistance. For LSP treatment, a Q-switched Nd:YAG laser with infrared radiation was used. Residual stress distribution as a function of depth was determined by the contour method. Compact tension specimens with a hole at the notch tip were subjected to LSP process and cold expansion and then tested under cyclic loading with R=0.1 generating fatigue cracks on the hole surface. Fatigue crack initiation and growth is analyzed and associated with the residual stress distribution generated by both treatments. It is observed that both methods are complementary; cold expansion increases fatigue crack initiation life, while LSP reduces fatigue crack growth rate.

• Structural Engineering and Mechanics
• /
• v.23 no.6
• /
• pp.651-674
• /
• 2006

The fatigue cracks initiate and propagate in the Armored Vehicle Launch Bridge (AVLB) components, especially like the splice doubler angle, splice plate, and bottom chord, due to the cyclic loading by repeated AVLB-launchings and tank-crossings. In this study, laboratory fatigue tests were conducted on six aluminum 2014-T6, four aluminum 7050-T76511, and four ASTM A36 steel compact-tension specimens to evaluate the crack growth behavior of the materials used for the components. The experimental results provide the relationship (Paris Law) between crack growth rate, da/dn, and stress intensity range, ${\Delta}K$, whose material dependent constants C and m can later be used in the life estimation of the components. Finite Element Method (FEM) was used to obtain the stress intensity factor, K, of the components with cracks. Because of the complexity of loading conditions and component geometry, several assumptions and simplifications are made in the FEM modeling. The FEM results, along with the results obtained from laboratory fatigue tests, are then utilized to estimate critical crack length and remaining life of the components.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.9 no.2
• /
• pp.135-139
• /
• 1985

A J$_{IC}$ test procedure by ultrasonic method performed to observe the crack opening behavior of fatigue precrack and detect the initiation of crack propagation of compact tension specimen in this paper. Pulse-echo method with 5 MHz transducer was used on the Cr-Mo steel quenched and tempered at 593.deg. C. We obtained the following results in the elastic-plastic fracture toughness test by ultrasonic method. Echo height is a little increased linearly and rapidly at the early stage of loading . Then it is decreased considerably, finally at the unstable crack growth stage, it is rapidly increased at an unpredictable rae. The initiation of crack propagation is supposed to be at the stage deviated from linearly decreased region and then blunted. J$_{IC}$ value(10.15-12.15 Kgf/mm) by ultrasonic method is lower than that(12.2 Kgf/mm) by R-curve method. But, it is required that the research for the more exact evaluation about correlation between echo height and the crack opening behavior of precrack tip will be continued. continued.ued.

• Journal of the Korean Society for Precision Engineering
• /
• v.18 no.9
• /
• pp.131-139
• /
• 2001

The use of fracture mechanics has traditionally concentrated on crack growth under an opening mechanism. However, many service failure occur from cracks subjected to mixed mode loadings. Hence, it is necessary to evaluate the fatigue behavior under mixed mode loading. Under mixed mode loading conditions, not only the fatigue crack propagation rate is of importance, but also the crack propagation direction. The mode I and II stress intensity factors of CTS specimen were calculated using elastic finite element method. The propagation behavior of the fatigue crack of the STS304 steeds under mixed mode loading condition was evacuated by using stress intensity factors $K_I$ and $K_II. The MTS criterion and effective stress intensity factor were applied to predict the crack propagation direction and the fatigue crack propagation rate.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.27 no.6
• /
• pp.960-968
• /
• 2003

The objective of this study is to investigate the effect of AE activities in the crack opening and closure during the fatigue test. The laboratory experiments for various materials and test conditions were carrie out to identify AE characteristics of fatigue crack propagation. Compact tension specimens of SWS 490B and Al 7075-T6 alloy were prepared for fatigue test. AE activities were analyzed based on the phase of the loading cycle. In case of SWS 490B, the most of AE was generated when the crack began opening and the crack closed fully, whereas a few in the full opening of the crack. On the other hand, in case of Al 7075-T6, a distinct AE activity was observed during crack opening process. AE activity in the peak loading of cycle was different with each specimen. However, in the same material, AE activity was not affected by the change of cyclic frequency (0.1, 0.2, 1.0 ㎐). It was found that AE activities during crack opening and closure depend on material properties such as micro-structure, yield strength and elongation.