• Corrosion Science and Technology
• /
• v.17 no.4
• /
• pp.166-175
• /
• 2018

In this study, the electrochemical properties of CP-Ti (commercially pure titanium) and Ti-64 (Ti-6Al-4V) were evaluated and the effect of hydrofluoric acid on corrosion resistance and electrochemical properties was elucidated. Additive manufactured materials were made by DMT (Directed Metal Tooling) method. Samples were heat-treated for 1 hour at $760^{\circ}C$ and then air cooled. Surface morphologies were studied by optical microscope and SEM. Electrochemical properties were evaluated by anodic polarization method and AC-impedance measurement. The oxide film formed on the surface was analyzed using an XPS. The addition of HF led to an increase in the passive current density and critical current density and decreased the polarization resistance regardless of the alloys employed. Based on the composition of the oxide film, the compositional difference observed by the addition of HF was little, regardless of the nature of alloys. The Warburg impedance obtained by AC-impedance measurement indicates the dissolution of the constituents of CP-Ti and Ti-64 through a porous oxide film.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.17 no.3
• /
• pp.380-388
• /
• 2016

Commercially pure titanium (CP Ti) has been actively used in plate heat exchangers due to its light weight, high specific strength, and excellent corrosion resistance. However, compared with automotive steels and aluminum alloys, there has not been much research on the plastic deformation characteristics and press formability of CP Ti sheet. In this study, the mechanical properties of CP Ti sheet are clarified in relation to press formability, including anisotropic properties and the stress-strain relation. The flow curve of the true stress-true strain relation is fitted well by the Kim-Tuan hardening equation rather than the Voce and Swift models. The forming limit curve (FLC) of CP Ti sheet was experimentally evaluated as a criterion for press formability by punch stretching tests. Analytical predictions were also made via Hora's modified maximum force criterion. The predicted FLC with the Kim-Tuan hardening model and an appropriate yield function shows good correlation with the experimental results of the punch stretching test.

• Journal of the Korean Society for Heat Treatment
• /
• v.31 no.1
• /
• pp.12-17
• /
• 2018

We investigated the corrosion behavior of commercially pure cold working processed (CP)-Ti with coarse-grained (CG) microstructure heat-treated at $400^{\circ}C$ and $600^{\circ}C$, respectively. It is observed that corrosion resistance of as-received CP-Ti heat-treated at $400^{\circ}C$, at which recrystallization proceeds, is largely improved. Interestingly, the mechanical property of CP-Ti sample at $400^{\circ}C$ was scarcely deteriorated. It is attributed to the decrease of the defects such as strain variance and dislocation density. On the other hand, the annealing treatment at $600^{\circ}C$ of CP-Ti plate causes to grain growth with the noticeable reduction of mechanical property. Hence, it is considered that defect density such as strain and dislocation density is important microstructural parameter for the improvement of corrosion resistance. The introduction of proper annealing treatment can help to improve corrosion resistance without scarifying mechanical property of CP-Ti.

• Journal of Periodontal and Implant Science
• /
• v.33 no.3
• /
• pp.499-518
• /
• 2003

The surface characteristics of titanium have been shown to have an important role in contact ossseointegration around the implant. Anodizing at high voltage produces microporous structure and increases thickness of surface titanium dioxide layer. The aim of present study was to analyse the response of rat calvarial osteoblast cell to commercially pure titanium and Ti-6A1-4V anodized in 0.06 mol/l ${\beta}$-glycerophosphate and 0.03 mol/l sodium acetate. In this study, rat calvarial osteoblasts were used to assay for cell viability and cell proliferation on the implant surface at 1,2,4,7 days. 1. Surface roughness was 1.256${\mu}m$ at 200V, and 1.745${\mu}m$ at 300V. 2. The thickness of titanium oxide layer was increased 1 ${\mu}m$ with the increase of 50V. 3. The proliferation rate of osteoblastic cells was increased with the increase of the surface roughness and the thickness of titanium oxide layer. 4. There was no difference in cell viability and cell proliferation between commercially pure titanium and Ti-6A1-4V anodized at the same condition. In conclusion, the titanium surface modified by anodizing was biocompatible, produced enhanced osteoblastic response. The reasons of enhanced osteoblast response might be due to reduced metal ion release by thickened and stabilized titanium dioxide layer and microporous rough structures.

• The Journal of Advanced Prosthodontics
• /
• v.1 no.1
• /
• pp.41-46
• /
• 2009

STATEMENT OF PROBLEM. The poor chemical bonding of a denture base resin to cast titanium framework often introduces adhesive failure and increases microleakage. PURPOSE. This study evaluated the shear bond strengths of a heat cure denture base resin to commercially pure titanium, Ti-6Al-4V alloy and a cobalt-chromium alloy using two adhesive primers. MATERIAL AND MATHODS. Disks of commercially pure titanium, Ti-6Al-4V alloy and a cobalt-chromium alloy were cast. Specimens without the primer were also prepared and used as the controls. The shear bond strengths were measured on a screw-driven universal testing machine. RESULTS. The primers significantly(P < .05) improved the shear bond strengths of the heat cure resin to all metals. However, the specimens primed with the Alloy $primer^{(R)}$(MDP monomer) showed higher bond strength than those primed with the MR $bond^{(R)}$(MAC-10 monomer) on titanium. Only adhesive failure was observed at the metal-resin interface in the non-primed specimens, while the primed specimens showed mixed failure of adhesive and cohesive failure. CONCLUSIONS. The use of appropriate adhesive metal primers makes it possible not only to eliminate the need for surface preparation of the metal framework before applying the heat cure resins, but also reduce the need for retentive devices on the metal substructure. In particular, the Alloy $primer^{(R)}$, which contains the phosphoric acid monomer, MDP, might be clinically more acceptable for bonding a heat cure resin to titanium than a MR $bond^{(R)}$, which contains the carboxylic acid monomer, MAC-10.

• Korean Journal of Materials Research
• /
• v.14 no.12
• /
• pp.893-899
• /
• 2004

Even though Ti-6Al-4V has gained popularity as an implant material, the possible dissolution of Al and V ions in body fluids remains a matter of concern. Though commercially pure Ti (Cp-Ti) overcomes this problem, the mechanical strength of pure titanium remains very low. Thus, in this experiment Cp-Ti was processed by Equal channel angular processing (ECAP), in order to increase the mechanical strength. The biocompatibility of ECAP-Ti, Cp-Ti and Ti-6Al-4V was examined by the apatite formation on each sample surface, after treating the surface with 5M NaOH and soaking in Simulated body fluids (SBF). Initially, the samples were mechanically polished on silicone carbide paper (#2000). The polished samples were treated with 5M NaOH solution at $60^{\circ}C$ for 24 hours. The NaOH treated samples were washed gently with distill water and dried at $40^{\circ}C$ for 1 day. The dried samples were heat treated in air at $600^{\circ}C$ for 1 hour. The surface morphology of these samples were studied using SEM and XRD. The SEM studies showed network of pores in all samples. The XRD showed oxide layer formation on Cp-Ti and Ti-6Al-4V. samples. However the oxide layer in ECAP-Ti was not substantial. These samples were immersed in SBF, kept at $36.5^{\circ}C$ for seven days period. At the end of 7 days, the apatite formation was confirmed only on Cp-Ti and was not observed in Ti-6Al-4V and ECAP-Ti. These observations of apatite formation relate to the fact that Cp-Ti showed greater oxide layer than other samples. The apatite examined was confirmed as tricalcium phosphate (TCP) using EDS and XRD.

• Journal of Microbiology and Biotechnology
• /
• v.28 no.10
• /
• pp.1664-1670
• /
• 2018

Titanium dioxide ($TiO_2$) has wide applications in food, cosmetics, pharmaceuticals and manufacturing due to its many properties such as photocatalytic activity and stability. In this study, the biosynthesis of $TiO_2$ nanoparticles (NPs) was achieved by using Baker's yeast. $TiO_2$ NPs were characterized by X-ray Diffraction (XRD), UV-Visible spectroscopy, Scanning Electron Microscopy (SEM), Transmission Electron Microscopy (TEM) and Energy Dispersive X-ray analysis (EDX) studies. The XRD pattern confirmed the formation of pure anatase $TiO_2$ NPs. According to EDX data Ti, O, P and N were the key elements present in the sample. SEM and TEM revealed that the nanoparticles produced were spherical in shape with an average size of $6.7{\pm}2.2nm$. The photocatalytic activity of $TiO_2$ NPs was studied by monitoring the degradation of methylene blue dye when treated with $TiO_2$ NPs. $TiO_2$ NPs were found to be highly photocatalytic comparable to commercially available 21 nm $TiO_2$ NPs. This study is the first report on antimicrobial study of yeast-mediated $TiO_2$ NPs synthesized using $TiCl_3$. Antimicrobial activity of $TiO_2$ NPs was greater against selected Gram-positive bacteria and Candida albicans when compared to Gram-negative bacteria both in the presence or absence of sunlight exposure. $TiO_2$ NPs expressed a significant effect on microbial growth. The results indicate the significant physical properties and the impact of yeast-mediated $TiO_2$ N Ps as a novel antimicrobial.

• The Journal of Korean Academy of Prosthodontics
• /
• v.45 no.6
• /
• pp.787-794
• /
• 2007

Statement of problem. Surface microgrooves on Ti substrata have been shown to alter the expression of genes responsible for various biological activities of cultured fibroblasts. However, their effect on enhancing cell proliferation is not yet clear. Purpose. The purpose of this study was to determine the dimension of surface microgrooves on Ti substrata that enhances proliferation and alters gene expression of cultured human gingival fibroblasts. Material and methods. Commercially pure Ti discs with surface microgrooves of monotonous $3.5{\mu}m$ in depth and respective 15 and $30{\mu}m$ in width were fabricated using photolithography and used as the culture substrata in the two experimental groups in this study (TiD15 and TiD30), whereas the smooth Ti was used as the control substrata (smooth Ti group). Human gingival fibroblasts were cultured on the three groups of titanium substrata and the proliferation, DNA synthesis, and gene expression of theses cells were analyzed and compared between all groups using XTT assay, BrdU assay, and reverse transcriptase-polymerase chain reaction (RT-PCR), respectively. Results. From the XTT assay at 48 h incubation, the proliferation of human gingival fibroblasts in TiD30 was significantly enhanced compared to that in smooth Ti and TiD15. The results from the BrdU assay showed that, at 24 h incubation, the DNA synthesis was significantly enhanced in TiD30 compared to that in smooth Ti. In RT-PCR, increase in the expression of PCR transcripts of fibronectin, CDK6, $p21^{cip1}$ genes was noted at 48h incubation. Conclusion. Surface microgrooves $30{\mu}m$ in width and $3.5{\mu}m$ in depth on Ti substrata enhance proliferation and alter gene expression of cultured human gingival fibroblasts.

• The Journal of Advanced Prosthodontics
• /
• v.12 no.6
• /
• pp.369-375
• /
• 2020

PURPOSE. This study evaluated the availability of multi-directionally forged (MDF) titanium (Ti) as a component of removable partial dentures (RPDs). MDF-Ti remarkably improved the mechanical properties of RPDs due to its ultrafine-grained structure. MATERIALS AND METHODS. The wear resistance, plaque adhesion, and machinability of MDF-Ti were tested. As controls, commercially pure (CP) titanium was used for wear, plaque adhesion, and machinability tests. For wear resistance, the volume losses of the titanium teeth before and after wear tests were evaluated. Plaque adhesion was evaluated by the assay of Streptococcus mutans. In the machinability test, samples were cut and ground by a steel fissure bur and carborundum (SiC) point. An unpaired t-test was employed for the analysis of the significant differences between MDF-Ti and the control in the results for each test. RESULTS. Wear resistance and plaque adherence of MDF-Ti similar to those of CP-Ti (P>.05) were indicated. MDF-Ti exhibited significantly larger volume loss than CP-Ti in all conditions except 100/30,000 g/rpm in machinability tests (P<.05). CONCLUSION. Although the wear resistance and plaque adherence of MDF-Ti were comparable to those of controls, MDF-Ti showed better machinability than did CP-Ti. MDF-Ti could be used as a framework material for RPDs.

• Journal of the Korean Society for Heat Treatment
• /
• v.18 no.2
• /
• pp.91-98
• /
• 2005

Both commercially pure titanium and Ti-6Al-4V alloy have been widely used as biomaterials because of their excellent biocompatibility, corrosion resistance and mechanical properties. However, in recent years, vanadium has been found to cause cytotoxic effects and adverse tissue reactions, while aluminium has been associated with potential neurological disorders. A newly designed ${\alpha}+{\beta}$ type Ti alloy, Ti-10Ta-10Nb alloy showed superior properties to CP Ti and Ti-6Al-4V alloy in the point of biomaterial, and elucidated the future uses as a biomaterial. Microstructural changes of Ti-10Ta-10Nb alloy after hot-rolling, warm-rolling, solution and aging treatment were investigated. According to TEM results, the microstructures after solution treatment were composed of mostly ${\alpha}$ phase with a trace of ${\beta}$ phase due to adding ${\beta}$-phase stabilizer tantalum and niobium. The microstructures after warm-rolling is coarse and elongated ${\alpha}$ phase and hot rolling resulted in very fine ${\alpha}$ widmanst$\ddot{a}$tten. The highest value of hardness was obtained by aging treatment at $400^{\circ}C$ for 20hr in which microstructure consisted of very fine ${\alpha}$ phase in ${\beta}$ matrix.