• Journal of the Korean Society of Clothing and Textiles
• /
• v.26 no.2
• /
• pp.263-269
• /
• 2002

This research was conducted to establish the efficient use of the colored rice bran fur dyeing textiles. To investigate the fabric dyeability of the colored rice bran extract, the anthocyanin pigments were extracted with water of different temperature ranges of 40 ~ 8$0^{\circ}C$ and were dyed on silk fabrics with different dyeing temperature $25^{\circ}C$~6$0^{\circ}C$, at acidic pH and neutral pH, respectively. Aluminum chloride was preheated with mordant K/S value and dyeing fastness of dyed silk fabrics were examined. The anthocyanins of the colored rice bran were stable and red color at acidic pH, red purple or purple blue at neutral pH, but unstable, blue color at alkaline pH. If extracting temperature and dyeing temperature of dyeing solution were higher, the dyeability was high, but the color of dyed fabric showed red tone. When extracting temperature was 8$0^{\circ}C$ and dyeing temperature of dyeing solution was 6$0^{\circ}C$, the dyeability was best. Without mordant, the dyeability of silk fabrics was higher in acidic pH than in neutral pH solution. With mordant, the dyeability was higher than without mordant, and also higher in acidic pH. Pretreatment of aluminum chloride resulted in the increase of color intensity and stability. The laundering fastness of dyed fabrics was good from grade 5 to grade 3-4. Because of the anthocyanins sensitivity on light radiation, the light fastness of dyed fabrics was poor from grade 3 to grade 1-2.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.47 no.5
• /
• pp.120-126
• /
• 2015

In this study, we used various dyes from natural pigments such as tumeric, goldthread, indigo, pagoda tree flower, sappanwood, and safflower to make the Hanji wallpaper with super eight colors of yellow, orange, green, turquoise, violet, red, blue, and magenta. As a result of measuring the lightfastness, magenta dyed with sappanwood showed the worst effect, but blue dyed with only indigo showed the best effect. In terms of the spot test by water, red wallpaper dyed with safflower showed the clear spot, but blue, turquoise, and green dyed with indigo resulted in a little spot. The orange, violet, and magenta dyed with goldthread and sappanwood showed antibacterial activity, and the turquoise, green, and blue also has a little antibacterial activity. However, yellow and red didn't show the some result as expected. In the experiment for efficiency of formaldehyde removal, all Hanji wallpapers dyed with natural pigments showed the significant removal effect of formaldehyde, especially turquoise and red were the highest.

• Journal of Conservation Science
• /
• v.31 no.4
• /
• pp.443-455
• /
• 2015

To verifying the stability of Natural pigments for Dancheong which is available on the market was carried out as light resistance and gas corrosion test. In this particular case, we will confirm the characteristics of the only pigments except of Dancheong technique and influence of substance. Medium using for coloring are animal glue and synthetic resin that widely used for Dancheong in currently. Selected to artificial light source is a xenon arc lamp, contaminated gas is nitrogen dioxide gas in experiment. Degree of degradation of pigment were compared by measuring the degree of color change. The result of light resistance test, mineral pigments were good; color is green and blue type, soil pigments also good; color is yellow ocher, white clay, red clay etc. Gamboge, unghwang, cinnabar, red lead were confirmed not good. The result of gas corrosion test, most of the natural pigments were good condition except the red lead. Generally, animal glue samples had better than a synthetic resin samples.

• Fashion & Textile Research Journal
• /
• v.11 no.2
• /
• pp.337-343
• /
• 2009

This study systematically investigated a method for extraction of safflower (Carthamus tinctorius Linnaeus) colorants by ultrasonic treatment. Compared to pigments productivity and cell wall structures of safflower after general and ultrasonic method, the ultrasonic method showed high extraction efficiency of safflower pigments due to destruction of safflower cell wall caused by high vibration energies. Microscopic analysis confirmed the hypothesis that the ultrasonic treatment of safflower caused its cell wall structure loosened and made efficient extraction of safflower pigments. And also, LC-MS/MS analysis revealed that productivities of the yellow and red safflower pigments by ultrasonic method were 21.9% and 14.6% higher, respectively, than those of pigments extracted by general method. The ultrasonic extracted yellow and red colorants could be used to dye not only natural fibers like cotton, silk and wool, but also synthetic fiber like nylon, and generally gave a better color tone than the general extracted colorants from safflower due to the affinities of red and yellow colorant on different fibers. As the yellow and red colorant were extracted by ultrasonic treatment in water, the K/S value on of 550/440nm of cotton and rayon was increased but in the case of silk and wool the change of this value was almost not detected. Finally, this technique might provide a solution to establish reproducibility and standardization for the extraction and dyeing methods on fabrics.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.14 no.6
• /
• pp.3102-3107
• /
• 2013

Inorganic pigments were prepared from $Al_2O_3$, CoO, $Cr_2O_3$, ZnO, $SrO_2$ and Kaolin. The pigment was prepared through the processes of mixing and crushing of the raw materials, sintering, milling and drying. The color of the pigments was changed from blue to green as $Cr_2O_3$ contents in the pigment increased. The color became brighter irrespective of the pigment composition as pigment particle size became smaller. Maximum sintering temperature was the most suitable at around $1,250^{\circ}C$. In the test of compatability between the pigment and glaze, the color became close to green as $Cr_2O_3$ contents in the pigment increased, and became close to blue as CoO contents increased.

• Korean Journal of Metals and Materials
• /
• v.49 no.5
• /
• pp.367-373
• /
• 2011

This paper studies the experimental method that uses the homogeneous precipitation method to prepare mica flakes coated with anatase-type titania pearlescent pigment with urea as precipitant. The optimum technology parameters, the chemical composition, the microstructure, and the color property of resulting pigments are discussed. The coating principle of mica coated titania with various coating thickness is analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy(TEM) and tested by spectrophotometer analysis. The colored nanocrystalline pigments with different morphology and coating thickness 45-170 nm were prepared by homogeneous precipitation treatment of $TiOSO_4$(titanum oxysulfate) aqueous solutions. Characterizations on the pigments show that the pearlescent effects of the pigments depend mainly on mica size, thickness of the metal oxide deposit, its chemical composition, and crystal structure.

• Journal of the Korean Ceramic Society
• /
• v.47 no.6
• /
• pp.608-612
• /
• 2010

Uvarovite Garnet is green pigment prepared by using $Cr_2O_3$, CaO and $SiO_2$ which are widely used in ceramic industry. The synthesis of above pigment was carried out by mixing $K_2Cr_2O_7$, $SiO_2$ and $CaCO_3$ as formulated and then firing at $1000{\sim}1200^{\circ}C$. To investigate the optimum synthesis condition of the Uvarovite Garnet. it was prepared by using CaO to replace $CaCO_3$, $CaF_2$ and $CaCl_2$. To get green brighter color, $Al^{3+}$ was substituted for $Cr^{3+}$. They were characterized by X-ray diffraction, UV-Vis spectroscopy, Raman spectroscopy and SEM analysis. When the pigments were applied to lime glazes (6 wt%), color parameters of Uvarovite Garnet showed the $L^*$=40.99, $a^*$=-16.23 and $b^*$=17.04.

• Korean Journal of Materials Research
• /
• v.24 no.1
• /
• pp.43-47
• /
• 2014

NiO-doped hibonite pigments were synthesized by the solid state method to get stabilized blue color pigment in both oxidation and reduction atmospheres. Optimum substitution condition with NiO for hibonite blue pigment was investigated. Experimental results were comparable to those of previous cobalt-minimization studies performed with other phosphate- or oxide-based cobalt-containing ceramic pigments (having olivine ($Co_2SiO_4$), spinel ($CoAl_2O_4$), or with co-doped willemite ($(Co,Zn)_2SiO_4$) structures). Composition was designed varying the NiO molar ratio increasing with $SnO_2$. The optimum substitution content is 0.93 mole NiO with 0.75mole $SnO_2$. The characteristics of the synthesized pigment were analyzed by XRD, Raman spectroscopy, SEM, and UV-vis. Synthesized pigment was applied to a lime-barium glaze with 10 wt% each and fired at an oxidation atmosphere of $1250^{\circ}C/1h$ and a reducing atmosphere $1240^{\circ}C/1h$. Blue color was obtained with $L^*a^*b^*$ values at 43.39, -6.78, -18.20 under a reducing atmosphere and 41.66, -6.36, -14.7 under and oxidation atmosphere, respectively.

• Journal of the Korean Ceramic Society
• /
• v.45 no.5
• /
• pp.268-275
• /
• 2008

In high temperature ceramic glazes, a stable range of pink-red colors producing $Cr_2O_3-SnO_2-CaO-SiO_2$ pigments are factored by Cassiterite and Malayaite relationship with $Cr_2O_3$. The experiment described the effect of $CrCl_3$ by adding $H_3BO_3$ as a mineralizer to increase the formation of Malayaite crystal, substituting $CrCl_3$ instead of $Cr_2O_3$ in pigment as a chromophore. Synthesized pigments were analyzed by XRD, FT-IR, Raman Spectroscop, UV and UV-vis. The result shows the differences in amount of crystal phases and oxidation state of Cr ion, which causes the color change. The melting point of $CrCl_3$ is lower than $Cr_2O_3$ which act as a mineralizer and makes the pigment synthesized in lower temperature at $1200^{\circ}C$. Holding 3 h firing at $900^{\circ}C$ where the synthesize forms shows better effect of Malayaite crystal phases and increasing engaged effect of $CrCl_3$ where the color pigmentation is more defined then in $Cr_2O_3$.

• Journal of the Korean Ceramic Society
• /
• v.47 no.3
• /
• pp.249-255
• /
• 2010

To investigate optical properties of (V, Pr)-doped $ZrSiO_4$ green pigments, samples were prepared by the ceramic method using NaF and NaCl as mineralizers. They were characterized by X-ray diffraction, UV-Vis spectroscopy and Raman spectroscopy. The changes of color in the samples during heating and effect of mineralizers were studied in terms of valence of the vanadium and praseodymium in the zircon matrix. (V, Pr)-doped $ZrSiO_4$ pigments give rise to green coloration in $800^{\circ}C$. The oxidation state of V and Pr ions of pigments in the glazed samples were confirmed by UV-Vis absorption spectra. This absorption spectra showed three typical bands of trivalent Pr at the 445, 480~490, 592 nm due to f-f transitions and two broad bands of 302~380, 400~500 nm due to f-d transitions of tetravalent Pr. According to the increasing amounts of $Pr_6O_{11}$, the two broad bands showed decreasing intensity at 290, 640 nm due to d-d transitions of tetravalent V.