• Journal of Powder Materials
• /
• v.8 no.3
• /
• pp.151-156
• /
• 2001

MgO based nanocomposite powder including ferromagnetic iron particle dispersions, which can be available for the magnetic and catalytic applications, was fabricated by the spray pyrolysis process using ultra-sonic atomizer and reduction processes. Liquid source was prepared from iron (Fe)-nitrate, as a source of Fe nano-dispersion, and magnesium (Mg)-nitrate, as a source of MgO materials, with pure water solvent. After the chamber were heated to given temperatures (500~$^800{\circ}C$), the mist of liquid droplets generated by ultrasonic atomizer carried into the chamber by a carrier gas of air, and the ist was decomposed into Fe-oxide and MgO nano-powder. The obtained powders were reduced by hydrogen atmosphere at 600~$^800{\circ}C$. The reduction behavior was investigated by thermal gravity and hygrometry. After reduction, the aggregated sub-micron Fe/MgO powders were obtained, and each aggregated powder composed of nano-sized Fe/MgO materials. By the difference of the chamber temperature, the particle size of Fe and MgO was changed in a few 10 nm levels. Also, the nano-porous Fe-MgO sub-micron powders were obtained. Through this preparation process and the evaluation of phase and microstructure, it was concluded that the Fe/MgO nanocomposite powders with high surface area and the higher coercive force were successfully fabricated.

• Journal of Magnetics
• /
• v.18 no.4
• /
• pp.395-399
• /
• 2013

The metallic glass ribbons of $[(Fe_xCo_{1-x})_{0.75}B_{0.2}Si_{0.05}]_{96}Mo_4$ (x = 0, 0.3, 0.6, 0.9 at.%) and $[(Fe_xCo_{1-x})_{0.75}B_{0.2}Si_{0.05}]_{96}Nb_4$ (x = 0, 0.3, 0.6, 0.9 at.%) were obtained by melt spinning with 25-30 ${\mu}m$ thickness. The thermal stability, mechanical properties and magnetic properties of Fe-Co-B-Si based systems were investigated. The values of thermal stability were measured using differential scanning calorimetry (DSC), including glass transition temperature ($T_g$), crystallization temperature ($T_x$) and supercooled liquid region (${\Delta}T_x=T_x-T_g$). These amorphous ribbons were identified as fully amorphous, using X-ray diffraction (XRD). The mechanical properties of Febased samples were measured by nano-indentation. Magnetic properties of the amorphous ribbons were measured by a vibrating sample magnetometer (VSM). The amorphous ribbons of $[(Fe_xCo_{1-x})_{0.75}B_{0.2}Si_{0.05}]_{96}Mo_4$ (x = 0, 0.3, 0.6, 0.9 at.%) and $[(Fe_xCo_{1-x})_{0.75}B_{0.2}Si_{0.05}]_{96}Nb_4$ (x = 0, 0.3, 0.6, 0.9 at.%) exhibited soft magnetic properties with low coercive force ($H_c$) and high saturation magnetization (Ms).

• Journal of the Korean Magnetics Society
• /
• v.10 no.5
• /
• pp.191-195
• /
• 2000

With the object of developing a non-gap choke core, effects of annealing in oxygen atmosphere on magnetic properties for Fe$_{78}$Si$_{9}$B$_{13}$ amorphous alloy were investigated. After annealing for 2 hrs at 440 $^{\circ}C$, optimum magnetic properties for choke core were obtained, where the effective permeability was 180 and was almost constant up to several MHz, and the decrease in permeability upon large DC bias current of 12 A or DC bias magnetic field of 8,000 A/m was very little. Moreover the AC magnetic loss was very low as compared to the conventional choke cores. Upon the optimum annealing, the magnetic hysteresis loop was inclined accompanying the increase of coercive force and the appearance of fine crystallites of $\alpha$-Fe phase. The good choke core properties was considered to be due to the suppression of domain boundary motion and domain refinement by the crystallites.

• Journal of the Korean Magnetics Society
• /
• v.8 no.2
• /
• pp.62-66
• /
• 1998

We have studied on the magnetic properties of the specimen with additives Bi$_2$O$_3$and$V_2O_5$ that sintered at 900 $^{\circ}C$ for 4 hours for sybthesizing optimal Ni-Zn-Cu ferrite. Curie temperature rises from 240 $^{\circ}C$ to 270 $^{\circ}C$ as Ni contents increase. Magentic maximum induction$(B_m)$ increases from 2650 G to 3300 G, 3500 G in the specimens with $V_2O_5$ and Bi$_2$O$_3$resectively. On the contrary coercive force $(H_c)$ lowers to 2.05 Oe~1.05 Oe. Permeability all increase in the specimen with additives. In the specimen with additive Bi$_2$O$_3$, we have obtained the low relative loss factor of $6.3{\times}10^{-5}~7.84{\times}10^{-5}$ in the range of 1MHz due to increase of resistivity in grain boundary. In the specimen with additive $V_2O_5$ in spite of increase permeability relative loss factor increase of due to decrease of Q-value.

• Journal of the Korean Magnetics Society
• /
• v.18 no.1
• /
• pp.14-18
• /
• 2008

Bismuth-substituted yttrium iron garnet(Bi:YIG) films, which show excellent magnetic and magneto-optical properties as well as low optical losses by optimizing their deposition and post-annealing condition, have been attracting great attention in optical device research area. In this study, the Bi:YIG thick films were deposited with the aerosol deposition method for the final purpose of applying them to optical isolators. Since the aerosol deposition is based on the impact adhesion of sub-micrometer particles accelerated by a carrier gas to a substrate, the flow rate of carrier gas, which is in proportion to mechanically collision energy, should be treated as an important parameter. The Bi:YIG($Bi_{0.5}Y_{2.5}Fe_5O_{12}$) particles with $100{\sim}500$ nm in average diameter were carried and accelerated by nitrogen gas with the flow rate of 0.5 l/min${\sim}$10 l/min. The coercive force decreased from 51 Oe to 37 Oe exponentially with increasing gas flow rate. This is presumably due to the fact that the optimal collision energy results in reduction of impurity and pore, which makes the film to be soft magnetically. The saturation magnetization decreased due to crystallographical distortion of the film with increasing gas flow rate.

• Journal of the Korean Magnetics Society
• /
• v.2 no.2
• /
• pp.91-98
• /
• 1992

In a $Co_{67}Fe_{4.5}Nb_{2}Si_{10}B_{15}$ amorphous alloy ribbon the effect to two-step annealing on the soft magnetic properties has been studied. By two-step annealing method which the second annealing at low temperature of $310^{\circ}C$ for 2 hours is undertaken after the primary annealing at high temperature above $480^{\circ}C$ for 20 minutes at the vacuum state, the coercive force and the squareness are not changed nearly but the initial permeability at d.c. and the effective permeability at a.c. are remark-ably increased compared with the one-step annealing. The maxima of the initial permeability and the effective permeability at 1 kHz after the two-step annealing are 290,000 and 41,000, respectively, which are 30% higher than those of the one-step annealing. The change of magnetic properties with annealing temperature is discussed in terms of the residual stress, the domain size, the cluster and the crystalline phase.

• Journal of Magnetics
• /
• v.2 no.3
• /
• pp.76-85
• /
• 1997

Magnetic and magnetostrictive properties of Tb-Fe and Tb-Fe-B thin films are systematically investigated over a wide composition range from 40.2 to 68.1 at. % Tb. The films were fabricated by rf magnetron sputtering using a composite target which consists of an Fe plate and Tb chips. The microstructure, examined by X-ray diffraction, mainly consists of an amorphous phase and, at high Tb contents, a pure Tb phase also exists. A progressive change in the direction of anisotropy from the perpendicular to in-plane occurs as the Tb content increases and the boundary at which the anisotropy change occurs shifts significantly towards to higher Tb contents with the addition of B. The saturation magnetization exhibits maxima at the Tb contents of 42 and 48 at. % for Tb-Fe and Tb-Fe-B thin films, respectively, and it is decreased by the addition of B. The coercive force, measured in the easy direction, decreases monotonically with the Tb content. Excellent magnetostrictive characteristics, particularly at low magnetic fields, are achieved in both Tb-Fe and Tb-Fe-B thin films; for example, a magnetostriction of 138 ppm is obtained in a Tb-Fe-B thin film at a magnetic field as low as 30 Oe. The excellent magnetostrictive properties of the present thin films are supported by the equally excellent magnetic softness, the coercivity below 10 Oe and a typical squared-loop shape with the saturation field as low as 1 kOe. Due to the excellent low field magnetostrictive characteristics, the present Tb-Fe based thin films are thought to be suitable for Si based microdevices.

• Journal of the Korean Magnetics Society
• /
• v.13 no.5
• /
• pp.198-203
• /
• 2003

To investigate whether the use of hard magnetic film is available to generate bias magnetic field for a magnetoimpedance sensor, the magnetic properties of SmCo hard magnetic films were investigated as a function of their compositions. The saturation magnetization decreased with Sm content increasing in SmCo films. And, the coercive force increased in the extent of Sm content of 28 at%, but decreased as Sm content increased moreover. The bias field effect of SmCo film to amorphous CoZrNb film was investigated with the magnetization corves, permeabilities, and magnetic domain structures of SmCo/CoZrNb multilayers. The bias field of about 60 Oe was observed in the film with 3 mm ${\times}$ 0.5 mm, which can be constructed as a MI sensor, and this result strongly indicates that the bias field generated from a hard magnetic film is adequate to enhance the sensitivity of a MI sensor with hard/soft magnetic multilayer structure.

• Journal of the Korean Magnetics Society
• /
• v.27 no.1
• /
• pp.23-29
• /
• 2017

In this study, the influences of magnetization reversal and magnetic interaction on the coercivity of Sr-ferrite particles with different sizes were investigated through various magnetic measurements. The shape of the initial magnetization curve and the magnetic field dependence of the coercive force indicate that the magnetization reversal changes from domain nucleation to wall pinning as the particle size decreases. On the other hand, the Henkel plot, interaction field factor and ${\Delta}M(H)$ obtained from the DCD and IRM curves show that the strength of the dipolar interaction is increased with increasing the particle size. Therefore, it can be concluded that coercivity is closely related to magnetic interaction as well as magnetization reversal mechanism.

• Journal of the Korean Magnetics Society
• /
• v.8 no.5
• /
• pp.255-260
• /
• 1998

Fabrication condition and magnetic properties of ultrathin Co-based amorphous alloy have been investigated. When the ejection gas pressure was lower than 0.05 kgf/$\textrm{cm}^2$ at the roll speed of 55 m/s, ultrathin ribbons with the thickness less than 10 ${\mu}{\textrm}{m}$ were successfully obtained. The ribbon thickness decreased linearly with the decrease in ejection pressure. Moreover the significant decrease in ribbon width was accompanied with the decrease of thickness in the range of ejection pressure to form an ultrathin ribbon. This behavior was attributed to the decrease of effective ejection pressure in the both end-sides of rectangular nozzle due to the larger friction between molten metal and nozzle wall. The effective permeability at low frequency (1 kHz) decreased largely with the decrease in ribbon thickness, while the coercive force increased with the thickness decrease. It was considered that these behaviors were due to the enhancement of surface effect leading to the suppression of wall motion. However effective permeability at high frequency (1 MHz) increased with the decrease in ribbon thickness, and this was ascribed to the easier magnetization rotation owing to the reduction of eddy current.