• Archives of Metallurgy and Materials
• /
• v.67 no.4
• /
• pp.1521-1524
• /
• 2022

Fe-Cr-B-based metamorphic alloy coating layers were manufactured by plasma spray with a Fe-Cr-B-Mo-Nb composition (hereinafter, M+) powder. The microstructure and wear properties of the coating layers were investigated and compared with a metamorphic alloy coating layer fabricated with commercial M material. XRD analysis revealed that the M and M+ coating layers were composed of α-Fe, (Cr, Fe)₂B, and some metallic glass phases. Wear test results showed that M+ coating layers had a superior wear resistance which had 1.48 times lower wear volume than M coating layers. Observations of the worn-out surfaces and cross-sections of the coating layers showed that M+ coating layer had relatively low oxides along the particle boundaries and it suppress a delamination behavior by the oxides.

• Journal of Ocean Engineering and Technology
• /
• v.25 no.6
• /
• pp.56-59
• /
• 2011

The demand for cold rolled steel (CR) for structural members is gradually increasing. If no surface treatment (coating for corrosion resistance) for CR is conducted, its use is very limited because CR is vulnerable to corrosion. Therefore, we need to develop a coating solution to provide high corrosion resistance for CR. In this study, an organic/inorganic coating solution with Si and Ti (Si polysilicate 7 wt.% + Urethane 13 wt.% + Ti amorphous 0.5 wt.%; LR-0727(1)) was used to evaluate the corrosion resistance of CR under a salt spray test. The specimens with the LR-0727(1) coating were heat treated in a drying oven at $120{\sim}210^{\circ}C$for 5 min. The corrosion resistance was investigated using a salt spray test of 7 h. In addition, an adhesive test was conducted. Rust showed under a heat treatment of $150^{\circ}C$, but no vestiges were found over $160^{\circ}C$. The specimens with heat treatment at $160^{\circ}C$ or more did not experience delamination. From these results, it is considered that the temperature limit for optimum heat treatment is $160^{\circ}C$ considering energy efficiency.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2004.11a
• /
• pp.75-78
• /
• 2004

Engine power cylinder parts are faced with more severe wear and friction environment. For instance, emission gas recirculation (EGR), one of the most valid technologies related to emission legislation, is known to accelerate wear of piston ring and cylinder liner. Therefore, advanced materials and surface treatments have been developed and adopted successively so that a need exists for an accurate and repeatable friction and wear bench test for various combination of piston ring and cylinder liner that more closely relates to engine test result. This paper introduces accelerative bench wear test method for piston ring and cylinder liner, presents the experimental result of friction and wear properties of piston ring surface treatments that noticed in substitution for hard chrome plating.

• The Journal of Advanced Prosthodontics
• /
• v.9 no.2
• /
• pp.130-137
• /
• 2017

PURPOSE. The purpose of this study was to evaluate the effect of nano-structured alumina surface coating on shear bond strength between Y-TZP ceramic and various dual-cured resin cements. MATERIALS AND METHODS. A total of 90 disk-shaped zirconia specimens (HASS CO., Gangneung, Korea) were divided into three groups by surface treatment method: (1) airborne particle abrasion, (2) tribochemicalsilica coating, and (3) nano-structured alumina coating. Each group was categorized into three subgroups of ten specimens and bonded with three different types of dual-cured resin cements. After thermocycling, shear bond strength was measured and failure modes were observed through FE-SEM. Two-way ANOVA and the Tukey's HSD test were performed to determine the effects of surface treatment method and type of cement on bond strength (P<.05). To confirm the correlation of surface treatment and failure mode, the Chi-square test was used. RESULTS. Groups treated with the nano-structured alumina coating showed significantly higher shear bond strength compared to other groups treated with airborne particle abrasion or tribochemical silica coating. Clearfil SA Luting showed a significantly higher shear bond strength compared to RelyX ARC and RelyX Unicem. The cohesive failure mode was observed to be dominant in the groups treated with nano-structured alumina coating, while the adhesive failure mode was prevalent in the groups treated with either airborne particle abrasion or tribochemical silica coating. CONCLUSION. Nano-structured alumina coating is an effective zirconia surface treatment method for enhancing the bond strength between Y-TZP ceramic and various dual-cured resin cements.

• Journal of the Society of Naval Architects of Korea
• /
• v.56 no.6
• /
• pp.532-540
• /
• 2019

This study describes a test method for evaluating the ice friction and abrasion performance of polar coatings. The evaluation methods of physical properties of general coatings for ocean-going vessels and polar coatings for ice-going vessels were investigated and their limitations were analyzed. We have also reviewed previous researches related to the development of polar paints and confirmed the necessity of developing test techniques. A flat steel plate was coated with several types of commercial coating, and cold model ice was used to cause ice friction and abrasion events between coated surface and ice. For evaluation of ice friction and abrasion performances, test procedures such as measurement of coating surface roughness, measurement of frictional force using model ice, implementation of ice abrasion and drying of coating surface were developed. The friction and abrasion characteristics of each coating are analyzed and summarized through the change of friction force and roughness data according to the progress of ice abrasion.

• The Journal of Advanced Prosthodontics
• /
• v.12 no.3
• /
• pp.157-166
• /
• 2020

PURPOSE. The aim of this study was to evaluate the clinical performance and reliability of plasma sprayed nanostructured zirconia (NSZ) coating. MATERIALS AND METHODS. This study consisted of three areas of analysis: (1) Mechanical property: surface roughness of NSZ coating and bond strength between NSZ coating and titanium specimens were measured, and the microstructure of bonding interface was also observed by scanning election microscope (SEM). (2) Biocompatibility: hemolysis tests, cell proliferation tests, and rat subcutaneous implant test were conducted to evaluate the biocompatibility of NSZ coating. (3) Mechanical compatibility: fracture and artificial aging tests were performed to measure the mechanical compatibility of NSZ-coated titanium abutments. RESULTS. In the mechanical study, 400 ㎛ thick NSZ coatings had the highest bond strength (71.22 ± 1.02 MPa), and a compact transition layer could be observed. In addition, NSZ coating showed excellent biocompatibility in both hemolysis tests and cell proliferation tests. In subcutaneous implant test, NSZ-coated plates showed similar inflammation elimination and fibrous tissue formation processes with that of titanium specimens. Regarding fatigue tests, all NSZ-coated abutments survived in the five-year fatigue test and showed sufficient fracture strength (407.65-663.7 N) for incisor teeth. CONCLUSION. In this study, the plasmasprayed NSZ-coated titanium abutments presented sufficient fracture strength and biocompatibility, and it was demonstrated that plasma spray was a reliable method to prepare high-quality zirconia coating.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.16 no.6
• /
• pp.273-277
• /
• 2006

High velocity of oxy-fuel (HVOF) thermal spray coating is progressively replacing the other classical hard coatings such as chrome plating and ceramic coating by the classical methods, since the very toxic $Cr^{6+}$ ion is well known as carcinogen causing lung cancer, and the ceramic coatings are brittle. Co-alloy T800 powder is coated on the Inconel 718 substrates by the HVOF coating procesess developed by this laboratory. For the study of the possibility of replacing of chrome plating, the wear properties of HVOF Co-alloy T800 coatings are investigated using the reciprocating sliding tester with a counter sliding SUS 304 ball both at room and at an elevated temperature of $1000^{\circ}F\;(538^{\circ}C)$. The possibility as durability improvement coating is studied for the application to the high speed spindles vulnerable to frictional heat and wear. Wear mechanisms at the reciprocating sliding wear test are studied far the application to the systems similar to the sliding test such as high speed spindles. Wear debris and frictional coefficients of T800 coatings both at room and at an elevated temperature of $538^{\circ}C$ are drastically reduced compared to those of non-coated surface of Inconel 718 substrates. Wear traces and friction coefficients of both coated and non-coated surfaces are drastically reduced at a high temperature of $538^{\circ}C$ compared with those at room temperature. These show that the coating is highly recommendable far the durability Improvement coating on the surfaces vulnerable to frictional heat and wear.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1999.04a
• /
• pp.433-436
• /
• 1999

Long-term durability of the reinforced concrete structures exposed to marine environment deteriorates seriously by the attack of the chloride ion from see water results in corrosion of steel reinforcement in concrete. Their coating effect is aluminum oxide-isocyanate-based coating material, resistance of chloride penetration, carbonation and freezing and thawing resistance were compared to acryl-based coating material and sealer type o waterproofing material. Aluminum oxide-isocyante-based and acryl-based coating material show higher resistance to chloride penetration and carbonation than the sealer type do waterproofing material and aluminum oxide-isocyanate-based coating resist about 99% of chloride penetration. Resultants to the accelerated test for freezing and thawing, coating concrete show higher resistance than non-coating concrete, respectively.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1996.11a
• /
• pp.171-173
• /
• 1996

Ag coating on the textured YBCO was prepared by means of a Ag$_2$O brushed coating method. The contact between Ag coating and textured YBCO was examined by sharp knife cut and by the observation of SEM. The critical current densities of different textured YBCO samples, which included YBCO with and without Ag coating, and YBCO with Ag coating after hot moist text, were compared. The Ag coating does not influence the oxygen absorption of textured YBCO, but Ag coating can protect YBCO well from moisture and $CO_2$

• Journal of Surface Science and Engineering
• /
• v.35 no.6
• /
• pp.408-414
• /
• 2002

TiN and TiAlN coating layer were deposited on WC-Co steel substrates by an arc ion plating(AIP) technique. The crystallinity and morphology for the deposited coating layers were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The impact behaviors of the deposited TiN and TiAlN coating layer were investigated with a ball-on-plate impact tester. Beyond $10^2$ impact cycle, TiAlN coating layer showed superior impact wear resistance compared to TiN coating layer. On the other hand, both TiN and TiAlN coating layers started to be partially failed between $10^2$ and $10^3$ impact cycle. Above $10^3$ impact cycle, TiN and TiAlN coating layers showed similar impact behavior because of the substrate effect.