• 한국세라믹학회지
• /
• 제40권12호
• /
• pp.1154-1158
• /
• 2003

Hydrothermal deposition of hydroxyapatite coatings on $Al_2$O$_3$ substrates was studied using aqueous solutions of Ca(NO$_3$)$_2$ㆍ4$H_2O$ and (NH$_4$)$_2$HPO$_4$ containing EDTA disodium salt as a chelating agent for $Ca^{2+}$. For the precipitation of the coatings the EDTA-Ca$^{2+}$ chelates were dissociated thermally at 20$0^{\circ}C$ or decomposed by oxidation with $H_2O$$_2$ at 9$0^{\circ}C$. Scanning electron microscopy and X-ray diffraction were used to investigate the deposition behavior and the phase of the coatings. Hydroxyapatite coatings were not deposited with the thermal dissociation method, whereas uniform deposition of the coatings (about 0.7 $\mu\textrm{m}$ thickness) was obtained with the oxidative decomposition method. The coatings consisted of fine rod-like hydroxyapatite crystals (hexagonal structure) with 60-80 nm diameters, having some preferred orientation with their length (i.e., the c axis) perpendicular to the substrate.ate.

• 한국환경과학회:학술대회논문집
• /
• 한국환경과학회 2003년도 International Symposium on Clean Environment
• /
• pp.103-108
• /
• 2003

A method to determine chromium(III) ion in aqueous solution by chemiluminescence method using a lucigenin entrapped silica sol-gel film has been studied. An optical probe for chromium(III) ion has been prepared by entrapping lucigenin into silica sol-gel film coated on a glass support by dip coating. The chromium(III) optical sensor is based on the catalytic effect of chromium(IIII) ion on the reaction between lucigenin and hydrogen peroxide in basic solutions. The effects of Nafion, DMF and Triton X-100 were investigated to find the optimum condition to minimize cracking and leaching from the probe. The effects of pH and concentrations of lucigenin and hydrogen peroxide on the chemiluminescence intensity were investigated. The chemiluminescence intensity was increased linearly with increasing chromium(III) concentration from $2.5{\times}10^{-4}$M to $8.0{\times}10^{-7}$M and the detection limit was $4.0{\times}10^{-7}$M.

• 한국레이저가공학회지
• /
• 제14권1호
• /
• pp.19-24
• /
• 2011

This work reports the results for laser shock peening of duplex stainless steel (22% Chromium - 5% Nickel) using a pulsed Nd:YAG laser (wavelength = 532nm, pulse width = 8ns). for the application to high-capacity pumps for seawater desalination plants. By properly selecting the process parameters such as laser intensity of 10GW/$cm^2$, laser pulse density of 75pulse/$mm^2$, and $100{\mu}m$ thick aluminum foil as an absorbent coating layer, the surface hardness of duplex stainless steel could be enhanced by 26%, from 256HV to 323HV with little changes in surface morphology and roughness. The depth of laser shock peened layer was measured to be around 2mm. The large enhancement of surface hardness is considered to have high practical importance in minimizing abrasive and corrosive deterioration of pump parts.

• Mass Spectrometry Letters
• /
• 제2권2호
• /
• pp.53-56
• /
• 2011

[ $C_8$ ]functionalized magnetic nanoparticles were synthesized by coating magnetic $Fe_3O_4$ nanoparticles with silicaamine groups using 3-aminopropyltriethoxysilane and by subsequently modifying the amine groups with chloro(dimethyl)octylsilane to produce octyl groups on the surface of the MNPs. The $C_8$-functionalized MNPs were used to enrich peptides from tryptic protein digests of myoglobin and ${\alpha}$-casein. The enriched peptides were analyzed by matrix-assisted laser desorption/ionization time-of-flight mass spectrometry (MALDI-TOF-MS). MALDI-MS was also used to investigate desalting of the $C_8$-functionalized MNPs. Sample solutions were prepared in 1.0 M NaCl, and the successful removal of salt was observed. Enrichment with $C_8$-functionalized MNPs was very effective for separating and concentrating tryptic peptides.

• 한국재료학회지
• /
• 제14권6호
• /
• pp.443-450
• /
• 2004

Parylene polymer thin film shows excellent homogeneous coverage chracteristics when it was deposited onto very complex three dimensional solid matters, such as deep hole and micro crack. The parylene deposition process can be conducted at room temperature although most of chemical vapor deposition processes request relatively high processing temperature. Therefore, the parylene coating process does not induce any thermal problems. Parylene thin film is transparent and has extremly high chemical stability. For example, it shows high chemical stability with high reactive chemical solutions such as strong acid, strong alkali and acetone. The bio-stability of this material gives good chances to use for a packaging of biomedical devices and electronic devices such as display. In this review article, principle of deposition process, properties and application fields of parylene polymer thin film are introduced.

• 한국염색가공학회지
• /
• 제25권4호
• /
• pp.292-302
• /
• 2013

Cotton fabrics treated with hybrid materials were developed and prepared. A halogen-free flame retardant and an aromatic amide were blended and applied to cotton fabrics. Thermal and physical properties of the treated cotton fabrics were investigated. The surface of the pure and coated cotton fabrics was characterized by Fourier transform infrared spectroscopy. The elemental composition of the coated surface of the cotton fabric was measured using X-ray photoelectron spectroscopy and compared with that of pure cotton fabric. After being solved in N,N-dimethylacetamide, m-aramid and triphenylphosphine oxide (TPP) were applied to cotton fabrics through a dip-pad-coagulation process. The treated cotton fabrics with recycled m-aramid/TPP resulted in increased limited oxygen index values and thermal resistance.

• 센서학회지
• /
• 제13권3호
• /
• pp.169-174
• /
• 2004

A fiber optic pH sensor has been fabricated using nile blue entrapped in an ammonia catalyzed silica sol-gel film coated on glass substrate by dip-coating. The sensor was fixed on the end of an optical fiber. The sensor showed pH sensitivity when dipped into liquids at different pHs. Linear and reproducible responses were obtained in standard buffer solutions in the pH range $6.0{\sim}8.5$, which encompasses the clinically-relevant range. The effects of interferences on the determination of pH were also investigated. The sensors were successfully applied to the determination of pH in different commercial ionic drinks.

• 대한전기학회논문지:전기물성ㆍ응용부문C
• /
• 제49권2호
• /
• pp.98-102
• /
• 2000

Ferroelectric PZT heterolayered thin films were fabricated by spin coating method on the Pt/Ti/SiO2/Si substrate using PZT(10/90) and PZT(90/10) m7etal alkoxide solutions. All PZT heterolayered films showed a homogeneous grain structures without presence of rosette structure. It can be assumed that the lower PZT layers played a role of nucleation site for the formation of the upper PZT layer. Pb-deficient PZT phase was formed at PZT/Pt interface due to the diffusion of Pb element into a Pt bottom electrode. The relative dielectric constant and the dielectric loss of the PZT-6 film were 567 and 3.6%, respectively. Increasing the number of coatings, remanent polarization and coercive field were decreased and the values of the PZT-6 heterolayered film were $7.18\muC/cm^2$ and 68.5kV/cm, respectively. Leakage current densities were increased with increasing the number of coatings, and the value of the PZT-4 film was about $7\times10-8A/cm^2$ at 0.05MV/cm.

• 한국전기전자재료학회논문지
• /
• 제13권8호
• /
• pp.694-699
• /
• 2000

S $r_{0.9}$/B $i_{2.1}$/T $a_{2}$/ $O_{9}$ solutions was synthesized by MOD (metalorganic decomposition) method. SBT thin films with 2000$\AA$ thickness were prepared on Ir $O_2$/ $SiO_2$/Si and Pt/Ti/ $SiO_2$/Si substrates using the spin coating process and then investigated the dielectric and electrical properties of them. In the case of using Ir $O_2$bottom electrode the hysteresis loop was saturated at lower temperature than Pt/Ti electrode but the breakdown phenomenon was occurred at low voltage because of the rough surface morphology and porous microstructure of SBT thin films. As the results of the fatigue and imprint characteristics related to the lifetime and reliability of devices after 10$^{10}$ cycles the fatigue rates were about 10% at the Ir $O_2$and Pt/Ti bottom electrodes. Both SBT thin films with Ir $O_2$ and with Pt/Ti bottom electrodes show a slight tendency to imprint after 10$^{9}$ cycles but do not lead to a failure.e.e.

• Corrosion Science and Technology
• /
• 제17권4호
• /
• pp.193-201
• /
• 2018

In order to suppress $CO_2$ emission and protect passengers in case of vehicle collision, continuous efforts are being made to increase the application ratio and tensile strength of advanced high strength steels used in the manufacturing of automotive body. Simultaneously, hydrogen embrittlement which was not a concern in the past has currently become a major issue due to microstructure that is sensitive to hydrogen uptake. The sensitivity increases with residual stress and hydrogen uptake content. Many automotive OEM companies and mill makers are setting specifications to control hydrogen embrittlement. The factors which lead to hydrogen embrittlement are material sensitivity, residual stress, and hydrogen concentration; researches are in progress to develop countermeasures. To reduce material sensitivity, mill makers add high energy trap elements or microstructure refinement elements. Automotive OEM companies design the car parts not to concentrate local stress. And they manage the levels to not to exceed critical hydrogen concentration. In this article, we have reviewed hydrogen embrittlement evaluation methods and corresponding solutions that are being studied in automobile manufacturing industries and mill makers.