• International Journal of Highway Engineering
• /
• v.8 no.3 s.29
• /
• pp.39-48
• /
• 2006

A laboratory investigation was conducted wherein smooth, rounded, siliceous river gravel aggregates were coated with fine-grained polyethylene, carpet co-product, or cement + styrene butadiene rubber latex and used to prepare hot mix asphalt concrete specimens. Only the coarse (+ No.4) aggregates were coated. The concept was that the coatings would enhance surface roughness of the aggregates and, thus, produce asphalt mixtures with superior engineering properties. Hot mix asphalt specimens were prepared and evaluated using several standard and non-standard test procedures. Based on experiences during the coating processes and analyses of these limited test results, the following was concluded: All three aggregate coating materials increased Hveem and Marshall stability, tensile strength, and resilient modulus(stiffness). These findings are indicative of improved resistance to rutting and cracking in hot mix asphalt pavements prepared using coated gravel aggregates in comparison to similar uncoated gravel aggregates.

• Progress in Superconductivity
• /
• v.9 no.2
• /
• pp.167-172
• /
• 2008

We fabricated $YBa_2Cu_3O_{7-x}$(YBCO) films on (00l) $LaAlO_3$ substrates prepared by metal organic deposition(MOD) method using trifluoroacetate(TFA) solution. The films with various thicknesses were prepared by repeating the dip-coating and calcining processes. The effects of film thickness on phase formation, microstructures, and critical properties were evaluated by X-ray diffraction, scanning electron microscopy, and transmission electron microscopy. The microstructure and resultant critical current($I_C$) and critical current density($J_C$) varied remarkably with film thickness: The ($I_C$) value increased from 39 to 160 A/cm-width as the number of coatings increased from one to four, while the corresponding $J_C$ was measured to be in the range of $0.84-1.21\;MA/cm^2$. Both the $I_C$ and $J_C$ decreased when an additional coating was applied due to microstructural degradation, indicating that the optimum thickness is in the range of $1.1-1.8\;{\mu}m$. The possible cause for the decrease in the $I_C$ and $J_C$ value for film thicker than $1.8\;{\mu}m$ include non-uniform thickness, increased surface roughness, and the poor formability of the YBCO phase and texture arising from the insufficient heat treatment time with respect to the increased thickness.

• Journal of Surface Science and Engineering
• /
• v.43 no.5
• /
• pp.238-242
• /
• 2010

In the present work, the influence of oxide on the Cr-Si-N coatings was investigated for the Cr-Si-O-N coatings on AISI 304 and Si wafer deposited by hybrid system, which combines the DC magnetron sputtering technique and arc ion plating (AIP) using Cr and Si target in an $Ar/N_2/O_2$ gaseous mixture. As the O content in the Cr-Si-N coatings increased, the diffraction patterns of the Cr-Si-O-N coatings showed CrN and $Cr_2O_3$ phases. However, as the O content increased to 28.8 at.%, diffraction peak of $Cr_2O_3$ was disappeared in the Cr-Si-O-N coating. The $d_{200}$ value was decreased with increasing of O content. The average grain size increased from about 40 nm to 65 nm as the O content increased. The maximum micro-hardness of the Cr-Si-O-N coating was obtained 4507 Hk at the O content of 24.8 at.%. The average friction coefficient of the Cr-Si-O-N coatings was gradually decreased by increasing the O content and the average friction coefficient decreased from 0.37 to 0.25 by increasing the O content. These results indicated that amorphous phase was increased in the Cr-Si-O-N coatings by increasing of O content.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2015.11a
• /
• pp.249-249
• /
• 2015

Silver films have been of considerable interest for years due to their better performance relative to other metal films for engineering applications. A series of multi-layer silver coatings with different thickness (i.e. 0.3 um to 1.5 um) were prepared on Aluminium substrate containing copper undercoat by direct current (DC) magnetron sputtering method. For the comparative purpose, similar thickness silver coatings were prepared by electrolytic deposition method. Microstructural, morphological, and mechanical characteristics of the silver coatings were evaluated by means of scanning electron microscope (SEM), X-ray diffraction (XRD), Surface roughness test, microhardness test and nano-scratch test. From the results, it has been elucidated that the silver films prepared by DC magnetron sputtering method has superior properties in comparison to the wet coating method. On the other hand, DC magnetron sputtering method is relatively easier, faster, eco-friendly and more productive than the electrolytic deposition method that uses several kinds of hazardous chemicals for bath formulation. Therefore, a New Work Item Proposal (NWIP) for the test methods standardization of DC magnetron sputtered silver coatings has recently been proposed via KATS, Korea and a NP ballot is being progressed within a technical committee "ISO/TC107-metallic and other inorganic coating".

• Journal of Surface Science and Engineering
• /
• v.42 no.3
• /
• pp.109-115
• /
• 2009

Magnesium is one of the lightest metals, and magnesium alloys have excellent physical and mechanical properties such as high stiffness/weight ratios, good castability, good vibration and shock absorption. However their poor corrosion resistance, wear resistance, hardness and so on, have limited their application. To improve these defects, many techniques are developed. Micro arc oxidation(MAO) is a one of the surface treatments under anodic oxidation in which ceramic coating is directly formed on the surface of magnesium alloy. In this study, the characteristics of anodic film were examined after coating the AZ31B magnesium alloy through the MAO process. MAO was carried out in potassium hydroxide, potassium fluoride, and various concentration of sodium silicate in electrolyte. The morphology and chemical composition of the coating layer were characterized by SEM, XRD, EPMA and EDS. The hardness of anodic films was measured by micro-vickers hardness tester. As a result, the morphology and composition of anodic film were changed by concentration of sodium silicate. Thickness and Si composition of anodic film was increased with increasing concentration of sodium silicate in electrolyte. The hardness of anodic film was highly increased when the concentration of sodium silicate was above 40 g/l in electrolyte.

• Korean Chemical Engineering Research
• /
• v.58 no.1
• /
• pp.36-43
• /
• 2020

A biliant stent was fabricated using a magnesium alloy wire, a biodegradable metal. In order to control the fast decomposition and corrosion of magnesium alloys in vivo, magnesium alloy wires were coated with biodegradable polymers such as polycaprolactone (PCL), poly(propylene carbonate) (PPC), poly (L-lactic acid) (PLLA), and poly (D, L-lactide-co-glycolide) (PLGA). In the case of PPC, which is a surface erosion polymer, there is no crack or peeling compared to other polymers (PCL, PLLA, and PLGA) that exhibit bulk erosion behavior. Also, the effect of biodegradable polymer coating on the axial force, which is the mechanical property of magnesium alloy stents, was investigated. Stents coated with most biodegradable polymers (PCL, PLLA, PLGA) increased axial forces compared to the uncoated stent, reducing the flexibility of the stent. However, the stent coated with PPC showed the axial force similar to uncoated stent, which did not reduce the flexibility. From the above results, PPC is considered to be the most efficient biodegradable polymer.

• Journal of the Korean Solar Energy Society
• /
• v.33 no.2
• /
• pp.11-17
• /
• 2013

Silicon nitride($SiN_x:H$) deposited by radio frequency plasma enhanced chemical vapor deposition(RF-PECVD) is commonly used for anti-reflection coating and passivation in crystalline silicon solar cell fabrication. In this paper, characteristics of the deposited silicon nitride was studied with change of working pressure, deposition temperature, gas ratio of $NH_3$ and $SiH_4$, and RF power during deposition. The deposition rate, refractive index and effective lifetime were analyzed. The (100) p-type silicon wafers with one-side polished, $660-690{\mu}m$, and resistivity $1-10{\Omega}{\cdot}cm$ were used. As a result, when the working pressure increased, the deposition rate of SiNx was increased while the effective life time for the $SiN_x$-deposited wafer was decreased. The result regarding deposition temperature, gas ratio and RF power changes would be explained in detail below. In this paper, the optimized condition in silicon nitride deposition for silicon solar cell was obtained as 1.0 Torr for the working pressure, $400^{\circ}C$ for deposition temperature, 500 W for RF power and 0.88 for $NH_3/SiH_4$ gas ratio. The silicon nitride layer deposited in this condition showed the effective life time of > $1400{\mu}s$ and the surface recombination rate of 25 cm/s. The crystalline silicon solar cell fabricated with this SiNx coating showed 18.1% conversion efficiency.

• Journal of Adhesion and Interface
• /
• v.6 no.3
• /
• pp.10-18
• /
• 2005

The hard coatings on the polycarbonate plate were performed with the object of substitution the glass in the car to the polycarbonate plate. In this research, tetraethyl orthosilicate (TEOS), methyltriethoxysilane (MTES) were used to prepare the coatings by sol-gel process. The optimum conditions and formulation to get the excellent physical properties were determined. The pretreatment condition of polycarbonate plate, the mole ratio of TEOS and MTES, selection of the solvent, the aging time, the amount of acid catalyst, and the number of folds of coating were characterized. Pretreatment with poly(methyl methacrylate) was very effective to increase the adhesion strength. The smooth coating which got the 2 H class in pencil hardness was formed in this research by sol-gel process.

• Macromolecular Research
• /
• v.16 no.8
• /
• pp.725-733
• /
• 2008

Polyimide (PI) multilayer thin films were prepared by spin-coating from a poly(amic acid) (PAA) and poly(amic acid) ammonium salt (PAAS). PI was prepared from pyromellitic dianhydride (PMDA) and 4,4'-oxydianiline (ODA) PAA. Different compositions of PAAS were prepared by incorporating triethylamine (TEA) into PMDA-ODA PAA in dimethylacetamide. PI multilayer thin films were spin-coated from PMDA-ODA PAA and PAAS. The PAAS comprising cationic and anionic moieties were spherical with a particle size of $20{\sim}40\;nm$. Some particles showed layers with ammonium salts, despite poor ordering. Too much salt obstructed the interaction between the polymer chains and caused phase separation. A small amount of salt did not affect the interactions of the interlayer structure but did interrupt the stacking between chains. Thermogravimetric analysis (TGA) showed that the average decomposition temperature of the thin films was $611^{\circ}C$. All the films showed almost single-step, thermal decomposition behavior. The nanostructure of the multilayer thin films was confirmed by X -ray reflectivity (XRR). The LF 43 film, which was prepared with a 4:3 molar ratio of PMDA and ODA, was comprised of uniformly spherical PAAS particles that influenced the nanostructure of the interlayer by increasing the interaction forces. This result was supported by the atomic force microscopy (AFM) data. It was concluded that the relationship between the uniformity of the PAAS particle shapes and the interaction between the layers affected the optical and thermal properties of PI layered films.

• The korean journal of orthodontics
• /
• v.46 no.3
• /
• pp.146-154
• /
• 2016

Objective: Different methods have been utilized to prevent enamel demineralization and other complications during orthodontic treatment. However, none of these methods can offer long-lasting and effective prevention of orthodontic complications or interventions after complications occur. Considering the photocatalytic effect of $TiO_2$ on organic compounds, we hoped to synthesize a novel bracket with a $TiO_2$ thin film to develop a photocatalytic antimicrobial effect. Methods: The sol-gel dip coating method was used to prepare $TiO_2$ thin films on ceramic bracket surfaces. Twenty groups of samples were composed according to the experimental parameters. Crystalline structure and surface morphology were characterized by X-ray diffraction and scanning electron microscopy, respectively; film thickness was examined with a surface ellipsometer. The photocatalytic properties under ultraviolet (UV) light irradiation were analyzed by evaluating the degradation ratio of methylene blue (MB) at a certain time. Antibacterial activities of selected thin films were also tested against Lactobacillus acidophilus and Candida albicans. Results: Films with 5 coating layers annealed at $700^{\circ}C$ showed the greatest photocatalytic activity in terms of MB decomposition under UV light irradiation. $TiO_2$ thin films with 5 coating layers annealed at $700^{\circ}C$ exhibited the greatest antimicrobial activity under UV-A light irradiation. Conclusions: These results provide promising guidance in prevention of demineralization by increasing antimicrobial activities of film coated brackets.