• 한국세라믹학회지
• /
• 제32권12호
• /
• pp.1401-1407
• /
• 1995

Zirconia powder coated with alumina was prepared by hydrolysis of alumina butoxide. The coated powder was obtained by a hydrolysis reaction between the adsorbed water on the surface of zirconia particles and aluminum sec-butoxide. Amorphous aluminum hydroxide was uniformly coated on the surface of zirconia particles with the thickness of about 30 nm. The shape and distribution of aluminum hydroxide was varied with an existence of surfactant. The coated layer of aluminum hydroxide consists of the fine particle size, and the zirconia powder coated by alumina hydroxide have the large specific surface area of 120 $m^2$/g, compared with that of starting zirconia powder.

• 한국분말재료학회지
• /
• 제21권3호
• /
• pp.191-195
• /
• 2014

This study reports a simple way of fabricating the porous Cu with unidirectional pore channels by freeze drying camphene slurry with Cu oxide coated Cu powders. The coated powders were prepared by calcination of ball-milled powder mixture of Cu and Cu-nitrate. Improved dispersion stability of camphene slurry could be achieved using the Cu oxide coated Cu powders instead of pure Cu powders. Pores in the frozen specimen at $-25^{\circ}C$ were generated by sublimation of the camphene during drying in air, and the green bodies were sintered at $750^{\circ}C$ for 1 h in $H_2$ atmosphere. XRD analysis revealed that the coated layer of Cu oxide was completely converted to Cu phase without any reaction phases by hydrogen heat treatment. The porous Cu specimen prepared from pure Cu powders showed partly large pores with unidirectional pore channels, but most of pores were randomly distributed. In contrast, large and aligned parallel pores to the camphene growth direction were clearly observed in the sample using Cu oxide coated Cu powders. Pore formation behavior depending on the initial powders was discussed based on the degree of powder rearrangement and dispersion stability in slurry.

• 한국정밀공학회지
• /
• 제32권9호
• /
• pp.765-771
• /
• 2015

In an Additive Manufacturing (AM) system emplying the Powder Bed Fusion (PBF) system, polyamide-12 powder is currently recognized as the general material used. The Polyamide-12 powder's properties include an average particle size of 58 $58{\mu}m$, a density of 0.59 g/cm3, and melting point of $184^{\circ}C$, and can also be to used coat materials for metal powder. For this reason, the sintering process is similar to the polymer powder and polymer coated metal powder process, except during the post-process. The polyamide-12 powder has some disadvantages such as its high cost and the fact that it can only be used for the provided equipment from the maker. Therefore, this study aims to perform the applicability of new material, polymer and polymer coated metal, to the PBF system.

• 한국세라믹학회지
• /
• 제35권7호
• /
• pp.653-658
• /
• 1998

Zirconia coated NiO powders were prepared by the thermal hydrolysis of $Zro(NO_3)_2$.$6H_2O$ in a mixed solvent of alcohol and water. Amorphous zirconium hydroxide was uniformly coated on the surface of NiO powder with the thickness of 20nm. The $ZrO_2$ coating layer was crystallized to tetragonal $ZrO_2$ with the size of 40-60nm at $900^{\circ}C$. The coated NiO powder containing 15 vol% $ZrO_2$ was found to have a similar isoelectric point to that of the $ZrO_2$ The grain growth inhibition effect of the coated powders was superior to the mechanically mixed powders.

• 약학회지
• /
• 제39권6호
• /
• pp.593-599
• /
• 1995

Erythromycin was formulated as enteric-coated pellets in order to reduce degradation in stomach and gastromtestmal irritation, and to maximize the absorption in intestine followmg its oral administration. Core pellets were prepared using fluid-bed granulator with two different methods (powder layering and solvent spraying) and enteric-coated with two different coating polymers (HPMCP and Eudragit E30D). Physical characteristics md dissolution rates of core pellets and enteric-coated pellets were evaluated to optimize the formulation. Powder layering method resulted in shorter initial dissolution time than solvent spraying method, but physicochmical properties of the product were worse than solvent spraying method with respect to hardness, ftiability and density. The dissolution rate of the drug was increased with the addition of surfactants, showing concentration-dependence. The scanning electron microscopic observation of pellets revealed significant differences on the surface appearances prepared with solvent spraying method. The core pellet made with powder layering method had crystals on the surface, which resulted in poor physical properties of the pellets. The dissolution profiles of erythromycin pellets coated with HPMCP or Eudragit L30D were close to that of commercially available erythromycin enteric-coated product.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.1097-1098
• /
• 2006

The Powder characteristics and sintering behavior of $SiO_2$ coated $BaTiO_3$ were studied. Silica coated $BaTiO_3$ powders were prepared by sol-gel method. The particle size of the $BaTiO_3$ powders were $\sim35$ nm and the thickness of the $SiO_2$ coating layer was $\sim5$ nm. As the $SiO_2$ content increased, the $SiO_2$ layers improved the powder dispersion. The Zeta potential of $SiO_2$ coated $BaTiO_3$ was getting close to that of pure silica with a more negative charge, compared with that of the uncoated $BaTiO_3$. The onset temperature of shrinkage curves shifted to higher temperatures with increasing $SiO_2$ contents

• 한국분말재료학회지
• /
• 제21권2호
• /
• pp.93-96
• /
• 2014

Cobalt coated tungsten carbide-cobalt composite powder has been prepared through wet chemical reduction method. The cobalt sulfate solution was converted to the cobalt chloride then the cobalt hydroxide. The tungsten carbide powders were added in to the cobalt hydroxide, the cobalt hydroxide was reduced and coated over tungsten carbide powder using hypo-phosphorous acid. Both the cobalt and the tungsten carbide phase peaks were evident in the tungsten carbide-cobalt composite powder by X-ray diffraction. The average particle size measured via scanning electron microscope, particle size analysis was around 380 nm and the thickness of coated cobalt was determined to be 30~40 nm by transmission electron microscopy.

• 한국분말재료학회지
• /
• 제1권1호
• /
• pp.27-34
• /
• 1994

Commercial pure iron powder and iron powder of coated 0.45% phosphorus were mixed with graphite powder in dry mixer to control carbon content from 0 wt% to 0.8 wt%. Mixed powder was pressed in the mould under the pressure of 510 MPa. Compacts were sintered at 118$0^{\circ}C$ for 40 min. in cracked ammonia gaseous atmosphere. Some of these sintered specimens were quenched in oil, and tempered in Ar gas. All of these specimens were investigated for microstructure, density and hardness in relation to coated phosphorus and carbon content. The results obtained were as follows: (1) The microstructure of the sintered speciments revealed that the amount of pearlite was increased with increasing C content but decreased by P-addition. (2) The P-addition affected the microstructure of pores in which the pore shape became round and its mean size was decreased by P-addition. (3) After tempering of sintered specimens the structure of pearlite was changed from fine structure to coarse one in P added specimen. (4) Hardness was higher in P added specimens.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2005년도 하계학술대회 논문집 Vol.6
• /
• pp.264-267
• /
• 2005

Soft magnetic iron powders have been coated with polyester or phenol resin. And the coated powder (soft magnetic composite) have been pressed into ring type core over the pressure of 870 MPa. Green density, magnetic flux density, permeability, core loss of the samples were measured to look at the effect of the coating materials and the amount of them. Green density is increased with the amount of coating materials and shows the maximum value, 6.5 $g/cm^3$ at 5 w/o, but decreased over it. And lowest value of the core loss is showed for the 5 w/o coated samples.

• 한국세라믹학회지
• /
• 제23권2호
• /
• pp.31-37
• /
• 1986

The effect of dehydration temperature on the reduction process of silica-coated hematite was invest-igated The particle shape and magnetic properties of the products reduced from hematite at various conditions and the oxidation resistance of silica-coated iron powder were examined. It was revealed that single phase iron powder obtained over 45$0^{\circ}C$ had good magnetic properties. The iron powder manufactured between 45$0^{\circ}C$ and 50$0^{\circ}C$ displayed the maximum coercive force as a result of maintaining its acicular shaped. However the coercive force of iron powder reduced over 50$0^{\circ}C$ was decreased. The oxidation resistance of silica-coated iron powder in air was very good up to 11$0^{\circ}C$ and for 12 days.