• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2015년도 추계학술대회 논문집
• /
• pp.189-189
• /
• 2015

In this study, the corrosion resistance and adhesion of electrophoretic paint (E-paint) were studied on AZ31 magnesium alloy pretreated in cerium chemical conversion coating solutions with the addition of various ethanol concentrations. It was found that with increasing ethanol concentration from 0 to 90 percent can decrease the formation of $Mg(OH)_2/MgO$ and increase the formation of nano-crystalline cerium oxides on the coating. Both corrosion resistance and adhesion of E-painted AZ31 increased with increasing ethanol concentration. The best E-paint sample was observed on the sample pretreatment in cerium chemical conversion coating solution with the addition of 80 percent of ethanol. This sample showed an excellent adhesion without paint detached after water immersion test for 500 h at $40^{\circ}C$, and only a few blisters observed at the near scratched sites after 1000 h salt-spray test.

• 한국표면공학회지
• /
• 제37권4호
• /
• pp.200-207
• /
• 2004

Molybdate chemical conversion coating layer formed on EGI has been studied in view of corrosion resistance, surface morphologies, and phases formed. It was found that coating layer consists of$ MoO_3$, $MoO_2$, Mo oxides having lower valences than 4 and ZnO. It is interesting to note that the coating layer formed at high Mo concentration (30 g/l) in the temperature range of $40-60^{\circ}C$ exhibited relatively high corrosion resistance, although thickness of coating layer is nearly identical with those formed under the other conditions. It was believed that an increase of driving force due to high Mo concentration plays an important role in the formation of corrosion-resistant coating layer, probably due to tile formation of dense coating layer.

• Bulletin of the Korean Chemical Society
• /
• 제32권3호
• /
• pp.993-999
• /
• 2011

The photoreactive prepolymers with multifunctional cinnamate and bisphenol Atype cinnamate groups that could perform photodimerization without photoinitiators were synthesized by the reaction of t-cinnamic acids (CAs) and epoxy resins. Their photocure reaction rates and the extent of reaction conversion were measured with Fourier transform infrared spectroscopy, and these increased with the intensity of UVirradiation. The experimental data of these reaction rates showed the characteristics of nth-order kinetics reaction, and all kinetic constants of each photoreactive polymer with this equation were summarized. Although the GTR-1800-HCA and KWG1-EP-HCA with hydroxyl group substituted cinnamate showed lower reaction conversion rates and rate constant than GTR-1800-CA and KWG1-EP-CAwith an unsubstituted cinnamate group, GTR-1800-MCAand KWG1-EP-MCAwith methoxy group substituted cinnamate showed similar and higher reaction conversion rates than the former, respectively. These results were explained in terms of segmental mobility for photopolymerization by molecular interactions.

• 한국마린엔지니어링학회:학술대회논문집
• /
• 한국마린엔지니어링학회 2006년도 전기학술대회논문집
• /
• pp.271-272
• /
• 2006

Zinc confers high corrosion resistance by acting as a sacrificial anode, and a zinc coating improves the appearance of steel. Chromate conversion coating (CCC) films are still one of the most efficient surface treatments for steel. Although such films can self-repair via the dissolution of Cr(VI), dissolved Cr(VI) have adverse effects on humans, and the environment. Therefore, we examined the corrosion protection property and morphology of colloidal silica conversion films as an alternative to CCC films. The corrosion behavior was investigated in 3% NaCl solution using electrochemical techniques, including electrochemical impedance spectroscopy, open circuit potential, and the salt spray test(SST). Corrosion was implied by the appearance of red rust on the specimen surface. In corrosion resistance at 3% NaCl solution, red rust appeared at 15-20, 55-70, and 83-98 days on Zn-electroplated steel, colloidal silica conversion-coated specimens, and CCC-coated specimens, respectively. In the salt spray test, the colloidal silica film provided better corrosion protection than CCC films, i.e., red rust appeared at 96 hours on the Zn-electroplated steel sheet, at 432 hours with the CCC films, and at 888 hours with silica conversion coating.

• Carbon letters
• /
• 제22권
• /
• pp.60-69
• /
• 2017

Nitrogen-doped carbon nanosheets with a developed porous structure were prepared from polyurethane foams by hydrothermal carbonization following $ZnCl_2$ chemical activation. Scanning electron microscopy, thermogravimetric analysis, Fourier transform infrared spectroscopy, solid state $^{13}C$ nuclear magnetic resonance (NMR) spectra and X-ray photoelectron spectroscopy were used to characterize the nitrogen-doped carbon nanosheet structure and composition. The removal of Cr(VI) by the N-doped carbon nanosheets was investigated. The results showed that the maximum removal capacity for chromium of 188 mg/g was found at pH=2.0 with PHC-Z-3. pH had an important effect on Cr(VI) removal and the optimal pH was 2.0. Moreover, amino groups and carboxyl groups in the nitrogen-doped carbon nanosheet played important roles in Cr(VI) removal, and promoted the reduction of Cr(VI) to Cr(III).

• 한국산학기술학회:학술대회논문집
• /
• 한국산학기술학회 2011년도 춘계학술논문집 1부
• /
• pp.141-143
• /
• 2011

Al-SBA-1(Si/Al = 40, 80 and 120) and Al,Mg-SBA-1 (Si/(Al+Mg) = 40 and 80) molecular sieves were synthesized and characterized. Acetalization of n-heptanal with methanol was studied under autogenous pressure between 80 and $150^{\circ}C$. Since protonation of n-heptanal was fast, addition of methanol to the same to formed hemiacetal slowly whereas conversion of hemiacetal to acetal was fast. The catalysts exhibited nearly similar conversion irrespective of their difference in acidity, and all of them showed more than 80 % conversion either at 80 or $100^{\circ}C$. Hence it is evident that the difference in acidity is not so important in differentiating the activity of the catalysts. The large pore size and hydrophilic and hydrophobic properties are suggested to be the main factors that control acetalization.

• Bulletin of the Korean Chemical Society
• /
• 제31권1호
• /
• pp.120-124
• /
• 2010

Monometallic, bimetallic and trimetallic particles consisting of different weight compositions of Pt-Pd-Rh over pure alumina wash coats have been synthesized and their catalytic performance on methane conversion was studied from 150 to $600^{\circ}C$. Different catalyst formulations with variable Pt, Pd and Rh contents for bimetallic and trimetallic systems were tried and $Pt_{(1.5)}Rh_{(0.3)}/Al_2O_3$ and $Pt_{(1.0)}Pd_{(1.0)}Rh_{(0.3)}/Al_2O_3$ shows low $T_{50}$ and $T_{90}$ temperatures. Bimetallic and trimetallic particle synergism acts as three way catalysts and therefore, all the catalysts show 100% methane conversion. The effect of supports such as $ZrO_2$ and $TiO_2$ on methane combustion was investigated; from $T_{50}$ and $T_{90}$ results both $Al_2O_3$ and $ZrO_2$ are suitable supports for low temperature methane combustion.

• 한국응용과학기술학회지
• /
• 제24권2호
• /
• pp.190-195
• /
• 2007

The transesterifications of beef tallow and the mixture of beef tallow and rapeseed oil were conducted at $65^{\circ}C$ respectively using TMAH, NaOH and their mixed catalysts. The reactants were emulsified with 1vol% emulsifier and propylene glycol. The overall conversion of beef tallow was 95% at such optimum conditions as the 1:8 of molar ratio and 0.8 wt% TMAH. The overall conversion of mixed fat at the 1:8 of molar ratio and mixed catalyst of 70 wt% TMAH 30 wt% NaOH was close to 97% which appeared at 0.8 wt% TMAH in 80min. And the kinematic viscosity of biodiesel mixture using the mixed catalyst was $6.5mm^2/s$ at $40^{\circ}C$.

• 한국수소및신에너지학회논문집
• /
• 제18권3호
• /
• pp.317-324
• /
• 2007

The conversion reaction of ortho to para hydrogen was studied. The percentage of ortho and para hydrogen is mainly dependent on the equilibrium temperature. Because this reaction is known to be accelerated by the catalyst such as nickel-silicate and ruthenium on silica, we focused in the test and development of the catalysts. We studied metal-silicates because they provide high metal dispersion on support. Nickel-silicate, ruthenium-silicate and mixed-silicate were prepared by the coprecipitation method and used in the reaction at the temperature of liquid nitrogen. The conversion was measured by the difference of thermal conductivity between reference gas and sample gas. The activation condition was important and it affected the activities of the catalysts. Nickel-silicate showed high activities. Ruthenium-silicate also showed relative high activities but mixed-silicate showed poor activities.

• 한국표면공학회지
• /
• 제44권3호
• /
• pp.82-88
• /
• 2011

A uniform chromium-free conversion coating treated with an alkaline phosphate- permanganate solution was formed on the AZ 31 magnesium alloy. The effect of acid pickling on the morphology and on the corrosion resistance of the alkaline phosphate-permanganate conversion coating was investigated. The chemical composition and phase structure of conversion coating layer were determined via optical microscopy, SEM, EDS, XPS and XRD. Results show that the conversion coatings are relatively uniform and continuous, with thickness 1.8 to $2.4\;{\mu}m$. The alkaline phosphate-permanganate conversion coating was mainly composed of elements Mg, O, P, Al and Mn. The conversion-coated layers were stable compounds of magnesium oxide and spinel ($MgAl_2O_4$). These compounds were excellent inhibitors to corrosion. The electrochemical corrosion behaviors of coatings in 3.5 wt.% NaCl solutions were evaluated by electrochemical impedance spectroscopy, potentiodynamic polarization technique. EIS results showed a polarization resistance of $0.1\;k{\Omega}$ for the untreated Mg and $16\;k{\Omega}$ for the alkaline phosphate-permanganate conversion treatment sample, giving an improvement of about 160 times. The results of the electrochemical measurements demonstrated that the corrosion resistance of the AZ 31 magnesium alloy was improved by the alkaline phosphate-permanganate conversion treatment.