• Nuclear Engineering and Technology
• /
• v.52 no.4
• /
• pp.811-818
• /
• 2020

Y-containing CLAM steels were melted via vacuum induction melting and electroslag remelting. In this study, the evolution, microstructure, and mechanical properties of the alloy inclusions (ESR-1 (0 wt.% Y), ESR-2 (0.016 wt.% Y) and ESR-3 (0.042 wt.% Y)) were investigated. Further, the number of inclusions in ESRed steel was observed to obviously decrease, and the distributions were more uniform. The fine Y-Al-O inclusions (1-2 ㎛) were the main inclusions in ESR-2. The addition of Y affected the prior austenite grain size (PAGZ), increasing the tensile strength at test temperature. Low ductile-brittle transition temperature (DBTT) was obtained because of the fine PAGZ and dispersive inclusions. For the ESRed CLAM steel with 0.016 wt.% Y, the yield strengths were 621 MPa at 20 ℃ and 354 MPa at 600 ℃ in air. Further, the uniform elongation and elongation of the ESR-2 alloy were 5.5% and 20.1% at 20 ℃, respectively. Meanwhile, the DBTT tested using full-size Charpy impact specimen (55 cm × 10 cm × 10 cm) was reduced to -83 ℃.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.33 no.4
• /
• pp.409-416
• /
• 2009

Standard procedures for a fracture toughness testing require very severe restrictions for the specimen geometry to eliminate a size effect on the measured properties. Therefore, the used standard fracture toughness data results in the integrity assessment being irrationally conservative. However, a realistic fracture in general structures, such as in nuclear power plants, may develop under the low constraint condition of a large scale yielding with a shallow surface crack. In this paper, cleavage fracture toughness tests have been made on side-grooved PCVN (precracked charpy V-notch) type specimens (10 by 10 by 55 mm) with various crack depths. The constraint effects on the crack depth ratios were evaluated quantitatively by the developed scaling method using the 3-D finite element method. After the fracture toughness correction from scaling model, the statistical size effects were also corrected according to the standard ASTM E 1921 procedure. The results were evaluated through a comparison with the $T_0$ of the standard CT specimen. The corrected $T_0$ for all of the PCVN specimens showed a good agreement to within $5.4^{\circ}C$ regardless of the crack depth, while the averaged PCVN $T_0$ was $13.4^{\circ}C$ higher than the real CT test results.

• Journal of Power System Engineering
• /
• v.5 no.2
• /
• pp.63-70
• /
• 2001

To obtain the optimal condition of heat treatment of wear-resistant alloy, hardness and Charpy V-notch test have been performed with Co-based Stellite No.4, No.6 and Tribaloy 800 alloys, following by heat treatment at the various conditions. Heat treatment at $1250^{\circ}C$ for 1 hours caused the as-casted Tribaloy 800 with FCC crystal structure to transform to HCP structure and lamellar eutectic structure was disappeared, which did not influence on the hardness. Aging at $800^{\circ}C$ for 20 hours, following by $1250^{\circ}C$ for 2 hours heat treatment has enhanced hardness significantly, which is due to the precipitation of large amounts of Laves-phase. The hardness of Stellite alloys was increased by the aging at $800^{\circ}C$ to 5 hours, and was nearly constant by the aging over 5 hours. The toughness of Stellite alloys was a few influenced by the aging treatment.

• Proceedings of the KWS Conference
• /
• 2010.05a
• /
• pp.25-25
• /
• 2010

8 wt.% 망간 (Mn) 이 함유된 마르텐사이트계 고 Mn강은 고강도용 강재로 산업현장에 적용될 수 있는 유용한 재료이다. 그러나, 다량의 망간의 함유로 인한 용접성 저하로 상용화를 위해서는 용접성 평가가 필요하다. 본 연구에서는 gleeble simulator 를 통해 열영향부를 재현한 후 local brittle zones(LBZs) 을 규명하였다. 모재는 Electron Probe Micro Analyzer (EPMA) 및 X-Ray Diffractometer(XRD) 로 분석결과 다량의 Mn 함유로 인해 lath마르텐사이트 미세조직과 소량의 잔류 오스테나이트로 구성되어 있었다. 용접부에서 모재까지 Vickers 경도계로 경도 분포를 측정한 결과 coarse-grained heat affected zone (CGHAZ) 에서 fine-grained heat affected zone (FGHAZ) 까지 경도 증가 후 subcritical heat affected zone (SCHAZ) 까지 급격한 경도 감소 거동을 보였다. 열영향부의 미세조직은 투과전자현미경 (TEM)으로 분석하였다. 연성취성천이온도 (DBTT) 측정을 위해 온도 구간을 상온, $0^{\circ}C$, $-20^{\circ}C$, $-40^{\circ}C$, $-60^{\circ}C$, $-80^{\circ}C$으로 설정하여 charpy impact test를 시행하였다. 그 결과 coarse-grained heat affected zone(CGHAZ) 에서 조대한 결정립으로 인해 낮은 충격값을 보였다.

• Korean Journal of Materials Research
• /
• v.30 no.2
• /
• pp.87-92
• /
• 2020

This study deals with the effects of austempering time on the microstructure and mechanical properties of ultra-high strength nanostructured bainitic steels with high carbon and silicon contents. The steels are composed of bainite, martensite and retained austenite by austempering and quenching. As the duration of austempering increases, the thickness of bainitic ferrite increases, but the thickness of retained austenite decreases. Some retained austenites with lower stability are more easily transformed to martensite during tensile testing, which has a detrimental effect on the elongation due to the brittleness of transformed martensite. With increasing austempering time, the hardness decreased and then remained stable because the transformation to nanostructured bainite compensates for the decrease in the volume fraction of martensite. Charpy impact test results indicated that increasing austempering time improved the impact toughness because the formation of brittle martensite was prevented by the decreased fraction and increased stability of retained austenite.

• Journal of Welding and Joining
• /
• v.17 no.3
• /
• pp.55-65
• /
• 1999

Metallurgical factors influencing toughness of the Intercritically Reheated Coarse-Grained Heat Affected Zone (ICCG HAZ) of multiple welded SA508-cl.3 Reactor Pressure Vessel Steel were evaluated. The recrystallized austenite formed along the prior austenite grain boundaries and late interfaced on heating to the intercritical range was transformed to bainite and/or martensite during cooling. The newly formed martensite always included some retained austenite(M-A constituents). The characteristics(amount, hardness, density, and size) of M-A constituents were found to be strongly associated with both peak temperature and cooling time(△t8/5(2)) of last pass. Toughness in the ICCG HAZ was deteriorated with increasing amount of M-A constituents which was increased with increasing the last peak temperature within the intercritical temperature range. Meanwhile, for the same intercritical peak temperature, toughness was decreased with increasing cooling time. When cooling time was short, the dominant factor influencing toughness of the ICCG HAZ was amount of M-A constituents. However, when cooling time was lengthened, the hardness difference between M-A constituents and softened matrix(tempered martensite) was found to be the dominant factor.

• Journal of Power System Engineering
• /
• v.18 no.4
• /
• pp.104-111
• /
• 2014

In this study, EH36 is thick steel plate, which welded by auto $CO_2$ gas welding machine, has been applied on offshore filed. The specimen was examined by indentation tester and it was measured for fracture toughness at $18^{\circ}C$, $0^{\circ}C$, $-20^{\circ}C$ and $-45^{\circ}C$ by low temperature chamber, respectively. The absorbed energy was got on same temperature by Charpy impact tester. The weld surface was observed for watch of changed crystalline structure by optical microscope, and fracture surface of impact test specimen were observed by scanning electron microscope(SEM).

• Journal of Welding and Joining
• /
• v.18 no.2
• /
• pp.232-232
• /
• 2000

The hydrogen attack characteristics of 3Cr-1Mo-V steel as simulated weld heat affected state were studied in this paper. The hydrogen attack susceptibility was evaluated by the ratios of Charpy impact absorbed energy at 0℃($vE_{0HA}$/$vE_{0}$) and reduction of area by tensile test ($RA_{HA}$/RA) before and after exposure to hydrogen at 600℃ under 450kgf/㎠ for 300hr. The values of $vE_{0HA}$/$vE_{0}$ and $RA_{HA}$/RA were aggravated as the peak temperature of the simulated heat affected zone(HAZ) raised. These results were due to the increase of the possession of bubbles along the grain boundaries, which were resulted in the reduction of grain boundary area to be precipitated carbides due to grain coarsening and the carbon dissolved in the martensite-austenite constituent near by the prior austenite grain boundary. The possession ratio of methane bubbles formed along prior austenite grain boundaries were increased with raising the peak temperature. (Received February 22, 2000)

• Journal of Welding and Joining
• /
• v.18 no.2
• /
• pp.105-111
• /
• 2000

The hydrogen attack characteristics of 3Cr-1Mo-V steel as simulated weld heat affected state were studied in this paper. The hydrogen attack susceptibility was evaluated by the ratios of Charpy impact absorbed energy at 0℃({TEX}$vE_{0} {HA}_/vE_{0}${/TEX}) and reduction of area by tensile test({TEX}$RA_{HA}/RA${/TEX}) before and after exposure to hydrogen at 600℃ under 450kgf/㎠ for 300hr. The values of {TEX}$vE_{0} {HA}_/vE_{0}${/TEX} and {TEX}$RA_{HA}/RA${/TEX} were aggravated as the peak temperature of the simulated heat affected zone(HAZ) raised. These results were due to the increase of the possession of bubbles along the grain boundaries, which were resulted in the reduction of grain boundary area to be precipitated carbides due to grain coarsening and the carbon dissolved in the martensite-austenite constituent near by the prior austenite grain boundary. The possession ratio of methane bubbles formed along prior austenite grain boundaries were increased with raising the peak temperature.

• Transactions of Materials Processing
• /
• v.28 no.4
• /
• pp.219-225
• /
• 2019

This study deals with the effect of austempering temperature and time on the microstructures and mechanical properties of high-carbon nano-bainite steels. Although all the austempered specimens are mainly composed of bainite, martensite, and retained austenite, the specimens which are austempered at lower temperatures contain finer packets of bainite. As the duration for austempering increases, bainite packets are clearly seen due to larger amount of carbon atoms being redistributes into bainite and retained austenite during bainite transformation. As the austempering time increases, the hardness of the specimens gradually decreases as a result of lower martensite volume fraction, and later increases again due to the formation of nano-bainite structure. The Charpy impact test results indicate that the impact toughness of the austempered specimens can be improved if the formation of nano-bainite structure and the transformation induced plasticity effect of retained austenite are optimized at higher austempering temperature.