• Journal of the Korean Ceramic Society
• /
• v.42 no.12 s.283
• /
• pp.808-815
• /
• 2005

[ $Bi_xCe_{l-x}O_{2-x/2}$ ](BD C : Bismuth Doped Ceria) powders with x = 0.1, 0.2, and 0.3 were synthesized using the Glycine Nitrate Process (GNP). They were then calcined at $500^{\circ}C$ for 2 hand sintered in a pellet or rod form at 900, 1000 or $1100^{\circ}C$ for 4 h for characterization as the alternative electrolyte material for intermediate temperature solid oxide fuel cells. The BDC powder consisted of a single phase of $CeO_2-Bi_2O_3$ solid solution in the as-synthesized state as well as in the as-calcined state with a mean powder size of 4.5nm in the former state and 6.5 - 10.1nm in the latter. On the contrary, the second phase of $\alpha-Bi_2O_3$ was observed to have been formed in the sinter with its amount increasing roughly with increasing temperature or $Bi_2O_3$ content. The BOC powder was superior in sinterability to other alternative electrolyte materials such as GDC, ScSZ, and LSGM with the minimum sintering temperature for a relative density of $95\%$ or larger as low as $1100^{\circ}C$. The ionic conductivity of BOC increased with $Bi_2O_3$ content and the maximum value of 0.119 S/cm was obtained at $800^{\circ}C$ for $Bi_{0.3}Ce_{0.7}O_{1.85}$.

• Journal of the Korean Ceramic Society
• /
• v.35 no.1
• /
• pp.97-105
• /
• 1998

20mol% Gd-doped CeO2 ultrafine powders as a promising electrolyte for the low temperature solid ox-ide fuel cells were synthesized with particle sizes of 15-20 nm using glycine nitrate process(GNP) fol-lowed by sintering their pellets at 150$0^{\circ}C$ for various times in air and then the electrical properties of the sintered pellets were investigated. The sintering behaviors and electrical properties for the sintered 20 sintered mol% Gd-doped CeO2 pellets were analyzed using dilatometer and SEM and AC two-terminal impedance technique respectively. As the heating temperature increased the synthesized powder had the sintering behaviors to show the start of the significant shrink at temperature of about $700^{\circ}C$ and to show the end of the shrink at the temperature of about 147$0^{\circ}C$. When the pellets were sintered with the vaious times at 150$0^{\circ}C$ the temperatuer which the shrink had been already completed the grain sizes in the sintered 20 mol% Gd-doped GeO2 pellets increased with the increase of the sintering time but their electrical resis-tivities showed the minimum value at the sintering time of 10h. It is due that the pellet sintered for 10h had the minimum activation energy fior the electtrical conduction. Thus it is thought that the decrease of the activation energy with the increase of the sintering time to 10h is induced by the enhanced mi-crostructure like the decrease of pore amount and the grain growth and its increase with the sintering times more than 10h is induced by the increase of the amounts of the impurities such as Mg. Al and Si from the sintering atmosphere.

• Applied Chemistry for Engineering
• /
• v.17 no.3
• /
• pp.267-273
• /
• 2006

We have prepared PP/Ba-ferrite composite fabrics by a melt-blown spinning method and investigated the relationship between the properties of PP/Ba-ferrite composite fabrics and melt-blown processing factors. A PP composite containing Ba-ferrite as a magnetic particulate filler was prepared in the form of pellet from PP resin and Ba-ferrite powder by melt compounding using a single extruder. Screw turning force (rpm), DCD (die-to-collector distance), and Ba-ferrite content were changed. We measured diameters of fiber, mechanical, thermal, and magnetic properties for the composited PP fabrics. The elongation was increased and a fiber diameter and tensile strength were decreased as the spinning distance increased or screw turning force decreased. The crystallinity was increased with increasing spinning distance according to XRD. It was assumed that the orientation of crystalline domain in the neat PP without ferrite was increased by drawing in mechanical direction, however, the orientation in the PP composite was decreased according to XRD analysis. We measured a magnetic property of PP nonwoven fabric containing Ba-ferrite powder. A coercive force, maximum magnetization, and residual magnetization are reduced with the spinning distance. According to the result of TGA measurement, the heat resistance was increased with the Ba-ferrite powder content and with decreasing the spinning distance.

• Proceedings of the Korean Nuclear Society Conference
• /
• 1998.05b
• /
• pp.216-221
• /
• 1998

A study on induction plasma deposition with ceramic materials, yttria-stabilized-zirconia ZrO$_2$-Y$_2$O$_3$ (m.p 264O $^{\circ}C$), was conducted with a view developing a new method for nuclear fuel fabrication Before making dense pellets more than 96％TD., the spraying condition was optimized through the process parameters, such as chamber pressure, plasma plate power powder spraying distance, sheath gas composition, probe position, particle size and powders different morphology. The results with a 5mm thick deposit on rectangular planar graphite substrates showed a 97.11％ theoretical density when the sheath gas flow rate was Ar/H$_2$120/20 l/min, probe position 8cm, particle size -75 ${\mu}{\textrm}{m}$ and spraying distance 22cm by AMDRY146 powder. The degree of influence of the main effects on density were powder morphology. particle size, sheath gas composition, plate power and spraying distance, in that order. Among the two parameter interactions, the sheath gas composition and chamber pressure affects density greatly. By using the multi-pellets mold wheel type, the pellet density did not exceed 94%T.D., owing to the spraying angle.

• Korean Journal of Medicinal Crop Science
• /
• v.21 no.1
• /
• pp.7-19
• /
• 2013

This study was carried out to select new pelleting binder and material for seeds from Fraxinus rhynchophylla Hance and Alnus sibirica Fisch. ex Turcz. The optimum treatments of the various concentrations and species of priming agents to improve seed germination of both woody medicinal plants were also estimated. Germinability was increased when the seeds of Fraxinus rhynchophylla Hance was soaked in -1.0 MPa of PEG6000 solution at $15^{\circ}C$ for 4 days significantly, the optimum treatment for improving germination of Alnus sibirica Fisch. ex Turcz was observed when the tested seeds was soaked in 100 mM of KCl at $15^{\circ}C$ for 4 days. The influence of physical and chemical properties of pelleting solid materials, the mixture of gypsum, diatomaceous earth, dalma ceramic and vermicuolite (6:1:1:1 ratio) were found as the best pelleting materials for Fraxinus rhynchophylla Hance and Alnus sibirica Fisch. ex Turcz. seeds. To satisfy the requirements of absorption and compatibility for multi-layer seed pelleting, SGPA (Starch-grafted cross-linked polyacrylates) hydrogel was prepared using starch, acrylonitrile, ceric ammonium nitrate, nitric acid, methyl alcohol and potassium hydroxide. The resulting SGPA hydrogel showed high water absorption but not plant compatibility. It suggested that seed pelleting using pelleting materials and SGPA hydrogel (multi-layer coating) after priming agent treatment is to increase germinability and seedling growth and it can reduced irrigation labours and can also save seed.

• Macromolecular Research
• /
• v.17 no.8
• /
• pp.616-622
• /
• 2009

In-depth understanding of the influence of hot pressing and melt processing on the properties of thermoplastic polyurethane (TPU) is critical for effective mechanical recycling of TPU scraps. Therefore, this study focused on the effects of hot pressing and melt mixing on molecular weight (MW), polydispersity index (PDI), melt index (MI), characteristic IR peaks, hardness, thermal degradation and mechanical properties of TPU. The original TPU pellet (o-TPU) showed two broad peaks at lower and higher MW regions. However, four TPU film samples, TPU-0 prepared only by hot pressing of o-TPU pellet and TPU-1, TPU-2 and TPU-3 obtained by hot pressing of melt mixed TPUs (where the numbers indicate the run number of melt mixing), exhibited only a single peak at higher MW region. The TPU-0 film sample had the highest $M_n$ and the lowest PDI and hardness. The TPU-1 film sample had the highest $M_w$ and tensile modulus. As the run number of melt mixing increased, the peak-intensity of hydrogen bonded C=O stretching increased, however, the free C=O peak intensity, tensile strength/elongation at break and average MW decreased. All the samples showed two stage degradations. The degradation temperatures of TPU-0 sample (359 $^{\circ}C$ and 394 $^{\circ}C$)were higher than those of o-TPU (342 $^{\circ}C$ and 391 $^{\circ}C$). While all the melt mixed samples degraded at almost the same temperature (365 $^{\circ}C$ and 381 $^{\circ}C$). The first round of hot pressing and melt mixing was found to be the critical condition which led to the significant changes of $M_n$/$M_w$/PDI, MI, mechanical property and thermal degradation of TPU.

• Journal of Powder Materials
• /
• v.28 no.3
• /
• pp.201-207
• /
• 2021

Ni-Cr-Al metal-foam-supported catalysts for steam methane reforming (SMR) are manufactured by applying a catalytic Ni/Al₂O₃ sol-gel coating to powder alloyed metallic foam. The structure, microstructure, mechanical stability, and hydrogen yield efficiency of the obtained catalysts are evaluated. The structural and microstructural characteristics show that the catalyst is well coated on the open-pore Ni-Cr-Al foam without cracks or spallation. The measured compressive yield strengths are 2-3 MPa at room temperature and 1.5-2.2 MPa at 750℃ regardless of sample size. The specimens exhibit a weight loss of up to 9-10% at elevated temperature owing to the spallation of the Ni/Al₂O₃ catalyst. However, the metal-foam-supported catalyst appears to have higher mechanical stability than ceramic pellet catalysts. In SMR simulations tests, a methane conversion ratio of up to 96% is obtained with a high hydrogen yield efficiency of 82%.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.21 no.2
• /
• pp.92-97
• /
• 2011

Landfill is the main treatment method for bottom-ash because it has not only an irregular particle size and ingredients but also not proper recycling treatment. The aim of this study is to raise recycling rate of bottom-ash(nonplasticity pulverulent) and for the purpose of alternatives of clay to investigate the properties of Bottom-ash (B/A)-Hard Clay (H/C) bodies with controlled interfacial chemistry properties. After investigating the sedimentation height of suspensions with controlled pH, it was discovered that there was no hetero-polar aggregation for mixed slips because hard clay and bottom-ash had similar interfacial chemistry properties. Also, bulk density, water absorption, and microstructure properties of each pellet was observed that made by silp casting method and manufactured at $50^{\circ}C$ intervals between $1000{\sim}1250^{\circ}C$. As a result, dispersed slip of clay and bottom ash are possible for slip casting and plastic forming process because they exhibit Bingham plastic behavior. Products that made by slip with dispersed clay and bottom ash are not only suitable for KS L 4201 and KS L 1001 at $1250^{\circ}C$ but it is also possible to apply for ceramic and sanitary ware because specific gravity was about 15 % lighter than general ceramic materials.

• Journal of the Korean Ceramic Society
• /
• v.34 no.2
• /
• pp.115-122
• /
• 1997

The powder preparation by using emulsion drying method, one of the chemical powder fabrication methods has the advantages; easy to control the chemical stoichiometry and to fabricate homogeneously fine particles. In the present study, the initial morphology and size distribution of the powder fabricated by using emulsion dry-ing method were controlled and were improved the homogeneity. By carefully controlling the mixing ratio of oil phase and aqueous solution and surfactant of preventing emulsion separation, the Bi(Pb)-Sr-Ca-Cu-O su-perconducting powders were prepared. The properties of the superconducting powder fabricated by this method and the microstructures and superconducting properties of the pelletized samples were investigated. The microstructures and electric properties of the tapes prepared by oxide powder-in-tube method were in-vestigated. The fabricated powder was spherical with less than 1$\mu$m but most of them was agglomerated with 2~5$\mu$m in size. The critical temperature of the pelletized sample annealed at 84$0^{\circ}C$ for 72 hours in oxygen par-tial pressure of 1/13atm in Ar atmosphere was 108K. And the critical current of the first and second annealed tapes in air prepared by oxide powder-in-tube process were 0.4A and 1.5A, respectively.

• Journal of the Korean Ceramic Society
• /
• v.40 no.9
• /
• pp.916-920
• /
• 2003

The change of structure and morphology in ( $U_{0.913}$G $d_{0.087}$) $O_2$ during oxidation at 475$^{\circ}C$ and heat treatment at 130$0^{\circ}C$ in air were investigated using XRD, SEM, and EPMA. The ( $U_{0.913}$G $d_{0.087}$) $O_2$ cubic phase converted to ( $U_{0.913}$G $d_{0.087}$)$_3$ $O_{8}$ orthorhombic phase by oxidation at 475$^{\circ}C$ in air. The XRD and EPMA result of the 130$0^{\circ}C$ heat treated powder revealed that ( $U_{0.913}$G $d_{0.087}$)$_3$ $O_{8}$ orthorhombic phase was separated into $U_3$ $O_{8}$ and ( $U_{0.67}$G $d_{0.33}$) $O_{2+}$x/ cubic phase. The weight variations of (U,Gd) $O_2$ with various Gd contents were measured using TGA at the same heat treated condition. The weight variation during the heat treatment of Gd dissolve (U,Gd) $O_2$ in air can be expressed in terms of phase reaction equations related with oxidation and phase separation. Based on these phase reaction, a initial content of Gd dissolved in (U,Gd) $O_2$ can be exactly calculated by measuring the weight change during the heat treatment.