• 대한치과기공학회지
• /
• 제34권2호
• /
• pp.113-119
• /
• 2012

Purpose: Zirconia blocks for all ceramic dentures are divided into two groups. One is pre-heated block and the other is binder added block. In this study, the possibility of recycling the remained parts of binder added block after CAD/CAM machining with slip casting process was investigated. Methods: Owing to the binder added block contain large amount of organic matter, Binder burn-out was must be carried out before ball milling for preparing the casting slip. Binder burn-out was accomplished at $600^{\circ}C$ for 10 hours. Ball milling was performed with 5mm zirconia ball and 60mm polyethylene bottle. From 0% to 5% at 1% intervals of alumina was added to zirconia powder for preparing slip. Solid casting was achieved with plaster mold. Cast bodies were dried and sintered at $1,500^{\circ}C$ for 1 hour. Linear shrinkage, apparent porosity, water absorption, bulk density, and flexural strength were tested. Microstructures were observed by SEM, EDS and XRD analysis were executed. Results: Optimum slips for casting was prepared with 300g ball, 100g powder, and 180g distilled water. Cast body without alumina showed 26% of linear shrinkage, 6.07 of apparent density, and 470MPa of three point bend strength. On the other hand, as received zirconia block, which was sintered at the same conditions, showed 23% of linear shrinkage, 6.10 of apparent density, and 680MPa of three point bend strength. When 3% of alumina was added to zirconia, sintered body showed 23% of linear shrinkage, 6.10 of apparent density, and 780MPa of three point bend strength. SEM photomicrographs and EDS analysis showed alumina particles uniformly dispersed in zirconia matrix, and XRD analysis showed no phase transformation of tetragonal zirconia particles was occurred when alumina was added. Conclusion: According to the all of this experimental results, 3% of alumina added cast zirconia body showed excellent mechanical properties more than as received binder containing zirconia block.

• 대한치과보철학회지
• /
• 제41권3호
• /
• pp.319-324
• /
• 2003

Statement of problem. Adhesives in dentistry playa major role in the success of restorative treatments. In the treatment of all ceramic restoration it is needed to find the adequate bond strength between enamel and dentin. Purpose. The purpose of this study was to evaluate shear bond strength of resin cement bonded to extracted human uncut enamel, cut enamel, and dentin in vitro. Material and methods. Ten freshly extracted anterior teeth without any previous restorative treatments were chosen. The extracted teeth were embedded in PMMA cold acrylic in the shape of a cylinder, 25 mm in diameter by 25 mm in height. The bonding system used was as follow: Uni-Etch (32% phosphoric acid), One-Step adhesive, Duolink resin cement. The specimens were acid etched and rinsed with water. Two layers of One-Step adhesive were coated with a disposable brush on the uncut enamel. VIP curing light at $500mV/cm^2$ was used to cure the adhesive. For cut enamel shear bond test, the specimen used for uncut enamel was further reduced approximately $0.3{\sim}0.5mm$ using a laminate preparation diamond bur (0.3 mm in depth). The specimens were subsequently treated with 320-grit SiC paper followed by 600-grit SiC paper and cleaned with distilled water. The bonding procedure on the cut enamel was same as uncut enamel bonding procedure. For dentin bonding test, the specimen used for cut enamel was further reduced approximately $0.5mm{\sim}1.0mm$ using a laminate preparation diamond bur (0.5 mm in depth of diamond cutting). The amount of reduction was evaluated with the silicone mold. The specimens were subsequently treated with 320-grit SiC paper followed by 600-grit silicon carbon paper and cleaned in distilled water. The bonding procedure on the dentin was same as uncut enamel bonding procedure. All samples were mounted and secured on the Ultradent shear bond test sample holder, and Ultradent restricted shear bond testing device was used with Universal Instron machine until fracture. Analysis of variance (ANOVA) test was performed comparing the result at P<0.05. Multiple comparison (Tukey) was used to compare each groups. Result. The result showed that the mean value in shear bond strength of resin cement bonded to uncut enamel, cut enamel and dentin were 27.04 Mpa, 30.25 Mpa and 26.39 Mpa with respect. Conclusion. Within the limitation of this study, the mean value of the shear bond strength of cut enamel was higher than those of uncut enamel or dentin. However there existed no statistical differences between three different human dentition substrates due to increased adhesive characteristics.