• Journal of the Korea Concrete Institute
• /
• v.27 no.2
• /
• pp.115-125
• /
• 2015

This study investigated the fluidity, heat of hydration, setting time, strength development, and characteristics of hydration and pozzolanic reactions of high-strength high-volume ground granulated blast-furnace slag(GGBFS) blended cement pasts with the water-to-binder ratio of 20% by experiments, and analyzed the effects of the replacement ratio and fineness of GGBFS on the hydration and pozzolanic reaction. The results show that, in the high-strength mixtures with low water-to-binder ratio, the initial hydration is accelerated due to the "dilution effect" which means that the free water to react with cement increases by the replacement of cement by GGBFS, and thus, strengths at from 3 to 28 days were higher than those of plain mixtures with ordinary Portland cement only. Whereas it was found that the long term strength development is limited because the hydration reaction rates rapidly decreases with ages and the degree of pozzolanic reaction is lowered due to insufficient supply of calcium hydroxide according to large replacement of cement by GGBFS. Also, the GGBFS with higher fineness absorbs more free water, and thus it decreases the fluidity, the degree of hydration, and strength. These results are different with those of normal strength concrete, and therefore, should be verified for concrete mixtures. Also, to develop the high-strength concrete with high-volume of GGBFS, the future research to enhance the long-term strength development is needed.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.21 no.5
• /
• pp.141-147
• /
• 2017

Recently, lots of researches on concrete with high volume mineral admixtures such as ground granulated blast-furnace slag(GGBS) have been carried out to reduce greenhouse gas. The high volume GGBS concrete has advantages such as low heat, high durability, but it has a limitation in practical field application, especially low strength development in early ages. This study investigated the compressive strength and hydration characteristics of high performanc and volume GGBS cement pastes with low water to binder ratio. The effects of fineness($4,330cm^2/g$, $5,320cm^2/g$, $6,450cm^2/g$, $7650cm^2/g$) and replacement(35%, 50%, 65%, 80%) of GGBS on the compressive strength, setting and heat of hydration were analyzed. Experimental results show that the combination of high volume slag cement paste with low water to binder ratio and high fineness GGBS powder can improve the compressive strength at early ages.

• Journal of the Korea Institute of Building Construction
• /
• v.20 no.4
• /
• pp.321-330
• /
• 2020

The addition of a limestone filler(LF) to fill into the voids between cement and aggregate particles can reduce the cementitious paste volume. In previous studies, it has been found that the addition of LF to reduce the cementitious paste volume would substantially increase the compressive strength, and reduce the heat generation. This paper aim to evaluate the influence of LF contents on the hydration kinetics and compressive strength. Hydration kinetics were evaluate using heat of hydration, ignition loss and thermal analysis. The heat of hydration was measured using Isothermal Calorimetry. The degree of hydration was measured using ignition loss. Hydration product analysis was carried out by Thermal Gravimetric and Differential Thermal Analysis. The results show that the addition of LF reduces not only the initial setting time and heat of hydration peak, also degree of hydration and rate of strength development at early age increase with the addition of LF. It can be concluded the LF fills the pore between cement particles due to formation of carboaluminate, which may accelerate the setting of cement pastes.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.7 no.4
• /
• pp.302-309
• /
• 2019

This paper shows an experimental study for fundamental characteristics of alkali activated fly ash-slag cement paste exposed to seawater of 5℃. Fly ash and slag were blended in three different ratios; 6:4, 7:3, and 8:2. Activators (NaOH and Na2SiO3) used 5% of the binder weight. It was shown that as the fly ash substitution rate in creased, compressive strength and density decreased, and water absorption rate increased. The results of X-ray diffraction and thermogravimetry showed that hydration reactants formed in samples did not differ significantly, however, C-S-H gel increased as the slag substitution rate increased. It showed that mechanical properties of fly ash-slag cement pastes under 5℃ seawater condition were affected by the slag substitution rate rather than fly ash.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.28 no.5
• /
• pp.54-61
• /
• 2024

This study conducted accelerated carbonation experiments on cement pastes using OPC and FA. It derived the correlation of pH prediction methods through component analysis of the carbonated pastes. Analysis of weight change due to thermal decomposition was performed using TG-DTA, and component analysis was conducted using XRF. A comparative review of each experimental result and pH measurement result was carried out. The study proposed a correlation analysis method between the component ratio of CO₂ and CaO, the component ratio of calcium carbonate and calcium hydroxide, and pH. By analyzing the relationship between the CO₂ components measured by XRF and pH, the correlation coefficients of all mixtures were 0.84 or higher, indicating a strong correlation.The correlation analysis of calcium carbonate and calcium hydroxide with pH using TG-DTA showed that the correlation coefficient for calcium carbonate was more than 0.86 for all formulations. However, the correlation coefficient between calcium hydroxide and pH was low, so a study was conducted to analyze the correlation with pH using the ratio of the results of the two components.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.18 no.1
• /
• pp.111-118
• /
• 2014

The present study concerns the leachability of alkali ions from hardened cement paste in terms of an increase in the pH together with the rate of alkali leaching. To evaluate the influence of mix design on the leaching capacity and rate of alkali, different water-cement ratios (W/C) and binders were used to manufacture paste specimens. The cement paste was made in the form of rectangular bucket where deionised water was subsequently supplied as solvent media. Then the specimen was wrapped in polythene film to avoid contact to atmospheric conditions, which may affect the water chemistry in the bucket. The pH of media was monitored until no further change in the pH value was observed, of which value then used to calculate the leaching capacity and rate. The influence of binder on the pH of solvent is more dominant than that of water to cement ratio: OPC paste produced the highest level of alkali leaching, whilst 30% PFA and 60% GGBS pastes imposed lower level of alkali leaching. After the monitoring of the pH, the inner bucket was ground with an increment of 1.0 mm to measure the leaching influence using the suspension consisting of paste powder and deionised water. It was found that the impact zone for OPC was about 7-8 mm, whilst 30% PFA and 60% GGBS had deeper impact depth of the alkali leaching.

• Journal of the Korea Concrete Institute
• /
• v.21 no.3
• /
• pp.255-264
• /
• 2009

Permeability coefficient of concrete is a substaintial key parameter for understanding the durability performance of concrete and its microstructural densification. Many researches for the issue have been accomplished, however, it is very rare to deal with the theoretical study on permeability coefficient in connection with carbonation of concrete and the the effect of volumetric fraction of cement paste or aggregate on the permeability coefficient. The majority of these researches have not dealt with this issue combined with carbonation of concrete, although carbonation can significantly impact on the permeability coefficient of concrete. The purpose of this study is to establish a fundamental approach to compute the permeability coefficeint of (non)carbonated concrete. When simulating a microstructural characteristics as a starting point for deriving a model for the permeability coefficient by the numerical simulation program for cementitious materials, HYMOSTRUC, a more realistic formulation can be achieved. For several compositions of cement pastes, the permeability coefficient was calculated with the analytical formulation, followed by a microstructure-based model. Emphasis was on the microstructural changes and its effective change of the permeability coefficient of carbonated concrete. For carbonated concrete, reduced porosity was calculated and this was used for calculating the permeability coefficeint. The computational result was compared with experimental outcome.

• Advances in materials Research
• /
• v.7 no.1
• /
• pp.45-72
• /
• 2018

In the present study, a special attention has been paid to the effects regarding the use of different superplasticizers in different dosages. To do so, 36 mixes of normal and self-compacting concrete with two water/binder ratios of 0.35 and 0.45, four different types of superplasticizer including melamine-formaldehyde, naphthalene-formaldehyde, carboxylic-ether and poly-carboxylate, four different superplasticizer/cement ratios of 0.4%, 0.8%, 1.2% and 1.6% and two silica fume/cement ratios of 0% and 10% have been cast. Moreover, the initial and final setting time of the pastes have been tested. For self-compacting mixes, flow time, slump flow, V-funnel, J-ring and L-box tests have been carried out as well as testing the compressive strength and rupture modulus. For normal concrete mixes,slump test has been conducted to assess the workability of the mix and then for each mix, the compressive strength and rupture modulus have been determined. The results indicate that in addition to the important role of superplasticizer type and dosage on fresh state properties of concrete, these parameters as well as the use of silica fume could affect the hardened state properties of the mixes. For instance, the mixes whose superplasticizer were poly-carboxylic-ether based showed better compressive and tensile strength than other mixes. Besides, the air contents showed robust dependency to the type of the superplasticizer. However, the use of silica fume decreased the air contents of the mixes.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.1053-1056
• /
• 2008

Permeability coefficient of concrete is a substantial key parameter for understanding the durability performance of concrete and its micro-structural densification. Many researches to deal with the issue have been accomplished, however, it is very rare to deal with the theoretical study on permeability coefficient in connection with carbonation of concrete and the effect of volumetric fraction of cement paste or aggregate on the permeability coefficient. The majority of these researches have not dealt with this issue combined with carbonation of concrete, although carbonation can significantly impact on the permeability coefficient of concrete. The purpose of this study is to establish a fundamental approach to compute the permeability coefficient of (non)carbonated concrete. When simulating micro-structural characteristics as a starting point for deriving a model for the permeability coefficient by the numerical simulation program for cementitious materials, HYMOSTRUC, a more realistic formulation can be achieved. For several compositions of cement pastes, the permeability coefficient is calculated with the analytical formulation, followed by a microstructure-based model. Emphasis is on the micro-structural changes and its effective change of the permeability coefficient of carbonated concrete. The results of micro-structural water permeability coefficient model will be compared with results achieved from permeability experiments.

• Journal of the Korea Institute of Building Construction
• /
• v.20 no.1
• /
• pp.11-18
• /
• 2020

Carbon nanotubes are used in various industries with their excellent mechanical properties and electrical conductivity. In the construction industry, research is being conducted to give self-sensing capabilities to structures, but the results of experiments vary among researchers, and the analysis is insufficient. Therefore, in this study, the hydration and electrical properties of MWCNT-added cement pastes were measured. The electrical resistance values of hydration heat, porosity, Rietveld quantitative analysis, compressive strength, and distance were measured.. The heat resistance, porosity, Rietvelt quantitative analysis, compressive strength and distance were measured according to electrical resistance. Experimental results showed that the heat of hydration decreased with increasing MWCNT. XRD Rietveld quantitative analysis showed that there was no significant difference in the amount of hydration products with increasing addition rate of MWCNT. As a result of SEM analysis, the MWCNT is agglomerated by van der Waals forces, and this area is considered to be caused by voids and weak areas. The electrical resistance value decreases as the addition rate is increased, and thus may play a role for magnetic sensing in the future.