• Proceedings of the Korea Concrete Institute Conference
• /
• 1997.04a
• /
• pp.136-145
• /
• 1997

The purpose of this study is to develope of alternative adimixture for manufacture of PHC pile(compressive strength above 800kg/$\textrm{cm}^2$). For the investigation, properties of alternative admixture admixed with II-anhydrite and pozollanic fine powders(e.q., Fly-ash, Silica-Fume), the fluidity and viscosity in the cement pastes, the fluidity and compressive strength in mortars at steam curing condition, were respectively examined. Also, properties of compressive strength of concretes with exiting admixture(specimen name SM) and alterantive admixture(specimen name AP) for PHC pile, at steam and standard curing condition, were compared each other. As a result of this experimental study, it was found that specimens admixed with II-anhydrite and pozollanic fine powders had an increase on the fluidity of cement paste and mortar, and compressive strength of mortar and concrete was as good as concrete with SM.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2006.11a
• /
• pp.469-472
• /
• 2006

The use of admixture(PNS type & PC type) played a important role in the development of rapid hardening concrete. This paper presents an experimental study on the effect of a kinds of admixture on hydration characteristics, mini slump, apparent viscosity of fresh cement pastes and workability, compressive strength properties of hardened concrete for rapid hardening. Measurements have showed that their characteristics depends on the type of the admixture. As a result, the excellent quality was obtained, also being widely used for the construction field is expected.

• Journal of the Korea Institute of Building Construction
• /
• v.17 no.3
• /
• pp.269-277
• /
• 2017

In this work, as a preliminary experimental works, which focuses on utilizing separated pastes from activated (or radioactive) concrete as solidifying agents for radioactive waste immobilization, were performed. It was found that density of hydrated cement paste, which was lower than that of ordinary portland cement, increased as temperature for heat treatment increased. Highest compressive strength was observed with the specimens that was heat treated at $600^{\circ}C$. However, heat treatment over $700^{\circ}C$ showed higher CaO content that caused higher heat of hydration after in contact with water, lows of workability, and lower strength. Based on experimental results, it is suggested that $600^{\circ}C$ heat treatment is more appropriate for waste cement paste to be used as a solidifying agent.

• Resources Recycling
• /
• v.3 no.3
• /
• pp.27-31
• /
• 1994

We tested the limestone sludge produced in Pohang Iron & Steel Co., Ltd. as a filler powder for the effective use of portland cement. Hydration process was investigated by measuring the hydration rate, the amounts of non-evaporable water and compressive strength of cement-limestone sludge paste prepared by mixing limes-tone sludge with cement. The results obtained in this study can be summarized as follows: 1. There is no significant difference between the cases of adding up to 10% limestone sludge and those of unmixed cement system. However the reaction rate increases in the 5% limestone sludge system(due to the effects of fine). 2. The compressive strength increases proportionally with increasing the measured amount of non-evaporable water, Adding 5% limestone sludge also increases the strength a little higher, and the compressive strength and calcium silicate hydrates. In the case of the mixed limestone sludge, $2\theta$=$11.7^{\circ}$ peak appears in the samples of 28 days hydration. This peak indicted the presence of calcium carboaluminate hydrate. Although limestone sludge is generally regarded as a inert materials, some kinds of cement can produce a calcium carboaluminate by reacting with aluminate in cement pastes.

• Journal of the Architectural Institute of Korea Structure & Construction
• /
• v.33 no.12
• /
• pp.63-70
• /
• 2017

When industrial by-products like slag and fly ash are using in concrete with cement, it improves strength and durability against external deterioration factors by densifying the structure through potential hydraulic and pozzolanic reaction. But it has been pointed out that high dependence on the quality variation and the curing condition using a admixure material for concrete. In this study, the characteristics of internal micropore structure according to curing condition were analyzed for pastes and mortar specimens under using blast furnace slag powder. As a result, the variation of compressive strength and the internal microstructure were observed according to curing conditions by binder type. Particularly, using blast furnace slag powder, decrease in compressive strength were clearly observed in indoor and carbonation curing compared with water curing. The pore structure analysis also clearly observed the decrease of the gel pore existing in the CSH hydrate layer and the increase of the capillary pore in indoor and carbonation curing compared with water curing condition.

• Journal of the Korea Concrete Institute
• /
• v.22 no.3
• /
• pp.375-380
• /
• 2010

In this study, physical properties of cement blended with Finex-slag powder(OPC-FS) were investigated by the measurement of flowability, compressive strength, hydration heat, and $Ca(OH)_2$ content. In addition, those properties of the cement blended with blast furnace slag(OPC-BFS) were also measured for comparison. It was found that OPC-FS and OPC-BFS showed similar trend in the rheological properties. In the blended cement pastes with the $4,000\;cm^2/g$ Blaine value the flowability of OPCFS was better than that of OPC-BFS. The initial 3 day mortar compressive strength and the hydration heat of paste of OPC-FS was a bit higher, compared with OPC-BFS. Accordingly $Ca(OH)_2$ produced in the cement hydration was decreased very rapidly.

• Journal of the Korean Ceramic Society
• /
• v.39 no.1
• /
• pp.99-107
• /
• 2002

Impedance Spectroscopy (IS) has been used to study microstructure and hydration mechanism of cement pastes. In this work, the early hydration behaviour of portland cement paste with different blame values and contents of blast-furnace slag was investigated by IS. As slag was added to portland cement, the values of $R_{t(s+1)}$ (the solid-liquid phase resistance) and $R_{t(int)}$ were decreased in the early hydration period. It showed that hydration of cement paste containing slag was slower than it of the reference cement paste. As the content of slag was increased, the values of $R_{t(s+1)}$ was decreased. Furthermore, the diameter of semicircle, $R_{t(int)}$ observed at 72 hours was decreased with the increment of slag content. However, the values of $R_{t(s+1)}$ and $R_{t(int)}$ were increased with blame value of slag from the early hydration period.

• Journal of the Korea Concrete Institute
• /
• v.16 no.3 s.81
• /
• pp.369-374
• /
• 2004

Calcium sulfoalumiante(CSA) was prepared for using natural calcite($CaCO_3$) and industrial by-products and wastes, such as $Al(OH)_3,\;CaSO_4{\cdot}2H_2O$. The mixture of raw materials was fired at 20, 400, 600, $1200^{\circ}C$ for 1h and cooled rapidly in air. The cement replaced by 10 wt% $C_4A_3S$ expansive additives was investigated by the measurement of the hydration products and compressive strength, setting time, expansion at wet curing condition. $C_4A_3S$ was found in x-ray diffraction pattern over the temperature $1200^{\circ}C$. The setting time or the cement pastes added clinkers fired at different temperature was shorter than ordinary portland cement. The compressive strength was higher than the ordinary portland cement about 20~30%. The mainly hydration products were ettringite, and $Ca(OH)_2$. The expansion due to the formation of ettringite during hydration decreased the drying shrinkage of hardened cement rather than the ordinary portland cement.

• Journal of the Korean Ceramic Society
• /
• v.39 no.6
• /
• pp.540-549
• /
• 2002

In this work, the hydration behaviour of portland cement pastes containing fly ash, blast-furnace slag and silica fume is investigated by Impedance Spectroscopy(IS). As fly ash or blast-furnace slag was added to portland cement, the values of R$_{t(s+1)}$ and R$_{t(s+1)}$ were decreased in the early hydration period. It showed that hydration of cement containing blending components was slower than it of the reference cement paste with the same W/C ratio. However, the cement paste containing silica fume had a large value of R$_{t(s+1)}$ and R$_{t(int)}$due to very rapid pozzolanic reactivity of silica fume in the hydration time. In OPC-fly ash system, a characteristic plateau region appeared between straight-line and semicircle. The plateau region continued to grow in range with the content of fly ash and the hydration time.

• Corrosion Science and Technology
• /
• v.8 no.3
• /
• pp.110-115
• /
• 2009

At the onset of corrosion of steel in concrete, hydrogen ions usually evolve in the process of electrochemical reaction, thereby decreasing the pH of the pore solution, which can be buffered by cement hydration products, as being representatively illustrated by calcium hydroxide. Hence, a fall in the pH is dependent on properties of cement hydration (i.e. hydration products and degree of hydration). The present study tested acid neutralization capacity (ANC) of cementitious binders of OPC(Ordinary Portland Cement), 30% PFA(Pulverized Fuel Ash), 60% GGBS(Ground Granulated Blast Furnace Slag), 10% SF(Silica Fume) to quantify the resistance of cement matrix to a pH fall. Cement pastes were cast at 0.4 of a free W/C ratio with 1.5% chlorides by weight of binder in cast. Powder samples obtained crushed and ground specimen after 200 days of curing were diluted in still water combined with different levels of 1M nitric acid solution, ranging from 0.5 to 20 mol/kg. Then, the pH of diluted solution was monitored until any further change in the pH did not take place. It was seen that the pH of the diluted solution gradually decreased as the molar amount of nitric acid increased. At some particular values of the pH, however, a decrease in the pH was marginal, which can be expressed in the peak resistances to a pH fall in the ANC curve. The peaks occurred at the variations in the pH, depending on binder type, but commonly at about 12.5 in the pH, indicate a resistance of precipitated calcium hydroxide. The measurement of water soluble chloride at the end of test showed that the amount of free chloride was significantly increased at the pH corresponding to the peaks in the ANC curve, which may reflect the adsorption of hydration products to chlorides.